• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.27 no.12
• /
• pp.2004-2010
• /
• 2003

Fracture life and crack retardation behavior were examined experimentally using CT specimens of aluminum alloy 5083. Crack retardation life and fracture life were a wide difference. between 0.8 and 0.6 in proportion to ratio of load reduction. The wheeler model retardation parameter was used successfully to predict crack growth behavior. By using a crack propagation rule, prediction of fracture life can be evaluated quantitatively. A statistical approach based on Weibull distribution was applied to the test data to evaluate the dispersion in the retardation life and fracture life by the change of load reduction.

• Proceedings of the KSME Conference
• /
• 2004.11a
• /
• pp.172-177
• /
• 2004

Fatigue life prediction is based on fracture mechanics and database which is established from experimental method. Rubber material also uses the same way for fatigue life prediction. But the absence of standardization of rubber material, various way of composition by each rubber company and uncertainty of fracture criterion makes the design of fatigue life by experimental method almost impossible. Tearing energy which has its origin in energy release rate is evaluated as fracture criterion of rubber material and the applicability of fatigue life prediction method are considered. The system of measuring tearing energy using the principal of virtual crack extension method and fatigue life prediction by the minimum number of experiments are proposed.

• International Journal of Automotive Technology
• /
• v.7 no.6
• /
• pp.741-747
• /
• 2006

It has been almost impossible to predict the fatigue life in the field of rubber materials by numerical methods. One of the reasons is that there are no obvious fracture criteria and excessively various ways of mixing processes. Tearing energy is considered as a fracture criterion which can be applied to rubber compounds regardless of different types of fillers, relative to other fracture factors. Fatigue life of rubber materials can be approximately predicted based on the assumption that the latent defect caused by contaminants or voids in the matrix, imperfectly dispersed compounding ingredients, mold lubricants and surface flaws always exists. Numerical expression for the prediction of fatigue life was derived from the rate of rough cut growth region and the formulated tearing energy equation. Endurance test data for dumbbell specimens were compared with the predicted fatigue life for verification. Also, fatigue life of industrial rubber components was predicted.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.18 no.6
• /
• pp.1448-1454
• /
• 1994

Data which gathered and used in the field of fatigue and fracture mechanics have a lot of uncertainties. In this case, those uncertainties will make scatter band in evaluation of fatigue life and fracture toughness. Thus, the probabilistic analysis of these data will be needed. For determining the fatigue life in mixed mode, using crack direction law and fatigue crack growth law, the problem is studied as a constrained life minimization. Stress intensity factor(SIF) is computed by approximate solution table(Ewalds/Wanhill 1984) and 0th order PFEM. The variance of fatigue life and SIF are computed by differentiation of tabulated approximate solution and 1st order PFEM. And these are used for criterion of design values, principal parameter determination and modelling. The problem of center cracked plate is solved for checking the PFEM model which is influenced by various parameters like as initial crack length, final crack length, two fatigue parameters in Paris Equation and applied stress.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.29 no.8 s.239
• /
• pp.1132-1138
• /
• 2005

Fatigue life of metal material can be predicted by the use of fracture theory and experimental database. Although prediction of fatigue life of rubber material uses the same way as metal, there are many reasons to make it almost impossible. One of the reasons is that there is not currently used fracture criteria for rubber material beacuse of non-standardization, various way of composition process of rubber and so on. Tearing energy is one of the fracture criteria which can be applied to a rubber. Even if tearing energy relaxes the restriction of rubber composition, it is also not currently used because of complication to apply in. Research material about failure process of rubber and tearing energy was reviewed to define the process of fatigue failure and the applicability of tearing energy in estimation of fatigue life for rubber. Also, 1file element formulation of tearing energy which can be used in FE analysis was developed.

• Journal of Ocean Engineering and Technology
• /
• v.1 no.2
• /
• pp.123-129
• /
• 1987

Corrosion fatigue fracture of dual phase steel(SS41) and raw material steel(SS41) were investigated in 3.5% NaCl aqueous solution at PH 4,6,9 and 11. The fatigue limit of dual phase steel is increased approximately 1.8 times larger than that of raw material in air. The corrosion fatigue life of dual phase steel is about 5-10 times larger than that of raw material in 3.5% NaCl aqueous solution. The reduction of fatigue life is larger for the acidsalt solution than for the alkali salt solution. The reduction of stress level on the reduction ratio of corrosion fatigue life is large as pH 6-11. The reduction ratio of corrosion fatigue life of dual phase steel and raw material is nearly coincided at pH 2. While at pH4-2 the reduction ratio of corrosion fatigue life only depends on the corrosion effect. It has been found that the corrosion resistance effect of dual phase steel is smaller than that of raw material in corrosion fatigue crack propagation rate. As pH below 6 is changed, it can be clearly observed from raw material that the brittle intergranular fracture is characterized, and from the above result, the influence of corrosion of dual phase steel is small.

• Structural Engineering and Mechanics
• /
• v.4 no.4
• /
• pp.347-364
• /
• 1996

Presently welded components are designed using S/N curves which predict only the fatigue life of the component. In order to ascertain the condition of the weld at any intermediate period of its life inspection is carried out. If cracks are detected in a weld fracture mechanics is used to find their remaining life. A procedure for assessment is developed here that can be used to verify the condition of a weld before inspection is carried out to detect cracks. This simple method has been developed using linear fracture envelopes by combining S/N curves with linear elastic fracture mechanics.

• BMB Reports
• /
• v.47 no.12
• /
• pp.666-672
• /
• 2014

The Wnt signaling pathway is well known to play major roles in skeletal development and homeostasis. In certain aspects, fracture repair mimics the process of bone embryonic development. Thus, the importance of Wnt signaling in fracture healing has become more apparent in recent years. Here, we summarize recent research progress in the area, which may be conducive to the development of Wnt-based therapeutic strategies for bone repair.

• Journal of Ocean Engineering and Technology
• /
• v.3 no.2
• /
• pp.587-587
• /
• 1989

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.9
• /
• pp.1119-1129
• /
• 2011

Shot-peening effects on the fatigue behavior of bearing steel were investigated under the high cyclic loading. Hourglass shape specimens were made of bearing steel(JIS-SUJ2) for rotary bending fatigue tests. Two kinds of treatments were performed : a heat treatment and a shot-peened surface treatment after the heat treatment. The fracture surfaces of specimens were classified into two types of fracture mode : the surface fracture mode induced by a surface defect and the internal fracture mode induced by a nonmetallic inclusion. Inclusion depth and shape affected considerably the fatigue life. Shot-peening treatment improved much the fatigue life of the bearing steel under low and high levels of cyclic loads. Probabilistic-stress-life (P-S-N) curves were suggested for the reliable fatigue life estimation of the improved bearing steel.