Preparation and Adhesion Characteristics of Binary Blended Waterborne Polyurethane

이성분계 혼합 폴리우레탄 수분산체의 제조 및 접착 특성 연구

  • Kim, Eun Ji (Department Korea Institute of Footwear & Leather Technology(KIFLT)) ;
  • Park, In Kyu (Department Korea Institute of Footwear & Leather Technology(KIFLT)) ;
  • Park, Jae Hyung (Department Korea Institute of Footwear & Leather Technology(KIFLT))
  • Received : 2017.12.04
  • Accepted : 2018.02.26
  • Published : 2018.03.31
Download PDF
⟨ Previous Next ⟩

Abstract

The purpose of this study is to evaluate the adhesive properties of polyurethane mixed aqueous dispersions by omitting the primer, dealing with the preparation of skins for synthetic leather with excellent adhesion by omitting the pre-treatment process. The two-component mixed polyurethane water dispersion was prepared by synthesizing an ester-based polyurethane resin (PU-T) and a carbonate-based polyurethane resin (PU-C) to obtain the final resin. As a result of measuring the peel strength of the adhesive specimens omitting the pre-treatment agent, it was confirmed that the state adhesive strength (ethylene vinyl acetate (middle): $4.2kg_f/cm$ and rubber (outsole): $4.4kg_f/cm$) there was. This makes it possible to omit the pre-treatment process which has been indispensably used in the shoe manufacturing process, thereby reducing the process time and reducing the amount of volatile organic compounds (VOCs) generated in the pre-treatment product, resulting in environmentally advantageous.

본 연구는 선처리제 공정을 생략하고 우수한 접착 특성을 가지는 합성피혁용 스킨(skin) 수지제조에 관한 것으로 이성분계 혼합 폴리우레탄 수분산체를 제조하여 이에 대한 선처리제(primer)를 생략한 접착 시편의 접착특성을 평가하는 것이다. 이성분계 혼합 폴리우레탄 수분산체의 제조는 에스터(ester)계 폴리우레탄 수지(PU-T)와 카보네이트(carbonate)계 폴리우레탄 수지(PU-C)를 각각 합성하고 이를 배합함으로써 최종 수지를 얻었다. 선처리제를 생략한 접착시편의 접착강도 측정결과, 우수한 상태접착강도 (Ethylene vinyl acetate(중창): $4.2kg_f/cm$, 고무(겉창) : $4.4kg_f/cm$)를 가짐을 확인할 수 있었다. 이는 신발 제조 공정에서 필수불가결하게 사용되었던 선처리제(primer) 공정을 생략가능하게 함으로써 공정의 단축과 선처리제(primer)에서 발생되는 휘발성유기화합물 (VOCs)의 감소를 가져와 친환경적인 장점을 지닌다.

