• Journal of the Korea Concrete Institute
• /
• v.25 no.1
• /
• pp.99-106
• /
• 2013

Concrete materials subjected to impact by high velocity projectiles exhibit responses that differ from those when they are under static loading. Projectiles generate localized effects characterized by penetration of front, spalling of rear and perforation as well as more widespread crack propagation. The magnitude of damage depends on a variety of factors such as material properties of the projectile, impact velocity, the mass and geometry as well as the material properties of concrete specimen size and thickness, reinforcement materials type and method of the concrete target. In this study, penetration depth of front, spalling thickness of rear and effect of spalling suppression of concrete by fiber reinforcement was evaluated according to compressive strength of concrete. As a result, it was similar to results of the modified NDRC formula and US ACE formula that the more compressive strength is increased, the penetration depth of front is suppressed. On the other hand, the increase in compressive strength of concrete does not affect spalling of rear suppression. Spalling of rear is controlled by the increase of flexural, tensile strength and deformation capacity.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.749-752
• /
• 2005

Normally, the degradation of concrete member exposed to fire is largely dependent on the fire scale and fire condition. With all ensuring the fire resistance structure as a method of setting the required cover thickness to fire, the RC is significantly affected from the standpoint of its structural stability that the compressive strength and elastic modulus is reduced by fire. Thus, this study is concerned with experimentally investigating fire resistance of high strength-light weight concrete. From the test result, high strength-light weight concrete is happened explosive spalling. The decrease of cross section caused by explosive spalling made sharp increasing gradient of inner temperature.

• Journal of the Korea Institute of Building Construction
• /
• v.14 no.3
• /
• pp.223-229
• /
• 2014

In this study, the fire resistance of high strength concrete with organic fibers and polymer powder (PW) was investigated. Two types of the specimens of ${\phi}100{\times}200mm$ and $300{\times}300{\times}600mm$ sizes were prepared. As a result of the test, it was found that the fiber-to-PW mixing ratio of 1:1 achieved the highest fluidity. Further, it was found that the mixing ratios of PP 0.05% + PW 0.05%, PNY 0.05% + PW 0.05% was sufficient to protect the high strength concrete from spalling. For the mock-up specimens of $300{\times}300{\times}600mm$ size, if the required amounts of fibers were added in the concrete. the concrete spalling was resisted. Likewise, in the case of the polymix (PM) together with PW, all the tested specimens were satisfactory for fire resistance performance.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2006.05a
• /
• pp.5-8
• /
• 2006

High strength concrete has been increasingly used in high rue building and it is very obvious re consider fire resistance performance of that. Unlike the normal strength concrete, high strength concrete in sudden elevating temperature at fire is susceptible to spalling with severe explosion and surface split, due to high density of concrete. In order to endure the spalling, inner space temperature of concrete should be control less than certain point. Therefore this study investigated the influence of covering materials on high strength concrete finishing spray-on materials of fiber composite spray mortar(FCSM). Both polypropylene(PP) and polyvinyl alcohol(PVA) fiber were used in this test. Test showed that concrete, covering 18mm mortar containing PVA fiber and confining metal lath 2.3mm thickness, decreased 50% of main bar ambient temperature. compared with control concrete. In addition, concrete covering 18mm mortar without fiber caused falling of covering materials and then it was exposed in elevating temperature. As a result, spatting of the concrete occurred same as control concrete. However, concrete covering spray-on mortar containing PVA or PP fiber resisted spatting occurrence.

• Journal of the Korea Concrete Institute
• /
• v.14 no.4
• /
• pp.449-456
• /
• 2002

Recently, the application of high strength and high performance concrete has been gradually increased as an important construction material for high rise and huge scaled construction. However, high performance concrete has undesirable characteristics of spalling subjected to high temperature due to its dense microstructure content. A spalling by fire brings surface failure and falling off concrete member. It is considered that spalling by fire should be taken into account for the safety of the concrete structure under fire. Therefore, in this paper, tests are carried out using high performance concrete containing polypropylene(PP) fiber in order to improve the fire resistance performance. PP fiber contents and member sizes are varied. According to experimental results, as for the influence of PP fiber contents, all the test specimens without PP fiber show entire failure in W/C of 35％, while they show nearly sound shape except some kinds of surface fracture in W/C of 55％. When PP fiber is contained more than 0.07％, favorable prevention effects of spatting by fire are obtained. As for the effects of test specimens size, it tends to increase the possibilities of spatting by fire as test specimens become larger. And spatting by fire at the edge of test specimens occurs more frequently than at the surface of test specimens. Residual compressive and tensile strength shows 45∼65 ％ of its original strength at W/C of 35％, and 30∼40％ at W/C of 55 ％.

