• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.1
• /
• pp.169-178
• /
• 1998

The crystal phases precipitated in various compositions glass of CaO-$SiO_2-P_2O_5$ system, were identified by XRD. E composition (CaO 49.4, $SiO_2\;36.8,\;P_2O_5$ 8.8 wt%) glass in which both apatite(($Ca_{10}(PO_4)_6O$ and $\beta$-wollastonite($CaSiO_3$) crystals would precipitate by heating, was selected as an experimental composition to prepare the glass ceramics with high bending strength and good bioactivity to the living bone. Glass powders of E composition were unidirectionally crystallized at $1050^{\circ}$C in the temperature-gadient furnace and the resultant glass ceramics were characterized. Bending strength of the glass ceramics was also measured. To investigate the bond forming ability between the glass ceramics and living bone tissue, soaking test of glass ceramics in simulated body fluid was carried out. Densed glass ceramics composed of apatite and $\beta$-wollastonite crystal were prepared by unidirectional crystallization under the optimum conditions. (2 0 2) plane of $\beta$-wollastonite crystals tended to grow perpendicularly to the crystallization direction. Average bending strength of this glass ceramics was 186.9 MPa, higher than that of the glass ceramics prepared by isothermal (not directional) crystallization In soaking test, a thin layer of apatite crystallite was formed on surface of the glass ceramics in 3 days. Apatite crystals formed on the glass ceramics could be act a role to make the chemical bond between the glass ceramics and living bone tissue.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.429-429
• /
• 2010

TFT 제조 방법 중 LTPS (Low Temperature Polycrystalline Silicon)는 저온과 저비용 등의 이점으로 인하여 flat panel display 제작에 널리 사용된다. 이동도와 전류 점멸비 등에서 이점을 가지는 ELA(Excimer Laser Annealing)가 널리 사용되고 있지만, 이 방법은 uniformity 등의 문제점을 가지고 있다. 이를 극복하기 위한 방법으로 MICC(Metal Induced Capping Crystallization)이 사용되고 있다. 이 방법은 $SiN_x$, $SiO_2$, SiON등의 capping layer를 diffusion barrier로 위치시키고, Ni 등의 금속을 capping layer에 도핑 한 뒤, 다시 한번 열처리를 통하여 a-Si에 Ni을 확산시키킨다. a-Si 층에 도달한 Ni들이 seed로 작용하여 Grain size가 매우 큰 film을 제작할 수 있다. 채널의 grain size가 클 경우 grain boundary에 의한 캐리어 scattering을 줄일 수 있기 때문에 MIC 방법을 사용하였음에도 ELA에 버금가는 소자의 성능과 안정성을 얻을 수있었다. 본 연구에서는 large grain TFT의 Gate bias stress에 따른 소자의 안정성 측정 및 분석에 목표를 두었다.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.5
• /
• pp.481-485
• /
• 2001

We investigated the structural and electrical properties of the Ba ($Zr_{x}$ $T_{il-x}$ )$O_3$ (BZT thin films with a mole fraction of x=0.2 and thickness 150 nm for the application in MLCC (Multilayer Ceramic Capacitor). BZT films were prepared on $Pt/SiO_2$/Si substrate at various substrate temperatures by the RF-magnetron sputtering system. When the substrate temperature was above $500^{\circ}C$, we could obtain multi-crystalline BZT films oriented at (110), (111), and (200) directions. The crystallization of the film and high dielectric constant were observed with the increase of substrate temperature. Capacitance of the film deposited at high temperature is more sensitive to the applied voltage than that of the film deposited at low temperature. This paper reports surface morphology, dielectric constant, dissipation factor, and C-V characteristics for BZT films deposited at three different temperatures. The BZT film deposited at 40$0^{\circ}C$ shows stable electrical properties but a little small dielectric constant for MLCC application.

• Journal of the Korean Chemical Society
• /
• v.50 no.3
• /
• pp.243-246
• /
• 2006

The LiCoO2 thin films were prepared on the Pt/Ti/SiO2/Si substrate by spin coating using citrate sol. The citrate sol was spin-coated on substrate and dried at 380oC for 15 min. to evaporate the solvents and remove the organic materials. The as-deposited films were annealed at 750oC for 10 min. in air for crystallization. The X-ray diffraction patterns for the film have been indexed hexagonal system with space group R3m. The active area of LiCoO2 films for electrochemical test was about 11cm2. A Li foil and 1M LiClO4 in propylene carbonate(PC) and ethylene carbonate(EC) (1:1)were used as an anode and an electrolyte, respectively. The galvanostatic charge-discharge test was carried out at constant current density ranging from 5 A/cm2 in the voltage window between 4.2 and 3.0 V. The first discharge capacity of the film is 0.35Ah/cm2-m. The cycling behavior of the LiCoO2 film is also reported.

