• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.45-49
• /
• 2001

We have investigated physical and electrical properties of the Hf $O_2$/HfS $i_{x}$/ $O_{y}$ thin film for alternative gate dielectrics in the metal-oxide-semiconductor device. The oxidation of Hf deposited directly on the Si substrate results in the H $f_{x}$/ $O_{y}$ interfacial layer and the high-k Hf $O_2$film simultaneously. Interestingly, the post-oxidation N2 annealing of the H102/H1Si70y thin films reduces(increases) the thickness of an amorphous HfS $i_{x}$/ $O_{y}$ layer(Hf $O_2$ layer). This phenomenon causes the increase of the effective dielectric constant, while maintaining the excellent interfacial properties. The hysteresis window in C-V curves and the midgap interface state density( $D_{itm}$) of Hf $O_2$/HfS $i_{x}$/ $O_{y}$ thin films less than 10 mV and ~3$\times$10$^{11}$ c $m^{-2}$ -eV without post-metallization annealing, respectively. The leakage current was also low (1$\times$10-s A/c $m^2$ at $V_{g}$ = +2 V). It is believed that these excellent results were obtained due to existence of the amorphous HfS $i_{x}$/ $O_{y}$ buffer layer. We also investigated the charge trapping characteristics using Fowler-Nordheim electron injection: We found that the degradation of Hf $O_2$/HfS $i_{x}$/ $O_{y}$ gate oxides is more severe when electrons were injected from the gate electrode.e electrode.e.e electrode.e.

• Transactions on Electrical and Electronic Materials
• /
• v.4 no.3
• /
• pp.34-37
• /
• 2003

[ $HfO_2$ ] and $HfO_xN_y$ films were deposited by plasma-enhanced chemical vapor deposition using $Hf[OC(CH_3)_3]_4$ as the precursor in the absence of $O_2$. The crystallization temperature of the $HfO_xN_y$ films is higher than that of the $HfO_2$ film. Nitrogen incorporation in $HfO_xN_y$ was confirmed by auger electron spectroscopy analysis. After post deposition annealing (PDA) at 800$\Box$, the EOT increased from 1.34 to 1.6 nm in the $HfO_2$ thin films, whereas the increase of EOT was suppressed to less than 0.02 nm in the $HfO_xN_y$. The leakage current density decreased from 0.18 to 0.012 $A/cm^2$ with increasing PDA temperature in the $HfO_2$ films. But the leakage current density of $HfO_xN_y$ does not vary with increasing PDA temperature because an amorphous $HfO_xN_y$ films suppresses the diffusion of oxygen through the gate dielectric.

• Journal of Information Display
• /
• v.4 no.2
• /
• pp.1-6
• /
• 2003

In this paper, we demonstrate that the organic electrophosphorescent device is driven by the organic thin film transistor with spin-coated photoacryl gate insulator. It was found that electrical output characteristics in our organic thin film transistors using the staggered-inverted top-contact structure showed the non-saturated slope in the saturation region and the sub-threshold nonlinearity in the triode region, where we obtained the maximum power luminance that was about 90 $cd/m^2$. Field effect mobility, threshold voltage, and on-off current ratio in 0.45 ${\mu}m$ thick gate dielectric layer were 0.17 $cm^2/Vs$, -7 V, and $10^6$ , respectively. In order to form polyimide as a gate insulator, vapor deposition polymerization process was also introduced instead of spin-coating process, where polyimide film was co-deposited by high-vacuum thermal evaporation from 4,4'-oxydiphthalic anhydride (ODPA) and 4,4'-oxydianiline (ODA) and cured at 150${\sqsubset}$for 1hr. It was also found that field effect mobility, threshold voltage, on-off current ratio, and sub-threshold slope with 0.45 ${\mu}m$ thick gate dielectric films were 0.134 $cm^2/Vs$, -7 V, and $10^6$ A/A, and 1 V/decade, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.12
• /
• pp.1122-1127
• /
• 1998

Group II-AF_2$films such as $CaF_2$, $SrF_2$, and $BaF_2$ have been commonly used many practical applications such as silicon on insulatro(SOI), three-dimensional integrated circuits, buffer layers, and gate dielectrics in filed effect transistor. This paper presents electrical and structural properties of fluoride films as a gate dielectric layer. Conventional gate dielectric materials of TFTs like oxide group exhibited problems on high interface trap charge density($D_it$), and interface state incorporation with O-H bond created by mobile hydrogen and oxygen atoms. To overcome such problems in conventional gate insulators, we have investigated $CaF_2$ films on Si substrates. Fluoride films were deposited using a high vacuum evaporation method on the Si and glass substrate. $CaF_2$ films were preferentially grown in (200) plane direction at room temperature. We were able to achieve a minimum lattice mismatch of 0.74% between Si and $CaF_2$ films. Average roughness of $CaF_2$ films was decreased from 54.1 ${\AA}$ to 8.40 ${\AA}$ as temperature increased form RT and $300^{\circ}C$. Well fabricated MIM device showed breakdown electric field of 1.27 MV/cm and low leakage current of $10^{-10}$ A/$cm^2$. Interface trap charge density between $CaF_2$ film and Si substrate was as low as $1.8{\times}10^{11}cm^{-2}eV^{-1}$.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2004.05a
• /
• pp.53-56
• /
• 2004

