• Journal of the Korean Society for Heat Treatment
• /
• v.6 no.1
• /
• pp.17-25
• /
• 1993

The Cu - $Nb_3Sn$ composites wire as a superconducting material was prepared by in situ method as follow: Cu - 15wt.% Nb alloys which were melted in a high -frequency induction furnace and casted in bar were cold-worked up to the final diameter of 0.24 mm, electroplated with Sn, pre-treated in two steps and then diffused at $550{\sim}650^{\circ}C$ for 24 ~ 96 hrs. The overall $J_c$ and $T_c$ of the specimens were measured by the four point-probe method at 10 K in the magnetic field of 0 Tesla. The overall $J_c$ of the composites wire which diffused at $550^{\circ}C$ after pre-treating in two steps were generally higher than those of the wire at either $600^{\circ}C$ or $650^{\circ}C$. For the specimens diffused at $550^{\circ}C$, the overall $J_c$ were increased until 72 hrs. of diffusion time and then decreased. However, in case of diffusion at $600^{\circ}C$ and $650^{\circ}C$, the overall $J_c$ were gradually decreased from the beginning. The maximum overall $J_c$ obtained in this experiment was $1.3{\times}10^4\;A/cm^2$, which was measured for the specimen diffused at $550^{\circ}C$ for 72 hrs. When the specimens were diffused at $550^{\circ}C$ for 72 hrs, after pre-treating, the measured critical temperature, $T_c$ was 16.19 K. Similar $T_c$ value were obtained in other specimens regardless of diffusion time and temperature.

• Journal of the Korean Magnetics Society
• /
• v.18 no.5
• /
• pp.195-199
• /
• 2008

Composites of $Fe_{93.5}Si_{6.5}$ powder and epoxy were prepared using a thermal curing process. Scanning electron microscope (SEM), vibrating sample magnetometer (VSM) and network analyzer were used to analyze the structure, electromagnetic properties and microwave absorption of the composites. Results show that the saturation magnetization depends on the fraction of the $Fe_{93.5}Si_{6.5}$ powder in the composite, which affects initial permeability. It is believed that the eddy current loss is a dominant factor over 1 GHz and that the resonance frequency of the composite decreases with increasing fractions of $Fe_{93.5}Si_{6.5}$ powder. Finally, reflection loss was calculated from the permeability and permittivity of these composites. Composite with 50 wt.% $Fe_{93.5}Si_{6.5}$ powder fractions and 5 mm thickness showed reflection loss below -20 dB from 3.66 GHz to 4.16 GHz. Therefore, it is believed that thin Fe-Si/epoxy composites may be a good candidate for microwave absorption application.

• Resources Recycling
• /
• v.11 no.5
• /
• pp.30-33
• /
• 2002

Recently in the progress of electronic equipment, power transformer was considered an important part. To make power transformer with miniaturization, lightening, low Power, we need a high efficiency core material. In this paper, we added $V_2$$O_{5}$ and $CaCo_3$ to Mn-Zn Ferrite to make a high efficiency, low loss core material. The compositions are MnO : ZnO : $Fe_2$$O_3$=37 : 11 : 52 mol%. They were sintered at 1250 for Three hours. Initial permeability was measured at 0.1 MHz. At 200 mT, Power loss was measured by temperature changing at 25 KHz, 50 KHz, 100 KHz. When we added $V_2$$O_{5}$ and $CaCo_3$, 0.08 wt%, 0.05 wt% respectively, we get 415 ㎾/㎥ at 200 mT, 100 KHz, $60^{\circ}C$. We can reduce eddy current loss as a main loss of high frequency by addition of a little mount of $V_2$$O_{5}$ $CaCo_3$. So we can decrease the power transformer's power loss.

• The Journal of Korean Institute of Electromagnetic Engineering and Science
• /
• v.24 no.4
• /
• pp.466-473
• /
• 2013

In this paper, a compact planar multi-loop self-resonant coil of high quality factor with a coaxial cross section is proposed for effective wireless charging. The proposed coil has high Q-factor and a resonant frequency of a coil can be easily controlled by adjusting distributed capacitance. For designing the coil, a self-inductance and a distributed capacitance are calculated theoretically. The self-inductance is calculated from the sum of the mutual energies between small circular loops that are made by dividing the cross section of the coil. To verify its properties and calculation results, the self-resonant coils are fabricated by using a coaxial cable with characteristic impedance of $50{\Omega}$. The measured frequencies are very consistent with the calculated ones. In addition, the resonant frequency can be adjusted slightly by the tuning parameter ${\gamma}$. The resonant coils are applied to a tablet PC, the Q-factors of the Tx and Rx resonant coils are 282 and 135, respectively. As a result of measurement when height between the two resonant coils is 4.4 cm, the power transfer efficiency is more than 80 % within a radius of 5 cm.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.28 no.1
• /
• pp.16-24
• /
• 2008

Near-field scanning microwave microscope (NSMM) has been used to characterize the electromagnetic properties of samples based on a cavity perturbation technique. We used a NSMM using a waveguide cavity to couple a metallic probe tip as a point like evanescent field emitter. We explained the quality of our NSMM system by applying the cavity perturbation theory. First, to make a shape perturbation, we inserted linear and loop probes in the waveguide resonator. To check up electric and magnetic field distribution inside the waveguide resonator by shape perturbation, we confirmed the field distribution by using a HFSS simulation. Second, to make material perturbation, we located a dielectric sample in front of the probe tip and measured reflection coefficient $(S_{11})$. We found that the resonance frequency$(f_r)$ was changed linearly as the dielectric constant of resonator$({\varepsilon}_r)$ increased when ${\Delta}{\varepsilon}\;and\;{\Delta}{\mu}$ were small.

