• The Journal of Korean Academy of Prosthodontics
• /
• v.57 no.4
• /
• pp.321-327
• /
• 2019

Purpose: To evaluate an effect of additional firing process after sintering of monolithic zirconia crown on marginal and internal fit through three-dimensional analysis. Materials and methods: Ten monolithic zirconia crowns were fabricated using titanium abutment model. Monolithic zirconia crowns were designed, milled, and sintered as a control group, and additional firing with coloring was performed as a test group. Three dimensional analysis were performed by using triple-scan protocol, and cross-section analysis on mesio-distal and disto-lingual section was evaluated to measure marginal and internal fitness. Then, three-dimensional surface difference on between two groups was evaluated (${\alpha}=.05$). Results: There was statistically significant difference between the control group ($32.0{\pm}24.3{\mu}m$) and the test group ($17.0{\pm}10.8{\mu}m$) in the mesial axial wall (P < .02) and the control group ($60.2{\pm}24.3{\mu}m$) and the test group ($71.8{\pm}21.5{\mu}m$) in the distal axial wall (P < .01). There was no statistically significant difference at the remaining point. Conclusion: There was no statistical significance on the deviation of inner surface of crown according to firing number, and the results of both group were considered clinically acceptable.

• Journal of Technologic Dentistry
• /
• v.36 no.4
• /
• pp.231-237
• /
• 2014

Purpose: This study was performed fracture strength test by conducted change of abutment and coping shape for suggesting monolithic all ceramic crown which has thin thickness and superior strength of the occlusal surface. Methods: The specimens on the four kinds abutment was made according to thickness of occlusal surface and angle of axis surface. And All ceramic coping specimens of 6 different kinds was made by the CAD/CAM Method. Compression strength test using the UTM and the verification of compression-stress situation using the 3D finite element method were conducted under optimum conditions. Results: 516C specimen was showed the strongest compression-fracture strength, followed by 516FR, 516F45, specimens. Did not show significant differences between 516FR and 516F45. 516C of the universal testing machine the specimen's surface that are within the vertical load is small, finite element method of a uniformly distributed load, so the value received suggests otherwise. Conclusion: In conclusion, abutments of monolithic ziconia ceramic when having a same thickness of the occlusal, as the angle of occlusal edge is small, the stress is well dispersed and it can endure well in the fracture.

• The Journal of Korean Academy of Prosthodontics
• /
• v.54 no.3
• /
• pp.210-217
• /
• 2016

Purpose: The aim of this study was to evaluate the marginal and internal adaptation of monolithic zirconia restoration made without physical model by digital intraoral scanner. Materials and methods: A prospective clinical trial was performed on 11 restorations as a pilot study. The monolithic zirconia restorations were fabricated after digital intraoral impression taking by intraoral scanner (TRIOS, 3shape, Copenhagen, Denmark), computer-aided designing, and milling manufacturing process. Completed zirconia crowns were tried in the patients' mouth and a replica technique was used to acquire the crown-abutment replica. The absolute marginal discrepancy, marginal gap, and internal gap of axial, line angle, and occlusal part were measured after sectioning the replica in the mesiodistal and buccolingual direction. Statistical analysis was performed using Kruskal-Wallis and Mann-Whitney U test (${\alpha}=.05$). Results: From the adaptation analysis by replica, the statistically significant difference was not found between mesiodistal and buccolingual sections (P>.05), but there was significant difference among the measurement location (P<.01). The amount of absolute marginal discrepancy was larger than those of marginal gap and internal gap (P<.01). Conclusion: Within the limitations of this study, the adaptation accuracy of model-free monolithic zirconia restoration fabricated by intraoral scanner exhibited clinically acceptable result. However, the margin of zirconia crown showed tendency of overcontour and cautious clinical application and follow up is necessary.

• The Journal of Advanced Prosthodontics
• /
• v.12 no.5
• /
• pp.283-290
• /
• 2020

PURPOSE. The present study aimed to evaluate the clinical applicability of monolithic zirconia (MZ) crowns of different thickness via determination of fracture resistance and marginal fit. MATERIALS AND METHODS. MZ crowns with 0.5, 0.8, 1.0, and 1.5 mm thickness and porcelain fused to metal (PFM) crowns were prepared, ten crowns in each group. Marginal gaps of the crowns were measured. All crowns were aged with thermal cycling (5 - 55℃/10000 cycle) and chewing simulator (50 N/1 Hz/lateral movement: 2 mm, mouth opening: 2 mm/240000 cycles). After aging, fracture resistance of crowns was determined. Statistical analysis was performed with one-way ANOVA and Tukey's HDS post hoc test. RESULTS. Fracture loads were higher in the PFM and 1 mm MZ crowns compared to 0.5 mm and 0.8 mm crowns. 1.5 mm MZ crowns were not broken even with the highest force applied (10 kN). All marginal gap values were below 86 ㎛ even in the PFM crowns, and PFM crowns had a higher marginal gap than the MZ crowns. CONCLUSION. The monolithic zirconia exhibited high fracture resistance and good marginal fit even with the 0.5 mm thickness, which might be used with reduced occlusal thickness and be beneficial in challengingly narrow interocclusal space.

