• Textile Coloration and Finishing
• /
• v.32 no.3
• /
• pp.121-127
• /
• 2020

The analysis method of relative adsorption of disperse dyes on impregnated polyurethane resin and polyester fiber separately was investigated. The solvents for extracting the dyes from polyurethane resin and polyester fiber were determined by acetone and DMF, respectively. By extracting the dyed fibers with acetone at room temperature within 30 minutes, the dyes adsorbed only on the polyurethane resin could be extracted. And then by additional extracting the same fabrics with DMF at 95℃ for longer than 1 hour, the dyes adsorbed on polyester fabrics was extracted. This means that the dyes adsorbed on polyurethane and polyester could be extracted separately and that relative adsorption of the dyes on the both components could be analyzed quantitatively. Using this analysis method, the relative adsorption of a disperse dye was investigated after reduction clearing with various conditions.

• Journal of the Korean Wood Science and Technology
• /
• v.39 no.2
• /
• pp.156-162
• /
• 2011

To evaluate the bonding performance of reinforced glulam, the textile type of glass fiber and aramid fiber, and the sheet type of glass fiber reinforced plastic (GFRP) and carbon fiber reinforced plastic (CFRP) were used as reinforcements. The reinforced glulam was manufactured by inserting reinforcement between the outmost and middle lamination of 5ply glulam. The types of adhesives used in this study were polyvinyl acetate resins (MPU500H, and MPU600H), polyurethane resin and resorcinol resin. The block shear strengths of the textile type in glass fiber reinforced glulam using MPU500H and resorcinol resin were higher than 7.1 N/$mm^2$, and these glulams passed the wood failure requirement of Korean standards (KS). In case of the sheet types, GFRP reinforced glulams using MPU500H, polyurethane resin and resorcinol resin, and CFRP reinforced glulams using MPU500H and polyurethane resin passed the requirement of KS. The textile type of glass fiber reinforced glulam using resorcinol resin after water and boiling water soaking passed the delamination requirement of KS. The only GFRP reinforced glulam using MPU500H after water soaking passed the delamination requirement of KS. We conclude that the bonding properties of adhesive according to reinforcements are one of the prime factors to determine the bonding performance of the reinforced glulam.

• Journal of the Korean Applied Science and Technology
• /
• v.32 no.4
• /
• pp.623-630
• /
• 2015

Prepared polyurethane resin for buffalo leather coating on surface was synthesized with addition reaction glycerol which had different mole ratio. Mechanical properties of the synthesized polyurethane resin were measured by the SEM, FT-IR, UTM. Growing concerns in the evnironment-friendly polymer resin, we have synthesized low late obtained solvent water dispersion resin to be coating on buffalo leather. The increase of aliphatic trihydric alcohol glycerol mole %, abrasion resistance and tensile strength had demonstrated reduce properties. On the contrary, elongation and flexibility properties had highly increased. In the result of toluene solvent resistance, there was no effect of increased or decreased by the ratio of glycerol mole %.

• Journal of the Korean Applied Science and Technology
• /
• v.32 no.1
• /
• pp.100-107
• /
• 2015

Prepared polyurethane resin for vegetable leather coating on surface was synthesized with glycerol which had different mole ratio. Mechanical properties of the synthesized polyurethane resin were measured by the SEM, FT-IR, UTM. Growing concerns in the evnironment-friendly polymer resin, we have synthesized low late obtained solvent water dispersion resin to be coating on vegetable leather. The increase of aliphatic trihydric alcohol glycerol mole %, abrasion resistance and tensile strength had highly stronger in intensity and longer durability. On the contrary, demonstrated reduce properties of elongation and flexibility. In the result of toluene solvent resistance, there was no effect of increased or decreased by the ratio of glycerol mole %.

• Textile Coloration and Finishing
• /
• v.12 no.1
• /
• pp.61-67
• /
• 2000

This study was carried out to develope antimicrobial artificial suede by coating with water soluble polyurethane resin and the copolymer of N,N'-dialkyl-N,N'-dialkyl ammonium chloride (DADAAC) and acrylamide as a antimicrobial additve. The copolymer of DADAAC and acrylamide was synthesized by free radical initiation and intra-intermolecular propagation, and the prepared copolymers had sufficient compatibility with water soluble polyurethane resin. The MIC values of the prepared copolymers and antimicrobial characteristics of the artificial suede coated by polyurethane were evaluated. With the increase in the proportion of DADAAC, which is antimicrobially active part in the DADAAC/acrylamide copolymers, the MIC value becomes lower. The MIC value of DADAAC-AA (1 : 1) copolymer is below 30 ppm against S. aureus, and below 90 ppm against K pneumoniae. The artificial suede coated by water soluble polyurethane resin with 1.0% owl concentration of DADAAC/acrylamide copolymer has good antimicrobial fastness as to show colony reduction of above 90% and 80% against S. aureus and K. pneumoniae respectively in the shake flask test after 10 times of washing, and above 95% and 85% after 10 times of dry-cleaning. The elastic recovery of coated suede fabric is not affected up to 1.0% owf concentration of DADAAC-AA copolymer in the polyurethane coating.

