• Bulletin of the Korean Chemical Society
• /
• v.3 no.2
• /
• pp.60-66
• /
• 1982

In relation to denaturation of proteins, thermally induced conformational change of poly(D-glutamic acid) was studied in the presence of poly(vinyl alcohol) at low pH, where poly(D-glutamic acid) undergoes a helix-to-${\beta}$ transition without any other polymer. In a dilute solution, poly(vinyl alcohol) enhanced the ${\alpah}-to-{\beta}_1$ transition of poly(D-glutamic acid) due to intermolecular interaction between the two polymers. On the other hand, this conformational change was interrupted to a large extent in a concentrated solution, due to the interpenetration of poly(vinyl alcohol) chain into poly(D-glutamic acid) chain which prevented the intramolecular association of poly(D-glutamic acid) chain. A conformational change from ${\beta}_1\;to\;{\beta}_2$ of poly(D-glutamic acid) was observed for the films obtained by casting during annealing the mixture solutions. The ${\beta}_2$ content in the cast film increased with increasing poly(vinyl alcohol) content in the mixture.

• Textile Coloration and Finishing
• /
• v.33 no.3
• /
• pp.147-152
• /
• 2021

Bulk polymerization was used to produce poly(vinyl acetate) with different molecular weights, which were then saponified to prepare poly(vinyl alcohol) (PVA) with different molecular weights. With P_n of 2,060 and 3,240, the optimum film formation concentrations of PVA were found 7.5wt.% and 6.5wt.%, respectively. The drawing characteristics of the PVA film prepared at the optimum film formation concentrations were experimented, as well as the thermal characteristics of the PVA film based on the drawing ratio were observed. When the drawing velocity was fixed, it was found that the drawing ratios of all samples decreased as the heat band gap increased, and the melting temperature of the PVA film slightly increased as the drawing ratio increased regardless of the P_n of PVA.

• Journal of the Korean Applied Science and Technology
• /
• v.11 no.1
• /
• pp.53-60
• /
• 1994

The Synthesis of azobenzene containing long chain fatty acid and poly vinyl alcohol by esterification reaction($C_{n}-Azo-PVA$) was optimized, starting from P-(P'-hydroxy phenyl azo)-benzoic acid and the product of reaction containing azobenzene chromophores was investigated by ultraviolet spectrophotometery in toluene solvent at room temperature. In addition, UV absorption spectra of Langmmuir Blodggett (LB) film deposited on quartz plate have been measured and the structure of these compounds were ascertained by means of Ultraviolet and FT-IR. Recrystallization of reaction product in the solvent results the experimental yield obtained about 22.27% P-(P'-octadecyloxy phenyl azo)-benzoic acid-poly vinyl alcohol. Long chain azobenzene derivative-poly vinyl alcohols are induced phtoisomerization by u, v, and visible light irradiation. The LB film of azobenzene containing long chain fatty acids($C_{18}-Azo-PVA$) are possible of being applied to functional molecular devices such as photomemory and light switching.

• Textile Coloration and Finishing
• /
• v.16 no.3
• /
• pp.14-21
• /
• 2004

In this research, we accomplished in order to improving color fastness of sublimation for Poly (vinyl alcohol) (PVA)-iodine polarized film. The poor iodine sublimation problem has greatly improved by $O_2$ low temperature plasma treatment. We obtained the followings: (1) plasma treatment has contributed in adhesive ability via peel strength, AFM image and roughness were investigated, But the improvement in adhesive strength was not linearly proportional to the treatment time. (2) $O_2$ plasma treated PVA-iodine polarized film was good enough as to maintain the transmittance and polarization even after iodine cone. of 0.05mol/L and dipping time of 50sec. (3) $O_2$ low temperature plasma treated PVA-iodine polarized film has obtain high durability because of good adhesive strength.

• Applied Chemistry for Engineering
• /
• v.26 no.4
• /
• pp.458-462
• /
• 2015

It is essential to employ a binder to prepare transparent films from conductive polymer such as poly(3,4-ethylenedioxythiophene)-poly(styrene sulfonate) (PEDOT/PSS). In this paper, poly(vinyl alcohol) (PVA), poly(vinyl pyrrolidone) (PVP), and PSS were selected as a binder, and their effects were investigated. The formation of the film was found to be primarily dependent on the surface tension of coating solution including PEDOT/PSS and a binder. When PSS was used as a binder, the film was not formed. In case of using PVP, it was easily peeled off from the substrate. However, when using the PVA or the mixtures of PVA and PSS or PVA and PVP as a binder, films with good transparency and uniform surface resistances were produced. Based on adhesion and long-term stability tests, we concluded that the mixture of PVA and PSS is the best binder for preparing antistatic films of PEDOT/PSS.

