• Transactions on Electrical and Electronic Materials
• /
• v.17 no.3
• /
• pp.139-142
• /
• 2016

β-AgVO₃ nanorods have been successfully synthesized using a soft chemistry route followed by heat treatment. They were characterized by X-ray diffraction and field emission scanning electron microscopy, and their electrochemical properties were investigated using cyclic voltammetry, impedance spectra, and charge-discharge tests. The results showed that the smooth-surfaced nanorods are very uniform and well dispersed, with diameters of ~100-200 nm and lengths of the order of several macrometers. The nanorods deliver a maximum specific discharge capacity of 275 mAh g^-1 at 30 mA g^-1. They also demonstrated good rate capability with a discharge capacity at the 100^th cycle of 51 mAh g^-1.

• Bulletin of the Korean Chemical Society
• /
• v.32 no.12
• /
• pp.4205-4209
• /
• 2011

The $Li_2Mn_{0.5}Fe_{0.5}SiO_4$ silicate was prepared by blending of $Li_2MnSiO_4$ and $Li_2FeSiO_4$ precursors with same molar ratio. The one of the silicates of $Li_2FeSiO_4$ is known as high capacitive up to ~330 mAh/g due to 2 mole electron exchange, and the other of $Li_2FeSiO_4$ has identical structure with $Li_2MnSiO_4$ and shows stable cycle with less capacity of ~170 mAh/g. The major drawback of silicate family is low electronic conductivity (3 orders of magnitude lower than $LiFePO_4$). To overcome this disadvantage, carbon composite of the silicate compound was prepared by sucrose mixing with silicate precursors and heat-treated in reducing atmosphere. The crystal structure and physical morphology of $Li_2Mn_{0.5}Fe_{0.5}SiO_4$ was investigated by X-ray diffraction, scanning electron microscopy, and high resolution transmission electron microscopy. The $Li_2Mn_{0.5}Fe_{0.5}SiO_4$/C nanocomposite has a maximum discharge capacity of 200 mAh/g, and 63% of its discharge capacity is retained after the tenth cycles. We have realized that more than 1 mole of electrons are exchanged in $Li_2Mn_{0.5}Fe_{0.5}SiO_4$. We have observed that $Li_2Mn_{0.5}Fe_{0.5}SiO_4$ is unstable structure upon first delithiation with structural collapse. High temperature cell performance result shows high capacity of discharge capacity (244 mAh/g) but it had poor capacity retention (50%) due to the accelerated structural degradation and related reaction.

• Bulletin of the Korean Chemical Society
• /
• v.35 no.2
• /
• pp.357-364
• /
• 2014

Size controlled, $LiNi_{0.8}Co_{0.15}Al_{0.05}O_2$ cathode powders were prepared by co-precipitation method followed by heat treatment at temperatures between 750 and $850^{\circ}C$. The synthesized samples are characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrochemical performance. The synthesized $LiNi_{0.8}Co_{0.15}Al_{0.05}O_2$ after calcined at $750^{\circ}C$ has a good electrochemical performance with an initial discharge capacity of $190mAhg^{-1}$ and good capacity retention of 100% after 30 cycles at 0.1C ($17mAg^{-1}$). The capacity retention of $LiNi_{0.8}Co_{0.15}Al_{0.05}O_2$ after calcined at $750^{\circ}C$ is better than that at 800 and $850^{\circ}C$ without capacity loss at various high C rates. This is ascribed to the minimized cation disorder, a higher conductivity, and higher lithium ion diffusion coefficient ($D_{Li}$) observed in this material. In the differential scanning calorimetry DSC profile of the charged sample, the generation of heat by exothermic reaction was decreased by calcined at high temperature, and this decrease is especially at $850^{\circ}C$. This behavior implies that the high temperature calcinations of $LiNi_{0.8}Co_{0.15}Al_{0.05}O_2$ prevent phase transitions with the release of oxygen.