• The Journal of Advanced Prosthodontics
• /
• v.13 no.5
• /
• pp.269-280
• /
• 2021

PURPOSE. The objective of this study was to evaluate the effect of thickness reduction and fatigue on the failure load of monolithic zirconia crowns. MATERIALS AND METHODS. 140 CAD-CAM fabricated crowns (3Y-TZP, inCorisTZI, Dentsply-Sirona) with different ceramic thicknesses (2.0, 1.5, 1.0, 0.8, 0.5 mm, respectively, named G2, G1.5, G1, G0.8, and G0.5) were investigated. Dies of a mandibular first molar were made of composite resin. The zirconia crowns were luted with a resin composite cement (RelyX Unicem 2 Automix, 3M ESPE). Half of the specimens (n = 14 per group) were mouth-motion-fatigued (1.2 million cycles, 1.6 Hz, 200 N/ 5 - 55℃, groups named G2-F, G1.5-F, G1-F, G0.8-F, and G0.5-F). Single-load to failure was performed using a universal testing-machine. Fracture modes were analyzed. Data were statistically analyzed using a Weibull 2-parameter distribution (90% CI) to determine the characteristic strength and Weibull modulus differences among the groups. RESULTS. Three crowns (21%) of G0.8 and five crowns (36%) of G0.5 showed cracks after fatigue. Characteristic strength was the highest for G2, followed by G1.5. Intermediate values were observed for G1 and G1-F, followed by significantly lower values for G0.8, G0.8-F, and G0.5, and the lowest for G0.5-F. Weibull modulus was the lowest for G0.8, intermediate for G0.8-F and G0.5, and significantly higher for the remaining groups. Fatigue only affected G0.5-F. CONCLUSION. Reduced crown thickness lead to reduced characteristic strength, even under failure loads that exceed physiological chewing forces. Fatigue significantly reduced the failure load of 0.5 mm monolithic 3Y-TZP crowns.

• The Journal of Advanced Prosthodontics
• /
• v.15 no.3
• /
• pp.114-125
• /
• 2023

PURPOSE. The aim of the study was to evaluate the optical properties of new generation (3Y-TZP) monolithic zirconia (MZ) with different abutment types and resin cement shades. MATERIALS AND METHODS. A1/LT MZ specimens were prepared (10 × 12 × 1 mm, N = 30) and divided into 3 groups according to cement shades as transparent (Tr), yellow (Y) and opaque (O). Abutment specimens were obtained from 4 different materials including zirconia (Group Z), hybrid (Group H), titanium (Group T) and anodized yellow titanium (Group AT). MZ and abutment specimens were then cemented. L^*, a^*, and b^* parameters were obtained from MZ, MZ + abutment, and MZ + abutment + cement. ∆E₀₀₁^* (between MZ and MZ + abutment), ∆E₀₀₂^* (between MZ and MZ + abutment + cement) and ∆E₀₀₃^* (between MZ + abutment and MZ + abutment + cement) values were calculated. Statistical analyses included 2-way ANOVA, Bonferroni, and Paired Sample t-Tests (P < .05). RESULTS. Abutment types and resin cements had significant effect on L^*, a^*, b^*, ∆E₀₀₁^*, ∆E₀₀₂^*, and ∆E₀₀₃^* values (P < .001). Without cementation, whereas zirconia abutment resulted in the least discoloration (∆E₀₀₁^* = 0.68), titanium abutment caused the most discoloration (∆E₀₀₁^* = 4.99). The least ∆E₀₀₂^* = 0.68 value was seen using zirconia abutment after cementation with yellow shaded cement. Opaque shaded cement caused the most color change (∆E₀₀₃^* = 5.24). Cement application increased the L^* values in all groups. CONCLUSION. The least color change with/without cement was observed in crown configurations created with zirconia abutments. Zirconia and hybrid abutments produced significantly lower ∆E₀₀₂^* and ∆E₀₀₃^* values in combination with yellow shaded cement. The usage of opaque shaded cement in titanium/anodized titanium groups may enable the clinically unacceptable ∆E₀₀^* value to reach the acceptable level.

• The Journal of Korean Academy of Prosthodontics
• /
• v.57 no.2
• /
• pp.134-141
• /
• 2019

Purpose: The purpose of this study was to compare the clinical outcomes of lithium disilicate ceramic pressed zirconia prostheses and monolithic zirconia prostheses and to investigate the complications after two years of follow-up in posterior edentulous site. Materials and methods: A total 17 patients (male: 12, female: 5) were treated with 60 posterior fixed implant-supported prostheses (LP. lithium disilicate ceramic pressed zirconia prostheses: n = 30, MZ. monolithic zirconia prostheses: n = 30). After 24-month, clinical examination of Implant survival rate, marginal bone resorption, probing depth, plaque index, bleeding index, calculus and complications were evaluated. Results: There were no failed implants and all implants were normal in function without mobility. Marginal bone resorption was lower in LP group than MZ group at 12-month (P < .05), and 12-month probing depth and calculus deposit in LP group were significantly higher than MZ group (P < .05). Most common complications in MZ were marginal bone resorptions more than 1.5.mm and 2 chipping occurred in LP group. Conclusion: Within the limitations of the present study, lithium disilicate ceramic pressed zirconia is considered as a predictable treatment option as much as monolithic zirconia in posterior fixed implant-supported prostheses.

