• 한국고분자학회:학술대회논문집
• /
• 한국고분자학회 2006년도 IUPAC International Symposium on Advanced Polymers for Emerging Technologies
• /
• pp.359-359
• /
• 2006

This study deals with development of new bio-based polymeric materials from epoxidized soybean oil (ESO). The curing of ESO in the presence of organophilic montmorillonite produced an oil polymer-clay nanocomposite ("green nanocomposite") showing flexible property. A green nanocomposite (oil polymer-silica nanocomposite) coatings were synthesized by an acidcatalyzed curing of ESO with 3-glycidoxypropyltrimethoxysilane. The curing of ESO in the presence of a biodegradable plastic, poly(caprolactone), produced a composite with semi-IPN structure. The mechanical properties of the composite was much superior to those of polyESO. These new oil-based materials have large potential for applications in various fields.

• 폴리머
• /
• 제26권6호
• /
• pp.767-777
• /
• 2002

본 실험에서는 4관능성 에폭시 수지 (4EP)와 생분해성 modified aliphatic polyester (MAP) 블렌드의 경화 거동, 열안전성, 유변학적 특성, 그리고 기계적 특성을 살펴보았다. DSC 측정 결과, 경화 활성화 에너지 ( $E_{a}$ )는 4EP에 대한 MAP의 비율이 10 wt%로 증가함에 따라 증가하였다. 이는 4EP와 MAP 사이의 분자상호작용이 증가하였기 때문으로 사료된다. 열안정성과 관련있는 분해 활성화 에너지 ( $E_{t}$ )는 Coats-Redfern 방법을 이용하여 구하였으며 MAP의 함량비가 10에서 30 wt% 내에서 증가하였다. 이는 블렌드 시스템에서의 가교 밀도의 증가 때문으로 사료된다. 유변학적 특성은 레오미터를 이용하여 등온 조건하에서 검토하였고, 겔화 시간과 경화 온도를 이용한 Arrhenius 방정식을 적용하여 가교 활성화 에너지 ( $E_{c}$ )를 검토한 결과, $E_{a}$ 와 유사한 경향을 나타내었다. 기계적 계면특성인 파괴인성 ( $K_{IC}$ )은 시편의 semi-IPN구조 거동으로 고찰하였다.

• Journal of the Korean Wood Science and Technology
• /
• 제48권4호
• /
• pp.431-449
• /
• 2020

기존 연질 구조의 하이드로겔은 낮은 기계적 강도로 인하여 생의학 분야에서 응용이 제한된다. 본 연구에서는 이러한 단점을 극복하기 위해서 폴리비닐알코올(PVA: poly(vinyl alcohol))기반 하이드로겔에 셀룰로오스 나노크리스탈(CNCs)을 첨가하여 CNCs가 기계적 특성 및 약물전달 효율에 미치는 영향을 확인하였다. 제조된 하이드로겔은 FT-IR 분석으로 아세탈 및 알데히드 결합으로 가교결합된 망상구조(semi-IPN: semi-interpenetrating polymer network)로 합성된 것이 확인되었다. CNCs 함량이 증가될수록 수분 흡수 및 팽윤도가 감소했으며, 점탄성은 증가하였다. 또한 CNCs의 첨가는 약물 로딩량의 증가와 약물 방출량의 지속성을 향상시켰다. 이러한 결과는 CNCs를 하이드로겔에 첨가하는 것이 하이드로겔의 약물전달 효율성 및 기계적 특성을 개선시키는 좋은 대안이 될 수 있음을 보여주었다.