Keywords

References

  1. M. J. Choi, D. H. Kim and G. N. Kim, "Studies on the surface changes and adhesion of EVA foam by plasma treatment", Adhesion and Interface, 9, 9-12, (2008).
  2. F. Garbassi, M. Morra and E. Occhiello, "Polymer surfaces: from physics to technology", John Willey and Sons, Chichester, pp.35, (1994).
  3. R. A. Pethrick, "Polymer Surface Modification and Characterization", C. M. Chan Ed., Hanser Publishers, New York, pp.20, (1993).
  4. D. H. Park, D. H. Moon and C. U. Lee, "Study on Bond Used in Shoes Manufacturing Industry", J. Assoc. Korean Ind. Hyg.,1, 200-213, (1991).
  5. C. S. Yoo and J. H. Chun, "Application of polyurethane as adhesive", Polym. Sci. Tech., 10, 578, (1999).
  6. J. S. Shin, J. M. Park, Y. H. Lee and H. D. Kim, "Preparation and Properties of Eco-friendly Waterborne Polyurethane-urea Primer for Thermoplastic Polypropylene Applied to Automobile Interiors", Clean Technology, 20, 232-240, (2014). https://doi.org/10.7464/ksct.2014.20.3.232
  7. M. C. Delpech, and F. M. B. Coutinho, "Waterborne anionic polyurethanes and poly(urethane-urea)s: influence of the chain extender on mechanical and adhesive properties", Polymer Testing, 19, 939-952, (2002).
  8. D. H. Shao, J. J. Huang, G. N. Chen, J. T. Yeh and K. N. Chen, "Thermal and combustion behaviors of aqueous-based polyurethane system with phosphorus and nitrogen containing curing agent" Polym. Degrad. Stab., 65, 359-371, (1999). https://doi.org/10.1016/S0141-3910(99)00025-7
  9. C. Hepburn, "Polyurethane Elastomer," Elsevier, London, pp.122-173, (1982).
  10. D. Dieterich, "Aqueous Emulsions, Dispersions and Solution of Polyurethane; Synthesis and Properties", Progress in Organic Coatings, 9, 281-340, (1981). https://doi.org/10.1016/0033-0655(81)80002-7
  11. S. L. Cooper and A. V. Tobosky, "Properties of Linear Elastomeric Polyurethanes", J. Appl. Polym. Sci., 10, 1837-1844, (1966). https://doi.org/10.1002/app.1966.070101204
  12. S. Mohanty and N. Krishnamurti, "Synthesis and characterization of aqueous cationomeric polyurethanes and their use as adhesives", J. Appl. Polym. Sci., 62, 1993-2003, (1996). https://doi.org/10.1002/(SICI)1097-4628(19961219)62:12<1993::AID-APP3>3.0.CO;2-D
  13. S. M. Lai and S. D. Liu, "Properties and Preparation of Thermoplastic Polyurethane/Silica Hybrids Using a Modified Sol-Gel Process", Polym. Eng. Sci., 47, 77-86, (2007). https://doi.org/10.1002/pen.20669
  14. Y. T. Shin, M. G. Hong, J. J. Choi, W. K. Lee, G. B. Lee, B. W. Yoo, M. G. Lee and K. C. Song, "Preparation of Waterborne Polyurethane/Silica Nanocomposites Using Tetraethylorthosilicate", Korean Chem. Eng. Res., 48, 428-433, (2010).
  15. Y. T. Shin, M. G. Hong, J. J. Choi, W. K. Lee, G. B. Lee, B. W. Yoo, M. G. Lee and K. C. Song, "Preparation and Properties of Aminosilane Terminated Waterborne Polyurethane", Korean Chem. Eng. Res., 48, 434-439, (2010).
  16. H. K. Shin, M. W. Huh and N. S. Yoon, "Fabrication of Silica-containing Breathable Waterproof Polyurethane Dispersion Film", Textile Coloration and Finishing, 27, 126-131, (2015). https://doi.org/10.5764/TCF.2015.27.2.126
  17. E. J. Kim, I. K. Paik, J. H. park, "Waterborne Polyurethane Skin Resin Used in the Fabrication of Synthetic Leather Adhesive", Textile Science and Engineering, 54, 28-35, (2017). https://doi.org/10.12772/TSE.2017.54.028
  18. T. Kiyotsukuri, T. Masuda, N. Tsutsumi and W. S. M. Nagata, "Poly(Ethylene-Terephthalate) Copolymers with a Smaller Amount of Poly(Ethylene Glycol)S and Poly(Butylene Glycol)s", Polymer, 36, 2629-2635, (1995). https://doi.org/10.1016/0032-3861(95)91211-O
  19. T. Kiyotsukuri, T. Masuda and N. Tsutsumi, "Preparation and properties of poly(ethylene terephthalate) copolymers with 2,2-dialkyl-1,3- propanediols", Polymer, 35, 1274-1279, (1994). https://doi.org/10.1016/0032-3861(94)90023-X