• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.5
• /
• pp.3286-3291
• /
• 2014

A study on the crack protection and thermal insulation properties of the expanded perlite inorganic composites was performed. Mixed expanded perlite with a water glass was stabilized for 24 hrs at room temperature in the mold and, thereafter, converted into a massive foamed body through complete drying process at $150^{\circ}C$. Aluminum phosphate and micron size mica powder were used as a reaction accelerator and a stabilizer for thermal crack, respectively. Especially, use of mica exhibited a remarkable effect on the protection of thermal crack at higher temperature over $500^{\circ}C$, and thermal conductivity of the composites was enhanced with higher perlite contents, showing ca. 0.09 W/mK for the sample of 100/200/10/1.5 water glass/perlite/mica/Al phosphate by weight. A severe dimensional deformation of the composite materials was observed over $600^{\circ}C$, however, showing a temperature limitation for a practical application. The facts were considered as the results from the glass transition temperature of the water glass, of which main component is sodium silicate.

• Journal of Biomedical Engineering Research
• /
• v.16 no.3
• /
• pp.331-336
• /
• 1995

A composite material was produced as an artificial bone substitute which is gradually degrAded and replaced by the regenerated natural bones after implantation. To detect the effect of the material on the cell's activity, the composite specimens were placed in MEMs and incubated at $37^{\circ}C$ for one week. Human uterus cervical cancer origin HeLa 3 cells and mouse subcutaneous origin L929 cells were cul- tured in the specimen dissolved MEMs for 5 days to investigate cytotoxicity via cell growth rates. ${Na_2}^{51}CrO_4$ solution was added to the media, to label the HeLa 53 cells, and the released amount of $^{51}Cr$ was measured by a $\gamma$-counter. On the cell growth investigation, no significant cytotoxic phenomena were revealed in both HeLa S3 and L929 cell cultures. On the released 51CR from the incubated HeLa 53 cells, no significant cell degeneration was observed from the composite embedded MEMs.

• Membrane Journal
• /
• v.19 no.2
• /
• pp.96-103
• /
• 2009

A series of organic-inorganic composite membranes from poly(vinyl chloride) (PVC) graft copolymer electrolyte and heteropolyacid (HPA) were prepared for proton conducting membranes. First, poly(vinyl chloride)-g-poly(styrene sulfonic acid) (PVC-g-PSSA) was synthesized by atom transfer radical polymerization (ATRP) using direct initiation of the secondary chlorines of PVC. HPA nanoparticles were then incorporated into the PVC-g-PSSA graft copolymer though the hydrogen bonding interactions, as confirmed by FT-IR spectroscopy. The proton conductivity of the composite membranes increased from 0.049 to 0.068 S/cm at room temperature with HPA contents up to 0.3 weight traction of HPA, presumably due to both the intrinsic conductivity of HPA particles and the enhanced acidity of the sulfonic acid of the graft copolymer. The water uptake decreased from 130 to 84% with the increase of HPA contents up to 0.45 of HPA weight traction, resulting from the decrease in number of water absorption sites due to hydrogen bonding interaction between the HPA particles and the polymer matrix. Thermal gravimetric analysis (TGA) demonstrated the enhancement of thermal stabilities of the composite membranes with increasing concentration of HPA.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.06a
• /
• pp.64.2-64.2
• /
• 2010

In order to improve the overall power conversion efficiency in dye-sensitized solar cells (DSSCs), it is very important to secure the sufficient surface area of photocatalytic nanoparticles layer for absorbing dye molecules. It is because increasing the amount of dye absorbed generally results in increasing the amount of light harvesting. In this work, we proposed a new method for increasing the specific surface area of photocatalytic titanium oxide ($TiO_2$) nanoparticles by using an inorganic templating method. Salt-$TiO_2$ composite nanoparticles were synthesized in this approach by spray pyrolyzing both the titanium butoxide and sodium chloride solution. After aqueous removal of salt from salt-$TiO_2$ composite nanoparticles, mesoporous $TiO_2$ nanoparticles with pore size of 2~50 nm were formed and then the specific surface area of resulting porous $TiO_2$ nanoparticle was measured by Brunauer-Emmett-Teller (BET) method. Generally, commercially available P-25 with the average primary size of ~25 nm $TiO_2$ nanoparticles was used as an active layer for dye-sensitized solarcells, and the specific surface area of P-25 was found to be ~50 $m^2/g$. On the other hand, the specific surface area of mesoporous $TiO_2$ nanoparticles prepared in this approach was found to be ~286 $m^2/g$, which is 5 times higher than that of P-25. The increased specific surface area of $TiO_2$ nanoparticles will absorb relatively more dye molecules, which can increase the short curcuit current (Jsc) in DSSCs. The influence of nanoporous structures of $TiO_2$ on the performance of DSSCs will be discussed in terms of the amount of dye molecules absorbed, the fill factor, the short circuit current, and the power conversion efficiency.

