• Korean Journal of Materials Research
• /
• v.17 no.3
• /
• pp.160-166
• /
• 2007

TRISO coatings on $ZrO_{2}$ surrogate kernels were conducted by a fluidized-bed chemical vapor deposition (FBCVD) method. Effects of the deposition temperature and the gas flow rate on the properties of SiC layer were investigated in the TRISO-coated particles. Deposition rate of the SiC layer decreased as the deposition temperature increased in the temperature range of $1460^{\circ}-1550^{\circ}C$. At the deposition temperature of $1550^{\circ}C$ the SiC layer contained an excess carbon, whereas the SiC layers had stoichiometric compositions at $1460^{\circ}C\;and\;1500^{\circ}C$. Hardness and elastic modulus measured by a nanoindentation method were the highest in the SiC layer deposited at $1500^{\circ}C$. The SiC layer deposited at the gas flow rate of 4000 sccm exhibited a high porosity and contained large pores more than $1{\mu}m$, being due to a violent spouting of particles. On the other hand, the SiC layer deposited at 2500 sccm revealed the lowest porosity.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.232-232
• /
• 2006

SiC single crystal Ingots were prepared onto different seed material using sublimation PVT techniques and then their crystal quality was systematically compared. In this study, the conventional SiC seed material and the new SiC seed material with an inserted SiC epitaxial layer on a seed surface were used as a seed for SiC bulk growth. The inserted epitaxial layer was grown by a sublimation epitaxy method called the CST with a low growth rate of $2{\mu}m/h$ N-type 2"-SIC single crystals exhibiting the polytype of 6H-SiC were successfully fabricated and carrier concentration levels of below $10^{17}/cm^3$ were determined from the absorption spectrum and Hall measurements. The slightly higher growth rate and carrier concentration were obtained in SiC single crystal Ingot grown on new SiC Seed materials with the inserted epitaxial layer on the seed surface, maintaining the high quality.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.322-322
• /
• 2010

For boron doping on n-type silicon wafer, around $1,000^{\circ}C$ doping temperature is required, because of the relatively low solubility of boron in a crystalline silicon comparing to the phosphorus case. Boron doping by fiber laser annealing and lamp furnace heat treatment were carried out for the uniformly deposited p-a-Si:H layer. Since the uniformly deposited p-a-Si:H layer by cluster is highly needed to be doped with high temperature heat treatment. Amorphous silicon layer absorption range for fiber laser did not match well to be directly annealed. To improve the annealing effect, we introduce additional lamp furnace heat treatment. For p-a-Si:H layer with the ratio of $SiH_4:B_2H_6:H_2$=30:30:120, at $200^{\circ}C$, 50 W power, 0.2 Torr for 30 min. $20\;mm\;{\times}\;20\;mm$ size fiber laser cut wafers were activated by Q-switched fiber laser (1,064 nm) with different sets of power levels and periods, and for the lamp furnace annealing, $980^{\circ}C$ for 30 min heat treatment were implemented. To make the sheet resistance expectable and uniform as important processes for the $p^+$ layer on a polished n-type silicon wafer of (100) plane, the Q-switched fiber laser used. In consequence of comparing the results of lifetime measurement and sheet resistance relation, the fiber laser treatment showed the trade-offs between the lifetime and the sheet resistance as $100\;{\omega}/sq.$ and $11.8\;{\mu}s$ vs. $17\;{\omega}/sq.$ and $8.2\;{\mu}s$. Diode level device was made to confirm the electrical properties of these experimental results by measuring C-V(-F), I-V(-T) characteristics. Uniform and expectable boron heavy doped layers by fiber laser and lamp furnace are not only basic and essential conditions for the n-type crystalline silicon solar cell fabrication processes, but also the controllable doping concentration and depth can be established according to the deposition conditions of layers.

• Corrosion Science and Technology
• /
• v.11 no.1
• /
• pp.9-14
• /
• 2012

The formation of the Fe-Al inhibition layer in hot-dip galvanizing is a confusing issue for a long time. This study presents a characterization result on the inhibition layer formed on C-Mn-Cr and C-Mn-Si dual-phase steels after a short time galvanizing. The samples were annealed at $800^{\circ}C$ for 60 s in $N_{2}$-10% $H_{2}$ atmosphere with a dew point of $-30^{\circ}C$, and were then galvanized in a bath containing 0.2 %Al. X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM) was employed for characterization. The TEM electron diffraction shows that only $Fe_{2}Al_{5}$ intermetallic phase was formed. No orientation relationship between the $Fe_{2}Al_{5}$ phase and the steel substrate could be identified. Two peaks of Al 2p photoelectrons, one from metallic aluminum and the other from $Al^{3+}$ ions, were detected in the inhibition layer, indicating that the layer is in fact a mixture of $Fe_{2}Al_{5}$ and $Al_{2}O_{3}$. TEM/EDS analysis verifies the existence of $Al_{2}O_{3}$ in the boundaries of $Fe_{2}Al_{5}$ grains. The nucleation of $Fe_{2}Al_{5}$ and the reduction of the surface oxide probably proceeded concurrently on galvanizing, and the residual oxides prohibited the heteroepitaxial growth of $Fe_{2}Al_{5}$.

