• Korean Journal of Materials Research
• /
• v.14 no.8
• /
• pp.579-586
• /
• 2004

A study on the effects of oxide growth on the mechanical properties degradation of pure zirconium and Zircaloy-4 is carried out with high temperature tensile tests. It is found that the mechanical properties can deteriorate with the oxide growth less than $1\%$ of total specimen cross section, especially at $300\~400^{\circ}C$ that is zirconium alloy cladding temperature during the nuclear reactor operation. It is also revealed that Young's modulus changes little but yield strength and tensile strength drop down to $20\% and 40\%$ of the room temperature strength, respectively, in the temperature range. Fractographic analysis shows that the number of dimples decreases and fractured surface becomes smooth with increasing oxide thickness.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.09a
• /
• pp.47-51
• /
• 2001

The electrical degradation phenomena of epoxy composites to be used as a molding material for transformers were studied. The electrets were first manufactured by applying high voltages to five kinds of specimens given a mixing rate, and then TSC(Thermally Stimulated Current) values at the temperature range of $-160\sim200[^{\circ}C]$ were measured from a series of experiments. The behaviour of carrier and its origin in epoxy composites were examined, respectively, And various effects of electrical degradation on epoxy composites were also discussed in this study.

• Composites Research
• /
• v.16 no.6
• /
• pp.33-40
• /
• 2003

The initial thermal degradation of polymer matrix composite is not observed easily. At the beginning of thermal degradation of polymer matrix composites, phase transformation such as chain scission, oxidation occur, and then micro delamination is produced in matrix and interface between matrix and fiber before blistering. Initial heat damage deteriorate mechanical properties of composites. We presented the detection method of the initial heat damage of composites conveniently using ultrasonic technique. Absorption coefficient and material velocity was measured with thermal degradation and degree of cure. The more thermal degradation was progressed, the more absorption coefficient was increased. When the cure temperature is more high, the absorption coefficient of cured composite is increased and material velocity is decreased. We concluded that cure temperature is more high, the defects such as void is increased and molecular structure cured at high temperature has cross-linking structure which is more absorb the ultrasonic waves.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.16 no.3
• /
• pp.598-607
• /
• 1992

The environment degradation of structural steel under high temperature is one of the key phenomena governing the availability and life of plant. This degradation resulted from the microstructural changes due to the long exposure at high temperature affect the mechanical properties such as creep strength and toughness. For instance, boiler tube materials usually tend to degrade, after long term operation, by precipitates, spherodizing, coarsening, and change in chemical composition of carbides. In this study, the material degradation under high temperature exposure was investigated by evaluating the carbide precipitation. The electrochemical polarization method was facilitated to investigate the precipitation and coarsening of carbides. It was shown by the modified electrochemical potentiokinetic reactivation (EPR) tests that the passivation of Mo-rich carbides did not occur even in the anodic peak current (Ip) which indicates the precipitation of Mo$_{6}$C was also observed. And it was assured that special electrolytic cell assembled in this research can be used for the detection of Mo$_{6}$C precipitation in the field.eld.

• Food Science and Biotechnology
• /
• v.18 no.3
• /
• pp.717-723
• /
• 2009

Thermal degradation characteristics of sucrose was investigated. A 20% sucrose solution was heated to temperatures of $110-150^{\circ}C$ for 1-5 hr. Chromaticity, pH, organic acids, 5-hydroxymethylfurfural (HMF), free sugars, electron donating ability (EDA), and ascorbic acid equivalent antioxidant capacity (AEAC) of the heated sucrose solutions were evaluated. With increasing temperatures and times, the L-, a-, and b-values decreased; however, total color difference (${\Delta}E_{ab}$) increased. The pH and sucrose contents decreased, and fructose and glucose contents increased with increasing heating temperature and time. Organic acids, such as formic acid, lactic acid, and levulinic acid, and HMF contents increased with increasing heating temperatures and times. EDA (%) and the AEAC of the heated sucrose solutions increased with increasing heating temperature and time. The heated sucrose solution was more effective than unheated sucrose solution, having higher EDA (90 fold), and AEAC (13 fold).

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.18 no.1
• /
• pp.31-37
• /
• 2019

This study investigates the effects of long-term artificial-aging on hardness variation in the dissimilar metal weldments for nuclear power plant facilities. These dissimilar welds are inevitably required to join the components in nozzle parts of pressurized vessels, such as austenitic stainless steels and ferritic steels. A artificial thermal aging was conducted in an electrical furnace to simulate material degradation at high temperatures. The test materials were held at the temperature of $600^{\circ}C$ for 10000 hours and interrupted at various levels of degraded specimens. The degradation of hardness is a well-known phenomenon resulting from long-term aging or high-temperature degradation of structural materials. In this study, the variation of hardness at each position was different, and complicated in relation to microstructures such as twins, grains, precipitates, phase transformations, and residual stresses in dissimilar weldments. We discussed the variation of hardness in terms of microstructural changes during long-term aging.

