• Journal of the Semiconductor & Display Technology
• /
• v.15 no.2
• /
• pp.81-86
• /
• 2016

Moisture vapor transmission rate (MVTR) is an important item for many applications of polymer breathable thin film. To determine the optimum values of the process parameters, it is essential to find their influence on The significance of six important process parameters namely, extruder cylinder temperature, extruder speed, extruder dies temperature, cooling roll temperature, stretching ratio, stretching roll temperature on breathable film strength of polymer extrusion was determined. Moreover, this paper presents the application of Taguchi method and analysis of variance (ANOVA) for maximization of the breathable film MVTR influenced by extrusion parameters. The optimum parameter combination of extrusion process was obtained by using the analysis of signal-to-noise ratio. The conclusion revealed that extruder speed and stretching ratio were the most influential factor on the film strength, respectively. The best results of film MVTR were obtained at higher extruder speed and stretching ratio.

• Proceedings of the Polymer Society of Korea Conference
• /
• 2006.10a
• /
• pp.369-369
• /
• 2006

Compatibilizers contribute to many processes in polymer industry, such as manufacturing polymer blends and composites. They are usually designed to be block or graft form which is combined in polar and non-polar parts in the first synthesis process level, for example, the general form of maleic anhydride (MA) as a compatiblizer is a grafted counterpart. However, the process of making the compatibilizer is related to the first synthesis level and it has some problems, such as high cost, poor processability, limitation on use and properties, and so on. So, in order to improve its poor processability and overcome the limitation on use, we developed compatibilizers which have various chemical forms by high intensity ultrasound and super critical fluid nitrogen in polymer melt reactive extrusion.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1997.10a
• /
• pp.585-590
• /
• 1997

Conventional foaming process has defects such as lower mechanical properties than ur~foaming material due to non-uniform cell distribution and environmental pollution problem caused by chemical blowing agency. So, a new foaming process such as Microcelluar plastics has been introduced to use inactive gases as a foaming agency. In order to apply Microcellular plastics for mass production process system such as extrusion, injection molding and blow molding, it needs to predict the change in material properties of polymer according to the amount of meltingas. In Polymer molding applying Microcelluar plastics, the change of viscosity among several material properties is the most important factor. Therefore, this paper is aimed to establish the method which not only finds out but also predicts the change of viscosity of ABS(Acrylonitri1e Butadiene Styrene) resin according to inert gas amount in extrusion molding.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.18 no.6
• /
• pp.585-589
• /
• 2009

Extruder is divided to greatly three part at extrusion process. First, by hopper(Hopper) second, barrel(Barrel) with Screw that is point of extruder and third that is raw material supply wealth extrusion into dies(DIES) Part that decide shape of do product greatly divide. Hopper is role that distribute in raw material supply wealth (Feeding zone) of Screw preserving raw material in state of high quality how at extrusion process, and make distributed raw material as Screw in barrel rotates and 3 stage and inflicting heat and pressure raw material melting(Melting) state. And raw material of melting state Screw's measuring stoker(Metering zone) whereabouts anaphora do and product is completed through pipe channel of dies. Dies that is the most important as Screw in extrusion is part that is last part of melting state process of raw material and causes huge effect in quality of product. If more than design of dies happens, manufacture itself of dies is hard, but there are a lot of amount of losses accordingly. In this research, make pipe channel that raw material of melting state flows in dies can present dies basic design method through flow analysis of ideal pipe channel using CFdesign.

• Polymer(Korea)
• /
• v.29 no.2
• /
• pp.198-203
• /
• 2005

Melt extrusion foaming process for the preparation of poly(L-lactic acid) (PLLA) scaffolds was carried out and the effects of foaming conditions on the pore structure of PLLA scaffolds and their mechanical properties were investigated. The porosity and mechanical properties of fabricated scaffolds were compared with the scaffolds obtained from the salt leaching method as well. It was found that the optimum pore structure was achieved when the PLLA melt was kept in extruder for the maximum decomposition time of blowing agent. In order to maintain the proper scaffolds structure, the blowing agent content should be less than $10\;wt\%$. It can be concluded that melt extrusion foaming process allows for the production of scaffold having higher mechanical properties with reasonable pore size and open cell structure for hard tissue regeneration even though it has less porosity than scaffolds made by salt leaching process.