• Applied Chemistry for Engineering
• /
• v.10 no.4
• /
• pp.603-607
• /
• 1999

The polarization characteristics of poly(vinyl alcohol)-iodine complex, (PVA-KI system) prepared by the oxidation process of PVA film containing a potassium iodide (KI) were investigated. The UV-visible spectrum of the PVA-KI system polarizing film showed avsorption bands corresponding to $I^{-}$, $I{_3}{^-}$ and $I{_5}{^-}$ chromophoric species at 220 nm, 290~360 nm, respectively. The polarization efficiency and transmittance of PVA-KI system film were significantly influenced by oxidation time, stretching ratio and concentration of KI. The prepared polarizing film exhibited a high polarization efficiency(99.5%) and transmittance(45%). Especially, the heat resistance of the polarizing film was higher than that of a commercial PVA-$I_2$ polarizing film. It may be argued that the result should come from a difference in oxidation process of PVA polarizing film.

• Polymer(Korea)
• /
• v.24 no.5
• /
• pp.713-720
• /
• 2000

A polymer/iodine complex film was prepared using syndiotactic poly(vinyl alcohol) (s-PVA) with number-average degree of polymerization of 900 and syndiotactic diad content of 63.1%. In comparison with atactic-PVA/iodine films, degree of polarization of the s-PVA/iodine film was improved up to over 99% although a lower transmittance was obtained. By soaking in iodine/potassium iodide aqueous solution of a lower iodine concentration and subsequent drawing by 4 times, s-PVA/iodine film of a higher transmittance and degree of polarization was produced. The degree of iodine desorption of the s-PVA/iodine film in water were very low. The crystallinity and the d-spacing and crystal size of (100) plane increased at the early stage of soaking time, however, remained constant or decreased slightly with increasing soaking time. In consequence, s-PVA/iodine complex formation took place mainly inside crystal region at the initial stage of soaking time, whereas it occurred outside crystal region or physical adsorption of iodine dominated after sufficient soaking.

• Journal of Sericultural and Entomological Science
• /
• v.40 no.2
• /
• pp.169-175
• /
• 1998

The morphology of silk fibroin/poly(vinyl alcohol)(PVA)blend films was investigated using optical microscopy and confocal laser scanning microscopy. The effects of blend ratio and molecular weight of silk fibroin and PVA on phase separation were studied. Macro-phase separation occurred for the silk fibroin-rich/poor region whereas micro-phase separation took place for the dispersed/continuous phase, In spite of differences in molecular weight and blend ratio, it is observed that the dispersed phase and continuous one are composed of silk fibroin and PVA component, respectively. As the molecular weight of silk fibroin and silk fibroin content in blend ratio are decreased, the compatibility of blend is increased due to the reduction of micro-phase separation.

• Proceedings of the Korean Fiber Society Conference
• /
• 2003.04a
• /
• pp.48-51
• /
• 2003

Poly(vinyl alcohol) (PVA) obtained by the saponification of poly(vinyl ester) like poly(vinyl acetate) or poly(vinyl pivalate) is a linen. semicrystalline polymer, which have been widely used as fibers for clothes and industries, films, membranes, medicines for drug delivery system, and cancer cell-killing embolic materials[1-3]. PVA fibers and films have high tensile and compressive strengths, high tensile modulus, and good abrasion resistance due to its highest crystalline lattice modulus. (omitted)

• Textile Coloration and Finishing
• /
• v.16 no.4
• /
• pp.19-25
• /
• 2004

Both poly(vinyl alcohol)$(PVA)-I_2$ and PVA-dye polarizing film were prepared using PVA with number-average degree of polymerization of 1,700, 2,300, 2,600. The optical property of used dye in this study closed to the that of iodine. The PVA-dye polarizing film was prepared through the dyeing process. In comparison of the result of the measurement of the heat and humidity resistance of two types polarizing films, it of PVA-dye polarizing film was higher than that of a conventional $PVA-I_2$polarizing film. The transmittance and the polarization efficiency of PVA-dye polarizing film was significantly influenced by dye concentration, dipping time, salt concentration, and temperature of dye bath. The PVA-dye polarizing film exhibited a high polarization efficiency of 99.3% and a good transmittance of 42.4%.