• 한국건설순환자원학회논문집
• /
• 제3권1호
• /
• pp.65-71
• /
• 2007

Since pop-outs are occurred recently on concrete surface occasionally, it is needed to find out accurate causes and to suggest appropriate methods. On this study, it is investigated the occurrence mechanism of pop-outs caused by electric arc furnace Oxidizing slags as fine aggregate for concrete. As a result, it is investigated the cause of pop-outs that extremely small quantities of free CaO and free MgO in the electric furnace slag react with water to produce $Ca(OH)_2$ and $Mg(OH)_2$, so that their volumes are expanded and erupted about two times. As a resolution, it is needed to remove the potential cause of expansion by replacing the deteriorated concrete section up to the depth to secure the safe of structural element with repairing polymer mortar, especially more than 50MPa.

• 한국건축시공학회지
• /
• 제11권5호
• /
• pp.442-451
• /
• 2011

Blast furnace slag is recycled as a high value-added material, while steel slag is difficult to recycle or is recycled as a low-grade filler material due to its expansive characteristics. Its property is caused by the high content of free lime and instable steel oxides. Recently, an innovative and rapid cooling method for melting steel slag has been developed in Korea, which reduces free lime content to a minimum level and increases the stability of steel oxides. However, researches on the long-term stability are not sufficient so far. Therefore, this study, focusing on the electric arc furnace oxidizing slag in the steel slag, aims to investigate the properties of the steel slag aggregate, its long-term volume stability and the engineering strength of mortar, and using it as a fine aggregate. This study result indicated that it was possible for it to be used as concrete aggregate because the volume change of the steel slag appeared to be stable.

• 전력전자학회:학술대회논문집
• /
• 전력전자학회 2014년도 추계학술대회 논문집
• /
• pp.109-110
• /
• 2014

신재생에너지의 신뢰성 및 효율의 발전과 함께 컴퓨터 및 각종 디지털 부하의 증가로 인하여, 효과적인 DC 에너지 공급 시스템을 위한 연구가 진행되고 있다. 그중 DC 전원의 경우, 아크 발생과 누설전류 검출이 중요한 문제가 된다. 본 연구에서는 반도체 소자를 사용하여 아크가 발생하지 않게 하는 콘센트에, 누설 감지 감도는 8mA, 감지 시간은 120ms 이내의 누설 전류 검출 기능을 보강한 DC 콘센트를 제안한다.

• 콘크리트학회논문집
• /
• 제11권3호
• /
• pp.101-111
• /
• 1999

Compared with the BF slag, the EAF slag has expansion due to the reaction with water and free CaO. Therefore it is specified in Concrete Specification that the FAP slag aggregated must not be used in concrete. Because of this reason it is unusual to use the EAF slag aggregate in concrete. The EAF slag aggregate treated with accelerated and water aging was comparatively satisfied with fundamental properties, which are specific gravity, unit weight, abrasion and immersion expansion ratio, as concrete aggregate. Therefore when we measured the compressive strength till 28 days, we found that the mortar and concrete replacing the natural aggregate with the EAF slag aggregate by 4 steps had better results than the concrete using the natural aggregate in a view of the compressive strength. But at 91 days, concrete using the EAF slag aggregate had no difference with it using the natural aggregate.

• Journal of Welding and Joining
• /
• 제30권2호
• /
• pp.54-58
• /
• 2012

Al-coated steel sheets with excellent heat and corrosion resistance are widely used in various applications. In welding of thin plate, some defects such as unmelted zone and metal-through occur easily in the beginning and ending of welding line. In the study, the welding defects in Al-coated steel sheets were investigated with respect to plasma arc current, height between Cu block and base metals, and using a roller to align the height of the base metal. Full penetration and voids free welds were obtained with a plasma arc current 52A and weld speed 2.3m/min. An unmelted zone increased and Ericshen rate decreased as the height between Cu block and base metal increased from 0 to 0.6mm. Using a roller moving ahead of the plasma arc, the length of unmelted zone decreased from 1.7mm to 0.5mm.

• Current Photovoltaic Research
• /
• 제8권4호
• /
• pp.114-119
• /
• 2020

In this study, Mitigation of Potential-induced degradation (PID) for PERC solar cells using SiO2 Structure of ARC layer. The conventional PID test was conducted with a cell-level test based on the IEC-62804 test standard, but a copper PID test device was manufactured to increase the PID detection rate. The accelerated aging test was conducted by maintaining 96 hours with a potential difference of 1000 V at a temperature of 60℃. As a result, the PERC solar cell of SiO2-Free ARC structure decreased 22.11% compared to the initial efficiency, and the PERC solar cell of the Upper-SiO2 ARC structure decreased 30.78% of the initial efficiency and the PID reliability was not good. However, the PERC solar cell with the lower-SiO2 ARC structure reduced only 2.44%, effectively mitigating the degradation of PID. Na+ ions in the cover glass generate PID on the surface of the PERC solar cell. In order to prevent PID, the structure of SiNx and SiO2 thin films of the ARC layer is important. SiO2 thin film must be deposited on bottom of ARC layer and the surface of the PERC solar cell N-type emitter to prevent surface recombination and stacking fault defects of the PERC solar cell and mitigated PID degradation.

• 열처리공학회지
• /
• 제25권1호
• /
• pp.14-21
• /
• 2012

The effects of cutting condition and tempering temperature for the shape of cutting chip were investigated. For this purpose, a lead-free brass containing 1wt.% of Bi extruded at $750^{\circ}C$ in straight turning was used in this study. The cutting chip preferred was mainly found to be loose form of arc chips with curling discontinuity, and these were formed by shear fracture. However, some of fragmental element chip were found to be mixed when tempering temperature was as high as $500^{\circ}C$. The form and size of chip was more affected by feed rate than by tempering temperature and cutting rate. In addition, the cutting surface was observed to be formed more rough in the case of high feed rate and low cutting rate compared to low feed rate and high cutting rate.

