• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.05b
• /
• pp.74-77
• /
• 2002

Ferroelectric Random Access Memory(FRAM) and MEMS applications require noble metal or refractory metal oxide electrodes. In this study, Ru thin films were etched using $O_2$+10% $CF_4$ plasma in an inductively coupled plasma(ICP) etching system. The etch rate of Ru thin films was examined as function of rf power, DC bias applied to the substrate. The enhanced etch rate can be obtained not only with increasing rf power and DC bias voltage, but also with small addition $CF_4$ gas. The selectivity of $SiO_2$ over Ru are 1.3. Radical densities of oxygen and fluorine in $CF_4/O_2$ plasma have been investigated by optical emission spectroscopy(OES). The etching profiles of Ru films with an photoresist pattern were measured by a field emission scanning electron microscope (FE-SEM). The additive gas increases the concentration of oxygen radicals, therefore increases the etch rate of the Ru thin films and enhances the etch slope. In $O_2$+10% $CF_4$ plasma, the etch rate of Ru thin films increases up to 10% $CF_4$ but decreases with increasing $CF_4$ mixing ratio.

• Proceedings of the KIEE Conference
• /
• 1999.11a
• /
• pp.31-34
• /
• 1999

In the present study, we fabricated stoichiometric $(Ba_{1-x}Sr_x)TiO_3$ thin films at various substrate temperature and contents using of magnetron sputtering method on optimized Pt-based electrodes (Pt/TiN/$SiO_2$/Si). The substate temperature deposited at 200[ $^{\circ}C$], 400[$^{\circ}C$] and 600[$^{\circ}C$] and crystalline BST thin films show above 400[$^{\circ}C$]. Also, the composition of $(Ba_{1-x}Sr_x)TiO_3$ thin films deposited on Si wafer substrate at 400[$^{\circ}C$] were closed to stoichiometry($1.015{\sim}1.093$ in A/B ratio), but compositional deviation from a stoichiometry is larger as $SrCO_3$ is added. The drastic decrease of dielectric constant and increase of dielectric loss in $(Ba_{1-x}Sr_x)TiO_3$thin films is observed above 100[kHz]. V-I characteristics of $(Ba_{1-x}Sr_x)TiO_3$ thin films show the decrease of leakage current with the increase of $SrCO_3$ contents.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.364.2-364.2
• /
• 2014

Magnesium oxide (MgO) thin films have attracted great scientific and technological interest in recent decades. Because of its distinguished properties such as a wide band gap (7.2 eV), a low dielectric constant (9.8), a low refractive index, an excellent chemical, and thermal stability (melting point=$2900^{\circ}C$), it is widely used as inorganic material in diverse areas such as fire resistant construction materials, optical materials, protective layers in plasma display panels, buffer layers of multilayer electronic/photonic devices, and perovskite ferroelectric thin films. Precursor used in the ALD requires volatility, stability, and low deposition temperature. Precursors using a heteroleptic ligands with different reactivity have advantage of selective reaction of the heteroleptic ligands on substrate during ALD process. In this study, we have synethesized new heteroleptic magnesium precursors ${\beta}$-diketonate and aminoalkoxide which have been widely used for the development of precursor because of the excellent volatility, chelating effects by increasing the coordination number of the metal, and advantages to synthesize a single precursor. A newly-synthesized Mg(II) precursor was adopted for growing MgO thin films using ALD.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.06a
• /
• pp.59-62
• /
• 1998

Thermal treatment dependences of MFS devices in $BaMgF_4$ on Si structures have been investigated. $BaMgF_4$ thin films have been directly deposited on the p-Si(100) wafers at a low temperature of $300^{\circ}$ in an ultra high vacuum(UHV) system. After in-situ post-deposition annealing was conducted for 20 s at $650^{\circ}$, bias and temperature were applied to $BaMgF_4/Si$ structures. Although X-ray diffraction analysis showed that the films were polycrystalline in nature before and after bias temperature, the C-V properties were some different between with and without bias-temperature treatment.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.04b
• /
• pp.157-160
• /
• 2004

Ferroelectric $(Ba_xSr_{1-x})TiO_3$ (BST) thin films have been deposited on (001) MgO single crystals by a pulsed laser deposition (PLD) method. The structure of deposited BST thin films were investigated by an x-ray diffractometer. Calculated c-axis lattice parameters of the BST films exhibit a strong lattice distortion, which was not observed in ceramic BST at room temperature. This lattice distortion of BST has been attributed to strains caused by lattice constant difference between film and substrate, oxygen vacancies in BST film, and thermal expansion difference between film and substrate. Ferroelectric properties at 10 GHz have been measured using a HP 8510C vector network analyzer. Dielectric properties, capacitance tunability and quality factor, of the interdigitaed capacitors fabricated on BST films were calculated from the measured s-parameters. Two distinct behaviors in structural, opitical, and microwave properties of BST films were observed; below and above 200 mTorr of oxygen pressure in the deposition chmber.