• Steel and Composite Structures
• /
• v.45 no.3
• /
• pp.369-388
• /
• 2022

Composite effect between steel and recycled aggregate concrete (RAC) in steel reinforced-RAC (SRRAC) structures can effectively improve RAC's adverse mechanical properties due to the natural defects of recycled coarse aggregate (RCA). However, the performance of SRRAC after thermal exposure will have a great impact on the safety of the structure. In this paper, firstly, the mechanical properties of SRRAC structures after high temperatures exposure were tested, including 24 SRRAC columns and 32 SRRAC beams. Then, the change rules of beams and columns performance with the maximum temperature and replacement percentage were compared. Finally, the formulas to evaluate the residual bearing capacity of SRRAC beams and columns after exposure to high temperatures were established. The experimental results show that the maximum exposure temperature can be judged by the apparent phenomenon and mass loss ratio of RAC. After high temperatures exposure, the mechanical properties of SRRAC beams and columns change significantly, where the degradation of bearing capacity and stiffness is the most obvious. Moreover, it is found that the degradation degree of compression member is more serious than that of flexural member. The formulas of residual bearing capacity established by introducing influence coefficient of material strength agree well with the experimental results.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.10a
• /
• pp.28.2-28.2
• /
• 2011

The selective catalytic reduction (SCR) of NOx by $NH_3$ is well known as one of the most convenient, efficient, and economical method to prevent NOx emission in flue gas from stationary sources. The degradation of the reactivity is the obstacle for its real application, since high concentrations of sulfur dioxide and thermal factor would deactivate the catalyst. It is necessary to develop high stability of catalysts for low-temperature SCR. Among the transition metal oxides, $WO_3$ is known to exhibit high SCR activity and good thermal stability. The $MnOx-WO_3-TiO_2$ catalysts prepared by sol-gel method with various $WO_3$ contents were investigated for low-temperature SCR. These catalysts were observed in terms of micro-structure and spectroscopy analyses. The $WO_3$ catalyst as a promoter is used to enhance the thermal stability of catalyst since it increases the phase transition temperature of $TiO_2$ support. It was found that the addition of tungsten oxides not only maintained the temperature window of NO conversion but also increased the acid sites of catalyst.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2003.11a
• /
• pp.91-94
• /
• 2003

Ceramic femoral heads in the total hip replacement have been developed to reduce the polyethylene liner wear. Alumina and zirconia (3Y-TZP) are using in clinical application worldwide and there are many good test reports. However, alumina has a risk of catastrophic failure, and zirconia has the low temperature degradation in spite of enhanced fracture toughness. Recently, novel zirconia/alumina composite having low temperature degradation-free character and high fracture tough . was developed and it leads the lower wear 3f polyethylene than alumina and zirconia. In the present study, in order to optimise the microstructure of low temperature degradation (LTD)-free zirconia/alumina composite for the best wear resistance of polyethylene, various compositions of (LTD)-free zirconia/alumina composites were fabricated, and the sliding wear of UHMWPE against these novel composites were examined and compared with that against alumina and zirconia ceramics used for total hip joint heads.

• Current Applied Physics
• /
• v.18 no.12
• /
• pp.1600-1604
• /
• 2018

This paper reports on a systematic and quantitative assessment of light induced degradation (LID) and regeneration in full Al-BSF and passivated emitter rear contact cells (PERC) along with the fundamental understanding of the difference between the two. After LID, PERC cells showed a much greater loss in cell efficiency than full Al-BSF cells (~0.9% vs ~0.6%) because the degradation in bulk lifetime also erodes the benefit of superior BSRV in PERC cells. Three main regeneration conditions involving the combination of heat and light ($75^{\circ}C/1\;Sun/48h$, $130^{\circ}C/2\;Suns/1.5h$ and $200^{\circ}C/3\;Suns/30s$) were implemented to eliminate LID loss due to BO defects. Low temperature/long time ($75^{\circ}C/48h$) and high temperature/short time ($200^{\circ}C/30s$) regeneration process was unable to reach 100% stabilization. The intermediate temperature/time ($130^{\circ}C/1.5h$) generation achieved nearly full recovery and stabilization (over 99%) for both full Al-BSF and PERC cells. We discussed the effect of temperature, time and suns in regeneration mechanism for two cells.