• The Journal of Korean Institute of Electromagnetic Engineering and Science
• /
• v.19 no.9
• /
• pp.1051-1057
• /
• 2008

In this paper, we analyzed the characteristics of the EM wave absorber which was fabricated by using flake sendust (soft metal magnetic powder). The flake sendust was made of 3 different granularity by attrition mill. First, we have fabricated 3 kind of EM wave absorbers using the flake sendust and CPE(Chlorinated Polyethylene) and measured the S-parameters of the EM wave absorber. The complex relative permittivity and permeability were calculated from the measured data and the variations according to a change of granularity were researched. As a result, it was confirmed that the EM wave absorber using flake sendust with the $140{\mu}m$ average granularity has outstanding absorption ability in high frequency range(C band) for the reduction of eddy current loss(increase of permeability) and the increase of space charge polarization(increase of permittivity).

• Polymer(Korea)
• /
• v.30 no.6
• /
• pp.572-575
• /
• 2006

In this work, a variety of polymer based jelly phantoms suitable for the hyperthermia operations to human organs was synthesized in order to confirm the possibility of auxiliary cancer therapy. Specifically, using an appropriate material composition including polyethylene, Jelly phantoms for brain was prepared and characterized their electrical properties suitable for the monitoring the effect of electromagnetic wave from code division multiple access (CDMA) and personal communication service (PCS) on the human body. In the future, after injection of ferromagnetic nanoparticle into the jelly phantoms, new approach to propose the cancer therapy can be anticipated by monitoring the degree of temperature rise in human body using the photograph of Infrared camera.

• Journal of the Korean Magnetics Society
• /
• v.24 no.2
• /
• pp.56-59
• /
• 2014

The samples of $Ba_2CoZnFe_{12}O_{22}$ was synthesized by the solid-state reaction method. The toroids of $Ba_2CoZnFe_{12}O_{22}$ were sintered with various sintering temperature at 1050, 1100, 1150, and $1200^{\circ}C$, and studied by x-ray diffractometer, vibrating sample magnetometer, network analyzer, and Mssbauer spectrometer. From the XRD patterns, the density of samples increased with increasing sintering temperature. From the magnetic hysteresis curves up to 10 kOe at 295 K, the saturation magnetization ($M_s$) of $Ba_2CoZnFe_{12}O_{22}$ samples in various sintered at 1050, 1100, 1150 ,and $1200^{\circ}C$ were showed around $M_s$= 33.0 emu/g. However, With increasing sintering temperature, the coercivity ($H_c$) of samples decrease. Complex permeability and permittivity of samples in various sintering temperatures were measured between 100MHz to 4 GHz. With increasing sintering temperature, the permeability of samples increase.

• Journal of the Korean Magnetics Society
• /
• v.7 no.1
• /
• pp.13-18
• /
• 1997

The effects of the various raw material composition and sintered temperature on the physical properties of Ni-Zn ferrite have been investigated. They turned out to be spinel structure by X-ray diffraction and the size of grain from microscope was from 6 ${\mu}{\textrm}{m}$ to 16 ${\mu}{\textrm}{m}$. As the sintering temperature was increased from 1030 $^{\circ}C$ to 1070 $^{\circ}C$, the initial permeability and magnetic induction has increased and the both of Q factor and coercive force has decreased. The coercive force and curie temperature were almost the same at each specimen. Their values were about 0.20 Oe and 220 $^{\circ}C$. The frequency of specimen will used in the range from 400 kHz to 20 MHz. The basic composition of $Ni_{0.14}Zn_{0.64}Cu_{0.22}Fe_2O_4$ (specimen B) sintered at 1050 $^{\circ}C$ shows the best results at magnetic induction($B_r & B_m$).

• Journal of the Korean Magnetics Society
• /
• v.5 no.4
• /
• pp.269-274
• /
• 1995

The basic composition of Mn-Zn ferrite was $Mn_{0.631}Zn_{0.316}Fe_{2.053}O_{4}$(specimen A), $Mn_{0.584}Zn_{0.312}Fe_{2.104}O_{4}$(specimen B) and $Mn_{0.538}Zn_{0.308}Fe_{2.154}O_{4}$(specimen C) with additional 0.1 mol % $CaCo_{3}$ and 0.04 mol % $V_{2}O_{5}$. For high per¬meability and acceleration of grain growth, $CaCo_{3}$ and $V_{2}O_{5}$. was added. The mixture of the law materials was calcinated at $950^{\circ}C$ for 3 hours and then milled. The compacts of toroidal type were sintered at different temperature($1250^{\circ}C$, $1300^{\circ}C$, $1350^{\circ}C$) for 2 hours in $N_2$ atmosphere. The effects of the various raw material composition and sintered temperature on the physical properties of Mn-Zn ferrite have been investigated. They turned out to be spinel structure by X-ray diffraction and the size of grain from SEM was from $18\;\mu\textrm{m}\;to\;23\;\mu\textrm{m}$. As the sintering temperature was increased from $1250^{\circ}C$ to $1350^{\circ}C$, the initial permeability and magnetic induction has increased and the both of Q factor and coercive force has decreased. The coercive force and curie temperature were almost the same at each specimen Their values were about 0.45 Oe and $200^{\circ}C$. The frequency of specimen will used in the range from 200 kHz to 2 MHz. The basic composition of $Mn_{0.584}Zn_{0.312}Fe_{2.104}O_{4}$(specimen B) sintered at $1300^{\circ}C$ shows the best results at magnetic induction (Br & Bm).