• The Korean Journal of Ceramics
• /
• v.2 no.1
• /
• pp.48-53
• /
• 1996

Ion beam assisted crystallization behavior of sol-gel derived $PbTiO_3$ thin films, deposited on bare silicon(100) substrates by spin-casting method, has been investigated. Ar ion bombardment was directly conducted on the spincoated film surface with or without heating the film from room temperature to $300^{\circ}C$. Ion dose was changed from $5{\times}10^{15}$ to $7.5{\times}10^{16}$ $Ar^-/cm^2$. Formation of (110) oriented perovskite phase was obseerved with ion dose above $5{\times}10^{16}\; Ar^+/cm^2$. Crystallization of $PbTiO_3$ thin film could be enhanced with increasing the Air ion dose, or heating the substrate during ion bombardment. Crystallization of the $PbTiO_3$ films by ion bombardment was related to the local heating effect during ion bombardment.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.404-407
• /
• 2003

Among the ferroeletric thin films that have been widely investigated for ferroelectric random access memory (FRAM) applications, the $SrBi_2Ta_2O_9$ (SBT) thin film is appropriate as a memory capacitor material due to its excellent fatigue endurance. SBT thin films were etched in high-density $Cl_2/Ar$ in inductively coupled plasma. The maximum etch rate of SBT film is $1834\;{\AA}/min$ under $Cl_2/(Cl_2+Ar)$ of 30 %, rf power of 700 W, dc-bias voltage of -250 V, chamber pressure of 11 mTorr and gas flow rate of 20 sccm.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.155-158
• /
• 2002

Eu-doped lead zirconium titanate $Pb_{1.1}(Zr_{0.3}Ti_{0.7})O_{3}$ thin films on the Pt/Ti/$SiO_2$/Si substrates prepared by a metalorganic decomposition (MOD) method. The effect on the structural and electrical properties of the films measured according to Eu content. Eu-doping altered significantly the dielectric and ferroelectric properties. The remanent polarization and coercive field decreased with increasing the concentration of Eu content. The dielectric constant and dielectric loss of the film decreased with increasing Eu contents. The 3 mol% of Eu-doped PZT thin film showed large remanent polarization and the fatigue characteristic of the film did not change up to $10^9$ switching cycles.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.7
• /
• pp.592-597
• /
• 2000

In this study (B $a_{0.5}$/S $r_{0.5}$)Ti $O_3$[BST(50/50)] ceramic thin films were prepared by the Sol-Gel method BST(50/50) stock solution was made and spin-coated on the Indium Tin Oxide(ITO)/glass substrate at 4000 rpm for 30 seconds. The coated films were dried at 35$0^{\circ}C$ for 10 minutes and annealed at 650~75$0^{\circ}C$ for 1 hour. The microstructural properties of the BST(50/50) thin film were studied by the XRD and AFM. The ferroelectric perovskite phase was formed at the annealing condition of 75$0^{\circ}C$ for 1 hour. Dielectric constant and loss of this thin were 370, 3.7% at room temperature respectively. The polarization switching voltage showed the good value of 3V. The leakage current density of the BST(50/50) thin film was 10$^{-7A}$c $m^2$with applied voltage of 1.5V. BST(50/50) thin film capacitors having good dielectric and electrical properties are expecting for the application to the dielectric material of DRAM.RAM.M.

• Journal of the Korean Vacuum Society
• /
• v.9 no.4
• /
• pp.360-366
• /
• 2000

$Sr_xBi_{2.4}Ta_2O_9$ (SBT) thin films of 150 nm thickness were prepared using LSMCD (Liquid Source Misted Chemical Deposition) process with variation of the Sr/Ta mole ratio of 0.35~0.65, and their crystalline phase, microstructure, ferroelectric properties and leakage current characteristics were investigated. Ferroelectric characteristics of the LSMCD-derived SBT films were optimized at the Sr/Ta moleratio of 0.425. The remanent polarization (2Pr) and coercive field (Ec) of the SBT film with the Sr/Ta mole ratio of 0.425 were measured as 15.01 $\mu$C/$ \textrm{cm}^2$ and 41 kV/cm at an applied voltage of $\pm$5 V respectively. LSMCD-derived SBT films with the Sr/Ta mole ratio of 0.35~0.5 exhibited leakage current densities lower than $10^{-5} A/\textrm{cm}^2$ at an applied field of 100 kV/cm, and excellent fatigue-free characteristics of the remanent polarization decrement less than 1% after $10^{10}$ switching cycles at$\pm$5 V.