• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2017.05a
• /
• pp.936-938
• /
• 2017

In this paper, the progressive failure analysis of a bolted composite joint which is used in combustion tubes of projectiles and weapon systems is performed. Hashin's failure criterion is considered as fiber tensile failure mode, fiber compressive failure mode, matrix tensile failure mode, and matrix compressive failure mode for this analysis. And this criterion is used to make user subroutine, UMAT. Through the progressive failure analysis we predicted failure strength and compared failure strength with specimen test result.

• Journal of the Korean Operations Research and Management Science Society
• /
• v.36 no.4
• /
• pp.29-41
• /
• 2011

As industires are evolving into a more advanced type industrial system, service economy has been more emphasized. But with the expansion of the service economy, the failure of the service has also increased. Customers flee caused by the service failure leads to from simple problems like financial loss to serious problems like damaging corporate image. Therefore, if possible, the system providing defect-free service should be established. If this is not possible, preventive measures should be taken in order to minimize the failure. The study as a tool to prevent service failure presents the concepts "service error matrix." And to confirm whether this idea is practical or not, this study investigated the hotel, one of the leading service industries, about actually occurring service failure and applied to service error matrix suggested in this study. Finally service blueprint and Poka-yoke are completed in order to reduce service failure of Y hotel which was the object of the interview for this study.

• Steel and Composite Structures
• /
• v.12 no.1
• /
• pp.53-72
• /
• 2012

In this study, the physically-based failure models for matrix and fibers in compression and tension loading are introduced. For the 3D stress based fiber kinking model a modification is proposed for calculation of the fiber misalignment angle. All of these models are implemented into the finite element code by using the advantage of damage variable and the numerical results are discussed. To investigate the matrix failure model, purely in-plane transverse compression experiments are carried out on the specimens made by Glass/Epoxy to obtain the fracture surface angle and then a comparison is made with the calculated numerical results. Furthermore, shear failure of $({\pm}45)_s$ model is investigated and the obtained numerical results are discussed and compared with available experimental results. Some experiments are also carried out on the woven laminated composites to investigate the fracture pattern in the matrix failure mode and shown that the presented matrix failure model can be used for the woven composites. Finally, the obtained numerical results for stress based fiber kinking model and improved ones (strain based model) are discussed and compared with each other and with the available results. The results show that these models can predict the kink band angle approximately.

• Journal of the Society of Naval Architects of Korea
• /
• v.52 no.2
• /
• pp.143-152
• /
• 2015

In the present study, the fiber and matrix failure of composite laminates under arbitrary biaxial stresses were evaluated based on separate mode criteria such as Hasnin and Puck theories. There is a limitation to predict the fiber-dominant and/or matrix-dominant failures under arbitrary stress states using limit criteria (maximum stress and maximum strain theories) and interactive criteria (Tsai-Hill and Tsai-Wu theories). There is little literature for failure analysis of ships and offshore composite structures considering advanced failure theories such as Hashin and Puck theories. Furthermore, there is not enough practical commercial finite element analysis (FEA) code which is basically adopted the separate mode criteria. Hence, in the present study, the user-defined subroutine of commercial FEA code ABAQUS for evaluation of fiber and matrix failures of composite structures was developed based on Hashin and Puck failure criteria. And then, the proposed subroutine was validated by comparing with a series of experimental results of carbon- and glass-implemented composite laminates to guarantee the reliability and usefulness of the developed method.

• Structural Engineering and Mechanics
• /
• v.62 no.1
• /
• pp.43-54
• /
• 2017

In this study, the failure behavior of composite material in the biaxial and off-axis loading is studied based on a computational micromechanical model. The model is developed so that the combination of mechanical and thermal loading conditions can be considered in the analysis. The modified generalized plane strain assumption of the theory of elasticity is used for formulation of the micromechanical modeling of the problem. A truly meshless method is employed to solve the governing equation and predict the distribution of micro-stresses in the selected RVE of composite. The fiber matrix interface is assumed to be perfect until the interface failure occurs. The biaxial and off-axis loading of the SiC/Ti and Kevlar/Epoxy composite is studied. The failure envelopes of SiC/Ti and Kevlar/Epoxy composite in off-axis loading, biaxial transverse-transverse and axial-transverse loading are predicted based on the micromechanical approach. Various failure criteria are considered for fiber, matrix and fiber-matrix interface. Comparison of results with the available results in the litreture shows excellent agreement with experimental studies.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.38 no.3
• /
• pp.275-282
• /
• 2014

