• Current Research on Agriculture and Life Sciences
• /
• v.5
• /
• pp.33-39
• /
• 1987

In order to study the degradation pattern of propanil in solution, the environmental factors such as temperature, pH and UV irradiation effect on propanil degradation were investigated. The degradation of propanil in solution was more rapid in high temperature than in low. The production amount of DCA was increased in high temperature, and then was decreased in a certain period of time because of conversion to TCAB, but the concentration of TCAB was maintained without more degradation. Propanil was rapidly hydrolyzed in alkaline solution as well as in strong acidic solution. Degradation product, DCA was rapidly produced and condensed to TCAB in strong acidic and alkaline condition. On exposur to ultraviolet light, 90% of original propanil was degraded within 20minutes, 0.3 ppm of DCA was produced in 10 minutes, and maintained the concentration throughout irradiation times.

• Journal of Practical Agriculture & Fisheries Research
• /
• v.22 no.2
• /
• pp.5-15
• /
• 2020

To extend the shelf life of draft makgeolli, UV irradiation and high hydrostatic pressure were conducted. UV irradiation did not reduce the total cell number in makgeolli, but high hydrostatic pressure treated drastically decreased. The number of viable cells in makgeolli was 2.2-5.8 × 10⁷ CFU/mL, but when treated with 300 MPa pressure for 1 minute, it decreased to 1.4-10 × 10³ CFU/mL, with 400 MPa to 4-68 CFU/mL, and with 500 MPa to under 40 CFU/mL. Yeast died at 400 MPa pressure, but Bacillus amyloliquefaciens and Rummeliibacillus stabekisii survived at 500 MPa pressure. The makgeolli treated with 400 and 500 MPa pressure did not increase the number of cells even when stored at room temperature (25℃) for 30 days, and changes in alcohol, acidity, and amino acid vlaue were also suppressed. However, when stored for more than 30 days at room temperature, the acidity and amino acid levels of makgeolli increased, making it difficult to drink. At low temperature (4℃) storage, the quality change of makgeolli was suppressed until 70 days of storage, so it had a taste similar to that of fresh makgeolli.

• Journal of Bio-Environment Control
• /
• v.17 no.4
• /
• pp.283-287
• /
• 2008

To investigate the effects of different wavelengths of photosynthetically active radiation on the morphology and leaf color changes of a single tomato (Lycopersicon esculentum) seedling, we stored the seedling at $10{\pm}0.5^{\circ}C$ under eight different wavelengths (peak wavelengths; 405, 450, 505, 545, 600, 645, 680, and 700 nm) with a constant photosynthetic photon flux of $3{\mu}mol\;m^{-2}s^{-l}$ for 28 d. Under the 405, 450, and 505 nm wavelength conditions, the leaves of the seedlings showed vigorous shape with an upright morphology. Rachis elongation was suppressed and hence compact appearance was observed under the 450 and 505 urn conditions. Although the difference in leaf color between before storage and on 28 days after storage was observed under all wavelength conditions, the 405 and 700 um irradiations changed the leaf color to light green. Application of light-emitting diode (LED) light irradiated from around 450 to 545 nm can contribute to vigorous shape with an upright morphology of tomato seedlings during low light irradiation-low temperature storage.

• Journal of the Korean Magnetics Society
• /
• v.17 no.2
• /
• pp.71-75
• /
• 2007

Ultrasonic irradiation in a solution during the chemical reaction may accelerate the rate of the reaction and the crystallization at low temperature. We have synthesized nanometer sized zinc ferrite particles using chemical co-precipitation technique through a sonochemical method with surfactant such as oleic acid. The thermal behaviour of the zinc ferrite was determined by the thermoanalytical techniques (TGA-DSC). Powder X-ray diffraction measurements show that the samples have the spinel structure. Magnetic properties measurement were performed using a superconducting quantum interference device (SQUID) magnetometer.

• Nano
• /
• v.13 no.12
• /
• pp.1850147.1-1850147.14
• /
• 2018

In this work, water-soluble and blue-emitting carbon nanodots (CDs) were synthesized from apple peels for the first time via one-step hydrothermal method. The synthetic route is facile, green, economical and viable. The as-prepared CDs were characterized thoroughly by transmission electron microscopy (TEM), X-ray diffraction (XRD), Raman, Fourier transform infrared (FT-IR), X-ray photoelectron (XPS), fluorescence and UV-Vis absorption spectroscopy in terms of their morphology, surface functional groups and optical properties. The results show that these CDs possessed ultrasmall size, good dispersivity, and high tolerance to pH, ionic strength and continuous UV irradiation. Significantly, the CDs had fast and reversible response towards temperature, and the accurate linear relationship between fluorescence intensity and temperature was used to design a novel nanothermometer in a broad temperature range from 5 to $65^{\circ}C$ facilely. In addition, the fluorescence intensity of CDs was observed to be quenched immediately by Cr(VI) ions based on the inner filter effect. A low-cost Cr(VI) ions sensor was proposed employing CDs as fluorescent probe, and it displayed a wide linear range from 0.5 to $200{\mu}M$ with a detection limit of $0.73{\mu}M$. The practicability of the developed Cr(VI) sensor for real water sample assay was also validated with satisfactory recoveries.

