• Polymer(Korea)
• /
• v.36 no.2
• /
• pp.155-162
• /
• 2012

Sulfonated poly(ether ether ketone) (SPEEK) nanofibers were prepared by electrospinning. The nanofibrous membrane for polymer electrolyte membrane fuel cell (PEMFC) was fabricated by compression molding. The maximum degree of sulfonation was 95% and the initial thermal degradation temperature was $280^{\circ}C$ and it's value was lower than that of PEEK. The contact angle of SPEEK increased with decreasing the degree of sulfonation. The optimum voltage, flow rate, tip to collector distance (TCD) and concentration of electrospinning conditions were 22 kV, 0.3 mL/hr, 15 cm, and 23 wt%, respectively. The average nanofibrous diameter was 47.6 nm. The water uptake and ion exchange capacity of SPEEK nanofibrous membrane increased with increasing the sulfonation time and the amount of sulfonating agent. The electrical resistance and proton ionic conductivity of SPEEK membrane increased with decreasing and increasing the sulfonation time, respectively. Their values were 0.58~0.06 ${\Omega}{\cdot}cm^2$and 0.099 S/cm.

• Membrane Journal
• /
• v.16 no.1
• /
• pp.1-8
• /
• 2006

Nanofiber is a broad phrase generally referring to a fiber with diameter less than 1 micron. Various polymers have been successfully electrospun into nanofibers in recent years. These nanofibers, due to their high surface area and porosity, have a great potential for use as filter medium, adsorption layers in protective clothing, etc. Nanofiber filters will enable new levels of filtration performance in the field of air filtration. In particular, nanofibers provide marked increases in filtration efficiency at relatively small pressure drop in permeability. Therefore, nanofiber filters could be substituted for conventional filter market due to the easy application of process and the possibility of coating to micron-sized non-woven sheets. This review is discussed on the trend of researche and development related to nanofiber filter including future marketability.

• Journal of Industrial and Engineering Chemistry
• /
• v.68
• /
• pp.416-424
• /
• 2018

Oil spill and oily wastewater have now become a serious threat to the freshwater and marine environments. Porous materials with super-hydrophobicity and super-oleophilicity are good candidates for the oil adsorption and oil/water separation. Here, flexible hybrid nanofibrous membrane (FHNM) containing $SiO_2$/polyvinylidene fluoride (PVDF) microspheres was prepared by simultaneous electrospinning and electrospraying. The obtained FHNM combined the flexibility of the nanofiber mat and super-hydrophobicity of the microspheres, which could not be achieved by either only electrospinning or only electrospraying. It was found that when the weight ratio between the $SiO_2$ and PVDF reached a critical value, the $SiO_2$ nanoparticles were present on the PVDF microsphere surface, significantly improving the surface roughness and hence the contact angle of the FHNM. Compared with the pure electrospun PVDF nanofiber mat, most of the FHNMs have a higher oil adsorption capacity. The FHNM could separate the oil with water quickly under the gravity and displayed a high efficiency and good reusability for the oil/water separation. More importantly, the FHNM could not only separate the oil with the pure water but also the corrosive solution including the salt, acid and alkali solution.

• Transactions of the Korean hydrogen and new energy society
• /
• v.24 no.3
• /
• pp.223-229
• /
• 2013

Polymer Electrolyte Membrane Fuel Cell (PEMFC) is a power generation system to convert chemical energy of fuels and oxidants to electricity directly by electrochemical reactions. As a catalyst support for PEMFCs, carbon black has been generally used due to its large surface area and high electrical conductivity. However, under certain circumstances (start up/shut down, fuel starvation, ice formation etc.), carbon supports are subjected to serve corrosion in the presence of water. Therefore, it would be desirable to switch carbon supports to corrosion-resistive support materials such as metal oxide. $TiO_2$ has been attractive as a support with its stability in fuel cell operation atmosphere, low cost, commercial availability, and the ease to control size and structure. However, low electrical conductivity of $TiO_2$ still inhibits its application to catalyst support for PEMFCs. In this paper, to explore feasibility of $TiO_2$ as a catalyst support for PEMFCs, $TiO_2$ nanofibers were synthesized by electrospinning and calcinated at 600, 700, 800 and $900^{\circ}C$. Effects of calcination temperature on crystal structure and electrical conductivity of electrospun $TiO_2$ nanofibers were examined. Electrical conductivity of $TiO_2$ nanofibers increased significantly with increasing calcination temperature from $600^{\circ}C$ to $700^{\circ}C$ and then increased gradually with increasing the calcination temperature from $700^{\circ}C$ to $900^{\circ}C$. It was revealed that the remarkable increase in electrical conductivity could be attributed to phase transition of $TiO_2$ nanofibers from anatase to rutile at the temperature range from $600^{\circ}C$ to $700^{\circ}C$.