• Journal of IKEEE
• /
• v.12 no.3
• /
• pp.131-137
• /
• 2008

A silicon Fabry-Perot tunable thermo-optic filter for WDM using the thin film silicon coating is proposed and experimented. The filter is implemented by using the CMP process and polishing both sides of the commercial silicon wafer with normal thickness of 100${\mu}m{\pm}$1%. The filter also has 2-layer or 3-layer dielectrics thin film coating mirror which are alternated ${\lambda}$/4 layers of $SiO_2$($n_{low}$=1.44) and a-Si($n_{high}$=3.48) for the central wavelength of 1550nm by RF sputtering. The experiment shows that FSR is 3.61nm and FWHM is 0.56nm and the finesse is 6.4 for 2-layer mirror with the reflection of 61%, and that FSR is 3.36nm and FWHM is 0.13nm and the finesse is 25.5 for 3-layer mirror with the reflection of 89%. According to thermo-optic effect, the transmitted central wavelength of 1549.73nm at $23^{\circ}C$ is shifted to 1550.91nm at $30^{\circ}C$ and 1553.46nm at $60^{\circ}C$ for 2-layer mirror, and the transmitted central wavelength of 1549.83nm at $23^{\circ}C$ is shifted to 1550.92nm at $30^{\circ}C$ and 1553.07nm at $60^{\circ}C$ for 3-layer mirror.

• Journal of the Korean Society for Marine Environment & Energy
• /
• v.7 no.1
• /
• pp.13-21
• /
• 2004

Temporal changes of Chl-α, physical and chemical factors were investigated by diurnal observation at 2-hour interval at three fixed stations in the western Chinhae Bay from 12 Aug. to 13 Aug. 1999. Difference of dissolved oxygen between surface and bottom layer was maximum when the thermocline were strong. Organic distribution such as COD was affected by the growth of phytoplankton. Limitting factor was nitrogen, that is, inorganic nitrogen plays a significant role on regulating the algal growth. Surface distribution of dissolved inorganic nitrogen was very low compared to bottom layer by uptake of organisms. Maximum value of Chl-α at station C2 and C11 were observed from subsurface layer, ranges of which exceeded possibility concentration of red tide outbreak, 10 mg/㎥. On the other hand, that of C15 exist at surface layer. In this area, DIN and DIP concentrations increased by input sources such as rainfall and benthic flux before the bloom of phytoplankton. Accumulation of phytoplankton occurred at subsurface layer by the rapid uptake of DIN, especially nitrate ion, when strong thermocline existed as approach to the afternoon, which led to the increase of organics in water column and oxygen deficiency water mass at bottom layer until late at evening. Since then, DIN increases gradually as water temperature decrease to minimum. The quantitative understanding of nitrogen of fluxed to and from the various sources is necessary for environmental management.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.10
• /
• pp.754-759
• /
• 2013

Aluminum oxide($Al_2O_3$) film deposited by atomic layer deposition (ALD) is known to supply excellent surface passivation properties on crystalline Si surfaces. Since $Al_2O_3$ has fixed negative charge, it forms effective surface passivation by field effect passivation on the rear side in p-type silicon solar cell. However, $Al_2O_3$ layer formed by ALD process needs very long process time, which is not applicable in mass production of silicon solar cells. In this paper, plasma-assisted ALD(PA-ALD) was applied to form $Al_2O_3$ to reduce the process time. $Al_2O_3$ synthesized by ALD on c-Si (100) wafers contains a very thin interfacial $SiO_2$ layer, which was confirmed by FTIR and TEM. To improve passivation quality of $Al_2O_3$ layer, the deposition temperature was changed in range of $150{\sim}350^{\circ}C$, then the annealing temperature and time were varied. As a result, the silicon wafer with aluminum oxide film formed in $250^{\circ}C$, $400^{\circ}C$ and 10 min for the deposition temperature, the annealing temperature and time, respectively, showed the best lifetime of 1.6ms. We also observed blistering with nanometer size during firing of $Al_2O_3$ deposited on p-type silicon.

• Proceedings of the KWS Conference
• /
• 2005.06a
• /
• pp.229-231
• /
• 2005

Friction surfacing of STS304 consumable rod on S45C substrate was investigated by microstructural observation and mechanical tests. STS304 layer formed a strongly-bonded thick layer under a wide range of surfacing conditions. The hardness distribution showed the peak value in the boundry layer, while the highest coating efficiency obtained in the condition of 1000rpm-2.5mm/sec-2.5mm/sec. As the consumable rotation rate and the traveling rate increased, the coating efficiency tended to decrease. On the other hand, as the feeding rate increased, the coating efficiency appeared to be increased.

• Journal of the Microelectronics and Packaging Society
• /
• v.18 no.1
• /
• pp.23-27
• /
• 2011

Fabrication of porous silicon(PS) double layer by electrochemical etching is the first step in process of ultrathin solar cell using PS layer transfer process. The porosity of the porous silicon layer can be controlled by regulating the formation parameters such as current density and HF concentration. PS layer is fabricated by electrochemical etching in a chemical mixture of HF and ethanol. For electrochemical etching, highly boron doped (100) oriented monocrystalline Si substrates was used. Ths resistivity of silicon is $0.01-0.02\;{\Omega}{\cdot}cm$. The solution composition for electrochemical etching was HF (40%) : $C_2H_5OH$(99 %) : $H_2O$ = 1 : 1 : 2 (by volume). In order to fabricate porous silicon double layer, current density was switched. By switching current density from low to high level, a high-porosity layer was fabricated beneath a low-porosity layer. Etching time affects only the depth of porous silicon layer.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.93-93
• /
• 2008

This paper presents the Raman scattering characteristics of poly (polycrystalline) 3C-SiC thin films deposited on AlN buffer layer by atmospheric pressure chemical vapor deposition (APCVD) using hexamethyldisilane (MHDS) and carrier gases (Ar + $H_2$).The Raman spectra of SiC films deposited on AlN layer of before and after annealings were investigated according to the growth temperature of 3C-SiC. Two strong Raman peaks, which mean that poly 3C-SiC admixed with nanoparticle graphite, were measured in them. The biaxial stress of poly 3C-SiC/AlN was calculated as 896 MPa from the Raman shifts of 3C-SiC deposited at $1180^{\circ}C$ on AlN of after annealing.