• Journal of Powder Materials
• /
• v.20 no.3
• /
• pp.221-227
• /
• 2013

$TiB_2$-reinforced iron matrix composite (Fe-$TiB_2$) powder was in-situ fabricated from titanium hydride ($TiH_2$) and iron boride (FeB) powders by the mechanical activation and a subsequent reaction. Phase formation of the composite powder was identified by X-ray diffraction (XRD). The morphology and phase composition were observed and measured by field emission-scanning electron microscopy (FE-SEM) and energy-dispersive X-ray spectroscopy (EDS), respectively. The results showed that $TiB_2$ particles formed in nanoscale were uniformly distributed in Fe matrix. $Fe_2B$ phase existed due to an incomplete reaction of Ti and FeB. Effect of milling process and synthesis temperature on the formation of composite were discussed.

• Journal of Powder Materials
• /
• v.13 no.6 s.59
• /
• pp.432-438
• /
• 2006

Aluminum nitride (AlN) nanopowders with low degree of agglomeration and uniform particle size were synthesized by carbothermal reduction of alumina and subsequent direct nitridization. Boehmite powder was homogeneously admixed with carbon black nanopowders by ball milling. The powder mixture was treated under ammonia atmosphere to synthesize AlN powder at lour temperature. The effect of process variables such as boehmite/carbon black powder ratio, reaction temperature and reaction time on the synthesis of AlN nanopowder was investigated.

• Progress in Superconductivity
• /
• v.14 no.2
• /
• pp.116-121
• /
• 2012

Effect of mixed gas and additional Mg powder in an annealing process of the $MgB_2$ is investigated. Four different type of samples were prepared, each in different annealing environment of Ar, $Ar+4%H_2$, Ar with Mg powder and $Ar+4%H_2$ with Mg powder. Different annealing environment did not affect the electron-phonon interaction which is reflected from the same superconducting transition of 36.6 K for all samples. The reducing effect of hydrogen is clearly depicted from the presence of excess Mg in sample synthesized in $Ar+4%H_2$ gas implying the reduced rate of reaction between Mg and B. This has manifested itself in terms of slightly increased high-field critical current density of the sample. In contrast, the sample synthesized in $Ar+4%H_2$ with Mg powder, has shown overall enhancement in the superconducting properties as presented by higher diamagnetic saturation and critical current density.

• Macromolecular Research
• /
• v.14 no.3
• /
• pp.287-299
• /
• 2006

To successively synthesize star-branched polymers, we developed a new iterative methodology which involves only two sets of the reactions in each iterative process: (a) an addition reaction of DPE or DPE-functionalized polymer to a living anionic polymer, and (b) an in-situ reaction of 1-(4-(4-bromobutyl)phenyl)-1-phenylethylene with the generated 1,1-diphenylalkyl anion to introduce one DPE functionality. With this methodology, 3-, 4-, and 5-arm, regular star-branched polystyrenes, as well as 3-arm ABC, 4-arm ABCD, and a new 5-arm ABCDE, asymmetric star-branched polymers, were successively synthesized. The A, B, C, D, and E arm segments were poly(4-trimethylsilylstyrene), poly(4-methoxystyrene), poly(4-methylstyrene), polystyrene, and poly(4-tert-butyldimethylsilyloxystyrene), respectively. All of the resulting star-branched polymers were well-defined in architecture and precisely controlled in chain length, as confirmed by SEC, $^1H$ NMR, VPO, and SLS analyses. Furthermore, we extended the iterative methodology by the use of a new functionalized DPE derivative, 1-(3-chloromethylphenyl)-1-((3-(1-phonyletheny1)phenyl) ethylene, capable of introducing two DPE functionalities via one DPE anion reaction site in the reaction (b). The number of arm segments of the star-branched polymer synthesized by the methodology could be dramatically increased to 2, 6, and up to 14 by repeating the iterative process.

• Bulletin of the Korean Chemical Society
• /
• v.18 no.12
• /
• pp.1291-1295
• /
• 1997

The catalytic dehydrocoupling of di-n-butylstannane n-Bu2SnH2 by the Cp2MCl2/Red-Al (M = Ti, Zr, Hf) and M(CO)6/Red-Al in situ combination catalysts yielded a mixture of two kinds of catenated products: one is a cross-linked insoluble solid, and the other is a non-cross-linked soluble solid (≒Sn5) or viscous oil (≒Sn2). The soluble oligostannanes could be produced by simple dehydrocoupling of n-Bu2SnH2, whereas the insoluble polystannanes could be obtained via disproportionation/dehydrocoupling combination process of n-Bu2SnH2. The disproportionation/dehydrocoupling combination process may initially produce a low-molecular-weight oligostannane with partial backbone Sn-H bonds which could then undergo an extensive cross-linking reaction of backbone Sn-H bonds, resulting in the formation of an insoluble polystannane.

