• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.693-696
• /
• 2008

In order to assess time-dependent behaviors of the high-strength concrete that applied in actual FCM bridges with various curing environments, the shrinkages of air-dried, sealed, and moist 100${\times}$100${\times}$400 mm prism specimens were measured. And the compressive creep test of 3 and 28 days aged concrete in the tap water and 10% CaCl$_2$ solutions were carried out, then results were compared with traditional test results of air-dried and sealed specimens. Time-dependent behaviors of the concrete that according to curing circumstances between sealed and moist specimens show remarkable differences not only on the shrinkage but also on the creep. Hence there need some reconsiderations to the traditional creep test manners that predicting the creep and shrink age of actual concrete structures.

• Journal of the Korean Society for Precision Engineering
• /
• v.30 no.8
• /
• pp.878-884
• /
• 2013

Stereolithography can be classified into two main categories according to the cross-sectional shape: scanning type and projection type. Projection stereolithography has significant advantages when making a layer using a single patterned beam, and results in improved speed and accuracy. To implement relatively low-cost projection stereolithography, we developed a system using a commercially available resin, which cures on exposure to visible light. The optimum photoinitiator was investigated, as well as the mixing ratio. The viscosity, shrinkage, curing depth and tensile strength were evaluated through several experiments on fabricated three-dimensional structures, and thus an optimal resin selection system was developed.

• International Journal of Highway Engineering
• /
• v.19 no.1
• /
• pp.11-19
• /
• 2017

PURPOSES : The purpose of this study is to verify the property of self-healing, and to propose an appropriate duration for wet curing of bridge deck concrete overlays. METHODS : In this study, reinforced bars were inserted into concrete molds in order to prevent brittle fracture and induced cracks in the concrete resulting from indirect tension mode. The induced time of concrete cracking was 3 to 7 days, following which the concrete specimens were cured in water. The resulting concrete crack width was measured using image analysis equipment. Additionally, the self-healing tests were performed using the following three mixtures: OPC, SFC, and LMC. RESULTS : Concrete mixtures with crack widths of $150{\mu}m$ or lower were completely healed by Day 28. Hydrates of crack fills were found to be the calcium carbonate. CONCLUSIONS : The cement-based mixtures exhibit properties of self-healing. Considering these properties, it is necessary to increase the curing duration of concrete overlays for bridge decks.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2000.04a
• /
• pp.19-25
• /
• 2000

Dielectric polymer films produced from benzocyclobutene (BCB) formulations (CYCLOTENE＊ family resins) are known to possess many desirable properties for microelectronic applications; for example, low dielectric constant and dissipation factor, low moisture absorption, rapid curing on hot plate without reaction by-products, minimum shrinkage in curing process, and no Cu migration issues. Recently, BCB-based products for thick film applications have been developed, which exhibited excellent dissipation factor and dielectric constant well into the GHz range, 0.002 and 2.50, respectively. Derived from these properties, the applications are developed in: bumping/wafer level packaging, Ga/As chip ILD, optical waveguide, flat panel display, and lately in BCB-coated Cu foil for build-up board. In this paper, we review the relevant properties of BCB, then the application areas in bumping/wafer level packaging and BCB-coated Cu foil for build-up board.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.15 no.3
• /
• pp.125-133
• /
• 2011

The requirement for durability of concrete bridge deck is increasing as the deterioration for the concrete bridge deck exposed to severe environment has been increased. For this reason, the concern about high-durable concrete is being high. Recently, a metakaolin is highly spotlighted as new admixture because its strength and durability are equivalent to silica fume. On the other hands, there are few researches for the metakaolin concrete bridge deck in domestic. So many various long-term data on the mechanical property and durability is needed to apply metakaolin concrete at the concrete bridge deck construction field. This study is aim to evaluate the long-term mechanical properties and durability of metakaolin concrete bridge deck with curing age. Mechanical properties are estimated by the compressive and flexural strength, and the drying shrinkage, the chloride resistance, the scaling, and freezing and thawing characteristics are compared with curing age. According to the results, when the metakaolin concrete is used, the development of compressive and flexural strength proceed in both the early and old ages. It is also improved the resistance of chloride penetration, freezing and thawing in concrete. It was showed that replacement of metakaolin was efficient for the reduction of the drying shrinkage.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.7
• /
• pp.72-79
• /
• 2019