• 접착 및 계면
• /
• 제7권2호
• /
• pp.12-18
• /
• 2006

산업과 기술이 발전하면서 점점 더 향상된 기능과 성능이 우수한 접착제를 요구하고 있다. 고무수지의 장점, viscoelastic 한 점을 이용하고 단점을 보완하기 위하여 반구조 형태의 점착 접착제를 개발하였다. 또 용매를 이용하지 않아 요즈음에 문제가 되는 환경에도 부담을 줄이는 친환경성 점착제라 할 수 있다. 한편에 epoxy functional group과 다른 한편에 hydroxyl functional group을 함유하고 있는 poly(ethylene/butylene)과 한편에 hydroxyl functional group를 가지고 있는 poly(ethylene/butylene)에 UV 개시제를 이용하여 interpenetrating polymer network (IPN) 구조를 형성하고 여기에 점착 부여 수지로써 hydrocarbon resin을 첨가하여 고온에서 고무 수지가 갖고 있는 단점을 보완하였다.

• Journal of the Korean Wood Science and Technology
• /
• 제41권2호
• /
• pp.134-140
• /
• 2013

UV curing was introduced via a chemical treatment by adding small amounts of a hexafunctional acrylic monomer and a photoinitiator to improve the mechanical properties of PLA. This study also employed a semi-interpenetrated structured polymer network through the process of UV-curing. The UV curing behaviors were investigated using FTIR-ATR spectroscopy and gel fraction determination. Also, the tensile strength was investigated with different hexafunctional acrylic monomer contents and UV doses. The results showed that the crosslinking of UV-induced chemically treated PLA started at a low content of hexafunctional acrylic monomer, resulting in a significant improvement of the mechanical properties compared to those of neat PLA due to crosslinking.

• 한국전기전자재료학회논문지
• /
• 제16권11호
• /
• pp.994-1000
• /
• 2003

In this study, gel polymer electrolytes (GPE) with semi-interpenerating network of poly (methyl methacrylate) and hexanediol dimethacrylate were synthesized and their electrochemical performances were evaluated. LiCoO$_2$/GPE/graphite cells were prepared and their performances depending on discharge currents and temperatures were evaluated. The precursor containing 5 vol% curable mixture had a low viscosity relatively. GPE showed good electrochemical stability up to potential of 4.8 V vs. Li/Li$\^$+/. Ionic conductivity of the gel polymer electrolyte at room temperature and -20$^{\circ}C$ was ca. 5.9 and 1.4${\times}$10$\^$-3/ Scm$\^$-1/, respectively. LiCoO$_2$/GPE/graphite cells showed good rate capability, low-temperature performance and cycleability.

• 폴리머
• /
• 제33권1호
• /
• pp.39-44
• /
• 2009

폴리페닐렌에테르[PPE, poly(phenylene ether)]를 기저수지로 사용하고, 가교제로 N,N'-m-phenylene-dimaleimide(PDMI), 난연제로 decabromodiphenylethane을 첨가하여 고분자 기판을 제작하였으며, 가교제와 난연제가 기판소재의 유전특성 등 물리적 특성에 미치는 영향을 고찰하였다. 개시제의 유무에 따른 PDMI의 열경화 특성을 DSC를 이용하여 분석하였으며, 이를 바탕으로 PPE-PDMI 테스트 조성을 설계하였다. 복합물 시트를 필름 코터로 성형한 후, 진공가압적층하여 테스트 기판을 제작하고, FDMI와 난연제의 함량에 따른 유전율, 유전손실, peel 강도, 납 내열성 및 난연성을 평가하였다. 유전율과 유전손실은 PDMI와 난연제의 함량에 따라 대체로 증가하는 경향을 나타내었으나, 납 내열성과 난연성은 개선된 결과를 나타내었다. Peel 강도는 PDMI가 10 wt% 이상 첨가되면 1 kN/m 이상의 높은 값을 나타내었지만, 난연제의 첨가량에 따라서는 소폭 감소하는 경향을 보였다. Gel content 측정결과로부터, PPE-PDMI의 반응 메카니즘은 semi-IPN 구조의 형성보다는 PPE와 PDMI의 crosslinking에 의한 망상구조 형성에 더 가까운 것으로 판단되었다. 최종적으로 1 GHz에서 유전율이 2.52$\sim$2.65, 유전손실이 0.002 미만으로 작은 고주파 대역용 고분자 복합체 기판소재를 얻을 수 있었다.