• International Journal of Highway Engineering
• /
• v.19 no.2
• /
• pp.25-34
• /
• 2017

PURPOSES: The purpose of this paper is to evaluate interface performance while using various tack coat materials for asphalt overlay. METHODS : The evaluation was conducted with tracking test, permeability, and interface bond strength. Tracking test was conducted using an image processing technique, to investigate the susceptibility of the tack coat materials. BBS and pull-off test were conducted to evaluate bond strength. The permeability test was conducted to evaluate the effect of tack coat materials. RESULTS : Results reveal that the trackless tack coat material demonstrates less tracking compared to other materials. Moreover, both BBS and pull-off tests can effectively evaluate the bond strength at the interface. RSC-4 was measured less bond strength. Moreover, tack coat prevents water penetration through the surface and aids the extension of the surface life of asphalt pavement. CONCLUSIONS : Trackless tack coat demonstrated a high and consistent bond strength performance. The tack coat types demonstrate marginally different performance as function of curing times. Field applicability was tested based on visual observation. Therefore, these should be considered when trackless tack coat is slightly enhanced the pavement performance based on limited this study results. Finally, it is necessary to allow reasonable time for the tack coat to completely cure.

• International Journal of Highway Engineering
• /
• v.18 no.5
• /
• pp.1-9
• /
• 2016

PURPOSES : This study focuses on the evaluation of interface performance with varying surface texture and tack coat application in an asphalt overlay. METHODS : The evaluation is carried out in two phases: tracking test and interface bond strength test. Using an image processing tool, tracking test is conducted to evaluate the susceptibility of the tack coat material to produce excessive tracking during application. Using the pull-off test method, the bond strength test is performed to determine the ability of the interface layer to resist failure. RESULTS : Results show that the underseal application yields less tracking compared to other applications. However, the bond strength is barely within the minimum acceptable value. On the other hand, RSC-4 produces higher bond strength for all surface types, but the drying time is long, which produces excessive tracking. CONCLUSIONS : While underseal application may be suitable for a trackless condition, the bond strength is less appealing compared to the rest of the tack applications available. RSC-4 demonstrated a high and consistent bond strength performance, but more time is required for drying to avoid excessive tracking. Tack coat application and surface type combination produce varying results. Therefore, these should be considered when selecting suitable future tack coat application options.

• International Journal of Highway Engineering
• /
• v.16 no.6
• /
• pp.121-128
• /
• 2014

PURPOSES : The objective of this study is to evaluate the tack-coating material's properties using the bitumen bond strength(BBS) test and damping test as function of changed curing times. In this study, bonding strength tests were performed according to the curing time of tack coating materials. METHODS : In order to investigate bonding characteristic of tack coating materials, the Pneumatic Adhesion tensile Testing Instrument(PATTI) device is used to measure the bond strength between the tack coating materials and aggregate substrate based on the AASHTO TP-91. Also, damping test as in situ test was used to determine an appropriate traffic openting time for construction vehicle. Four different tack-coating materials were used in this study. The BBS tests were performed a one hour curing and testing temperatures of $5^{\circ}C$, $15^{\circ}C$, and $25^{\circ}C$. Damping test was conducted at 30min, 60min, 90min, and 120 min of curing times with temperatures of $20^{\circ}C$ and $30^{\circ}C$. RESULTS and CONCLUSIONS : The BBS test results show various bond strength as function of tack coat materials. At the same testing condition, A tack coat material shows almost two times higher than D tack coat materials although both materials are satisfied the criteria of material's physical properties. Also, Dampting test results shows similar trend with BBS test result. The damping test result was significantly changed as function of tack coat materials. Based on this study, the tack coating material's curing time is very important. Therefore, both curing time and the bond strength's characteristic has to be considered in standard specification.

• Resources Recycling
• /
• v.10 no.1
• /
• pp.32-41
• /
• 2001

Bond shear strengths of recycled asphalt concrete were evaluated under different tack coat applications. Regardless of the new and old mixtures, the bond shear strengths at $30^{\circ}C$ were increased by 10-20% than those at 1$0^{\circ}C$. The bond shear strengths of recycled asphalt concrete without tack coat showed very low ones. These are the main reasons for the frequent longitudinal interface crack in the field. The effect of tack coat curing time on bond shear strengths was inferior to the tack coat construction temperature.