Concrete is vulnerable to cracks due to volume changes caused by temperature changes, shrinkage during curing, external forces, or poor construction. In particular, concrete placed in electric power tunnel structures can generate cracks by a variety of factors. As a result, these tunnel structures require continuous maintenance. In this study, we investigated the mechanical properties of electric power tunnel concrete using alpha-calcium sulfate hemihydrate, which is an industrial byproduct that has excellent expansion performance. To compensate for the decrease in compressive strength when substituting alpha-calcium sulfate hemihydrate, based on previous research, we added 9% alpha-calcium sulfate hemihydrate and adjusted the amount of admixture while using the same amount of cement. We then evaluated the mechanical properties of the concrete. The results showed that the compressive strength of the concrete was higher than that of ordinary Portland cement (OPC), and the shrinkage of concrete was reduced by more than 30% compared to that of OPC. Therefore, adding 9% of alpha-calcium sulfate hemihydrate is expected to have a significant effect in reducing concrete cracks.

• Journal of the Korea Concrete Institute
• /
• v.23 no.2
• /
• pp.225-233
• /
• 2011

The volume change in concrete takes place with changes in temperature and water content immediately after concrete casting. In the early age stage, the thermal and drying shrinkages can cause cracks that are very crucial to the durability of concrete. It was reported that when the cement with lightly-burnt MgO powder was used, the shrinkage of concrete can be reduced. This study investigates fundamental properties of cement composites with lightly burnt MgO powder by performing various experiments. The stability test results verified that MgO powder in cement composites does not cause any abnormal expansion. Also, the hydrate product analysis results obtained from MgO cement paste showed that MgO powder reduces the shrinkage at the longterm ages. In addition, the cement composites containing the proper amount of MgO powder could improve compressive strength. Finally, the shrinkage reduction from using MgO powder can be optimized by increasing MgO replacement level and curing temperature.

• Journal of the Korea Institute of Building Construction
• /
• v.15 no.5
• /
• pp.451-456
• /
• 2015

This study aimed to evaluate of the hardened properties (mortar consistency, setting time, absorption properties, drying shrinkage, and bond strength) of the basalt powder sludge mortar recycling a basalt powder sludge occurred during the manufacture process of basalt stone as a replacing material for the sea-sand used to cement filling compound for surface preparation. The hardened mortar made of the basalt powder sludge showed an enhanced performance or similar with the properties of normal mortar used to cement filling compound for surface preparation. But, the drying shrinkage was increased more than a normal cement mortar in the hardened mortar made of the basalt powder sludge since curing 8 - 9days. And the bond strength is low in the hardened mortar used the basalt powder sludge. On the whole, properties of the hardened mortar used the basalt powder sludge correspond to the required minimum quality criterion in the KS F 4716 'cement filling compound for surface preparation'.

• Composites Research
• /
• v.27 no.4
• /
• pp.174-181
• /
• 2014

This study describes viscoelasticity analysis of carbon-fiber reinforced polymer matrix composite material. One of the most important problem during high temperature molding process is residual stress. Residual stress can cause warpage and cracks which can lead to serious defects of the final product. For the difference in thermal expansion coefficient and change of resin property during curing, it is difficult to predict the final deformed shape of carbon-fiber reinforced polymer matrix composite. The consideration of chemical shrinkage can reduce the prediction errors. For this reason, this study includes the viscoelasticity and chemical shrinkage effects in FE analysis by creating subroutines in ABAQUS. Analysis results are compared with other researches to verify the validity of the subroutine developed, and several stacking sequences are introduced to compare tested results.

• The Journal of Korean Academy of Prosthodontics
• /
• v.38 no.6
• /
• pp.782-790
• /
• 2000

The mainly used polymeric material for the denture is PMMA because of its cost and easiness to handle. So it was widely used material among dentists for past decades. But the acrylic-based denture materials have several common weak points such as shrinkage after curing and lack of strength. In order to solve these problems, we adapted one of hybrid system using acrylic polymer and vinyloligosilsesquioxane(POSS). POSS, which is a well known expandable monomer during polymerization process, may eventually suppress volumetric shrinkage. And the hybrid system makes it possible for the polymer to be stable in various severe conditions. Eight different kinds of samples were designed and synthesized. Each samples were characterized with dynamic mechanical analyser(DMA) to confirm their thermodynamic properties, fractured to analyze the cross-sectional morphology of the samples. And elongation, flexural and impact tests were also executed to evaluate the mechanical properties of the samples. From the results, hybrid composites had well defined crosslinked network structure compared to the widely used denture materials, and the mechanical strength improved without changing any surface condition as increment with POSS ratio in hybrid system. Fractured morphology showed homogeneous surfaces in spite of mutli component system, therefore we can conclude that the adoption of the POSS brought the reinforcement of the denture resin.