• Macromolecular Research
• /
• v.12 no.4
• /
• pp.367-373
• /
• 2004

We have developed a rigorous heat treatment method to improve the biocompatibility of chitosan as a tissue-engineered scaffold. The chitosan scaffold was prepared by the controlled freezing and lyophilizing method using dilute acetic acid and then it was heat-treated at 110$^{\circ}C$ in vacuo for 1-3 days. To explore changes in the physicochemical properties of the heat-treated scaffold, we analyzed the degree of deacetylation by colloid titration with poly(vinyl potassium sulfate) and the structural changes were analyzed by scanning electron microscopy, Fourier transform infrared (FT-IR) spectroscopy, wide-angle X-ray diffractometry (WAXD), and lysozyme susceptibility. The degree of deacetylation of chitosan scaffolds decreased significantly from 85 to 30% as the heat treatment time increased. FT-IR spectroscopic and WAXD data indicated the formation of amide bonds between the amino groups of chitosan and acetic acids carbonyl group, and of interchain hydrogen bonding between the carbonyl groups in the C-6 residues of chitosan and the N-acetyl groups. Our rigorous heat treatment method causes the scaffold to become more susceptible to lysozyme treatment. We performed further examinations of the changes in the biocompatibility of the chitosan scaffold after rigorous heat treatment by measuring the initial cell binding capacity and cell growth rate. Human dermal fibroblasts (HDFs) adhere and spread more effectively to the heat-treated chitosan than to the untreated sample. When the cell growth of the HDFs on the film or the scaffold was analyzed by an MTT assay, we found that rigorous heat treatment stimulated cell growth by 1.5∼1.95-fold relative to that of the untreated chitosan. We conclude that the rigorous dry heat treatment process increases the biocompatibility of the chitosan scaffold by decreasing the degree of deacetylation and by increasing cell attachment and growth.

• The korean journal of orthodontics
• /
• v.28 no.6 s.71
• /
• pp.927-935
• /
• 1998

The purpose of this study is to investigate the changes of mechanical properties and surface topography of various nickel titanium wires after heat sterilization for recycling with quantitative method. The materials used were four kinds of nickel titanium orthodontic wires including a Korean product. Experimental specimens were treated with two kinds of heat sterilization methods ; dry heat ($180^{\circ}C$, 60min) and autoclave ($121^{\circ}C$, 15-20psi, 30min). Mechanical properties were evaluated by tensile test with Instron 4466 (load cell capacity:.1000 kg, cross head speed:5mm/min, grip distince:40mm in room temperature). Surface topography of various wires was compared with each other qualitatively by using scanning electron microscopy and quantitatively by using profilometer. The findings were analyzed statistically with student t-tests. The results were as follows; 1. Neither method of heat sterilization had any effects on tensile properties of the nickel-titanium wires used in this experiment. 2. Before heat sterilization, the surface smoothness was highest in Optimalloy, followed by Align and Sentalloy, with NiTi showing the lowest smoothness value. 3. In surface topography, Align and Optimalloy were not influenced by heat sterilization. NiTi, on the other hand, had increased roughness after dry heat sterilization and Sentalloy showed the same tendency after each of the two heat sterilization procedures.

• Journal of Microbiology and Biotechnology
• /
• v.32 no.3
• /
• pp.287-293
• /
• 2022

The hydroxylation of methane (CH₄) is crucial to the field of environmental microbiology, owing to the heat capacity of methane, which is much higher than that of carbon dioxide (CO₂). Soluble methane monooxygenase (sMMO), a member of the bacterial multicomponent monooxygenase (BMM) superfamily, is essential for the hydroxylation of specific substrates, including hydroxylase (MMOH), regulatory component (MMOB), and reductase (MMOR). The diiron active site positioned in the MMOH α-subunit is reduced through the interaction of MMOR in the catalytic cycle. The electron transfer pathway, however, is not yet fully understood due to the absence of complex structures with reductases. A type II methanotroph, Methylosinus sporium 5, successfully expressed sMMO and hydroxylase, which were purified for the study of the mechanisms. Studies on the MMOH-MMOB interaction have demonstrated that Tyr76 and Trp78 induce hydrophobic interactions through π-π stacking. Structural analysis and sequencing of the ferredoxin domain in MMOR (MMOR-Fd) suggested that Tyr93 and Tyr95 could be key residues for electron transfer. Mutational studies of these residues have shown that the concentrations of flavin adenine dinucleotide (FAD) and iron ions are changed. The measurements of dissociation constants (K_ds) between hydroxylase and mutated reductases confirmed that the binding affinities were not significantly changed, although the specific enzyme activities were significantly reduced by MMOR-Y93A. This result shows that Tyr93 could be a crucial residue for the electron transfer route at the interface between hydroxylase and reductase.

