• Proceedings of the Korean Institute of Navigation and Port Research Conference
• /
• 2013.06a
• /
• pp.134-135
• /
• 2013

In this study, the physical properties and antifouling were investigated to make the Marine growth antifouling coatings by blending of synthesized silicone resin and pigment with a low surface tension. To examine the film properties and foul release of the prepared coatings, film specimens were prepared with the prepared coatings and anti corrosion coatings. The test results showed that the silicone type antifouling coatings had very excellent antifouling properties rather than any other coatings because of the coating films had followed the low surface tension and elasticity, and prevention of adhesion for marine growth and mechanical adhesions.

• Corrosion Science and Technology
• /
• v.17 no.6
• /
• pp.257-264
• /
• 2018

Anti-graffiti coatings have become more important. These layers must guarantee excellent corrosion protection properties, and graffiti must be easily removable, without reducing protection and aesthetic properties. In this study, anti-graffiti and corrosion behavior of two anti-graffiti polyurethane powder coatings were studied. These layers were deposited on aluminum substrate, with two different surface finishes, smooth, and wrinkled. The action of four different removers are investigated. Graffiti were drawn on coatings by means of red acrylic spray paint. Methyl-ethyl-ketone (MEK) and a "commercial" remover were the most effective solvents, in terms of graffiti removal capability, producing limited change in aesthetical surface aspect for smooth finishing. The wrinkled surface was less resistant. Corrosion protection properties, after removal action and contact with the remover, were evaluate by electrochemical impedance spectroscopy. After approximately 5 hours, coatings were no longer protective due to formation of defects. To simulate the weathering effect, UV-B cyclic test (4 hours of UV exposure followed by 4 hours of saturated humidity at $50^{\circ}C$) were performed for 2000 hours. Gloss and color changes were measured, and electrochemical impedance spectroscopy measurements were performed after aging and graffiti removal.

• Journal of the Korean institute of surface engineering
• /
• v.46 no.6
• /
• pp.242-247
• /
• 2013

Zr-Al-N coatings were synthesized by the hybrid coating system combining arc ion plating and DC magnetron sputtering from a Zr and an Al target in argon-nitrogen atmosphere, respectively. By changing the power applied on the Al cathodes, the Zr-Al-N coatings with various Al contents were deposited. The microstructure and chemical compositions of the Zr-Al-N coatings were studied by X-ray diffraction (XRD), high-resolution transmission electron microscopy (HRTEM). With increasing of Al content in the coatings, the solid solution (Zr, Al)N crystallites were observed in the Zr-Al-N coatings. The nanohardness of the Zr-Al-N coatings exhibited a maximum value of 42 GPa for the Zr-Al (7.9 at.%)-N, and decreased with further increase in Al content in the coatings. The oxidation and corrosion behavior of the Zr-Al-N coatings revealed better properties compared than those of ZrN coatings due to the formation of a solid solution.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.6
• /
• pp.691-694
• /
• 1996

Two models of scratch testers developed recently are applied to the adhesion measurement of thin coatings. In both models the critical load is determined from the frictional irregularity when coated surface is broken in the scratching process. One model is effective for coatings thicker than 1m and the other for thin coatings down to $0.1\mu\textrm{m}$. The mechanism and the measurement principle of these testers are described. High sensitivity and good reproducibility of the measurement are attained primarily by the employment of new detection devices. These testers are even more useful for the quality control and the inspection of commercial products of coatings because only a small area of specimen is required for the test.

• Journal of the Korean institute of surface engineering
• /
• v.47 no.4
• /
• pp.168-173
• /
• 2014

The paper presents the comparative results of TiAlN coatings deposited by DC and pulsed DC asymmetric bipolar magnetron sputtering systems. The results show that, with the decreasing duty cycle and increasing pulse frequency, the coating morphology changes from a columnar to a dense structure, with finer grains. Pulsed sputtered TiAlN coatings showed higher hardness, higher residual stress, and smaller grain sizes than dc prepared TiAlN coatings. Moreover residual stress of pulsed sputtered TiAlN coatings increased on increasing pulse frequency. Meanwhile, the surface roughness decreased continuously with increasing pulsed DC frequency up to 50 kHz.