• ETRI Journal
• /
• v.13 no.2
• /
• pp.21-27
• /
• 1991

Effects of annealing on the dielectric properties and microstructures of thin tantalum oxide film(25nm) deposited on p-type Si substrate with rf reactive magnetron sputtering were investigated. The leakage current density was remarkably reduced from $10^-8$ to $10^-12$ A/$\mum^2$at the electric field of 2MV/cm after rapid thermal annealing(RTA) in $O_2$at $1000^{\circ}C$, while little leakage reduction was observed after furnace annealing in $O_2$ at $500^{\circ}C$. The structural changes of thin tantalum oxide film after annealing were examined using high resolution electron microscope(HREM). The results of HREM show that substantial reduction in the leakage current density after the RTA in $O_2$ can be attributed to crystallization and reoxidation of the thin amorphous tantalum oxide film.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2009.10a
• /
• pp.1028-1031
• /
• 2009

High quality poly-SiGe thin films were prepared on 6-inch substrates using Reactive-thermal CVD with $Si_2H_6$ and $GeF_4$ around at $500^{\circ}C$ directly. Its thickness uniformity was ~ 3% on the entire substrate area. N-channel mobility of ~30 nm thick bottom-gate TFTs exceeded 20 $cm^2$/Vs without any further crystallization.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.171-171
• /
• 2007

Dysprosium-doped bismuth titanate (BDT) thin films were successfully deposited on Pt(111)/Ti/$SiO_2$/Si(100) substrates by liquid delivery MOCVD process and their structural and ferroelectric properties were characterized. Fabricated BDT thin films were found to be random orientations, which were confirmed by X-ray diffraction experiment and scanning electron microscope analysis. The crystallinity of the BDT films was improved and the average grain size increased as the crystallization temperature increased from 600 to $720^{\circ}C$ at an interval of $40^{\circ}C$. The BDT thin film annealed at $720^{\circ}C$ showed a large remanent polarization (2Pr) of $52.27\;{\mu}C/cm^2$ at an applied voltage of 5V. The BDT thin film exhibits a good fatigue resistance up to $1.0{\times}10^{11}$ switching cycles at a frequency of 1 MHz with applied pulse of ${\pm}5\;V$. These results indicate that the randomly oriented BDT thin film is a promising candidate among ferroelectric materials useti비 in lead-free nonvolatile ferroelectric random access memory applications.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.04b
• /
• pp.3-5
• /
• 2008

The $SrBi_2Ta_2O_9$ thin films are deposited on Pt-coated electrode(Pt/$TiO_2/SiO_2$/Si) using RF magnetron sputtering method. The ferroelectric properties of SBT capacitors with annealing temperatures were studied. Through the x-ray diffraction analysis and the scanning electron microscopy (SEM), it could be observed that crystallization of the SBT thin film started around $650^{\circ}C$ and complete crystallization was accomplished around $750^{\circ}C$ and grains grew from a small spheric form to rod-like. For the leakage current density of the SBT capacitor depending upon various annealing atmospheres, capacitor annealed in the oxygen atmosphere showed the most excellent characteristic, and they were respectively about $2.13\times10^{-9}[A/cm^2]$ at 5V and 340.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.34 no.2
• /
• pp.99-104
• /
• 2021

Ion-beam sputtering (IBS) was used to deposit semiconducting IZTO (indium zinc tin oxide) thin films onto heavily-doped Si substrates using a sintered ceramic target with the nominal composition In0.4Zn0.5Sn0.1O1.5, which could work as a channel layer for oxide TFT (oxide thin film transistor) devices. The crystallization behavior and electrical properties were examined for the films in terms of deposition parameters, i.e. target tilt angle and substrate temperature during deposition. The thickness uniformity of the films were examined using a stylus profilometer. The observed difference in electrical properties was not related to the degree of crystallization but to the deposition temperature which affected charge carrier concentration (n), electrical resistivity (ρ), sheet resistance (Rs), and Hall mobility (μH) values of the films.

• The Journal of Korean Institute of Communications and Information Sciences
• /
• v.24 no.12A
• /
• pp.2002-2007
• /
• 1999

In this paper, the n-channel poly-Si thin-film transistors (poly-Si TFT's) formed by solid phase crystallization (SPC) on glass were investigated by measuring the electrical properties of poly-Si films, such as I-V characteristics, mobility, leakage current, threshold voltage, and subthreshold slope. It is done to decide to be applied on TFT-LCD with large-size and high density. In n-channel poly-Si TFT with 2, 10, 25$\mu\textrm{m}$ of channel length, the field effect mobilities are 111, 126 and 125 $\textrm{cm}^2$/V-s and leakage currents are 0.6, 0.1, and 0.02 pA/$\mu\textrm{m}$, respectively. Low threshold voltage and subthreshold slope, and good ON-OFF ratio are shown, as well. Thus, the poly-Si TFT’s used by SPC are expected to be applied on TFT-LCD with large-size and high density, which can integrate display panel and peripheral circuit on a large glass substrate.