• Applied Chemistry for Engineering
• /
• v.34 no.5
• /
• pp.488-492
• /
• 2023

In this study, a carbon film derived from a polymer/lignin composite precursor was produced by a carbonization cycle with a controlled temperature profile. The feasibility of successful formation of the carbon film using the carbonization cycle was monitored. The adsorption behavior of the carbon film toward various molecules, such as nonpolar and polar organic molecules, and dyes was investigated using ultraviolet/visible (UV/Vis) spectroscopy compared with that of carbonized lignin. Cyclic voltammetry (CV) analysis proved that a robust carbon film was prepared by the carbonization cycle. It was also demonstrated that the carbonized lignin and carbon film showed adsorption capability toward all types of organic molecules, in particular organic dyes, owing to the carbonized lignin. This work provides important information for future relevant research.

• Clean Technology
• /
• v.24 no.1
• /
• pp.77-84
• /
• 2018

In this study, $Li_4Ti_5O_{12}$ anode materials for lithium ion battery were synthesized by dry ball-mill method. Polyvinyl chloride (PVC) as a carbon source was added to improve electrochemical properties. When the PVC was added after $Li_4Ti_5O_{12}$ formation, the spinel structure was well synthesized and it was confirmed by X-ray diffraction (XRD) experiments. When the carbon material was added before the synthesis and the heat treatment was performed, it was confirmed that a material having a different crystal structure was synthesized even when a small amount of carbon material was added. In the case of $Li_4Ti_5O_{12}$ without the carbon material, the electrical conductivity value was about $10{\mu}S\;m^{-1}$, which was very small and similar to that of the nonconductor. As the carbon was added, the electrical conductivity was greatly improved and increased up to 10,000 times. Electrochemical impedance spectroscopy (EIS) analysis showed that the size of semicircle corresponding to the resistance decreased with the carbon addition. This indicates that the resistance inside the electrode is reduced. According to the Cyclic voltammetry (CV) analysis, the potential difference between the oxidation peak and the reduction peak was reduced with carbon addition. This means that the rate of lithium ion insertion and deinsertion was increased. $Li_4Ti_5O_{12}$ with 9.5 wt% PVC added sample showed the best properties in rate capabilities of $180mA\;h\;g^{-1}$ at 0.2 C-rate, $165mA\;h\;g^{-1}$ at 0.5 C-rate, and $95.8mA\;h\;g^{-1}$ at 5 C-rate.

• Applied Chemistry for Engineering
• /
• v.18 no.3
• /
• pp.205-212
• /
• 2007

In this work, polyacrylonitrile (PAN) fiber was prepared by electrospinning methods from dimethyl formamide solutions with various conditions, such as 8~20 kV applied voltage, 5~15 wt% PAN concentration, and 15 cm tip-to-collector distance (TCD). The nanofibers were stabilized by oxidation at $250^{\circ}C$ for 1 h, and then subsequently carbonized at $800{\sim}1000^{\circ}C$ for 1 h. The structured characteristics of the nanofibers before and after carbonization were studied by Fourier transform infrared spectroscopy. The resulting diameter distribution and morphologies of the nanofiber were evaluated by scanning electron microscope analysis. The electrochemical behaviors of the nanofiber were observed by cyclic voltammetry tests. From the results, the diameter of electrospinning nanofibers was predominantly influenced by the concentration of polymer solution and the applied voltage. The average diameter of the fibers was decreased with increasing the polymer concentration up to 10wt%. It was also found that the nanofibers with uniform diameter distribution and fine diameter could be achieved at 15kV input voltage and 15 cm TCD.

• Applied Chemistry for Engineering
• /
• v.17 no.2
• /
• pp.183-187
• /
• 2006

The choice of solvents for electrolytes solutions is very important to improve the characteristics of charge/discharge in the Li-ion battery system. Such solvent systems have been widely investigated as electrolytes for Li-ion batteries. In this paper, the electrochemical properties of the solid electrolyte interphase film formed on carbon anode surface and the solvent decomposition voltage in 1 M LiPF6/EC:MA(x:y) electrolyte solutions prepared from the various mixing volume ratios are investigated by chronopotentiometry, cyclic voltammetry, and impedance spectroscopy. As a result, the solvent decomposition voltages are varied with the ionic conductivity of the electrolyte. Electrochemical properties of the passivation film were different, which are dependent on the mixture ratio of the solvents. Therefore, the most appropriate mixing ratio of EC and MA as a solvent in 1 M $LiPF_6/(EC+MA)$ system for Li-ion battery is approximately 1:3 (EC:MA, volume ratio).