• International Journal of Highway Engineering
• /
• v.17 no.2
• /
• pp.39-46
• /
• 2015

PURPOSES: The objectives of this study were to develop a new polymer-modified emulsion for application to tack coats and to evaluate its properties by comparing it with other types of asphalt emulsions, with the goal of providing an enhanced tack coat material for use in construction. METHODS: Modified asphalt binders were developed from using SBS and SBR latex in the laboratory, and their fundamental properties, such as their penetration index and PG grade, were evaluated. Based on the properties, a new tack coat material was developed. To evaluate the newly developed asphalt emulsion, the bonding strength between the two layers of HMA was measured by applying a uniaxial tensile test and shear test. For the tests, a total of four different conditions were applied to the specimens, including the developed asphalt emulsion, latex modified asphalt emulsion, conventional asphalt emulsion, and non-tack coating. RESULTS AND CONCLUSIONS: Overall, the developed asphalt emulsion exhibits the best bonding strength behavior among all of the three types. Also, the two types of polymer-modified emulsions were found to be better for application for use as a tack coat than a conventional emulsion. Especially, at a high temperature ($50^{\circ}C$), the conventional asphalt emulsion no longer acts as a tack coating material. Therefore, the polymer-modified emulsion should be considered for application to tack coat construction during the summer.

• International Journal of Highway Engineering
• /
• v.18 no.6
• /
• pp.137-143
• /
• 2016

OBJECTIVES : Bituminous materials, such as tack coat, are utilized between pavement layers for improving the bond strength in pavement construction sites. The standards regarding the application of bituminous material are not clearly presented in the Korean construction guideline without RS(C)-4. Hence, the objective of this study is to determine the optimum content of bituminous materials by analyzing interlayer shear strength (ISS) from the direct shear tester, which was developed in this research. The shear strength of tack coat was defined with the sort of bituminous materials. METHODS : The mixtures for the shear test were made using marshall mix design. The specimens were vertically and horizontally separated for the direct shear test. The separated specimens were bonded using bituminous material. The objectives of the experiment are to determine the performance of bond and shear properties resulting from slippage, rutting, shovel, and corrugation of asphalt pavements. A machine based on the Louisiana interlayer shear strength tester (LISST) of NCHRP Report-712 was developed to determine the ISS. The applied types of tack coat were RS(C)-4, AP-3, QRS-4, and BD-coat with contents of $0.3{\ell}/m^2$, $0.45{\ell}/m^2$, $0.6{\ell}/m^2$, and $0.8{\ell}/m^2$, respectively. RESULTS : Table 2 gives the results of the direct shear test using the developed shear machine. The BD-coat type indicated the highest average ISS value compared to the others. Between the surface and binder course, optimum tack coat application rates for AP-3, RS(C)-4, QRS-4, and BD-Coat were $0.6{\ell}/m^2$, $0.3{\ell}/m^2$, $0.6{\ell}/m^2$, and $0.45{\ell}/m^2$, respectively. These optimum contents were determined using the ISS value. CONCLUSIONS : The ISS values of AP-3, RS(C)-4, and QRS-4 showed similar tendencies when ISS increased in the range $0.3{\sim}0.6{\ell}/m^2$, while ISS decreased when the applied rate exceeded $0.6{\ell}/m^2$. Similarly, the highest ISS value of the BD-coat was observed when the applied rate was $0.45{\ell}/m^2$. However, shear strength was similar to the maximum value of ISS when the tack-coat application rate of BD-Coat exceeded $0.45{\ell}/m^2$.

• International Journal of Highway Engineering
• /
• v.19 no.2
• /
• pp.97-102
• /
• 2017

PURPOSES : Emulsified asphalt is critical for road construction. The objective of applying asphalt emulsion as an adhesive is to prevent the phenomenon of debonding between the upper and lower layers. The quantity and veriety of bituminous material can be varied according to the type of pavement and site conditions. The objective of this study is to reveal the optimum application rates of the emulsified asphalt materials by types of tack-coats using Interface Shear Strength(ISS). METHODS : In the research, emulsified asphalt was paved on the surface of the divided mixture. The specimens of paving asphalt emulsion were utilized to evaluate the bond strength of tack-coat materials. In the evaluation process, NCHRP Report 712 was utilized to investigate the Interface Shear Strength, which reflects the bond capacity of asphalt emulsion. Then, the optimum residual application rates by tack-coat types were determined using regression analysis. RESULTS :As a consequence of squared R values investigated from 0.7 to 1 as part of the regression analysis, the tendency of predicted ISS values was compared with the results. The optimum residual application rates of AP-3, RS(C)-4, QRS-4, and BD-Coat were determined to be $0.78{\ell}/m^2$, $0.51{\ell}/m^2$, $0.53{\ell}/m^2$, and $0.73{\ell}/m^2$, respectively, utilizing 4th regression analysis. CONCLUSIONS :Based on the result of this study, it was not feasible to conclude whether higher residual application of tack-coat material leads to improved bond capacity. Rather, the shearing strength varies depending on the type of pavement.

