• Journal of the Korean institute of surface engineering
• /
• v.55 no.2
• /
• pp.120-132
• /
• 2022

In the non-cyanide-based electroless Au plating solution using thiomalic acid as a complexing agent and aminoethanethiol as a reducing agent, analysis of each component constituting the plating solution is essential for the analysis of the reaction mechanism. And component analysis in the plating solution is important for monitoring component changes in the plating process and optimizing the management method. Capillary Electrophoresis (CE) method is rapid, sensitive and quantitative and could be readily applied to analysis of Auⁿ⁺ ion, complexing agent and reducing agent in electroless Au plating solution. In this study, the capillary electrophoresis method was used to analyze each component in the electroless Au plating solution in order to elucidate the complex bonding form and the plating mechanism of the non-cyanide-based electroless Au plating bath. The purpose of this study was to establish data for optimizing the monitoring and management method of plating solution components to improve the uniformity of precipitation and stability. As a result, it was confirmed that the analysis of thiomalic acid as a complexing agent and Auⁿ⁺ ions and the analysis of aminoethanethiol as a reducing agent were possible by capillary electrophoresis. In the newly developed non-cyanide-based electroless Au plating solution, it was confirmed that Auⁿ⁺ ions exist in the form of Au⁺ having a charge of +1, and that thiomalic acid and Au⁺ are combined in a molar ratio of 2 : 1. In addition, it was confirmed that aminoethanethiol can form a complex by combining with Au⁺ ions depending on conditions as well as acting as a reducing agent.

• Resources Recycling
• /
• v.10 no.2
• /
• pp.27-33
• /
• 2001

Reusing of electroless Ni-Cu-P waste solution was investigated in the plating time, plating rate, solution composion and deposit. Plating time of nickel-catalytic surface took longer than that of zincated-catalytic surface. Initial solution with 50f) waste solution additive at batch type was possible to reusing of waste solution. Plating time of initial solution at continuous type took longer 10 times over than that of batch type. Plating time of 50% waste solution additive at continuous type took longer 3.7 times over than that of batch type. Component change of nickel-copper for electroless deposition was greatly affected by depolited inferiority and larger decreased plating rate.

• Resources Recycling
• /
• v.12 no.1
• /
• pp.18-24
• /
• 2003

Reusing of electroless Ni-Cu-B waste solution was investigated in the plating time, plating rate, solution composition and deposit. Plating time of nickel-catalytic surface took longer than that of zincated-catalytic surface. Initial solution with 40% waste solution additive at batch type was possible to reusing of waste solution. Plating time of initial solution at continuous type took longer 6 times over than that of batch type. Plating time of 40% waste solution additive at continuous type took longer 2 times over than that of batch type. Component change of nickel-copper for electroless deposition was greatly affected by deposited inferiority and larger decreased plating rate.

• Journal of the Korean institute of surface engineering
• /
• v.55 no.2
• /
• pp.102-119
• /
• 2022

Gold plating is used as a coating of connecter in printed circuit boards, ceramic integrated circuit packages, semiconductor devices and so on, because the film has excellent electric conductivity, solderability and chemical properties such as durability to acid and other chemicals. As increasing the demand for miniaturization of printed circuit boards and downsizing of electronic devices, several types of electroless gold plating solutions have been developed. Most of these conventional gold plating solutions contain cyanide compounds as a complexing agent. The gold film obtained from such baths usually satisfies the requirements for electronic parts mentioned above. However, cyanide bath is highly toxic and it always has some possibility to cause serious problems in working environment or other administrative aspects. The object of this investigation was to develop a cyanide-free electroless gold plating process that assures the high stability of the solution and gives the excellent solderability of the deposited film. The investigation reported herein is intended to establish plating bath composition and plating conditions for electroless gold plating, with thiomalic acid as a complexing agent. At the same time, we have investigated the solution stability against nickel ion and pull strength of solder ball. Furthermore, by examining the characteristics of the plated Au plating film, the problems of the newly developed electroless Au plating solution were improved and the applicability to various industrial fields was examined. New type electroless gold-plating bath which containing thiomalic acid as a complexing agent showing so good solution stability and film properties as cyanide bath. And this bath shows the excellent stability even if the dissolved nickel ion was added from under coated nickel film, which can be used at the neutral pH range.