• 한국진공학회지
• /
• 제17권3호
• /
• pp.189-194
• /
• 2008

플라즈마 진단법 중 손쉽고 구동이 용이한 장점으로 인해 범용 플라즈마 진단 장치로 사용되는 랑뮤어 (Langmuir) 탐침법은 탐침이 직접 플라즈마 내에 삽입됨으로써 플라즈마를 간섭하기 때문에 플라즈마 고유의 특성을 변형시키는 약점이 있다. 본 연구에서는 대기압 아르곤 자유 연소 아크 (free-burning arc)에 삽입된 랑뮤어 탐침에 의한 교란 영향을 고찰하기 위하여 탐침 유무에 따른 열플라즈마 상태를 수치계산 하였고, 온도장과 속도장이 왜곡된 정도를 비교 분석하였다. 열플라즈마를 모델링하기 위하여 열유동장과 전자기장에 관한 두 종류의 지배방정식을 상용 CFD 프로그램과 자체 제작한 서브루틴을 이용하여 연계 계산하였다. 삽입된 탐침에 의해 열플라즈마 온도장은 탐침의 앞뒤에서 모두 플라즈마 축의 수직 방향으로 큰 변화를 나타내는 열적 교란이 발생되었다. 속도장에서는 탐침 선단의 정체 영역과 후단 후류 영역에서 유동 교란이 발생되었으며, 삽입 된 탐침의 영향이 국부적인 것이 아닌 플라즈마 유동장 대부분 영역에 영향을 미침을 확인할 수 있었다. 따라서 탐침법의 신뢰성을 높이기 위해서는 탐침 삽입에 의한 플라즈마의 열유체역학적 교란을 고려해야 한다.

• 한국건설순환자원학회논문집
• /
• 제11권1호
• /
• pp.70-78
• /
• 2023

철강산업 부산물인 고로슬래그는 대부분이 콘크리트 혼화재 등으로 재활용되고 있지만, 제강슬래그는 아직까지 뚜렷한 재활용 용도가 마련되지 않고 있다. 특히 제강슬래그는 배출과정에 있어서 다량의 유리석회(Free CaO)를 함유하고 있어, 유리석회에 의한 팽창 붕괴성을 가지고 있기 때문에 콘크리트용 골재로 재활용하기 위해서는 이에 대한 검토가 필요한 실정이다. 최근에는 고온의 액상 제강슬래그를 고압의 압축공기로 분무하여 슬래그를 매우 작은 크기의 입자로 공기 중에 노출시킴으로써 급냉하는 방식인 아토마이징 공정이 개발되어 적용되고 있다. 따라서 이러한 방법으로 배출되는 전기로 산화슬래그 잔골재를 콘크리트용 골재로 사용하기 위해서는 충분한 물리·화학적 검토가 필요하다. 본 연구에서는 국내 E사에서 철강제조 공정의 부산물로 배출되는 전기로 산화슬래그 잔골재를 대상으로 물리·화학적 검토를 실시하였다. 즉, 아토마이징 공정을 통해 생산되는 전기로 산화슬래그 잔골재가 콘크리트용 골재로서 사용 가능한가에 대하여 실험적으로 검토함으로써 향후 전기로 산화슬래그 잔골재의 활용에 기초적인 자료를 제공하고자 한다. 실험결과, 전기로 산화슬래그 잔골재는 대부분의 항목에서 콘크리트용 잔골재의 품질규준을 만족하고 있는 것으로 나타났다.

• 한국건설순환자원학회논문집
• /
• 제6권4호
• /
• pp.112-118
• /
• 2012

철강 산업에서는 고로 슬래그, 전기로 슬래그, 전로 슬래그 등 많은 부산물이 발생한다. 그 중 제강 슬래그는 일반 골재와 달리 높은 CaO와 낮은 $SiO_2$가 존재하며, 이를 시멘트와 콘크리트에 적용하게 되면 일부 알칼리 반응을 발생시키는 원인이 된다. 한편, 국내외적으로 제강 슬래그 중 전기로 산화슬래그의 콘크리트 구조용 골재로 사용하는 기준이 제정되어 사용을 장려하고 있지만, 슬래그에 대한 체적 안정성은 해결하지 못하였다. 최근에 이런 문제점을 해결하기 위하여 제강 슬래그의 고속의 공기로 냉각하는 방법이 국내에서 개발되었으며, 이를 적용할 경우 슬래그의 체적 붕괴를 야기시키는 유리 석회의 함유량을 최소화시키고 철 산화물에 대한 안정성을 갖는 것으로 보고되고 있다. 이에 본 연구에서는 철강 산업에서 발생되는 제강슬래그의 고속의 공기로 냉각한 급냉 전기로 산화슬래그의 콘크리트용 골재로서 활용하기 위한 기초 연구이다. 이를 위해 급냉 전기로 산화슬래그 잔골재의 품질 특성을 검토하였으며, 골재의 입도별에 따른 모르타르 특성을 검토하였다. 실험 결과 급냉 전기로 산화슬래그 잔골재의 특성은 아토마이저 공정에 의한 특성을 반영하고 있으며, 기존 콘크리트용 골재 입도 분포 범위에 비해 작은 입도 분포 범위를 가지는 것으로 나타났다.