• Journal of the Korean institute of surface engineering
• /
• v.48 no.4
• /
• pp.136-141
• /
• 2015

The paper presents the comparative results of NbN coatings deposited by DC and pulsed DC asymmetric bipolar magnetron sputtering systems. The results show that, with the decreasing duty cycle and increasing pulse frequency, the coating morphology changes from a columnar to a dense structure, with finer grains. The Pulsed sputtered NbN coatings showed higher hardness, higher residual stress, and smaller grain sizes than those of DC prepared NbN coatings. Moreover residual stress of pulsed sputtered NbN coatings increased on increasing pulse frequency. Meanwhile, the surface roughness decreased continuously with increasing pulsed DC frequency up to 50 kHz.

• Journal of the Korean institute of surface engineering
• /
• v.21 no.2
• /
• pp.39-46
• /
• 1988

Corrosion behavior of 5-26wt% Ni-Zn electrodeposited alloys was investigated by means of dipping electrochmical polarization measurement and galvanic coupling test. The weight loss and anodic polarization curve of coatings were measured by means of dipping and polarization measurement respectively. The galvanic protection effect of alloy coatings was measured by galvanic coupling test and the surface morpholgy of coatings was observed after corrosion testing. Our findings support thous of previous investigations showing that ${\gamma}$single phase coatings, while galvanic pprotection effect of dual phase coatings improved in comparison with ${\gamma}$single phase coating. The formation of colony in coating of ${\gamma}$and η+${\gamma}$ dual phsae caused the localized corrsion and increased the corrosion rate of the Ni-Zn coating.

• Journal of the Korean institute of surface engineering
• /
• v.43 no.4
• /
• pp.165-169
• /
• 2010

$Ni-Al_2O_3$ nanocomposite coatings were fabricated by conventional electrodeposition technique using nickel sulfamate bath. Effect of plating parameters on electrodeposition of $Ni-Al_2O_3$ nanocomposite were studied. The properties of the nano composite were investigated by using SEM, XRD, and Vicker's microhardness test. The results demonstrated that $Al_2O_3$ incorporation in the composite coatings was found to be increased by increasing stir rate and $Al_2O_3$ content in plating bath. Microhardness of the composite coatings was also increased with increasing content of the nano particles in the plating bath. The surface morphologies of the nanocomposite coatings were found to be varied with varying pH, current densities as well as alumina content in the plating bath.

• Journal of the Korean institute of surface engineering
• /
• v.47 no.6
• /
• pp.323-329
• /
• 2014

Effects of sealant and sealing procedure on corrosion resistance of high velocity oxy-fuel (HVOF) sprayed coatings were studied. HVOF-sprayed CrC-20NiCr coatings were sealed using three commercial sealants based on phenolics and epoxy. Penetration depth of sealants, measured by fluorescent microscope technique, was between $19{\mu}m$ and $340{\mu}m$ depending on sealant, sealing condition or sealing procedure. It was found that sealing on rotation status was more effective than that on stationary specimen due to the Coriolis effect of fluid in pores of the coating. From the CASS results, corrosion resistance of properly sealed CrC-20NiCr coatings was equal to that of hexa-valent chromium plating.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2005.11a
• /
• pp.183-184
• /
• 2005

Four different coatings deposited using cold spray process were studied with two different powder agglomerating techniques (spray d교 and evaporated powder) and using $TiO_2$ nano-sized powders with and without a 10wt% addition of ZnO. Characterization was performed by SEM, XRD and roughness test. Also the photocatalytic effect of the coatings was evaluated. Although the change of powder preparation techniques and the addition of ZnO into $TiO_2$ did not show appreciable variations in the surface morphology and Anatase phase transformation, it did show influence on the surface roughness of the coating, the highest roughness being found in the coatings made by spray powder prepared method. Regarding the photocatalytic effect it was observed that the using the spray dry coating and the addition of ZnO are promoter of purification at higher rates.