• Journal of Adhesion and Interface
• /
• v.14 no.2
• /
• pp.82-87
• /
• 2013

Preliminary studies on the synthesis of magnetic nanoparticles including nanoporous carbon materials have been done via a direct carbonization process from resol, ferric nitrate and triblock copolymer F127. The results show that the nanoporous magnetite/carbon ($Fe_3O_4$/carbon) with a low $Fe_3O_4$ content (1 wt%) possesses an ordered 2-D hexagonal (p6mm) structure, uniform nanopores (3.6 nm), high surface areas (up to 635 $m^2/g$) and pore volumes (up to 0.48 $cm^3/g$). Magnetite nanoparticles with a small particle size (10.2 nm) were confined in the matrix of amorphous carbon frameworks with superparamagnetic property (7.7 emu/g). The nanoporous magnetite/carbon showed maximum adsorption amount (995 mg/g) of ibuprofen after 24 h at room temperature. The nanoporous magnetite/carbon was separated from solution easily by using a magnet. The nanoporous magnetite/carbon material is a good adsorbent for hydrophobic organic drug molecules, i.e. ibuprofen.

• Journal of the Korean Chemical Society
• /
• v.58 no.1
• /
• pp.100-104
• /
• 2014

Magnetite nanoparticles were prepared by co-precipitation method and then silica was coated onto the surface of $Fe_3O_4$ by hydrolysis of TEOS. The silica coated magnetite nanoparticles were characterized for its structural, microstructural, optical, vibrational and magnetic properties by X-ray diffraction analysis, Scanning electron microscopy, UV-visible spectroscopy, Infrared spectroscopy and Vibration sample magnetometer, respectively. XRD study confirmed the presence of $SiO_2$ on the surface of magnetite nanoparticles. SEM study indicated that with increase in TEOS content the particles become bigger and mono-disperse. It was also found that the silica coating prevents magnetic particles from aggregation and imparts excellent stability.

• Journal of Magnetics
• /
• v.16 no.4
• /
• pp.368-373
• /
• 2011

Particle size distributions in 10 nm magnetite ferrofluids are analyzed based on both dc and ac magnetic measurements. Modified log-normal distributions are used for fitting the experimental results, which allows for a proper account of the narrow distributions. The calculated average particle sizes are in good agreement with the TEM results. However the ac method gives a much narrower distribution width than that of the dc magnetization curve fit. The proposed measurements combined with the analysis methods are useful for the characterization of ferrofluids being considered for biomedical applications.

• Journal of the Korean Magnetics Society
• /
• v.16 no.4
• /
• pp.221-227
• /
• 2006

We have synthesized uniform nanometer sized magnetite particles using chemical coprecipitation technique through a sonochemical method with surfactant such as oleic acid. Magnetite phase nanoparticles could be observed from X-ray diffraction. Magnetite nanoparticles is surface phase morphology and biopolymer-microspheres for Application Medical. Magnetite nanoparticles coated biopolymer. Atomic Force Microscope (AFM) was used to image the coated nanoparticles. Magnetic colloid suspensions containing particles with sodium oleate, chitosan and $\beta$-glucan have been prepared. The morphology of the magnetic biopolymer microsphere particles were characterized using optical microscope. Magnetic hysteresis measurement were performed using a superconducting quantum interference device (SQUID) magnetometer at room temperature to investigate the magnetic properties of the biopolymer microspheres and magnetite coated biopolymer including magnetite nanoparticles. Magnetic Resonance (MR) imaging was used to investigate biopolymer coated nanoparticles and biopolymer microspheres.

• Journal of Magnetics
• /
• v.15 no.4
• /
• pp.179-184
• /
• 2010

We have investigated the effects of post annealing on iron oxide nanoparticles synthesized by the novel hydrothermal synthesis method with the $FeSO_4{\cdot}7H_2O$. To investigate the post annealing effect, the as-synthesized iron oxide nanoparticles were annealed at different temperatures in a vacuum chamber. The morphological, structural and magnetic properties of the iron oxide nanoparticles were investigated with high resolution X-ray powder diffraction (XRD), high resolution transmission electron microscopy (HRTEM), Mossbauer spectroscopy, and vibrating sample magnetometer analysis. According to the XRD and HRTEM analysis results, as-synthesized iron oxide nanoparticles were only magnetite ($Fe_3O_4$) phase with face-centered cubic structure but post annealed iron oxide nanoparticles at $700^{\circ}C$ were mainly magnetite phase with trivial maghemite ($\gamma-Fe_2O_3$) phase which was induced in the post annealing treatment. The crystallinity of the iron oxide nanoparticles is enhanced by the post annealing treatment. The particle size of the as-synthesized iron oxide nanoparticles was about 5 nm and the particle shape was almost spherical. But the particle size of the post annealed iron oxide nanoparticles at $700^{\circ}C$ was around 25 nm and the particle shape was spherical and irregular. The as-synthesized iron oxide nanoparticles showed superparamagnetic behavior, but post annealed iron oxide nanoparticles at $700^{\circ}C$ did not show superparamagnetic behavior due to the increase of particle size by post annealing treatment. The saturation of magnetization of the as-synthesized nanoparticles, post annealed nanoparticles at $500^{\circ}C$, and post annealed nanoparticles at $700^{\circ}C$ was found to be 3.7 emu/g, 6.1 emu/g, and 7.5 emu/g, respectively. The much smaller saturation magnetization value than one of bulk magnetite can be attributed to spin disorder and/or spin canting, spin pinning at the nanoparticle surface.

