• Journal of IKEEE
• /
• v.22 no.3
• /
• pp.780-785
• /
• 2018

In this work, We investigated the frequency-dependent capacitance tunability of a metal-ferroelectric-metal variable capacitor fabricated using ALD $HfO_2$ ferroelectric material. The capacitance of the MFM capacitor could be tuned as a function of the bias voltage, up to the microwave frequency range. We observed a capacitance tuning range of ~3 % up to 2.5 GHz, proving the feasibility of the use of ALD $HfO_2$ in the microwave frequency band.

• Transactions on Electrical and Electronic Materials
• /
• v.7 no.2
• /
• pp.67-71
• /
• 2006

In this paper, we have investigated the structure and dielectric properties of the $(Ba_{0.6}Sr_{0.4})TiO_3$ (BST) thin films fabricated on MgO(100)/Si substrate by an alkoxide-based sol-gel method. Both the structure and morphology of those films were analyzed by x-ray diffraction (XRD) and atomic force microscope (AFM). For the MgO(100)/Si substrate, the BST thin films exhibited highly (100) orientation. The highly (100)-oriented BST thin films showed high dielectric constant, tunability, and figure of merit (FOM). The dielectric constant, dielectric loss and tunability of the BST thin films annealed at $700^{\circ}C$ deposited on the MgO(100)/Si substrate measured at 10 kHz were 515.9, 0.0082, and 54.3%, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.30-33
• /
• 2001

This thesis deal with ferroelectric and ferrimagnetic materials, PZT/Ferrite ceramics. We conducted test of magnetical and electrical measurement. From this measurement, We obtained tunability and we can control characteristic impedance($Z_0$) from permeability($\mu$) and dielectric constant($\varepsilon$) for impedance matching in transmission line.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.30-33
• /
• 2001

This thesis deal with ferroelectric and ferrimagnetic materials, PZT/Ferrite ceramics. We conducted test of magnetical and electrical measurement. From this measurement, We obtained tunability and we can control characteristic impedance(Z$_{0}$) from permeability($\mu$) and dielectric constant($\varepsilon$) for impedance matching in transmission line.e.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.42-45
• /
• 2001

$(Ba_{0.6}Sr_{0.4}Ca_{x})TiO_{3}+yZrO_{2}$ wt% (x=0.10, 0.15, 0.20, y=0.5~3.0) specimens were fabricated by the mixed-oxide method and then the structural and dielectric properties as a function of the composition ratio and $ZrO_2$ contents were studied. All BSCT specimens showed dense and homogeneous structure without the presence of the seconds phase. The Curie temperature and the dielectric constant at room temperature decreased with increasing the Ca/Ba composition ratio and $ZrO_2$ content. The BSCT(50/40/10) specimens showed the excellent tunability property. And the tunability were increased with increasing the contents of $ZrO_2$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.42-45
• /
• 2001

(Ba$_{0.6-x}$Sr$_{0.4}$Ca$_{x}$)TiO$_3$+yZrO$_2$wt% (x=1.10, 0.15, 0.20, y=0.5~3.0) specimens were fabricated by the mixed and ZrO$_2$ contents were studied. All BSCT specimens contents were studied. All BSCT specimens showed dense and homogeneous structure without the presence of the seconds phase. The Curie temperature and the dielectric constant at room temperature decreased with increasing the Ca/Ba composition ratio and ZrO$_2$ content. The BSCT(50/40/10) specimens showed the excellent tunability property. And the tunability were increased with increasing the contents of ZrO$_2$./TEX>.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.11
• /
• pp.1178-1185
• /
• 2004