• Journal of the Korea Institute of Building Construction
• /
• v.13 no.5
• /
• pp.465-473
• /
• 2013

Concrete is an outstanding material in terms of its impact and blast resistance performance. However, there a limitation of concrete is its risk of collapse due to the brittle failure and spalling. Increasing the thickness of members was used as a method to enhance the protective performance of concrete, despite the resulting inefficient space. To solve this problem, different types of fiber reinforced concrete were developed. Recently, another type of fiber reinforced concrete is also being developed and applied as a material that offers protection against impacts and blasts by increasing the flexural toughness of concrete. In this study, the test was conducted to evaluate the impact resistance performance of fiber reinforced concrete and mortar according to impact of high-velocity projectile. A concrete T-wall was also tested to evaluate its protective performance from fragment by 155mm-thick artillery shell. The test results revealed that improving flexural strength through fiber reinforcement inhibited cracks and spalling of rear, and spalling of front by high-velocity impact. As such, it is expected to improve the protective performance of the T-wall and reduce the thickness of the member.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.945-948
• /
• 2008

Fire resistance is a measure of the ability of building element to resist a fire. For concrete columns, the fire resistance depends on many factors, including strength, density, and moisture content of concrete, fire intensity, column size and shape, reinforcement detail, loading condition, and aggregate type etc. However, it is well-known that the high strength concrete (HSC) is more susceptible to spalling than normal strength concrete (NSC) and the behaviour of HSC column exposed to fire is significantly affected by the spalling. Recently, as one of the measures to reduce the spalling of HSC, incorporating polypropylene(PP) fiber has been investigated and successfully used in construction fields. However, the establishment of assessment method on the fire resistance of HSC column is very important as well as the improvement of fire performance of HSC. In this study, the variations on the fire resistance of HSC column with assessment methods was studied for the columns controlled the concrete spalling by PP fiber.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.16 no.3
• /
• pp.311-320
• /
• 2014

High strength concrete is not only vulnerable to the occurrence of spalling which generates the loss of cross-section in concrete structures but produces faster degradation in its mechanical properties than normal strength concrete in the event of fire. This study aims to evaluate fire resistance of high strength segment concrete with PET fibers mixed to prevent spalling under ISO834 (2hr) and RABT fire curve. As results, the samples without PET fibers show the concrete loss up to the depth of about 8 cm and 9.5 cm from the surface exposed to fire under ISO834 and RABT fire curve respectively. The samples mixed with PET fiber of 0.1% show no spalling under ISO834 fire curve and the spalled thickness of 6.5 cm under RABT fire curve after the fire tests. Finally, the sample mixed with PET fiber of 0.2% shows no spalling under RABT fire curve. The results indicate that the suitable amounts of PET fiber for securing fire resistance performance of this high strength segment concrete are 0.1% under ISO834 fire curve and 0.2% under RABT fire curve. However, even though spalling does not occur, it is necessary to repair the deterioration of concrete up to 4 cm from the surface exposed to fire after fire.

• Magazine of the Korea Concrete Institute
• /
• v.17 no.3 s.86
• /
• pp.40-44
• /
• 2005

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.11a
• /
• pp.481-484
• /
• 2006

This study investigates the engineering and fire endurance properties of ultra high strength concrete. The mixture proportions with water to binder ratios (W/B) of 0.15 and 0.25 consist of various adding ratios, such as 0, 0.05, 0.1, 0.15, 0.2, 0.25 and 0.3 percent respectively, of polypropylene (PP) fiber. As for the parameters of specimens, fluidity, compressive strength and unloading fire test were carried out. Test showed that an increase of fiber contents had the favorable properties in fire endurance performance; specimens in W/B 15% required 0.3vol% of PP fiber and specimens in W/B 25% needed only 0.1vol% to prevent spalling.