• Textile Coloration and Finishing
• /
• v.30 no.4
• /
• pp.321-328
• /
• 2018

Wet polyurethane resin was synthesized by using polytrimethylene ether glycol prepared from 1,3-propanediol produced by fermentation from corn sugar as bio polyol and polyether-polyol(PTMG). Physical properties and cell characteristics by wet coagulation were investigated using the synthesized wet polyurethane resin. The tensile strength of wet polyurethane resin decreased with increasing content of bio polyol as copolymer polyol, but it tended to increase elongation at break and tear strength. As a result of thermal characteristic analysis, it was found that the glass transition temperature was slightly increased as the content of bio polyol increased. As a result of comparing the cell characteristics by the wet coagulation method, it was found that the shape of the cell was good when the ether polyol and the bio polyol were used alone.

• Journal of Adhesion and Interface
• /
• v.19 no.1
• /
• pp.5-12
• /
• 2018

The purpose of this study is to evaluate the adhesive properties of polyurethane mixed aqueous dispersions by omitting the primer, dealing with the preparation of skins for synthetic leather with excellent adhesion by omitting the pre-treatment process. The two-component mixed polyurethane water dispersion was prepared by synthesizing an ester-based polyurethane resin (PU-T) and a carbonate-based polyurethane resin (PU-C) to obtain the final resin. As a result of measuring the peel strength of the adhesive specimens omitting the pre-treatment agent, it was confirmed that the state adhesive strength (ethylene vinyl acetate (middle): $4.2kg_f/cm$ and rubber (outsole): $4.4kg_f/cm$) there was. This makes it possible to omit the pre-treatment process which has been indispensably used in the shoe manufacturing process, thereby reducing the process time and reducing the amount of volatile organic compounds (VOCs) generated in the pre-treatment product, resulting in environmentally advantageous.

• Journal of the Korean Applied Science and Technology
• /
• v.36 no.4
• /
• pp.1358-1364
• /
• 2019

The mechanical properties of Heavy duty resin of synthetic polyurethane-epoxy resin for stainless steel were measured by SEM, FT-IR, tensile properties, and specific mass loss by EIS analysis, etc. As interest in eco-friendly medium coatings increased, the Heavy duty coatings were synthesized for various metals such as stainless steel composed of Polyol, MDI, water bored Epoxy resin, filling agent, silicon surfactant, catalyst etc. The coatings of synthetic Heavy duty resin were increased tensile strength due to various temperature change, and the low-Specific Mass Loss was measured in a highly electrolytic solution. In conclusion, the Heavy Duty coatings composed of polyurethane and waterbored Epoxy resin were synthetic microstructure with cross linkage can be good material for coating of anticorrosion of metal substrates such as stainless steel.

• Journal of Adhesion and Interface
• /
• v.16 no.1
• /
• pp.22-28
• /
• 2015

In this study, Waterborne polyurethanes (WPU) using Epoxy group were synthesized with polyester polyol, epoxy resin, 4,4-dicyclohexylmethane diisocyanate ($H_{12}MDI$), dimethylol propionic acid (DMPA) to improve the hydrolysis resistance and adhesion. In addition, the properties of the synthesized waterborne polyurethane was evaluated through DSC, UTM, adhesion strength. Tg of the synthesized waterborne polyurethane is shown in the vicinity of $-50^{\circ}C$. Tg were increased with as epoxy resin contents increased. The tensile strength was increased as the content of epoxy resin increases, elongation was decreased. Optimum adhesion and hydrolysis-resistance strength were obtained when polyol : epoxy ratio was 99 : 1.

• Journal of Adhesion and Interface
• /
• v.11 no.1
• /
• pp.35-40
• /
• 2010

In this study, solvent based polyurethane (PU) adhesives were prepared with the hydrocarbon resin and the acrylic modified hydrocarbon resin contents. The solvent based PU adhesive were increased with increasing tackifier concentration. The surface state of films showed good compatibility with increasing the PX-95 concentration but A-1100 series didn't present homogeneous phase more than 10 phr. Mechanical strength and peel strength were maximum at 5 phr tackifier concentration especially PX-95 series in solvent based PU adhesive.