ZnO:Al thin film can be used as a transparent conducting oxide(TCO) which has low electric resistivity and high optical transmittance for the front electrode of amorphous silicon solar cells and display devices. This study of electrical, crystallographic and optical properties of Al doped ZnO thin films prepared by Facing Targets Sputtering (FTS), where strong internal magnets were contained in target holders to confine the plasma between the targets, is described. Optimal transmittance and resistivity was obtained by controlling flow rate of O$_2$ gas and substrate temperature. When the of gas rate of 0.3 and substrate temperature 200$^{\circ}C$ , ZnO:Al thin film had strongly oriented c-axis and lower resistivity(<10$\^$-4/Ω-cm).

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.27 no.8
• /
• pp.483-485
• /
• 2014

Transparent amorphous In-Si-O (ISO)/Ag/In-Si-O (ISO) has been reported for low emissivity (low-e) applications. Effective Si doping into the $In_2O_3$ matrix led to a completely amorphous ISO film as well as a low resistivity and a high optical transmittance. The optical and electrical performances were examined by measuring transmittance with a UV-VIS spectrophotometer and resistivity with a Hall effect measurement. Consequently, low-e glass with ISO/Ag/ISO showed a high transparency in the visible region and low emissivity in the infrared region, indicating that ISO is a promising amorphous transparent electrode for low-e glass.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.103-104
• /
• 2006

Transparent conductive oxide (TCO) are necessary as front electrode for increased efficiency of LED. In our paper, transparent conducting alminum-doped Zinc oxide films (AZO) were prepared by rf magnetron sputtering on glass (corning 1737) substrate, were then annealed at temperature $400^{\circ}C$ for 2hr. The smooth AZO films were etched in diluted HCL (0.5%) to examine the surface morphology properties as a variation of the time. The surface morphology of AZO films increased as a time. We observed texture structure of AZO thin film etched for 1min.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.239.2-239.2
• /
• 2016

Numerous studies and approaches have been performed for solar cells to improve their photoelectric conversion efficiencies. Among them, the study for electrode containing transparent conducting oxide (TCO) layers is one of issues as well as for the cell structure based on band theory. In this study, we focused on an interfacial layer between p-type silicon and indium tin oxide (ITO) well-known as TCO materials. According to current-voltage characteristics for the sample with the interfacial layers, the improvement of band alignment between p-type silicon and ITO was observed, and their ohmic properties were enhanced in the proper condition of deposition. To investigate cause of this improvement, spectroscopic ellipsometry and ultraviolet photoelectron spectroscopy were utilized. Using these techniques, band alignment and defect in the band gap were examined. The major materials of the interfacial layer are vanadium oxide and tungsten oxide, which are notable as a hole transfer layer in the organic solar cells. Finally, the interfacial layer was applied to silicon solar cells to see the actual behavior of carriers in the solar cells. In the case of vanadium oxide, we found 10% of improvement of photoelectric conversion efficiencies, compared to solar cells without interfacial layers.

• The Korean Journal of Ceramics
• /
• v.2 no.1
• /
• pp.1-10
• /
• 1996

Transparent conducting $SnO_2$-based thin films have been coated on float substrates such as fused quartz, and ceramic fiber cloths such as the Nexel and E-glass cloth from tin alkoxides by the sol-gel technique. Also, thin films of alternating layers of $SnO_2$ and $SiO_2$ have been fabricated by dip coating. The sheet resistance and average visible transmittance of the films were investigated in the aspect of the applications as transparent electrodes such as liquid crystal displays, photo-detectors and solar cells. The Nextel and E-glass cloths coated with antimony-doped tin oxide (ATO) had sheet resistance of as low as $20 \;ohm/{\Box}$ and $120ohm/\;{\Box}$, respectively. The promotion effects of additives as $La_2O_3$ and Pt on the ethanol gas sensing properties of the films were investigated in the aspects of the applications as an alcohol sensor and a breath alcohol checker. Possible evidence of quantum well effects in the oxide multilayers of $SnO_2$ and $SiO_2$ was investigated.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.297-297
• /
• 2010

Transparent conductive Oxide (TCO) is an essential material in the various optoelectronic applications as a transparent electrode, such as solar cells, flat panel displays and organic light emitting diodes. Currently, Indium tin oxide (ITO) is commonly used in industry due to its low electrical resistivity, high transmittance and high adhesion to substrate. However, ITO is expensive and should be prepared at high temperature, which makes it hard to use ITO in flexible devices. In this regard, Ga-doped ZnO is expected as an ideal candidate for replacing ITO.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.10
• /
• pp.923-929
• /
• 2008