• Journal of Technologic Dentistry
• /
• v.34 no.2
• /
• pp.83-93
• /
• 2012

Purpose: The objective of this study is to find out physical properties and the flexural strength changed by the low temperature degradation of the block which is needed to make bio-prosthetic dentistry which is better than feldspar affiliated ceramic made by building up ceramic powder and also to apply this to the clinical use of zirconia monolithic all-ceramic crown. Methods: Flexural strength of each sample was evaluated before and after the Low Temperature Degradation, and physical properties of the Tetra Zirconia Block containing 3mol % was evaluated as well. The average and standard deviation of each experimental group were came out of the evaluation. Statistical package for social science 18.0 was used for statistics. Results: The average density of the monolithic all-ceramic crown was $6.0280{\pm}0.0147g/cm$, the relative density was 99.01 %. When the sample was sintered at $1480^{\circ}C$ the diameter of average particle was $396.62{\pm}33.71nm$. All the samples had no monolithic peak after XRD evaluation but only had tetragonal peak. There were statistically significant differences in the result of flexural strength of the samples evaluated after and before the low temperature degradation, the flexural strength before the low temperature degradation was $1747.40{\ss}{\acute{A}}$, at the temperature of $130^{\circ}C$ the flexural strength after the low temperature degradation was 1063.99MPa (p<0.001). There was statistically significant difference in the result of strength of 1020.07MPa after the low temperature degradation at the temperature of $200^{\circ}C$ (p<0.001). Conclusion: The block which was made for this evaluation possesses such an excellent strength among dental restorative materials that it is thought to have no problems to use for tetragonal zirconia polycrystal.

• The Journal of Korean Academy of Prosthodontics
• /
• v.59 no.2
• /
• pp.190-200
• /
• 2021

Purpose. The aim of this study was to evaluate biaxial flexural strength and hardness of colored monolithic zirconia after dipping in different time intervals of coloring solution. Materials and Methods. Disk shaped specimens were prepared from monolithic zirconia (Eclipse V2.0, AMS, Gimpo, Korea). Four experimental groups were categorized (n = 12) due to coloring time (PU (0s); ST (8s); OV (1 min); PS (preshade)), to evaluate biaxial flexural strength and Vickers hardness. After fracture, X-ray diffraction analysis was performed using fractured specimens. Results were analyzed with one-way ANOVA test. Results. There was no significant difference between groups in the biaxial flexural strength test. However, in the Vickers hardness test, the group with standard dipping time (ST) showed significantly higher value than the group without dipping in coloring liquid (PU)(P=.038). Also, there was no significant difference in the rest of the groups (P>.05). As a result of X-ray diffraction analysis, specific peaks of tetragonal phase were shown and the volume of monoclinic phase fraction was lower than 25%. Conclusion. Although this study has several limitations, coloring liquids had no significant effect on biaxial flexural strength. Vickers hardness was significantly different between the group to which the coloring liquid was applied and the group to which the coloring solution was not applied, but there was no significant difference between the other groups. Also, the flexural strength of monolithic zirconia corresponds to Class 5 of the minimal flexural strength standard according to the use of dental ceramics.

• The Journal of Advanced Prosthodontics
• /
• v.13 no.4
• /
• pp.246-257
• /
• 2021

PURPOSE. This study aimed to investigate the Vickers Hardness Number (VHN) of light- and dual cured resin cements cured through monolithic zirconia specimens (VITA YZ) of various translucencies: translucent (T); high translucent (HT); super translucent (ST); and extra translucent (XT) at 0, 24, and 48 h after curing. MATERIALS AND METHODS. Four zirconia specimens from each translucency were prepared. Two light-cured resin cements (Variolink N LC; VL and RelyX Veneer; RL) and two dual-cured resin cements (Variolink N DC; VD and RelyX U200; RD) were used. The cement was mixed and loaded in a mold and cured for 20 s through the zirconia specimen. The upper surface of cements was tested for VHN using a microhardness tester at 0, 24, and 48 h after curing. The VHN were analyzed using two-way repeated, Brown-Forsythe ANOVA with Games Howell post-hoc analysis and independent t-tests (P < .05). RESULTS. All cements showed significantly higher VHN from 0 h to 24 h (P < .001). At 48 h, the VHN of light-cured cements were significantly lower when cured under the T groups than under XT groups (P = .001 in VL, P = .014 in RL). At each post curing time of each translucency, VD showed higher VHN than VL (P < .05), and RD also showed higher VHN than RL (P < .05). CONCLUSION. The translucency of zirconia has an effect on the VHN for light-cured resin cements, but has no effect on dual-cured resin cements. Dual-cured resin cement exhibited higher VHN than the light-cured resin cement from the same manufacturer. All resin cements showed significantly higher VHN from 0 h to 24 h.