• The Journal of Advanced Prosthodontics
• /
• v.8 no.1
• /
• pp.1-8
• /
• 2016

PURPOSE. The purpose of this study was to evaluate the efficacy of two different metal conditioners for non-precious metal alloys for the bonding of porcelain to a cobalt-chromium (Co-Cr) alloy. MATERIALS AND METHODS. Disk-shaped specimens ($2.5{\times}10.0mm$) were cast with Co-Cr alloy and used as adherend materials. The bonding surfaces were polished with a 600-grid silicon carbide paper and airborne-particle abraded using $110{\mu}m$ alumina particles. Bonding specimens were fabricated by applying and firing either of the metal conditioners on the airborne-particle abraded surface, followed by firing porcelain into 5 mm in diameter and 3 mm in height. Specimens without metal conditioner were also fabricated. Shear bond strength for each group (n=8) were measured and compared (${\alpha}=.05$). Sectional view of bonding interface was observed by SEM. EDS analysis was performed to determine the chemical elements of metal conditioners and to determine the failure modes after shear test. RESULTS. There were significant differences among three groups, and two metal conditioner-applied groups showed significantly higher values compared to the non-metal conditioner group. The SEM observation of the sectional view at bonding interface revealed loose contact at porcelain-alloy surface for non-metal conditioner group, however, close contact at both alloy-metal conditioner and metal conditioner-porcelain interfaces for both metal conditioner-applied groups. All the specimens showed mixed failures. EDS analysis showed that one metal conditioner was Si-based material, and another was Ti-based material. Si-based metal conditioner showed higher bond strengths compared to the Ti-based metal conditioner, but exhibited more porous failure surface failure. CONCLUSION. Based on the results of this study, it can be stated that the application of metal conditioner is recommended for the bonding of porcelain to cobalt-chromium alloys.

• Journal of Technologic Dentistry
• /
• v.31 no.1
• /
• pp.17-21
• /
• 2009

This experimental study was to determine the fitness on each cervical margin of recast using crown base metal alloy. The alloy used in this experimental study was a Ni-Cr alloy(Wirolloy, Bego, Germany) for the fabrication of full cast crown prosthesis. Twenty-five copings were divided into the five groups. And the group A, B, C, D and E were cording successively according to the frequency of recast to five times. Each specimen was recasted without adding new metal. The experimental results were as follows: 1. The group A and B showed good fitness had subtle differences in each cervical margin adaptation, in other words, the mesio and disto cervical margin showed worse adaptation than the bucco and linguo cervical margin. 2. The group C got good fitness in bucco and linguo cervical margins, but the mesio and disto cervical margin showed inaccurate fitness. And I could not get good casting bodies without adding new metal. 3. The group D and E showed bad fitness for each cervical margin. Therefore the group D and E lost its function as a dental restoration.

• Journal of Technologic Dentistry
• /
• v.31 no.4
• /
• pp.15-23
• /
• 2009

The aim of this study was to evaluate the bond strength of using a Au bonding agent applied on cp-Ti and nonprecious metal-gold-ceramic system. Metallic frameworks(diameter: 5mm, height: 20mm)(N=56, n=7per group) cast in Ni-Cr alloy, Co-Cr alloy and cp-Ti were obtained using acrylic templates and airborne particle abraded with $110{\mu}m$ aluminum oxide. Au bonding agent was applied on wash opaque firing as intermediate layer. SEM and SEM/EDS line profile were performed on the cutting the cross-section of the metal substrate-porcelain with intermediate Au coating. Groups were tested using shear bond strength(SBS) testing at 0.5mm/min. The mean SBS values for the ceramic-Au layer-metal combination were significantly higher than those ceramic-metal combination. While ceramic-Au layer-cp-Ti combinations failed to increase bond strength instead of using a titanium bonding porcelain. The appication of using Au intermediate layer significantly improve the bond strength combination with metal-ceramic system.

• The Journal of Advanced Prosthodontics
• /
• v.7 no.5
• /
• pp.392-399
• /
• 2015

PURPOSE. The aim of this study was to evaluate the effect of metal primers on the bonding of dental alloys and veneer resin. Polyvinylpyrrolidone solution's tarnish effect on bonding strength was also investigated. MATERIALS AND METHODS. Disk-shape metal specimens (diameter 8 mm, thickness 1.5 mm) were made from 3 kinds of alloy (Co-Cr, Ti and Au-Ag-Pd alloy) and divided into 4 groups per each alloy. Half specimens (n=12 per group) in tarnished group were immersed into polyvinylpyrrolidone solution for 24 hours. In Co-Cr and Ti-alloy, Alloy Primer (MDP + VBATDT) and MAC-Bond II (MAC-10) were applied, while Alloy Primer and V-Primer (VBATDT) were applied to Au-Ag-Pd alloys. After surface treatment, veneering composite resin were applied and shear bond strength test were conducted. RESULTS. Alloy Primer showed higher shear bond strength than MAC-Bond II in Co-Cr alloys and Au-Ag-Pd alloy (P<.05). However, in Ti alloy, there was no significant difference between Alloy Primer and MAC-Bond II. Tarnished Co-Cr and Au-Ag-Pd alloy surfaces presented significantly decreased shear bond strength. CONCLUSION. Combined use of MDP and VBATDT were effective in bonding of the resin to Co-Cr and Au-Ag-Pd alloy. Tarnish using polyvinylpyrrolidone solution negatively affected on the bonding of veneer resin to Co-Cr and Au-Ag-Pd alloys.