On the piezoelectric polymer, PVDF (poly vinylidene fluoride), the transparent conducting oxide (TCO) electrode material thin film was deposited by roll to roll sputtering process mentioned as a mass product-friendly process for display application. The deposition method for ITO Indium Tin Oxides) as our TCO was DC magnetron sputtering optimized for polymer substrate with the low process temperature. As a result, a high transparent and good conductive ITO/PVDF film was prepared. During the process, especially, the gas mixture ratio of Ar and Oxygen was concluded as an important factor for determining the film's physical properties. There were the optimum ranges for process conditions of mixture gas ratio for ITO/PVDF From these results, the doping mechanism between the oxygen atom and the metal element, Indium or Tin was highly influenced by oxygen partial pressure condition during the deposition process at ambient temperature, which gives the conductivity to oxide electrode, as generally accepted. With our studies, the process windows of TCO for display and other application can be expected.

• Journal of Ceramic Processing Research
• /
• v.13 no.spc2
• /
• pp.394-397
• /
• 2012

In this work, we studied the influence of the dopant elements concentration on the properties of SnO2 thin films deposited by pulsed laser deposition. X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), Hall effect measurement and UV-Vis studies were performed to characterize the deposited films. XRD results showed that the films had polycrystalline nature with tetragonal rutile structure. FE-SEM micrographs revealed that the as deposited films composed of dense microstructures with uniform grain size distribution. All the films show n-type conduction and the best transparent conductive oxide (TCO) performance was obtained on 6 wt% Sb2O5 doped SnO2 film prepared at pO2 of 60mtorr and Ts of 500 ℃. Its resitivity, optical transmittance, figure of merit are 7.8 × 10-4 Ω cm, 85% and 1.2 × 10-2 Ω-1, respectively.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.67 no.1
• /
• pp.68-74
• /
• 2018

All transparent UV photodetector based on ZnO was fabricated with structure of NiO/ZnO/$SnO_2$/ITO by using RF and DC magnetron sputtering system. ZnO was deposited with 4 inch ZnO target (purity 99.99%) for a quality film. In order to build p-n junction up, p-type NiO was formed on n-type ZnO by using reactive sputtering method. The indium tin oxide (ITO) which is transparent conducting oxide (TCO) was applied as a transparent electrode for transporting electrons. To improve the UV photodetector performance, a functional $SnO_2$ layer was selected as an electron transporting and hole blocking layer, which actively controls the carrier movement, between ZnO and ITO. The photodetector (NiO/ZnO/$SnO_2$/ITO) shows transmittance over 50% as similar as the transmittance of a general device (NiO/ZnO/ITO) due to the high transmittance of $SnO_2$ for broad wavelengths. The functional $SnO_2$ layer for band alignment effectively enhances the photo-current to be $15{\mu}A{\cdot}cm^{-2}$ (from $7{\mu}A{\cdot}cm^{-2}$ of without $SnO_2$) with the quick photo-responses of rise time (0.83 ms) and fall time (15.14 ms). We demonstrated the all transparent UV photodetector based on ZnO and suggest the route for effective designs to enhance performance for transparent photoelectric applications.

• Korean Journal of Materials Research
• /
• v.29 no.5
• /
• pp.311-316
• /
• 2019

Transparent conducting electrodes are essential components in various optoelectrical devices. Although indium tin oxide thin films have been widely used for transparent conducting electrodes, silver nanowire network is a promising alternative to indium tin oxide thin films owing to its lower processing cost and greater suitability for flexible device application. In order to widen the application of silver nanowire network, the electrical conductance has to be improved while maintaining high optical transparency. In this study, we report the enhancement of the electrical conductance of silver nanowire network transparent electrodes by copper electrodeposition on the silver nanowire networks. The electrodeposited copper lowered the sheet resistance of the silver nanowire networks from $21.9{\Omega}{\square}$ to $12.6{\Omega}{\square}$. We perform detailed X-ray diffraction analysis revealing the effect of the amount of electrodeposited copper-shell on the sheet resistance of the core-shell(silver/copper) nanowire network transparent electrodes. From the relationship between the cross-sectional area of the copper-shell and the sheet resistance of the transparent electrodes, we deduce the electrical resistivity of electrodeposited copper to be approximately 4.5 times that of copper bulk.