• Journal of Hydrogen and New Energy
• /
• v.25 no.6
• /
• pp.561-569
• /
• 2014

Ceria ($CeO_2$) was used to increase the durability of the membrane in the polymer electrolyte membrane water electrolysis (PEMWE) circumstance. The sulfonated polyether ether ketone (SPEEK) as polymer matrix was prepared in the sulfonation reaction of polyether ether ketone (PEEK) to improve electrochemical characteristics. After sulfonation reaction, the organic-inorganic blended composite membranes were prepared by means of sol-gel casting method with loading the highly dispersed $CeO_2$ and Cs-substituted molybdophosphoric acid (Cs-MoPA) with cross-linking agent (tetrapropyl orthosilicate). Consequently, the composite membrane CL-SPEEK/Silane 4wt%/Cs-MoPA/Ceria(1%) showed the improved characteristics such as 82% of water content, 0.11136 S/cm of proton conductivity at $80^{\circ}C$, 55.50 MPa of tensile strength and 4.37% of breeding out of MoPA.

• Membrane Journal
• /
• v.26 no.6
• /
• pp.432-448
• /
• 2016

In the last decade, various types of energy harvesting and conversion systems based on ion exchange membranes (IEMs) have been developed for eco-friendly power generation and energy-grid systems. In these membrane-based energy systems, high ion selectivity and conductivity properties of IEMs are critical parameters to improve efficiency of the systems such as proton exchange membrane fuel cells, anion exchange membrane fuel cells, redox flow batteries, water electrodialysis for hydrogen production, and reverse electrodialysis. This article suggests variable approaches to overcome trade-off limitation of polymeric membrane ion transport properties by reviewing various types of composite ion-exchange membranes including novel inorganic-organic nanocomposite membrane, surface modified membranes, cross-linked and pore-filled membranes.

• Applied Chemistry for Engineering
• /
• v.16 no.1
• /
• pp.112-116
• /
• 2005

We investigated the surface modification method for the preparation of organic-inorganic hybrid composite thin film. Gelatin obtained from the decomposition of collagen was allowed to adsorb in a polystyrene tissue culture dish for 2 h to from layers of gelatin. Supersaturated ionic solution of calcium and phosphorus was injected on the gelatin adsorbed layer to form calcium phosphate thin film. During the initial period of incubation, nucleates were formed. With increase of the incubation time, CaP (calcium phosphate) thin film grew on the surface of the culture dish. The gelatin/CaP thin film displayed the highly porous three-dimensional surface structure. Attenuated, total reflectance Fourier transform, infra-red spectroscopy (ATR-FTIR) was used to analyze the chemical properties of CaP film. The analysis demonstrated that the CaP film formed at initial period of treatment appeared to be amorphous. With increase of incubation time, the crystallinity of the film was slightly increased, but the presence of the peaks for the low crystalline CaP confirmed that the CaP thin film prepared in this study was poorly crystallized.

• Journal of Hydrogen and New Energy
• /
• v.26 no.3
• /
• pp.212-220
• /
• 2015

The engineering plastic of sulfonated polyether ether ketone (SPEEK) as a polymer matrix has been developed in this lab to replace Nafion, solid polymer electrolytes of perfluorosulfonic acid membrane which has several flaws such as high cost, and limited operational temperature above $80^{\circ}C$. The SPEEK was prepared in the sulfonation reaction of polyether ether ketone (PEEK). The organic-inorganic blended composite membranes were prepared by sol-gel casting method with loading the highly dispersed ceria and cesium-substituted tungstosilicic acid (Cs-TSiA) with cross-linking agent contents of 0.01 mL. In conclusion, CL-SPEEK/Cs-TSiA/ceria 1% membrane showed the optimum results such as 0.1882 S/cm of proton conductivity at $80^{\circ}C$, and 99.61 MPa of tensile strength which were better than Nafion 117 membrane.

• Elastomers and Composites
• /
• v.52 no.1
• /
• pp.22-26
• /
• 2017

The thermal conductivity and the adhesive properties were measured, after synthesis of thermal conductive composite which was obtained as a result of mixing alumina or graphite with acrylic adhesive synthesized by UV polymerization. The adhesive properties of the composite were evaluated measuring the peel strength at 180 degrees, the retention, and the initial tack;the thermal conductivity was estimated using laser flash analysis. As the filler contents increased, a decrease in peel strength and initial tack and an increase in retention and thermal conductivity were observed. When compared to alumina, the adhesion of graphite showed a dramatic decrease, whereas the thermal conductivity was further enhanced. It was found out that the small size of graphite increased the mechanical interlocking between the polymer and the filler, and it was easier for graphite to come into contact with other graphite in the matrix.

• Composites Research
• /
• v.15 no.1
• /
• pp.32-40
• /
• 2002

This study developed fabrication process of $SiC_p/Al$ metal matrix composites as electronic packaging materials by squeeze casting method. The $SiC_p$ preform were fabricated in newly designed preform mold using about 0.8 % of inorganic binder(SiO$_2$) and 5 vol.% of $Al_2O_3$fiber. To infiltrate the molten metal into the preform, fabrication condition such as the temperature and the pressure were selected. Applying the fabrication conditions, heat transfer analysis were preformed using finite element method and thus analyzed the temperature distribution and cooling characteristic during the squeeze casting. For the fabricated composites, impact toughness and thermal expansion coefficient were measured. The metal matrix composites developed in this study have 0.2~0.3 J impact toughness, $8~10 ppm/^{\circ}C$ thermal expansion coefficient and $2.9~3.0g/cm^3$density which is appropriate properties for electronic packaging application.