The a-Si:H TFT using ferroelectric of SrTi $O_3$as a gate insulator is fabricated on glass. Dielectric characteristics of ferroelectric are superior to $SiO_2$and S $i_3$ $N_4$. Ferroelctric increases on-current, decreases thresh old voltage of TFT and also improves breakdown characteristics. The a-SiN:H has optical band gap of 2.61 eV, refractive index of 1.8~2.0 and resistivity of 10$^{13}$ - 10$^{15}$ $\Omega$cm, respectively. Insulating characteristics of ferroelectrics are excellent because dielectric constant of ferroelectric is about 60~100 and breakdown strength is over 1MV/cm. TFT using ferroelectric has channel length of 8~20${\mu}{\textrm}{m}$ and channel width of 80~200${\mu}{\textrm}{m}$. And it shows that drain current is 3.4$mutextrm{A}$ at 20 gate voltage, $I_{on}$ / $I_{off}$ is a ratio of 10$^{5}$ - 10$^{8}$ and $V_{th}$ is 4~5 volts, respectively. In the case of TFT without ferroelectric, it indicates that the drain current is 1.5 $mutextrm{A}$ at 20 gate voltage and $V_{th}$ is 5~6 volts. With the improvement of the ferroelectric thin film properties, the performance of TFT using this ferroelectric has advanced as a gate insulator fabrication technology is realized.zed.d.

• The Journal of Korea Institute of Information, Electronics, and Communication Technology
• /
• v.16 no.4
• /
• pp.180-186
• /
• 2023

Positive bias temperature instability (PBTI) degradation of n⁺ and p⁺ poly-Si gate high-voltage(HV) SiO2 dielectric nMOSFETs was investigated. Unlike the expectation that degradation of n⁺/nMOSFET will be greater than p⁺/nMOSFET owing to the oxide electric field caused by the gate material difference, the magnitude of the PBTI degradation was greater for the p⁺/nMOSFET than for the n⁺/nMOSFET. To analyze the cause, the interface state and oxide charge were extracted for each case, respectively. Also, the carrier injection and trapping mechanism were analyzed using the carrier separation method. As a result, it has been verified that hole injection and trapping by the p⁺ poly-Si gate accelerates the degradation of p⁺/nMOSFET. The carrier injection and trapping processes of the n⁺ and p⁺ poly-Si gate high-voltage nMOSFETs in PBTI are detailed in this paper.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.9 no.3
• /
• pp.576-581
• /
• 2005

In this paper. the a-Si:H TFT using ferroelectric of $SrTiO_3$ as a gate insulator is fabricated on glass. High k gate dielectric is required for on-current, threshold voltage and breakdown characteristics of TFT Dielectric characteristics of ferroelectric are superior to $SiO_2$ and $Si_3N_4$. Ferroelectric increases on-current and decreases threshold voltage of TFT and also ran improve breakdown characteristics.$SrTiO_4$ thin film is deposited by e-beam evaporation. Deposited films are annealed for 1 hour in N2 ambient at $150^{\circ}C\~600^{\circ}C$. Dielectric constant of ferroelectric is about 60-100 and breakdown field is about IMV/cm. In this paper, the TFT using ferroelectric consisted of double layer gate insulator to minimize the leakage current. a-SiN:H, a-Si:H (n-type a-Si:H) are deposited onto $SrTiO_3$ film to make MFNS(Metal/ferroelectric/a-SiN:H/a-Si:H) by PECVD. In this paper, TFR using ferroelectric has channel length of$8~20{\mu}m$ and channel width of $80~200{\mu}m$. And it shows that drain current is $3.4{\mu}A$at 20 gate voltage, $I_{on}/I_{off}$ is a ratio of $10^5\~10^8,\;and\;V_{th}$ is$4\~5\;volts$, respectively. In the case of TFT without having ferroelectric, it indicates that the drain current is $1.5{\mu}A$ at 20gate voltage and $V_{th}$ is $5\~6$ volts. If properties of the ferroelectric thin film are improved, the performance of TFT using this ferroelectric thin film can be advanced.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2002.05a
• /
• pp.128-128
• /
• 2002

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2002.05a
• /
• pp.52-52
• /
• 2002

• Proceedings of the Korean Vacuum Society Conference
• /
• 2007.02a
• /
• pp.108-108
• /
• 2007