• Korean Journal of Metals and Materials
• /
• v.48 no.6
• /
• pp.565-569
• /
• 2010

We report on the characteristics of indium-oxide-doped ZnO (IZO) ohmic contact to p-GaN. The IZO ohmic contact layer was deposited on p-GaN by a Roll-to-Roll (RTR) sputter method. IZO contact film with a thickness of 360, 230 and 100 nm yielded an ohmic contact resistance of $4.70{\times}10^{-4}$, $5.95{\times}10^{-2}$, $4.85{\times}10^{-1}\;{\Omega}cm^{2}$ on p-GaN when annealed at $600{^{\circ}C}$ for 1 min under a nitrogen ambient, respectively. While the transmittance of IZO film with a thickness of 360 nm slightly increased in the wavelength range of 380-800 nm after annealing, the transmittance rapidly increased up to 80% after annealing at $600{^{\circ}C}$ in the wavelength range of 380~430 nm because the crystallization of IZO film and created Ga vacancies near the p-GaN surface region were affected by the annealing. These results indicate that ohmic contact resistance and transmittance of the IZO films improved.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.380-381
• /
• 2007

This paper reports on the deposition conditions and properties of ITO films used as electrode layer in a organic light emitting diodes on a PET substrate. The deposition technique employed was specially designed roll-to-roll sputtering. The oxide was deposited at room temperature in an argon and oxygen plasma on a transparent conducting ITO layer on a PET film. The influence of deposition parameters such as DC power, working pressure and oxygen partial pressure has been investigated, in order to obtain the best compromise between a high deposition rate and adequate electro-optical properties. Electrical and optical properties of ITO films were analyzed by Hall measurement examinations with van der pauw geometry at room temperature and UV/Vis spectrometer analysis, respectively. In addition, the structural properties and surface smoothness were measured by x-ray diffraction and scaning electron microscopy, respectively. From optimized ITO films grown by roll-to-roll sputter system, good electrical$(6.44{\times}10^{-4}\;{\Omega}-cm)$ and optical(above 86 % at 550 nm) properties were obtained. Also, the ITO films exhibited amorphous structure and very flat surface beacause of low deposition temperature.

• Journal of the Korean Ceramic Society
• /
• v.51 no.3
• /
• pp.190-196
• /
• 2014

Flexible $TiO_2$ films were deposited as dielectric materials for high-energy-density capacitors on polyethylene terephthalate (PET) substrates using a roll-to-roll sputtering method. Both the growth behavior and electrical properties of the flexible $TiO_2$ films were dependent on the sputtering pressure and $O_2$/Ar gas ratio during the sputtering process. All $TiO_2$ films had an amorphous structure regardless of the sputtering conditions due to the low substrate temperature. Microstructural characteristics such as the surface morphology and roughness of the films degraded with an increase in the sputtering pressure and $O_2$ gas concentration. The $TiO_2$ films deposited at a low pressure showed better electrical properties than those of films deposited at a high pressure. The $TiO_2$ films prepared at 10 mTorr exhibited a dielectric constant of approximately 90 at 1 kHz and a leakage current density of $5{\sim}6{\times}10^{-7}A/cm^2$ at 3 MV/cm.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.181.1-181.1
• /
• 2016

플렉서블 디스플레이 및 태양전지가 지향하고 있는 저가, 고속의 대량 생산을 위해서는 필름을 기반으로 하는 연속 공정에 의한 대량의 ITO 박막의 증착이 필수적이다. 이로 인해 롤투롤(roll-to-roll) 스퍼터링법을 이용한 ITO 박막의 연속 증착 공정이 차세대 플렉서블 디스플레이 및 태양전지의 대량 생산을 위한 해결책으로 각광받고 있다. 그러나 대부분의 폴리머 필름의 경우 증착 시 발생되는 열 또는 플라즈마에 의해 방출되는 수분과 유기 솔벤트 같은 오염 물질들에 의한 ITO 박막의 특성 저하와, 낮은 열적 안정성을 가지는 기판 특성상 고온(>$200^{\circ}C$)에서 증착이나 후 열처리를 할 수가 없기 때문에, 낮은 저항과 높은 광투과도 특성을 가지는 ITO 필름을 제작하기 위한 공정 최적화가 필요하다. 따라서, 본 연구에서는 롤투롤 스터링법으로 PET 필름 위에 Sn함량이 각각 3, 5, 7.5 10% 도핑된 ITO 타겟을 사용하여 ITO 박막을 증착 하였고, 전기적 광학적 특성을 조사하여 롤투롤 스퍼터링법으로 우수한 전기 전도도와 광투과도 특성을 가지는 ITO/PET 필름의 증착 조건을 최적화 하였다. 또한, ITO 증착 시 필름에서 발생하는 수분에 의한 ITO 박막의 특성 저하 현상에 대하여 조사하였다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.244.1-244.1
• /
• 2014

