• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.501-504
• /
• 1999

In the shallow trench isolation(STI) chemical mechanical polishing(CMP) process, the key issues are the optimized thickness control within- wafer-non-uniformity, and the possible defects such as nitride residue and pad oxide damage. These defects after STI CMP process were discussed to accomplish its optimum process condition. To understand its optimum process condition, overall STI related processes including reverse moat etch, trench etch, STI filling and STI CMP were discussed. It is represented that the nitride residue can be occurred in the condition of high post CMP thickness and low trench depth. In addition there are remaining oxide on the moat surface after reverse moat etch. It means that reverse moat etching process can be the main source of nitride residue. Pad oxide damage can be caused by over-polishing and high trench depth.

• Proceedings of the KIEE Conference
• /
• 2006.10a
• /
• pp.103-104
• /
• 2006

$Pb(Zr,Ti)O_3(PZT)$ is very attractive ferroelectric materials for ferroelectric random access memory (FeRAM) applications because of its high polarization ability and low process temperature. However, Chemical Mechanical Polishing (CMP) pressure and velocity must be carefully adjusted because FeRAM shrinks to high density devices. The contaminations such as slurry residues due to the absence of the exclusive cleaning chemicals are enough to influence on the degradation of PZT thin film capacitors. The surface characteristics of PZT thin film were investigated by the change of process parameters and the cleaning process. Both the low CMP pressure and the cleaning process must be employed, even if the removal rate and the yield were decreased, to reduce the fatigue of PZT thin film capacitors fabricated by damascene process. Like this, fatigue characteristics were partially controlled by the regulation of the CMP process parameters in PZT damascene process. And the exclusive cleaning chemicals for PZT thin films were developed in this work.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.39-42
• /
• 2002

Recently, CMP (chemical mechanical polishing) technology has been widely used for global planarization of multi-level interconnection for ULSI applications. However, COO (cost of ownership) and COC (cost of consumables) were relatively increased because of expensive slurry. In this paper, we have studied the possibility of recycle of reused silica slurry in order to reduce the costs of CMP slurry. The post-CMP thickness and within-wafer non-uniformity(WIWNU) were measured as a function of different slurry composition. As a experimental result, the performance of reused slurry with annealed silica abrasive of 2 wt% contents was showed high removal rate and low non-uniformity. Therefore, we propose two-step CMP process as follows In the first-step CMP, we can polish the thick and rough film surface using remaked slurry, and then, in the second-step CMP, we can polish the thin film and fine pattern using original slurry. In summary, we can expect the saving of high costs of slurry.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.9
• /
• pp.759-764
• /
• 2003

Recently, CMP (chemical mechanical polishing) technology has been widely used for global planarization of multi-level interconnection for ULSI applications. However, COO (cost of ownership) and COC (cost of consumables) were relatively increased because of expensive slurry. In this paper, we have studied the possibility of recycle of roused silica slurry in order to reduce the costs of CMP slurry. The post-CMP thickness and within-wafer non-uniformity (WIWNU) wore measured as a function of different slurry composition. As an experimental result, the performance of reused slurry with annealed silica abrasive of 2 wt％ contents was showed high removal rate and low non-uniformity. Therefore, we propose two-step CMP process as follows , In tile first-step CMP, we can polish the thick and rough film surface using remaked slurry, and then, in the second-step CMP, we can polish the thin film and fine pattern using original slurry. In summary, we can expect the saying of high costs of slurry.

• Journal of Sasang Constitutional Medicine
• /
• v.10 no.1
• /
• pp.269-284
• /
• 1998

The purpose of this study was to investigate the effect of ILIB(Intravenous Laser Irradiation of blood) on Meridian-Heart Circulation CMP and Hyperlipidemia. Circulatory symptom of 20 patients was treated with ILIB. After 10 times' treatment, changes of total cholesterol, HDL-cholesterol, triglyceride and Meridian-Heart Circulation CMP value were observed. The results were as follows : 1. In observation of Meridian-Heart Circulation CMP value, significant increase was observed in both pre-ID generation and post-ID generation. So, distinctive observation between pre-ID generation and post-ID generation became not relatively significant. 2. In observation of Meridian-Heart Circulation CMP value, significant increase was observed in both left and right. So, distinctive observation between left and right became not relatively significant. 3. In observation of Meridian-Heart CMP value, significant increase was not observed in control group, but significant increase close to normal value was observed in treatment group after treatment of Intravenous He-Ne Laser Irradiation. 4. In observation of Meridian-Circulation CMP value, significant increase was not observed in control group, but significant increase close to normal value was observed in treatment group after treatment of Intravenous He-Ne Laser Irradiation. 5. In concentration of plasma total cholesterol and plasma triglyceride, significant decrease was not observed in control group, but significant increase was observed in treatment group after treatment of Intravenous He-Ne laser Irradiation. 6. Significant concentration change of plasma HDL-cholesterol was not observed in both control group and treatment group. From above results, it was thought that Intravenous He-Ne Laser Irradiation was significant effect on heart circulatory system in human body.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07a
• /
• pp.235-238
• /
• 2004