In the atmosphere of $N_2$ gas, BaZ $r_{0.08}$ $Ti_{0.92}$ $O_3$ polycrystal was grown by floating zone technique using BaZ $r_{0.08}$ $Ti_{0.92}$ $O_3$ ceramics as a feed and SrTi $O_3$(1l0) single cystal as a seed. The dielectric constant and loss at 10 kHz, 100 kHz, and 1 MHz for the as-grown sample were measured as a function of temperature in the temperature range between -10$0^{\circ}C$ and 150 $^{\circ}C$ to find a dielectric peak with frequency dispersion at Curie point. The hysteresis loop showed that the grown sample had very small polarization which was 0-0.01 $\mu$C/$\textrm{cm}^2$ for the applied dc-electric fields from -7 kV/cm to +7 kV/cm. However, the normal hysteresis loop was appeared after oxygen annealing. The electric-field dependence of the dielectric constant for both the as-grown and the post-annealed samples was studied by measuring the dielectric constants as a function of the biased-electric fields and their tunability was figured out from it at room temperature(27 $^{\circ}C$) and cryotemperature( -73$^{\circ}C$). Tunability for the as-grown sample was 51 % and the figure of merit 20.4 at 10kHz with the biased electric-field of 12 kV/cm. The tunability for the grown sample may be increased up to 80 % if the electric field of 25 kV/cm is applied. Tunability for the post-annealed sample was 41 % and the figure of merit 10.3 at 10 kHz with the biased electric-field of 12 kV /cm. Post-annealing improved the crystallinity of the as-grown sample but decreased its tunability.ability.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.794-797
• /
• 2004

The object of investigation is represented by PbxSrl-xTiO3(PST) thin films, which were fabricated by the alkoxide-based sol-gel method on Pt/Ti/SiO2/Si substrate. We have investigated both structural and dielectric properties of PST thin films aimed to tunable microwave device applications as a function of Pb/Sr ratio. PST thin films showedtypical polycrystalline structure with a dense microstructure without secondary phase formation. Dielectric properties of PST films were found as strongly dependent on Pb/Sr composition ratio. Increasing of Pb content leads to simultaneous increasing of both dielectric constant and dielectric loss characteristics of PST films. The figure of merit (FOM) Parameter (FOM : (%) tunability / tan (%)) reached a maximal value of 27.5 corresponding to Pb/Sr ratio of 40/60. The tunability increased with increasing Pb content. The dielectric constants, dielectric loss and tunability of the PST thin films at Pb/sr ratio of 40/60 measured at 100 kHz were 335, 0.0174 and 47.89 %, respectively.

• Transactions on Electrical and Electronic Materials
• /
• v.16 no.1
• /
• pp.1-4
• /
• 2015

(111)-oriented and random oriented $Pb_{0.8}Ba_{0.2}ZrO_3$ (PBZ) perovskite relaxor ferroelectric thin films were fabricated on Pt(111)/$TiO_x$/$SiO_2$/Si substrate by sol-gel method. Nano-scaled antiferroelectric and ferroelectric two-phase coexisted in both (111)-oriented and random oriented PBZ thin film. High dielectric tunability (${\eta}=75%$, E = 560 kV/cm) and figure-of-merit (FOM ~ 236) at room temperature was obtained in (111)-oriented thin film. Meanwhile, giant electrocaloric effect (ECE) (${\Delta}T=45.3K$ and ${\Delta}S=46.9JK^{-1}kg^{-1}$ at $598kVcm^{-1}$) at room temperature (290 K), rather than at its Curie temperature (408 K), was observed in random oriented $Pb_{0.8}Ba_{0.2}ZrO_3$ (PBZ) thin film, which makes it a promising material for the application to cooling systems near room temperature. The giant ECE as well as high dielectric tunability are attributed to the coexistence of AFE and FE phases and field-induced nano-scaled AFE to FE phase transition.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.288-291
• /
• 2002

An alkoxide-based sol-gel method was used to fabricate $(Pb_{x},Sr_{1-x})$TiO3 (PST) thin films on a Pt/Ti/SiO2/Si substrate, and the dielectric properties of the PST thin films were investigated as a function of the Pb/Sr composition for use in tunable microwave device applications. The dielectric properties of the PST films were strongly dependent on the Pb/Sr ratio. The dielectric constant and dielectric loss of the PST films increased with increasing Pb content, and the figure of merit (FOM) reached a maximum value of 27.5 at a Pb/Sr ratio of 4:6. The tunability increased with increasing Pb content. The dielectric constant, loss factor, and tunability of PST (50/50) thin films were 404, 0.023, and 51.73%, respectively. From the result, the PST films with good dielectric properties are useful candidates for tunable microwave device.