• Carbon letters
• /
• v.16 no.2
• /
• pp.86-92
• /
• 2015

Multi-walled carbon nanotube (MWCNT)/polycarbonate (PC) nanocomposite was prepared by direct melt mixing to investigate the effect of the shear rate on the surface resistivity of the nanocomposites. In this study, an experiment was carried out to observe the shear induced orientation of the MWCNT in the polymer matrix using a very simple melt flow indexer with various loads. The compression-molded, should be eliminated. MWCNT/PC nanocomposite sample exhibited lower percolation thresholds (at 0.8 vol%) and higher electrical conductivity values than those of samples extruded by capillary and injection molding. Shear induced orientation of MWCNT was observed via scanning electron microscopy, in the direction of flow in a PC matrix during the extrusion process. The surface resistivity rose with increasing shear rate, because of the breakdown of the network junctions between MWCNTs. For real applications such as injection molding and the extrusion process, the amount of the MWCNT in the composite should be carefully selected to adjust the electrical conductivity.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.9
• /
• pp.77-83
• /
• 2018

Thermoplastic elastomers are being used increasingly throughout industry owing to their superior properties, such as superior elasticity, formability, and recoverability. Currently, research related to thermoplastic elastomers is focused on the development of composite elastomers by combining with various materials and the development of equipment. On the other hand, in the field of small and medium sized companies, it is necessary to study not only the application of these new materials, but also the process conditions that enable the extrusion of thermoplastic elastomers in inexpensive uniaxial screwing equipment. If extrusion is performed in a single screw extruder, it is important to maintain a uniform thickness through process control of the extruder. This study examined the effects of the processing temperature, which is an extrusion process variable, on the formability of a tube in the thermoplastic elastomer TPE-800L uniaxial extrusion process. The nozzle zone temperature is the most important factor in the extrusion of thermoplastic elastomer TPE-800L; the most excellent moldability was confirmed at $165-170^{\circ}C$.

• Macromolecular Research
• /
• v.16 no.1
• /
• pp.6-14
• /
• 2008

Polypropylene (PP)-layered silicate nanocomposites were developed using a new processing method involving a supercritical carbon dioxide ($scCO_2$)-assisted co-rotating twin-screw extrusion process. The nanocomposites were prepared through two step extrusion processes. In the first step, the PP/clay mixture was extruded with $CO_2$ injected into the barrel of the extruder and the resulting foamed extrudate was cooled and pelletized. In the second step, the foamed extrudate was extruded with venting to produce the final PP/clay nanocomposites without $CO_2$. In this study, organophilic-clay and polypropylene matrix were used. Maleic anhydride grafted polypropylene (PP-g-MA) was used as a compatibilizer. This study focused on the effect of $scCO_2$ on the dispersion characteristics of the clays into a PP matrix and the rheological properties of the layered silicate based PP nanocomposites. The dispersion properties of clays in the nanocomposites as well as the rheological properties of the nanocomposites were examined as a function of the PP-g-MA concentration. The degree of dispersion of the clays in the nanocomposites was analyzed by X-ray diffraction and transmission electron microscope. Various rheological properties of the nanocomposites were measured using a rotational rheometer. In the experimental results, the $scCO_2$ assisted continuous manufacturing extrusion system was used to successfully produce the organophilic-clay filled PP nanocomposites. It was found that $scCO_2$ had a measurable effect on the clay dispersion in the polymer matrix and the melt intercalation of a polymer into clay layers.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2013.05a
• /
• pp.1169-1170
• /
• 2013

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.10a
• /
• pp.1046-1050
• /
• 2005

Micro Cellular Plastics create a sensation at polymer industrial for lowering product cost & overcoming a lowering of mechanical intensity. There Is much development from injection molding pans but Extrusion parts is slow. This research is MCPs Extrusion parts, It is basis experiment for Process to make beads that is basis raw material of Package used most by shock mitigative of industry.