• Journal of the Korean Vacuum Society
• /
• v.17 no.1
• /
• pp.23-27
• /
• 2008

We have investigated the effect of annealing on the structural and optical properties of polycrystalline Ga doped ZnO (GZO) films grown on glass substrates by RF-magnetron sputter at room temperature. The structural and optical properties of as-grown GZO films were characterized and then samples were annealed at $400{\sim}600^{\circ}C$ in $N_2$ ambient for 30, 60 minutes, respectively. The field emission scanning electron microscopy (FE-SEM) and X-ray diffraction (XRD) were used to measure the grain size and the crystalline quality of the films. We found that the crystalline quality was improved and the grain size tends to be increased. The optical properties of GZO thin films were analyzed by UV-VIS-NIR spectrophotometers. It is found that optical properties of thin films are increased by annealing and can be used for transparent electrode application. We believe that the appropriate post-growth heat treatment could be contributed to the improvement of GZO-based devices.

• Korean Journal of Materials Research
• /
• v.13 no.8
• /
• pp.519-523
• /
• 2003

We report the synthesis of cubic spinel $ZnCo_2$$O_4$thin films and the tunability of the conduction type by control of the oxygen partial pressure ratio. Zinc cobalt oxide films were grown on$ SiO_2$(200 nm)/Si substrates by reactive magnetron sputtering method using Zn and Co metal targets in a mixed Ar/$O_2$atmosphere. We found from X-ray diffraction measurements that the crystal structure of the zinc cobalt oxide films grown under an oxygen-rich condition (the $O_2$/Ar partial pressure ratio of 9/1) changes from wurtzite-type $Zn_{1-x}$ $Co_{X}$O to spinel-type $ZnCo_2$$O_4$with the increase of the Co/Zn sputtering ratio,$ D_{co}$ $D_{zn}$ . We noted that the above structural change accompanied by the variation of the majority electrical conduction type from n-type (electrons) to p-type (holes). For a fixed $D_{co}$ $D_{zn}$ / of 2.0 yielding homogeneous spinel-type $_2$O$ZnCo_4$films, the type of the majority carriers also varied, depending on the$ O_2$/Ar partial pressure ratio: p-type for an $O_2$-rich and n-type for an Ar-rich atmosphere. The maximum electron and hole concentrations for the Zn $Co_2$ $O_4$films were found to be 1.37${\times}$10$^{20}$ c $m^{-3}$ and 2.41${\times}$10$^{20}$ c $m^{-3}$ , respectively, with a mobility of about 0.2 $\textrm{cm}^2$/Vs and a high conductivity of about 1.8 Ω/$cm^{-1}$ /.

• Proceedings of the KIEE Conference
• /
• 2001.07c
• /
• pp.1399-1401
• /
• 2001

We studied on structure and resistivity, temperature coefficient of resistance (TCR) of NiCr and NiCr-N thin resistor films prepared by do reactive magnetron sputtering of NiCr target. It is found that while pure NiCr films are polycrystalline, an addition of nitrogen (N2/(Ar+N2) ratios are between 10% and 70%) into the film is changed into amorphous structure and sheet resistance of films is increased. Measurement temperatures of TCR are ratios of $5^{\circ}C$ per 15min from $25^{\circ}C$ to $130^{\circ}C$. TCR for an as-deposited NiCr-N thin film is varied from positive to negative.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2000.02a
• /
• pp.59-59
• /
• 2000

Recently low resistance of bus line is required for large screen size TFT-LCD panels. As a result, lower resistance Al-alloy is currently reviewed extensively. The resistivity is required smaller than 10 $\mu$$\Omega$cm. In this paper, Al-Nd thin film were deposited on glass substrates by D.C. magnetron sputtering system under various condition. Its properties were characterized by SEM, AFM, XRD, 4-ping-probe. The optimal condition of Al-Nd was 12$0^{\circ}C$, 125W, 0.4Pa, 30sccm(Ar) and 35$0^{\circ}C$, 20min. annealing. At that condition the resistivity of Al-Nd(2wt.%) was about 4 $\mu$$\Omega$cm. The minimum contact resistance of ITO/Nd was about 110$\mu$$\Omega$cm in the condition of 30$0^{\circ}C$, Ar 30 sccm. O2.

• Journal of Integrative Natural Science
• /
• v.9 no.4
• /
• pp.223-227
• /
• 2016

The Zn, Sn, and ZnSn thin films were deposited on Si(100) substrate using radio frequency (RF) magnetron co-sputtering method. A surface profiler and X-ray photoelectron spectroscopy (XPS) were used to investigate the Zn, Sn, and ZnSn thin films. Thickness of the thin films was measured by a surface profiler. The deposition rates of pure Zn and Sn thin films were calculated with thickness and sputtering time for optimization. From the survey XPS spectra, we could conclude that the thin films were successfully deposited on Si(100) substrate. The chemical environment of the Zn and Sn was monitored with high resolution XPS spectra in the binding energy regions of Zn 2p, Sn 3d, O 1s, and C 1s.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.12 no.2
• /
• pp.34-40
• /
• 2013