• Korean Journal of Food Science and Technology
• /
• v.14 no.4
• /
• pp.355-363
• /
• 1982

In order to develop the commercial storage method of potatoes by irradiation combined with natural low temperature, storage room($450{\times}650{\times}250cm$; year round temperature change, $2-17^{\circ}C;\;70-85%\;R.H.$) on a batch scale followed by irradiation with optimum dose level. Irish cobbler and Shimabara were 100% sprouted after 3 months storage in control, whereas in 15 Krad irradiated group, sprouting was completely inhibited at Irish cobbler for 9 months storage, and at Shimabara for 12 months. The extent of loss due to rot attack after 9 months storage was 6% in control, 6-8% in 10-15 Krad irradiated group at Irish cobbler and weight loss was 16.5% in control, 5.1-5.6% in irradiated group, whereas rotting rate of Shimabara after 12 months storage was 100% in control, 15% in irradiated group and the weight loss of its was 12.6% in control, $7.3{\sim}7.4%$ in irradiated group. The moisture content in whole storage period of two varieties were $72{\sim}82%$ without remarkable changes. The total sugar and ascorbic acid contents were slightly decreased according to the dose increase and elapse of storage period, whereas reducing sugar content was increased. Irish cobbler was 90% marketable after 9 months storage and 85% in Shimabara after 12 months storage.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.261-261
• /
• 2016

플래시 메모리 (flash memory)는 DRAM(dynamic racdom access memory)이나 SRAM(static random access memory)에 비해 소자의 구조가 매우 단순하기 때문에 집적도가 높아서 기기의 소형화가 가능하다는 점과 제조비용이 낮다는 장점을 가지고 있다. 또한, 전원을 차단하면 정보가 사라지는 DRAM이나 SRAM과 달리 전원이 꺼지더라도 저장된 정보가 지워지지 않는다는 특징을 가지고 있어서 ROM(read only memory)과 정보의 입출력이 자유로운 RAM의 장점을 동시에 가지기 때문에 활용도가 크다. 또한, 속도가 빠르고 소비전력이 작아서 USB 드라이브, 디지털 TV, 디지털 캠코더, 디지털 카메라, 휴대전화, 개인용 휴대단말기, 게임기 및 MP3 플레이어 등에 널리 사용되고 있다. 특히, 낸드(NAND)형의 플래시 메모리는 고집적이 가능하며 하드디스크를 대체할 수 있어 고집적 음성이나 화상 등의 저장용으로 많이 쓰이며 일정량의 정보를 저장해두고 작업해야 하는 휴대형 기기에도 적합하며 가격도 노어(NOR)형에 비해 저렴하다는 장점을 가진다. 최근에는 smart watch, wearable device 등과 같은 차세대 디스플레이 소자에 대한 관심이 증가함에 따라 투명하고 유연한 메모리 소자에 대한 연구가 다양하게 진행되고 있으며 유리나 플라스틱과 같은 기판 위에서 투명한 플래시 메모리를 형성하는 기술에 대한 관심이 높아지고 있다. 전하트랩형 (charge trap type) 플래시 메모리는 플로팅 게이트형 플래시 메모리와는 다르게 정보를 절연막 층에 저장하므로 인접 셀간의 간섭이나 소자의 크기를 줄일 수 있기 때문에 투명하고 유연한 메모리 소자에 적용이 가능한 차세대 플래시 메모리로 기대되고 있다. 전하트랩형 플래시메모리는 정보를 저장하기 위하여 tunneling layer, trap layer, blocking layer의 3층으로 이루어진 게이트 절연막을 가진다. 전하트랩 플래시 메모리는 게이트 전압에 따라서 채널의 전자가 tunnel layer를 통해 trap layer에 주입되어 정보를 기억하게 되는데, trap layer에 주입된 전자가 다시 채널로 빠져나가는 charge loss 현상이 큰 문제점으로 지적된다. 따라서 tunnel layer의 막질향상을 위한 다양한 열처리 방법들이 제시되고 있으며, 기존의 CTA (conventional thermal annealing) 방식은 상대적으로 높은 온도와 긴 열처리 시간을 가지고, RTA (rapid thermal annealing) 방식은 매우 높은 열처리 온도를 필요로 하기 때문에 플라스틱, 유리와 같은 다양한 기판에 적용이 어렵다. 따라서 본 연구에서는 기존의 열처리 방식보다 에너지 전달 효율이 높고, 저온공정 및 열처리 시간을 단축시킬 수 있는 마이크로웨이브 열처리(microwave irradiation, MWI)를 도입하였다. Tunneling layer, trap layer, blocking layer를 가지는 MOS capacitor 구조의 전하트랩형 플래시 메모리를 제작하여 CTA, RTA, MWI 처리를 실시한 다음, 전기적 특성을 평가하였다. 그 결과, 마이크로웨이브 열처리를 실시한 메모리 소자는 CTA 처리한 소자와 거의 동등한 정도의 우수한 전기적인 특성을 나타내는 것을 확인하였다. 따라서, MWI를 이용하면 tunnel layer의 막질을 향상시킬 뿐만 아니라, thermal budget을 크게 줄일 수 있어 차세대 투명하고 유연한 메모리 소자 제작에 큰 기여를 할 것으로 예상한다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.1
• /
• pp.7-15
• /
• 2004