• Korean Journal of Materials Research
• /
• v.32 no.9
• /
• pp.361-368
• /
• 2022

The overall process, from the pre-treatment of aluminum substrates to the eco-friendly neutral electroless Ni-P plating process, was observed, compared, and analysed. To remove the surface oxide layer on the aluminum substrate and aid Ni-P plating, a zincation process was carried out. After the second zincation treatment, it was confirmed that a mostly uniform Zn layer was formed and the surface oxide of aluminum was also removed. The Ni-P electroless plating films were formed on the secondary zincated aluminum substrate using electroless plating solutions of pH 4.5 and neutral pH 7.0, respectively, while changing the plating bath temperature. When a neutral pH7.0 electroless solution was used, the Ni-P plating layer was uniformly formed even at the plating bath temperature of 50 ℃, and the plating speed was remarkably increased as the bath temperature was increased. On the other hand, when a pH 4.5 Ni-P electroless solution was used, a Ni-P plating film was not formed at a plating bath temperature of 50 ℃, and the plating speed was very slow compared to pH 7.0, although plating speed increased with increasing bath temperature. In the P contents, the P concentration of the neutral pH 7.0 Ni-P electroless plating layer was reduced by ~ 42.3 % compared to pH 4.5. Structurally, all of the Ni-P electroless plating layers formed in the pH 4.5 solution and the neutral (pH 7.0) solution had an amorphous crystal structure, as a Ni-P compound, regardless of the plating bath temperature.

• Journal of the Korean institute of surface engineering
• /
• v.43 no.2
• /
• pp.111-120
• /
• 2010

In this study, the effects of multi-complex agents addition on characteristics of electroless Ni plating solution are investigated. The species and the concentration of complexing agents are major factors to control the deposition rate, P concentration, and surface morphology of plating films. Adipic acid increases the deposition rate in regardless of single- or mutli-complex agent addition. However, lactic acid effectively increases the deposition rate in case of multi-addition as the complex agents with adipic or sodium succinate acid. In addition, sodium citric acid and malic acid show good stabilizing effects of plating solution and lowering the deposition rate, because they have high complexibility. Therefore, it is suggested that the development of Ni-P plating solution suitable for diverse usages can be carried out systematically using the database from this study.

• Resources Recycling
• /
• v.14 no.4 s.66
• /
• pp.34-40
• /
• 2005

Reusing of electroless Co-Cu-P waste solution was investigated in the respect of plating time, plating rate, solution composition and deposit. Plating time of cobalt-catalytic surface took longer than that of zincated-catalytic surface. It was possible to reuse the waste solution by mixing $50\%$ fresh solution at batch type. Plating time of initial solution at continuous type took longer 7.5 times over than that of batch type. Plating time of $50\%$ waste solution additive at continuous type took longer 2.5 times over than that of batch type. Component change of cobalt-topper for electroless deposition was greatly affected by deposit inferiority and rapid decrease in plating rate.

• Journal of the Korean institute of surface engineering
• /
• v.50 no.3
• /
• pp.155-163
• /
• 2017

In this study, the effects of the concentration of metal ions and the applied current density in the Sn-Ag plating solutions were examined in regards to the resulting composition and morphology of the solder bumps' surface. Furthermore the effect of any impurities present in the methanesulfonic acid used as a base acid in the Sn-Ag solder plating solution on the stability of plating solution as well as the characteristics of the Sn-Ag alloys films was also explored. As expected, the uniform bump was obtained by means of removing impurities in the plating solution. Consequently the resultant solder bump was obtained in an optimal current density of the range of $1A/dm^2$ to $15A/dm^2$, which has acceptable bump shape and surface roughness with 12inch wafer trial results.

• Journal of the Korean institute of surface engineering
• /
• v.47 no.3
• /
• pp.128-136
• /
• 2014

In the present study, we successfully developed an eco-friendly chemical etching solution and proper condition for plating on ABS material. The mechanism of forming Ni plating layer on ABS substrate is known as following. In general, the etching solution used for the etching process is a solution of chromic acid and sulfuric acid. The etching solution is given to the surface resulting in elution of butadiene group, so-called anchor effect. Such a rough surface can easily adsorb catalyst resulting in the increase of adhesion between ABS substrate and Ni plating layer. However a use of chromic acid is harmful to environment. It is, therefore, essential to develop a new alternative solution. In the present study, we proposed an eco-friendly etching solution composed of potassium permanganate, sulfuric acid and phosphoric acid. This solution was testified to observe the surface microstructure and the pore size of electrical Ni plating layer, and the adhesive correlation between deposited layers fabricated by electro Ni plating was confirmed. The result of the present study, the newly developed, eco-friendly etching solution, which is a mixture of potassium permanganate 25 g/L, sulfuric acid 650ml/L and phosphoric acid 250ml/L, has a similar etching effect and adhesion property, compared with the commercially used chromium acid solution in the condition at $70^{\circ}C$ for 5 min.

• Journal of the Microelectronics and Packaging Society
• /
• v.24 no.3
• /
• pp.57-62
• /
• 2017

In the process for preparing Ag-coated Cu flakes by electroless silver plating using hydroquinone reducing agent, Ag coating qualities were compared by changing various process parameters such as type of pretreatment solution, plating temperature, pH of plating solution, type and injection rate of plating solution, and pulp density. Effective pretreatment solution for removing the oxide layer on a Cu flake was preferentially suggested. The conditions of low plating temperature, pH value of 4.34, slow injection rate of Ag plating solution, elimination of deionized water in the Ag plating solution, and high pulp density significantly suppressed the formation of separated tiny Ag particles, and thus the surface coverage of Ag coating on Cu flakes was enhanced.