• Progress in Superconductivity and Cryogenics
• /
• v.14 no.4
• /
• pp.5-11
• /
• 2012

In this review article, we focus on various co-evaporation technologies developed for the fabrication of high performance $REBa_2Cu_3O_{7-{\delta}}$ (RE: Y and Rare earth elements, REBCO) superconducting films. Compared with other manufacturing technologies for REBCO films such as sputtering, pulsed laser deposition (PLD), metal-organic deposition (MOD), and metal organic chemical vapor deposition (MOCVD), the co-evaporation method has a strong advantage of higher deposition rate because metal sources can be used as precursor materials. After the first attempt to produce REBCO films by the co-evaporation method in 1987, various co-evaporation technologies for high performance REBCO films have been developed during last several decades. The key points of each co-evaporation technology are reviewed in this article, which enables us to have a good insight into a new high throughput process, called as a Reactive Co-Evaporation by Deposition and Reaction (RCE-DR).

• Polymer(Korea)
• /
• v.27 no.1
• /
• pp.75-83
• /
• 2003

Dicyanate-clay nanocomposite has been prepared by a melt in-situ polymerization method for different modifiers and cation exchange capacity (CEC) values in order to study dispersion and mechanical property. Various dicyanate nanocomposites were prepared by using different MMT systems containing different intercalants which led to different initial gallery heights and packing density. Depending on compatibility between dicyanate and clays, the degree of dispersion varied. Dispersion of clay plates in dicyanate resin depended mainly on CEC and aliphatic chain length of modifier. The lower CEC and shorter aliphatic chain length of modifier gave the exfoliation structure. It was also found that the reactivity of intercalant with dicyanate resin was one of the key factors facilitating the intercalation/exfoliation process of dicyanate/MMT nanocomposites. Shear modulus of reaction-induced dicyanate nanocomposite was significantly increased.

• Bulletin of the Korean Chemical Society
• /
• v.32 no.7
• /
• pp.2351-2357
• /
• 2011

Three new metal-organic copper(II) complexes, $[Cu(H_2PZTC)_2]_n{\cdot}2nH_2O$ (1), $[Cu(HPZTC){\cdot}2H_2O]_n{\cdot}2nH_2O$ (2), and $Cu_2[(PZHD)(OH)(H_2O)_2]_n$ (3) ($H_3PZTC$ = pyrazine-2,3,5-tricarboxylic acid, $PZHD^{3-}$ = 2-hydroxypyrazine-3,5-dicarboxylate), have been synthesized from $Cu(II)/H_3PZTC$ system under different synthetic conditions, and characterized by single-crystal X-ray diffraction, elemental analysis, IR spectroscopy and thermogravimetric analysis. In complexes 1 and 2, $H_3PZTC$ ligands loose one and two protons, which were transformed into $H_2PZTC^-$ anion and $HPZTC^{2-}$ dianion under different preparation condition, respectively. Furthermore, two ligands coordinate with Cu(II) cations in different modes, leading to the formation of the different chain structures. In complex 3, $H_3PZTC$ ligand was converted into a new ligand-PZHD by in situ decarboxylation and hydroxylation under a higher pH value than that for complexes 1 and 2. PZHD ligands link the Cu(II) cations to form a 2D layer structure. These results demonstrate that the preparation conditions, including pH value and reaction temperature etc, play an important role in the construction of complexes based on $H_3PZTC$ ligand.

• Journal of Environmental Science International
• /
• v.21 no.4
• /
• pp.507-515
• /
• 2012

To improve the mechanical properties of hydroxyapatite (HA)/waterborne polyurethane (WBPU) composites, the hydroxyl group of HA was modified by urethane reactions: the hydroxyl groups of HA were reacted with aliphatic or cyclic diisocyanate, and then the modified HAs were extended by adding polyol and/or ${\varepsilon}$-caprolactone. Composites were prepared by the prepolymer process method: the modified HA was directly pured into the urethane reaction of isocyanate and polyol. The properties of modified HA/WBPU composites were investigated by thermogravimetric analysis, tensile strength, and water resistance. The results showed that the reactivity of aliphatic diisocyanate to the hydroxy group of HA was faster than that of cyclic one. Comparing to those of pure HA/WBPU composite films, the thermal stability, water resistance, and mechanical properties of the modified composite films increased with a degree of modification of HA.

• Proceedings of the KSR Conference
• /
• 2011.10a
• /
• pp.261-267
• /
• 2011

The test fit has commonly used for the evaluation of the railbed condition, and indirect methods by using the compressional wave are also studied. the direct evaluation method by penetration test has not been studied. For the measurement of in-situ cone tip resistance of the railbed with minimizing the disturbance of the upper railbed. the cone penetrometer with the helical type outer rod(CPH) was developed. The outer rod, which has helical screw, is penetrated through the gravel layer and provides the reaction force for cone penetration testing. the cone tip resistances are measured by the mini cone penetrometer, where diameter is 15mm. For the developing the mini cone, strain gauge installation, circuit configuration, penetration rates and calibration process are considered. For the easy penetration of the screw rod in the field, the reaction force stepping plate and guide column are arranged. The screw rod are penetrated through the gravel layer. And the mini cone was pushed into the subgrade railbed at the penetration rate of 1mm/sec. The penetration test shows that the cone tip resistance increases along the depth. In addition, the subgrade condition is evaluated. This study demonstrates that the CPH may be effectively used for the evaluation of subgrade method any damage of the gravel layer.