디스플레이 패널의 터치 스크린에 가장 널리 사용되는 ITO 전극은 사용자의 눈에 전극 면이 시각적으로 구분되지 않도록 해야 한다. 따라서 최근에는 ITO 전극 면이 구분되지 않도록 하기 위해 다층 박막으로 이루어진 인덱스 매칭(index matching, IM) 기술을 이용하여 ITO 전극 필름을 제작하고 있다. 이러한 인덱스 매칭된 ITO 필름은 기판이나 공정 조건, 인덱스 매칭 층의 물질 종류에 따라 ITO 박막의 전기적 광학적 특성이 각각 다르게 나타나기 때문에 이에 대한 많은 연구가 이루어지고 있다. 본 연구에서는 롤투롤 스퍼터링(roll to roll sputtering) 방법으로 고굴절과 저굴절이 순차적으로 코팅 처리된 PET 기판 위에 ITO 박막을 증착하여 IM-ITO 필름을 제작하고 전기적 광학적 특성을 관찰하였다. 이를 위해 습식(wet) 코팅 방법으로 저굴절층과 고굴절층을 PET 필름 위에 코팅하여 IM층을 제작한 PET 필름 위에 ITO 박막을 증착하고, $150^{\circ}C$로 후 열처리를 하여 인덱스 매칭된 ITO 필름을 제작하였다. 제작된 필름은 GIXD를 이용하여 박막의 구조와 결정성을 조사하였고, 면저항 측정기와 홀측정 장치를 이용하여 전기적 특성을 관찰하였다. 그리고 분광광도계와 탁도(haze) 측정기를 이용하여 광학적 특성을 조사하였다. 본 연구를 통해 롤투롤 스퍼터링 방법으로 유무기 복합막으로 구성된 IM-ITO 박막의 전기적 광학적 구조적 특성에 대해 보고하고자 한다.

• Korean Journal of Materials Research
• /
• v.21 no.5
• /
• pp.255-262
• /
• 2011

This paper has relatively high technical standard and experimental skill. The fabrication of TCO film with high transparency, low resistance and low chromaticity require exact control of several competing factors. This paper has resolved these problems reasonably well, thus recommended for publication. Indium tin oxide(ITO) thin films were by D.C. magnetron roll-to-roll sputter system utilizing ITO and $SiO_2$ targets of ITO and $SiO_2$. In this experiment, the effect of D.C. power, winding speed, and oxygen flow rate on electrical and optical properties of ITO thin films were investigated from the view point of sheet resistance, transmittance, and chromaticity($b^*$). The deposition of $SiO_2$ was performed with RF power of 400W, Ar gas of 50 sccm and the deposition of ITO, DC power of 600W, Ar gas of 50 sccm, $O^2$ gas of 0.2 sccm, and winding speed of 0.56m/min. High quality ITO thin films without $SiO_2$ layer had chromaticity of 2.87, sheet resistivity of 400 ohm/square, and transmittance of 88% and $SiO_2$-doped ITO Thin film with chromaticity of 2.01, sheet resistivity of 709 ohm/square, and transmittance of more than 90% were obtained. As a result, $SiO_2$ was coated on PET before deposition of ITO, their chromaticity($b^*$) and transmittance were better than previous results of ITO films. These results show that coating of $SiO_2$ induced arising chromaticity($b^*$) and transmittance. If the thickness of $SiO_2$ is controlled, sheet resistance value of ITO film will be expected to be better for touch screen. A four point probe and spectrophotometer are used to investigate the properties of ITO thin films.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.213-213
• /
• 1999