Particle-reinforced metal matrix composites exhibit a strengthening effect due to the particle size-dependent length scale that arises from the strain gradient, and thus from the geometrically necessary dislocations between the particles and matrix that result from their CTE(Coefficient of Thermal Expansion) and elastic-plastic mismatches. In this study, the influence of the size-dependent length scale on the particle-matrix interface failure and ductile failure in the matrix was examined using finite-element punch zone modeling whereby an augmented strength was assigned around the particle. The failure behavior was observed by a parametric study, while varying the interface failure properties such as the interface strength and debonding energy with different particle sizes and volume fractions. It is shown that the two failure modes (interface failure and ductile failure in the matrix) interact with each other and are closely related to the particle size-dependent length scale; in other words, the composite with the smaller particles, which is surrounded by a denser dislocation than that with the larger particles, retards the initiation and growth of the interface and matrix failures, and also leads to a smaller amount of decrease in the flow stress during failure.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.21 no.2
• /
• pp.317-326
• /
• 1997

An investigation was performed to study the matrix cracking and delamination in laminated composite plates due to transverse impact. A model was developed for predicting the initiation of the matrix cracking and the shape and size of impact-induced delamination in laminated composite plates resulting from the ballistic impact. The model consists of a stress analysis and a failure analysis. A transient finite element analysis which was based on the higher-order shear deformation theory was adopted for calculating the stresses inside the laminated composite plates during impact. A failure analysis was used to predict the initial intraply matrix cracking and the shape and size of the interface delamination in the laminates. As a results, a shear matrix cracking which was governed by the transverse interlaminar shear stress occured at the middle layer near the midplane of laminates and a bending matrix cracking which was governed by the transverse inplane stress occured at the bottom layer near the surface of laminates. In a thick laminates, a shear matrix cracking generated first at the middle layer of laminates, but in a thin laminates, a bending matrix cracking generated first at the bottom layer of laminates.

• Proceedings of the KSR Conference
• /
• 2010.06a
• /
• pp.1231-1235
• /
• 2010

The tensile failure behavior of polymer matrix composite materials was investigated with the aid of a nondestructive evaluation (NDE) technique. The materials, E-glass fiber reinforced epoxy matrix composites, which are applicable to carbody materials in railway vehicles to reduce weight, were used for this investigation. In order to explain stress-strain behavior of polymer matrix composite sample, the infrared thermography technique was employed. A high-speed infrared (IR) camera was used for in-situ monitoring of progressive damages of polymer matrix composite samples during tensile testing. In this investigation, the IR thermography technique was used to facilitate a better understanding of damage evolution, fracture mechanism, and failure mode of polymer matrix composite materials during monotonic loadings.

• Composites Research
• /
• v.29 no.2
• /
• pp.66-72
• /
• 2016

Porosity in polymer matrix composites increases rapidly during thermochemical decomposition at high temperatures. The generation of pores reduces elastic moduli and failure strengths of composite materials, and gas pressures in internal pores influence thermomechanical behaviors. In this paper, micromechanical finite element analysis is carried out by using two-dimensional representative volume elements for unidirectionally fiber-reinforced composites with porous matrix. According to the state of the pores, effective elastic moduli, poroelastic parameters and failure strengths of the overall composites are investigated in detail. In particular, it is confirmed that the failure strengths in the transvers and through-thickness directions are predicted much more weakly than the strength of nonpored matrix, and decrease consistently as the porosity of matrix increases.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.6 s.177
• /
• pp.1456-1469
• /
• 2000

Mechanical behaviors of uniaxially fiber-reinforced metal matrix composites under transverse loading conditions were studied at room and elevated temperatures. A mono-filament composite was selecte d as a representative analysis model with perfectly bonded fiber/matrix interface assumption. The elastic-plastic and visco-plastic models were investigated by both theoretical and numerical methods. The product of triaxiality factor and effective strain as well as stress components and strain energy was obtained as a function of location to estimate the failure sites in fiber-reinforced metal matrix composite. Results showed that fiber/ matrix interfacial debond plays a key role for local failure at the room temperature, while void creation and growth in addition to the interfacial debond are major concerns at the elevated temperature. It was also shown that there would be an optimal diameter of fiber for the strong fiber-reinforced metal matrix composite.