• Korean Journal of Food Science and Technology
• /
• v.35 no.6
• /
• pp.1117-1123
• /
• 2003

The effects of heat treatment on the physical and physical and physiological properties of wax gourd (Benincasa hispida) were examined. The applied heat treatments were autoclaved at $121^{\circ}C$ for 1 hr, boiled for 30 min, and microwaved at 680 W for 5 min. The water retention capacity (WRC) of the wax gourds was 9.43 g/g for the microwaved samples, 5.12 g/g for the boiled samples, 4.63 g/g for the raw samples, and 2.61 g/g for the autoclaved samples. Heat treatment caused to increase swelling by up to $4.4{\sim}7.8\;mL/g$. Calcium binding capacity of heat-treated wax gourd increased in the order of microwaved, boiled, raw, autoclaved samples. Scanning electron microscopy (SME) showed that autoclaving caused the most severe structural modifications, while microwave treatment produced the least modifications. The retarding effect on glucose and bile acid transport depended on the heat treatment. Only boiling showed the glucose retardation effect. Bile acid retardation effect increased in order of boiling (22.9%), autoclaving (17.1%), microwave treatment (14.3%), and raw wax gourd (8.6%). The cadmium retardation effect was significantly high in all samples.

• Korean Journal of Materials Research
• /
• v.30 no.6
• /
• pp.279-284
• /
• 2020

In this work, a carbon-doped carbon nitride photocatalyst is successfully synthesized through a simple centrifugal spinning method after heat treatment. The morphology and properties of the prepared photo catalyst are characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), UV-vis spectrophotometer (UV-vis), and specific surface area. The results show that the band gap of the prepared sample, g-CN-10 is 2.1 eV, is significantly lower than that of pure carbon nitride, 2.7 eV. As the amount of cotton candy increased, the absorption capacity of the prepared catalyst for visible light is significantly enhanced. In addition, the degradation efficiency of Rhodamine B (RhB) by sample g-CN-10 is 98.8 % over 2 h, which is twice that value of pure carbon nitride. The enhancement of photocatalytic ability is attributed to the increase of specific surface area after the carbon doping modifies carbon nitride. A possible photocatalytic degradation mechanism of carbon-doped carbon nitride is also suggested.

• 한국전산유체공학회:학술대회논문집
• /
• 2011.05a
• /
• pp.117-123
• /
• 2011

The low electric power and high efficiency chips are required because of the appearance of smart phones. Also, high-capacity memory chips are needed. e-MMC(embedded Multi-Media Card) for this is defined by JEDEC(Joint Electron Device Engineering Council). The e-MMC memory for research and development is a memory mulit-chip module of 64GB using 16-multilayers of 4GB NAND-flash memory. And it has simplified the chip by using SIP technique. But mulit-chip module generates high heat by higher integration. According to the result of study, whenever semiconductor chip is about 10 $^{\circ}C$ higher than the design temperature it makes the life of the chip shorten more than 50%. Therefore, it is required that we solve the problem of heating value and make the efficiency of e-MMC improved. In this study, geometry of 16-multilayered structure is compared the temperature distribution of four different geometries along the numerical analysis. As a result, it is con finned that a multilayer structure of stair type is more efficient than a multilayer structure of vertical type because a multi-layer structure of stair type is about 9 $^{\circ}C$ lower than a multilayer structure of vertical type.

• Applied Biological Chemistry
• /
• v.30 no.3
• /
• pp.242-249
• /
• 1987

Physicochemical properties on heat-moisture treatment of sweet potato starch were investigated. Starch granules of sweet potato observed by photomicroscope, polarized-light microscope and scanning electron microscope were round and polygonal. X-ray diffraction pattern was changed from Ca-pattern to A-pattern upon heat-moisture treatment. Water binding capacity was drastically increased as the moisture level was increased. The swelling power and solubility at the same temperature were decreased by heat-moisture treatment. Transmittance of 0.1% starch suspensions was increased rapidly from $65^{\circ}C$ in case of untreated starch and from $70^{\circ}C$ in case of treated starch. The starch on heat-moisture treatment was gelatinized over higher temperature range than the untreated starch.