현재 LCD용 기판재료는 ITO/glass를 전극으로 사용하고 있다. 그러나 유리기판은 무겁고 깨지기 쉽기 때문에 사용상 곤란한 점이 많다. 최근 flexible하고 가공성 및 생산성이 우수한 플라스틱한 ITO를 성막하여 EL용, Touch panel, plastic LCD용 사용하려는 시도로, roll-to-roll 연속 스퍼터링에 의한 ITO성막공정에 대한 연구가 최근 활발하게 이루어지고 있다. 폴리머는 유리에 비해 Tg 온도가 낮고, 기판으로부터의 수분 및 여러 종류의 가스방출이 심하기 때문에 유리와는 달리 ITO막의 제조에 있어 큰 차이점이 있다. 따라서, 폴리머에 반응성 스퍼터링을 하기 위해서는 표면처리가 중요한 변수가 되며, roll to roll sputter로 ITO 필름을 얻기 위해서는 폭과 길이 방향으로 균일한 막을 얻는 것이 중요하다. 두께 75$\mu\textrm{m}$, 폭 190mm, 길이 400m로 권취된 광학용 Polyethylene terephthalate(PET:Tg:8$0^{\circ}C$)위에 In-10%Sn의 합금타겟과 Unipolar pulsed DC power supply를 사용하여 반응성 마그네트론 스퍼터링 방법으로 0.2m/min의 속도로 연속 스퍼터링 하였다. PET를 Ar/O2 혼합가스로 플라즈마 전처리를 한 후, AFM, XPS를 이용하여 효과를 분석을 하였고, 성막전에 가스방출을 막기 위해 TiO를 코팅하였다. Pilot 연속 생산공정에서 재현성을 위해 PEM(Plasma Emission Monitor)의 optical emission spectroscopy를 이용, 금속과 산화물의 천이구역에서 sprtter된 I/Sn 이온과 산소 이온의 반응에 의한 최적의 플라즈마의 강도값을 입력하여 플라즈마의 radiation을 검출하고, 스퍼터링 공정중 실질적인 in-situ 정보로 이용하였다. PEM을 통하여 In/Sn의 플라즈마 강도변화를 조사하였다. 초기 In/Sn의 플라즈마 강도(intensity)는 강도를 100하여, 산소를 주입한 결과, plasma intensity가 35 줄어들었고, 이때 우수한 ITO 박막을 얻을 수 있었다. Pulsed DC power를 사용하여 아크 현상을 방지하였다. PET 상에 coating 된 ITO 박막의 표면저항과 광투과도는 4-point prove와 spectrophotometer를 이용하여 분석하였고, AES로 박막의 두께에 따른 성분비를 확인하였다. ITO 박막의 광투과도는 산소의 유량과 sputter 된 In/Sn ion의 plasma emission peak에 따라 72%-92%까지 변화하였으며, 저항은 37$\Omega$/$\square$ 이상을 나타내었다. 박막의 Sn/In atomic ratio는 0.12, O/In의 비율은 In2O3의 화학양론적 비율인 1.5보다 작은 1.3을 나타내었다.

• Korean Journal of Materials Research
• /
• v.18 no.1
• /
• pp.32-37
• /
• 2008

The electrical, optical, structural and surface properties of an indium tin oxide (ITO) film grown on a flexible PET substrate using a specially designed roll-to-roll (R2R) sputtering system as a function of the DC power, $Ar/O_2$ flow ratio, and rolling speed is reported. It was observed that both the electrical and optical properties of the ITO film on the PET substrate were critically dependent on the $Ar/O_2$ flow ratio. In addition, x-ray diffraction examination results showed that the structure of the ITO film on the PET substrate was an amorphous structure regardless of the DC power and the $Ar/O_2$ flow ratio due to a low substrate temperature, which was maintained constant by a main cooling drum. Under optimized conditions, ITO film with resistivity of $6.44{\times}10^{-4}{\Omega}-cm$ and transparency of 86% were obtained, even when prepared at room temperature. Furthermore, bending test results exhibited that R2R-grown ITO film had good flexibility which would be applicable to flexible displays and solar cells.

• Journal of the Korean Vacuum Society
• /
• v.16 no.2
• /
• pp.79-90
• /
• 2007

Prototype of $800{\ell}$ vacuum web coater (Vic Mama) consisting of ion source with low energy less than 250 eV for high speed surface modification and 4 magnetron sputter cathodes was designed and constructed. Its performance was evaluated through fabricating the adhesiveless flexible copper clad laminate (FCCL). Pumping speed was monitored in both upper noncoating zone pumped down by 2 turbo pumps with 2000 l/sec pumping speed and lower surface modification and sputter zone vacuumed by turbo pumps with 450 1/sec and 1300 1/sec pumping speed respectively. Ion current density, plasma density, and uniformity of ion beam current were measured using Faraday cup and the distribution of magnetic field and erosion efficiency of sputter target were also investigated. With the irradiation of ion beams on polyimide (Kapton-E, $38{\mu}m$) at different fluences, the change of wetting angle of the deionized water to polyimide surface and those of surface chemical bonding were analyzed by wetting anglometer and x-ray photoelectron spectroscopy. After investigating the deposition rate of Ni-Cr tie layer and Cu layer was investigated with the variations of roll speed and input power to sputter cathode. FCCL fabricated by sputter and electrodeposition method and characterized in terms of the peel strength, thermal and chemical stability.