• Journal of the Korean Society of Hazard Mitigation
• /
• v.9 no.1
• /
• pp.27-32
• /
• 2009

The main objective of this study is to develop a test for measuring the bond shear strength between pavement layers. The research is also conducted to evaluate tack coat materials and application rate in porous pavement. The experiment includes using two types of emulsions (RSC-4, Modified Emulsion) and a asphalt binder type (HM-1). HM-1 was developed to be applied in porous pavement. The bond shear strengths were measured by a direct shear type device under various test conditions. The shear strength may not be appropriate in the evaluation of the bond shear strength, while the toughness of the test may be useful. In case of the tack coat application rate in porous pavement, RSC-4 has to be used a minimum amount of $0.8l/m^2$ and modified emulsion asphalt has to be applied a volume of use $0.5{\sim}0.6l/m^2$. HM-1, asphalt cement type, is far stronger bond shear strength than emulsified asphalt tack coat and had showed the excellent trackless property.

• International Journal of Highway Engineering
• /
• v.15 no.4
• /
• pp.85-94
• /
• 2013

PURPOSES: The performance of tack coat, commonly used for layer interface bonding, is affected by application rate and curing time. In this study, bonding strength tests were performed according to the application rate and curing time of asphalt emulsion. Based on finding from this study, optimum application rates and curing times are proposed. METHODS: In order to investigate bonding characteristic of asphalt emulsion, tests were performed on both asphalt concrete pavement and portland concrete pavement. Also, asphalt emulsions were tested at the application rate of 0, 0.2, 0.4, 0.6, and $0.8{\ell}/m^2$ and at the curing time of 0, 0.5, 1, 2, and 24 hours. Pull-off test and shear bonding strength test, which commonly used for bonding strength measurement of asphalt emulsion, were adopted for this study. To assess field performance under different testing condition, asphalt emulsions were applied to in-service pavement. Throughout coefficient of determination analysis between material index properties from asphalt emulsion and mechanical response from bonding strength tests, performance correlativity was analyzed. RESULTS: Test results show that optimum application rate for asphalt overlay on asphalt concrete pavement (AOA) and asphalt overlay on concrete pavement (AOC) was $0.4{\sim}0.5{\ell}/m^2$ and $0.3{\sim}0.5{\ell}/m^2$, respectively. According to the curing time increment, tensile strength and shear strength of AOC were increased to 22~44% and 20~39%, respectively. AOA case also show strength increment in tensile strength (42%) and shear strength (9%). We tested the applicability of tack coat materials at the field sites, and our findings demonstrated that the bonding (for D and E) and rapid curing (for B, C, and D, E) performances were superior than others. Among material index properties, there was a high correlation between penetration ratio and bonding strength test result. CONCLUSIONS : Result show that interlayer bonding strength was affected by asphalt emulsion type, application rate and curing time. AOC required slightly higher application ($0.1{\ell}/m^2$) than AOA. Both AOA and AOC cases show higher strength at longer curing time. Up to 2hours of curing, rapid strength increments were observed, but strength increment ratio was decreased after 2hours of curing. From the observed correlation between penetration ratio and bonding strength, it is expected that penetration ratio can be used as one of important factors affecting bonding strength analysis.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.41 no.6
• /
• pp.737-744
• /
• 2021

Spray paving minimizes material lost during the construction or repair of a road surface, and it can be done in conjunction with tack coating. This approach involves applying the asphalt mixture at the same time as spraying the tack coat by attaching a spraying device to the asphalt paver. When applying an asphalt overlay to an aged concrete surface, it is important to ensure the adhesion performance between different material properties. Accordingly, there is a need for a tack coat that can be applied by spray paving and that exhibits good adhesive performance on different materials. In this study, bonding strength tests under various conditions were performed to evaluate the basic performance of a tack coat developed for use with a spray paver. The bonding performance of the tack coat was observed to be affected by curing conditions and material lost during construction. The test results also showed that the tensile and shear bonding strengths of the developed tack coat were 1.21 and 1.99 times higher than those of a conventional one, respectively. As a result, the developed tack coat is considered suitable for application to spray paving.