The ferroelectric SBT thin films as a material of capacitors for non-volatile FRAMs have some problems that its remanent polarization value is relatively low and the crystallization temperature is quite high abovc 80$0^{\circ}C$. Therefore, in this paper, SBTN solution with S $r_{0.9}$B $i_{2.1}$T $a_{1.8}$N $b_{0.2}$$O_{9}$ composition was synthesized by sol-gel method. Sr(O $C_2$ $H_{5}$)$_2$, Bi(TMHD)$_3$, Ta(O $C_2$ $H_{5}$)$_{5}$and Nb(O $C_2$ $H_{5}$)$_{5}$ were used as precursors, which were dissolved in 2-methoxyethanol. SBTN thin films with 200 nm thickness were deposited on Pt/Ti $O_2$/ $SiO_2$/Si substrates by spin-coating. UV-irradiation in a power of 200 W for 10 min and rapid thermal annealing in a 5-Torr-oxygen ambient at 76$0^{\circ}C$ for 60 sec were used to promote crystallization. The films were well crystallized and fine-grained after annealing at $650^{\circ}C$ in oxygen ambient. The electrical characteristics of 2Pr=11.94 $\mu$C/$\textrm{cm}^2$, Ps＋/Pr＋=0.54 at the applied voltage of 5 V were obtained for a 200-nm-thick SBTN films. This results show that 2Pr values of the UV irradiated and rapid thermal annealed SBTN thin films at the applied voltage of 5 V were about 57% higher than those of no additional processed SBTN thin films. thin films.lms.s.s.

• Journal of Industrial Technology
• /
• v.28 no.A
• /
• pp.19-22
• /
• 2008

In recent years, much attention has been paid to "Photocatalytic oxidation" as an alternative technique, where the pollutants are degraded by UV-irradiation in the presence of a semiconductor suspension such as titanium dioxide. $TiO_2$ is the most often used photocatalyst due to its considerable photocatalytic activity, high stability, non-environmental impact and low cost. 1n this research, the photocatalytic degradation of humic acid, acetaldehyde and methylene blue in $UV/TiO_2$ systems has been stydied. The effect of calcination temperature for manufacturing of $TiO_2$ photocatalysts and type of photocatalysts on photodegradation has been investigated. Photocatalysts with various metal ions(Mn, Fe, Cu and Pt) loading are tested to evaluate the effects of metal ions impurities on photodegradation. The photodegradation efficiency with $Pt-TiO_2$ or $Fe-TiO_2$ or $Cu-TiO_2$ is higher than Degussa P-25 powder. However, the photodegradation efficiency with $Mn-TiO_2$ is lower than Degussa P-25 powder. The photocatalytic properties of the nanocrystals were strongly dependent upon the crystallinity, particle size, standard reduction potential of various transition metal and electronegativity of various transition metal. As a result photocatalysts with various metal ion loading evaluated the effect of photodegradation.

• Journal of the Korean Vacuum Society
• /
• v.13 no.1
• /
• pp.29-33
• /
• 2004

In this paper, we investigated the ultra-low temperature(<$150^{\circ}C$) polycrystalline silicon film on plastic substrate application using RF-magnetron sputtering and excimer laser annealing. Amorphous silicon films were deposited using Ar/He mixture gas at $120^{\circ}C$ and in-film argon concentration was less than 2%, which was measured to Rutherford Backscattering Spectrometry. At energy density 320mJ/$\textrm{cm}^2$, RMS roughness was 267$\AA$ and UV crystallinity was 62%. The grain size varies from 50nm to 100nm after excimer laser irradiation.