• Membrane and Water Treatment
• /
• v.8 no.1
• /
• pp.51-71
• /
• 2017

Antimicrobial polyethersulfone ultrafiltration membranes containing zerovalent iron ($Fe^0$) and magnetite ($Fe_3O_4$) nanoparticles were synthesized via phase inversion method using polyethersulfone (PES) as membrane material and nano-iron as nanoparticle materials. Zerovalent iron nanoparticles (nZVI) were prepared by the reduction of iron ions with borohydride applying an inert atmosphere by using $N_2$ gases. The magnetite nanoparticles (nMag) were prepared via co-precipitation method by adding a base to an aqueous mixture of $Fe^{3+}$ and $Fe^{2+}$ salts. The synthesized nanoparticles were characterized by scanning electron microscopy, X-ray powder diffraction, and dynamic light scattering analysis. Moreover, the properties of the synthesized membranes were characterized by scanning electron microscopy energy dispersive X-ray spectroscopy and atomic force microscopy. The PES membranes containing the nZVI or nMag were examined for antimicrobial characteristics. Moreover, amount of iron run away from the PES composite membranes during the dead-end filtration were tested. The results showed that the permeation flux of the composite membranes was higher than the pristine PES membrane. The membranes containing nano-iron showed good antibacterial activity against gram-negative bacteria (Escherichia coli). The composite membranes can be successfully used for the domestic wastewater filtration to reduce membrane biofouling.

• Journal of the Korean Magnetics Society
• /
• v.16 no.1
• /
• pp.107-110
• /
• 2006

Magnetite nanoparticles encapsulated with biodegradable polymer [poly(D,L-lactide-co-glycoiide), PLGA] were prepared by an emulsification-diffusion method. To investigate the effect of type of organic solvents on the mean particle sizes of obtained composite particles, different organic solvents [ethyl acetate (EA), propylene carbonate (PC) and acetone (ACE)] were used with a stabilizer [didodecyl dimethyl ammonium bromide (DMAB)]. The particle size of nanoparticles was observed by the dynamic light scattering method. When EA and PC as partially water-soluble solvents were used, small composite nanoparticles below 80nm were obtained, while large composite nanoparticles above 330nm were prepared for ACE as a fully water-soluble solvent.

• Journal of the Korean Magnetics Society
• /
• v.26 no.6
• /
• pp.190-195
• /
• 2016

We report the effect of pressure varying from 0 to 1500 bar on the magnetic properties of magnetite nanoparticles synthesized from $Fe(OH)_2$ suspension using a high pressure homogenizer without any dispersing agent and oxidant. The observed X-ray diffraction (XRD) patterns showed that all the synthesized nanoparticles had the inverse spinel structure of magnetite. It was found from transmission electron microscopy (TEM) and XRD analysis that the average size of the synthesized magnetite particles could be controlled by the pressure of the high pressure homogenizer. The average particle size was found to range from 21 to 26 nm and decrease with increasing pressure. Magnetic hysteresis measurements performed at room temperature using a vibrating sample magnetometer (VSM) revealed the appearance of a superparamagnetic behavior in the magnetite nanoparticles synthesized at a pressure of 1500 bar.

• Resources Recycling
• /
• v.9 no.5
• /
• pp.33-37
• /
• 2000

• Journal of the Korean Magnetics Society
• /
• v.16 no.1
• /
• pp.102-106
• /
• 2006

Magnetic nanoparticles can be used for a variety of biomedical applications. They can be used in the targeted delivery of therapeutic agents in vivo, in the hyperthermic treatment of cancers. in magnetic resonance (MR) imaging as contrast agents and in the biomagnetic separations of biomolecules. We have synthesized magnetite $(Fe_3O_4)$ nanoparticles using chemical coprecipitation technique with sodium oleate as surfactant. Nanoparticle size can be varied from 2 to 8nm by controlling the sodium oleate concentration. Magnetite phase nanoparticles could be observed from X-ray diffraction. Magnetic colloid suspensions containing particles with sodium oleate and chitosan have been prepared. Nanoparticles, both oleate-coated and chitosan-coated, have been characterized by several techniques. Atomic farce microscope (AFM) was used to image the coated nanoparticles. Magnetic hysteresis measurement were performed using a superconducting quantum interference device (SQUID) magnetometer at room temperature to investigate the magnetic properties of the magnetite nanoparticles. The SQUID measurements revealed superparamagnetism of nanoparticles.