• Journal of Technologic Dentistry
• /
• v.32 no.1
• /
• pp.17-21
• /
• 2010

This experimental study was to determine the fitness in each cervical margin of reusing porcelain gold alloy. The gold alloy used in this experimental study was a Au-Pt-Pd alloy (BDCG-898, Bukwang Inc, Korea) for the fabrication of porcelain fused to metal crown. Twenty-five copings were divided into the five groups. And the group A, B, C, D and E were cording successively according to the frequency of reuse to five times. Each specimen was reused without adding new metal. The experimental results were as follows: 1. The group A, B, C showed good fitness in each cervical margin. 2. The group D got good fitness in labio and linguo cervical margin, but the mesio and disto cervical margin showed more than $40{\mu}m$ 3. The group E showed worse fitness than the other groups in each cervical margin.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2013.05a
• /
• pp.81-82
• /
• 2013

In this study, precipitation behaviors of hydroxyapatite on highly ordered nanotubular Ti-35Ta-xNb alloy surface were researched. Ta and Nb additions to Ti increased corrosion resistance. The surface characteristics of anodized alloy depended on the nanotube formed voltage and alloy element. The HA precipitation morphology was influenced by nanorubular structure of alloys.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2013.05a
• /
• pp.194-194
• /
• 2013

In order to investigate nanotube morphology change of Ti-6Al-4V alloys by heat treatments, the Ti-6Al-4V alloys were used in this study. In non-treated Ti-6Al-4V alloy case, nanotubes only exhibited at ${\alpha}$ phase region with dissolved V-oxide area of ${\beta}$ phase. However, in Ti-6Al-4V alloy at $800^{\circ}C$ WQ case, nanotubes exhibited at both ${\alpha}$ and ${\beta}$ phase region. Electrochemical corrosion studies showed that the nanotubular alloy at $800^{\circ}C$WQ possesses slightly higher corrosion resistance than non-treated nanotubular alloy.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.213-213
• /
• 2012

In this study, effect of EB-PVD coated Si/HA film thickness on surface characteristics of Ti-35Nb-10Zr alloy was investigated. The Ti-35Nb-10Zr alloy was fabricated by arc melting method. The Si/HA layers were coated with 0.8 wt.% of Si in pure HA by EB-PVD method. The coating thickness was consisted with 100 - 300 nm for each group, the surface characteristics was analyzed by FE-SEM, EDS, XRD, XRF and corrosion test. The Si/HA coating layer was well deposited on the alloy surface by EB-PVD, the thickness was correlative factor with HA peaks and corrosion resistance value.

• Journal of Technologic Dentistry
• /
• v.45 no.4
• /
• pp.87-94
• /
• 2023

Purpose: This study aimed to observed changes in the shape of dental barrels based on application time. Machinability measures the angle of alloy specimens. Polishing performance measures the surface roughness of alloy specimens. Methods: The dental barrel polishing equipment used in this study was a Snow Barrel (DK Mungyo). Three types of cobalt-chromium alloys for partial dentures were used as specimens (BC CAST R [BP]; Bukwang, Vera PDI [VP]; Aalbadent, and GM 800+ [GP]; Dentaurum). Specimens were prepared in the form of plates (10 mmx10 mmx2 mm). Dental barrel polishing was performed at 450 rpm for 60 minutes with intervals of 5 minutes. The processing angle was measured using a microscope (SZ61; Olympus). Results: For the angle measurement, the VPC specimen was measured at 78.64°, 36.00° for the VP60 specimen, 79.57° for the BP control (BPC) specimen, 28.07° for the BP60 specimen, 75.01° for the GPC specimen, and 39.92° for the GP60 specimen. For the surface roughness measurements, the average surface roughness of the VPC and VP15 specimens were 1.09 ㎛ and 0.26 ㎛, respectively. The average surface roughness of the BPC and BP20 specimens were 1.77 ㎛ and 0.29 ㎛, respectively. The average surface roughness of the GPC and GP15 specimens were 1.08 ㎛ and 0.27 ㎛. Conclusion: The results were excellent after about 20 minutes of dental barrel polishing conditions presented in this study.

• Korean Journal of Materials Research
• /
• v.22 no.3
• /
• pp.150-154
• /
• 2012

Ti-6Al-4V ELI (Extra Low Interstitial) alloy have been widely used as alternative to bone due to its excellent biocompatibility, although it still has many problems such as high elastic modulus and toxicity. Therefore, biomaterials with low elastic modulus and non toxic characteristics have to be developed. A novel ${\beta}$ Ti-35wt%Nb-7wt%Zr-Calcium pyrophosphate (CPP) composite that is a biocompatible alloy without elemental Al or V was fabricated by spark plasma sintering (SPS) at $1000^{\circ}C$ under 70 MPa using high energy mechanical milled (HEMM) powder. The microstructure and phases of the milled powders and the sintered specimens were studied using SEM, TEM, and XRD. Ti-35wt%Nb-7wt%Zr alloy was transformed from ${\alpha}$ phase to ${\beta}$ phase in the 4h-milled powder by sintering. The sintered specimen using the 4h-milled powder showed that all the elements were distributed very homogeneously and had higher density and hardness. ${\beta}$ Ti alloy-CPP composite, which has nanometer particles, was fabricated by SPS using HEMMed powder. During the sintering process, $CaTiO_3$, TixOy, and CaO were formed because of the reaction between Ti and CPP. The Vickers hardness of the composites increases with the increase of the milling time and the addition of CPP. The biocompatibility of the Ti-Nb-Zr alloys was improved by addition of CPP.