• Journal of the Korean Electrochemical Society
• /
• v.11 no.2
• /
• pp.109-114
• /
• 2008

Though ethanol can theoretically generate 12 electrons during oxidation to carbon dioxide, the complete oxidation of ethanol is hard to achieve due to the strong bond between the two carbons in its molecular structure. Therefore, development of high activity catalyst for ethanol oxidation is necessary for the commercialization of direct ethanol fuel cell. In this study, some binary and ternary electrocatalysts of PtSn/C and PtSnAu/C have been synthesized and characterized. The catalysts were fabricated with modified polyol method with the amounts of 20 wt%, where the Pt : Sn ratios in the PtSn/C were 1 : 0, 4 : 1, 3 : 1, 2 : 1, 1.5 : 1, 1 : 1, 1 : 1.5 and Pt:Sn:Au ratios in the PtSnAu/C were 5 : 5 : 0, 5 : 4 : 1, 5 : 3 : 2, 5 : 2 : 3. From the XRD and TEM analysis results, the catalysts were found to have face centered cubic structure with particle size of around $1.9{\sim}2.4\;nm$. The activity in the ethanol oxidation was examined with cyclic voltammetry and the results indicated that PtSn(1.5 : 1)/C and PtSnAu(5 : 2 : 3)/C had the highest activity in each catalyst system. Further tests with single cell were performed with those catalysts. It was found that PtSn/C(1.5 : 1) exhibited the best performance while the long term stability of PtSnAu/C(5 : 2 : 3) is better than PtSn/C(1.5 : 1).

• Journal of the Korean Chemical Society
• /
• v.33 no.2
• /
• pp.192-202
• /
• 1989

Tetradentate schiff bases cabalt (II) complexes; Co(SED) and Co(ο-BSDT) were synthesized and these complexes allowed to reaction with dry oxygen to form oxygen adduct cobalt(III) complexes such as $[Co(o-BSDT)(DMSO)]_2O_2,\;[Co(SED)(Py)]_2O_2\;and\;[Co(o-BSDT)(Py)]_2O_2$ in DMSO and pyridine solutions. It has been found that the oxygen adduct cobalt(III) complexes have hexacoordinated octahedral configuration with tetradentate schiff base cobalt(II), DMSO or pyridine and oxygen, and the mole ratio of oxygen to cobalt(II) complexes are 1:2. The redox processes, were investigated for Co(SEDT) and Co(ο-BSD) complexes in 0.1M TEAP-DMSO and 0.1M TEAP-pyridine by cyclic voltammetry with glassy carbon electrode. As a result the redox processes of Co(II)/Co(III) and Co(II)/Co(I) found to be reversible or quasi-reversible for non uptake oxygen complexes but oxygen adduct complexes found to be irreversible processes and reaction processes of oxygen for oxygen adduct complexes are quasi-reversible process, the potential range was $E_{pc}=-0.85{\sim}-1.19V\;and\;E_{pa}=-0.74{\sim}-0.89V$.

• Journal of the Korean Chemical Society
• /
• v.33 no.2
• /
• pp.215-224
• /
• 1989

Electrochemical reductions of $trans-[Co(en)_2X_2](ClO_4)_n$ (where X is cyanide, nitrite, ammonia, and isothiocyanate) were investigated by cyclic voltammetry and polarography at mercury and glassy carbon electrode. $trans-[Co(en)_2(CN)_2]ClO_4$ was reduced to Co(II) complex followed by adsorption to the mercury electrode. Cyanide ion was not released from the reduced Co(II) complex but the cyanide and (en) were released after the reduction to metallic cobalt. The other complexes except $trans-[Co(en)_2(CN)_2]ClO_4$ were reduced to cobalt(II) complexes followed by release of monodendate ligand, and (en) was released at the reduction step to metallic cobalt. $trans-[Co(en)_2(NO_2)_2]ClO_4$ was reduced to cobalt(Ⅱ) complex, and $NO_2^-$ ion was released followed by electroreduction through ECE mechanism at pH 2. On glassy carbon electrode, all complexes of Co(III) were reduced to Co(II) complexes with irreversible one-electron diffusion controlled reaction in which (en) was not released at this step. Increasing absorption wave number of complexes caused to negative shift of peak potential.