Various depositional conditions, such as substrate, pressure, deposition time, temperature of substrate, power and gas composition, have mainly been studied to attain DLC films using RF sputtering system up to the current. In this study, the $N_2/Ar/CH_4$ gas mixture factored on characteristics of DLC deposited film such as structure, hardness, electrical property were investigated. The concentration of the $N_2$ gas in the sputtering gas may be a significant effect on the growth rate of the doped films, because nitrogen ions react not only with the carbon atoms on the target but also with $C_xH_y$ ions in the plasma on the substrate surface. It was seen from this experimental that the resistance of deposited film is decreased, and the relative intensity ratio of D to G peak is increased as nitrogen content of film deposition is increased.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.920-923
• /
• 2000

All solid-state thin film supercapacitor(TFSC) based on $RuO_2$ electrode was fabricated. Ruthenium oxide$(RuO_2)$ thin film was deposited on Pt/Ti/Si subsrate by d.c. magnetron sputtering. LiPON(lithium phosphorus oxynitride) thin film were deposited by r.f. reactive sputtering. X-ray diffraction patterns of $RuO_2$ and LiPON films revealed that crystal structures of both films were amorphous. To decrease resistivity of $RuO_2$ thin film, $RuO_2$ thin film was deposited with $H_2O$ vapor. In order to decide the maximum ionic conductivity, the LiPON films were prepared by various sputtering condition. The maximum ionic conductivity was $9.5\times{10}^7S/cm$. A charge-discharge measurements showed the capacity of $3\times{10-2}\;F/cm^2-\mu{m}$ for the as-fabricated TFSC. The discharging efficiency was decreased after 500 cycles by 40 %.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.46 no.7
• /
• pp.7-14
• /
• 2009

In this paper, the effects of annealing conditions on the structural ((002) intensity, FWHM, d-spacing, grain size, (002) peak position), optical (UV peak, UV peak position) and electrical properties (carrier concentrations, resistivity, mobility) of ZnO films were investigated. ZnO films were deposited onto SiO$_2$/si substrates by RF magnetron sputtering from a ZnO target. The substrate was not heated during deposition. ZnO films were annealed in temperature ranges of $500\sim650^{\circ}C$ in the O$_2$ flow for 5$\sim$20 min. The film average thicknesses were in the range of 291 nm. The surface morphologies and structures of the samples were characterize by SEM and XRD, respectively. The optical properties were evaluated by photoluminescence (PL) measurement at room temperature (RT) using a He-Cd 325 nm laser. As the annealing temperature and time vary, the following relations were also observed: (1) proportional relationships among UV intensity (002) intensity, and grain size exist, (2) UV intensity is inversely proportional to FWHM, (3) there is no special relationship between UV intensity and electron carrier concentrations, (4) d-spacing is inversely proportional to (002) peak position, (5) UV peak position in the range of 3.20$\sim$3.24 eV means that ZnO films have a n-type conductivity which was consistent with that obtained from the electrical property, (6) the optimal conditions for the best optical and structural characteristics were found to be oxygen fraction, (O$_2$/(O$_2$+Ar)) of 0.2, RF power of 240W, substrate temperature of RT, annealing condition of 600$^{\circ}C$ for 20 min, and sputtering pressure of 20 mTorr.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.08a
• /
• pp.127-127
• /
• 2011

We investigate the transparent TFTs using a transparent ZnSnO3 (ZTO)/Ag/ZTO multilayer electrode as S/D electrodes with low resistivity of $3.24{\times}10^{-5}$ ohm-cm, and high transparency of 86.29% in ZTO based TFTs. The Transparent TFTs (TTFTs) are prepared on glass substrate coated 100 nm of ITO thin film. On atomic layer deposited $Al_2\;O_3$, 50 nm ZTO layer is deposited by RF magnetron sputtering through a shadow mask for channel layer using ZTO target with 1 : 1 molar ratio of ZnO : $SnO_2$. The power of 100W, the working pressure of 2mTorr, and the gas flow of Ar 20 sccm during the ZTO deposition. After channel layer deposition, a ZTO (35 nm)/Ag (12 nm)/ZTO(35 nm) multilayer is deposited by DC/RF magnetron sputtering to form transparent S/D electrodes which are patterned through the shadow mask. Devices are annealed in air at 300$^{\circ}C$ for 30 min following ZTO deposition. Using UV/Visible spectrometer, the optical transmittances of the TTFT using ZTO/Ag/ ZTO multilayer electrodes are compared with TFT using Mo electrode. The structural properties of ZTO based TTFT with ZTO/Ag/ZTO multilayer electrodes are analyzed by high resolution transmission electron microscopy (HREM) and X-ray photoelectron spectroscopy (XPS). The transfer and output characterization of ZTO TTFTs are examined by a customized probe station with HP4145B system in are.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.456-456
• /
• 2013

We report the modifications in the electronic structureof ZnO thin films induced by swift heavy ion (SHI) irradiated ZnO thin films by using near edge X-ray absorption fine structure (NEXAFS) spectroscopy at O K-edge was performed at BL10D XAS-KIST beamline at Pohang Accelerator Lab (PAL). ZnO films of 250 nm thickness oriented in [200] plane deposited by RF magnetron sputtering using equal $Ar:O_2$ atmosphere and air annealed at $500^{\circ}C$ for 6 hours for stability were irradiated with 120 MeV Au and 100 MeV O beams separately with different doses ranging from $1{\times}10^{11}$ to $5{\times}10^{12}$ ions/$cm^2$. High Resolution X-ray diffraction and NEXAFS analysis indicates significant changes in the electronic structure and the SHI effect is different for Ag and O-beams. The NEXAFS measurements provide direct evidence of O 2p and Zn 3d orbital hybridization. The NEXAFS results will be presented in detail.