본 연구는 반도체소자 제조공정에 적용되는 CMP공정 중 LPP(Landing Plug Poly) Contact간의 소자 분리를 위해 진행되는 LPP CMP의 후 세정 과정에서 유발되는 방사형 Defect 제거에 관한 내용이다. 방사형 Defect은 LPP CMP 후에 노출되는 BPSG, Poly, Nitride Film과 연마재로 사용되는SiO2 입자, 후 세정과정에서 적용되는 SC-1, DHF, $NH_4OH$ Chemical과 Brush와의 상호작용에 의해 발생되며, Cleaning시의 산성 분위기 하에서 각 물질간의 pH와 Zeta Potential의 차이에서 기인한다. 이 Defect을 제거하기 위해 LPP CMP후에 Film 표면에 노출되는 각 물질의 표면 특성과 CMP 후 오염입자의 흡착과 재 흡착에 영향을 미치는 Electrostatic force와 Van der Waals force, PVA Brush에 의한 Mechanical force의 상호작용을 고려하여 최적 후 세정 조건을 제시 하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.537-537
• /
• 2008

Copper (Cu) has been widely used for interconnection structure in intergrated circuits because of its properties such as a low resistance and high resistance to electromigration compared with aluminuim. Damascene processing for the interconnection structure utilizes 2-steps chemical mechanical polishing(CMP). After polishing, the removal of abrasive particles on the surfaces becomes as important as the polishing process. In the paper, buffing process for the removal of colloidal silica from polished Cu wafer was proposed and demonstrated.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.05b
• /
• pp.171-174
• /
• 2000

We have investigated the CMP slurry properties of silicate oxide thin films surface on CMP cleaning process. The metallic contaminations by CMP slurry were evaluated in four different oxide films, such as plasma enhanced tetra-ethyl-ortho-silicate glass(PE-TEOS), $O_3$ boro-phospho silicate giass( $O_3$-BPSG), PE-BPSG, and phospho-silicate glass(PSG). All films were polished with KOH-based slurry prior to entering the post-CMP cleaner. The Total X-Ray Fluorescence(TXRF) measurements showed that all oxide surfaces are heavily contaminated by potassium and calcium during polishing, which is due to a CMP slurry. The polished $O_3$-BPSG films presented higher potassium and calcium contaminations compared to PE-TEOS because of a mobile ions gettering ability of phosphorus. For PSG oxides, the slurry induced mobile ion contamination increased with an increase of phosphorus contents.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.2
• /
• pp.131-136
• /
• 2000

We have investigated the slurry induced metallic contaminations of undoped and doped silicate oxides surface on CMP cleaning process. The metallic contaminations by CMP slurry were evaluated in four different oxide films, such as plasma enhanced tetra-ethyl-orthyo-silicate glass(PE-TEOS), O3 boro-phos-pho-silicate glass(O3-BPSG), PE-BPSG, and phospho-silicate glass(PSG). All films were polished with KOH-based slurry prior to entering the post-CMP cleaner. The Total X-Ray fluorescence(TXRF) measurements showed that all oxide surfaces are heavily contaminated by potassium and calcium during polishing which is due to a CMP slurry. The polished O3-BPSG films presented higher potassium and calcium contaminations compared to PE-TEOS because of a mobile ions gettering ability of phosphorus. For PSG oxides, the slurry induced mobile ion contamination increased with an increase of phosphorus contents. In addition, the polishing removal rate of PSG oxides had a linear relationship as a function of phosphorus contents.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.366-367
• /
• 2006

In general, HF chemistry lifts off the particles during scrubbing after polishing and effectively removes particles. It is sometimes impossible to apply HF chemistry on W plug due to the degradation of electrical characteristics of a device. In this paper, a post W CMP cleaning process is proposed to remove residue particles without applying HF chemistry. After W CMP, recessed plugs are created, therefore they easily trap slurry particles during CMP process. These particles in recessed plug are not easy to remove by brush scrubbing when $NH_4OH$ chemistry is used for the cleaning because the brush surface can not reach the recessed area of plugs. Buffing with oxide slurry was followed by W CMP due to its high selectivity to W. The buffing polishes only oxide slightly which creates higher plug profiles than surrounding oxide. Higher profiles make the brush contact much more effectively and result in a similar particle removal efficiency even in $NH_4OH$ cleaning to that in HF brush scrubbing.