• Journal of the Korean Chemical Society
• /
• v.37 no.5
• /
• pp.483-490
• /
• 1993

Voltammetric behavior of heavy lanthanide ions has been investigated by the DC, DPP and CV in acetonitrile solution. The reduction of $Gd^{3+}, Tb^{3+}, Dy^{3+}, Ho^{3+}, Er^{3+}, Tm^{3+} 및 Lu^{3+} proceed by three-electron change to the metallic state with totally irreversibility in 0.1M tetraethylammonium perchlorate. However, the reduction of Yb(Ⅲ) proceeds in two steps $(Yb^{3+} ＋ e^- \Leftrightarrow Yb^{2+} and Yb^{2+} ＋ 2e^- → Yb^0)$. The first reduction of Yb(Ⅲ) showed quasi reversible behavior, but the second reduction was irreversible in cyclic voltammetry. The cathodic peak current showed adsorptive properties in high concentration with lower sweep rate. The electroreduction of heavy lanthanides in water-acetonitrile mixture has been studied. In water-acetonitrile mixture, the negative shift of the peak potential and the decrease peak current were observed increasing water concentration. Also the Yb(Ⅲ) reduction to Yb(Ⅲ) has been deviated from quasi-reversible character with increase water amount. These results drive from the high solvation abilities of water which has high donor number.

• Applied Chemistry for Engineering
• /
• v.21 no.4
• /
• pp.435-439
• /
• 2010

Pt-$MoO_3$ electrodes were fabricated on ITO-coated glass by electrodeposition method using 20 mM hydrogen hexachloroplatinate ($H_2PtCl_6$) and 10 mM Mo-peroxo electrolyte. Deposition order was varied, and catalytic activities of synthesized electrodes were compared with that of pure Pt electrode. Scanning Electron Microscopy (SEM) was utilized to examine surface morphology. The crystallinity of synthesized films was analyzed by X-ray Diffraction (XRD), and the oxidation state of both the platinum and molybdenum were determined by X-ray Photoelectron Spectroscopy (XPS) analyses. The catalytic activity and stability for methanol oxidation were measured using cyclic voltammetry (CV) and chronoamperometry (CA) in a mixture of 0.5 M $H_2SO_4$ and 0.5 M $CH_3OH$ aqueous solution. $MoO_3$ electrodeposited on the surface of Pt showed much higher catalytic acitivity and stability than pure Pt electrode due to the good contact between Pt and $MoO_3$.

• Journal of the Korean Electrochemical Society
• /
• v.17 no.1
• /
• pp.30-36
• /
• 2014

Redox complexes to transport electrons from enzyme to electrodes are very important part in glucose sensor. Pentacyanoferrate-bound aniline ($Fe(CN)_5$-aminopyridine), was prepared as a potential redox mediator in a glucose dehydrogenase (GDH)-glucose sensor. The synthesized pyridyl-$NH_2$ to pentacyanoferrate was characterized by the electrochemical and spectroscopic methods. A amperometric enzyme-linked electrode was developed based on GDH, which catalyses the oxidation of glucose. Glucose was detected using GDH that was co-immobilized with an $Fe(CN)_5$-aminopyridine and gold nano-particles (AuNPs) on ITO electrodes. The $Fe(CN)_5$-aminopyridine and AuNPs immobilized onto ITO electrodes provided about a two times higher electrochemical response compared to that of a bare ITO electrode. As glucose was catalyzed by wired GDH, the electrical signal was monitored at 0.4 V versus Ag/AgCl by cyclic voltammetry. The anode currents was linearly increased in proportion to the glucose concentration over the 0~10 mM range.