• International Journal of Highway Engineering
• /
• v.12 no.4
• /
• pp.101-110
• /
• 2010

In this paper, it has been studied about the CRCO to maintain or rehabilitate the aged JCP. The CRCO and JCO was constructed at useless section of Seo-Hae-Ahn express highway in South Korea. The performance evaluation was conducted. Especially, it was focused on the roll of longitudinal reinforced steels inserted into the CRCO. On crack survey results from field construction section, the reflection cracks at joint of the existing pavement occurred in CRCO. However, due to the constraints of longitudinal reinforced steels, crack width was small. Total crack length and quantity in the CRCO more than that in the JCO. And crack spacing in the CRCO was narrower than it in the CRCP. Through the bonding strength test results, if the cold milling and cleaning as well as surface treatment is applied, there will be no debonding problem at interlayer in the early age. From analysis of the horizontal behavior at the joint, the longitudinal reinforced steels constrained crack width which became wider than initial state over time. Also, that steel in the CRCO reduced the horizontal movement due to temperature variation(4 times than that in the JCO). But, if interface is debonded, the roll decreased. Vertical VWG data showed that CRCO did not occur debonding problem at steel location, but there was some problem in JCO. It was confirmed by field coring. The tensile strain appeared in the CRCO, But the compressive strain occurred in the JCO in early age. Through the FWD test result, deflection in the CRCO was less than that in the JCO. And K value in the CRCO was greater than it in the JCO.

• Journal of Korean Association for Spatial Structures
• /
• v.4 no.3 s.13
• /
• pp.49-56
• /
• 2004

This paper predicted the shear deformation, such as strain of shear reinforcement and shear track width, of reinforced concrete (RC) members using Transformation Angle Truss Model (TATM) in order to apply to the shea, analysis of RC buildings. To check the validity of TATM for the shear deformation of RC beams, four RC beams with different shear span-to-depth ratios were cast, instrumented and tested. Observed results were compared with theoretical results by MCFT(Response-2000), RA-STM, FA-STM, and TATM. The proposed model, TATM, better predicted the relationships of the shear stress-strain of shear reinforcement and the shear stress-shear track width than other truss models.

• Journal of the Korea Concrete Institute
• /
• v.14 no.4
• /
• pp.615-622
• /
• 2002

To reasonably predict the behaviors for RC flat-plate structures, analysis model considering the flexural stiffness of slabs is required. FEMA 273 and ACI 318-99 refer to theoretical analysis models of two-way slab systems under lateral loading but the actual application method is not suggested. In this study, the modeling and application methods of the flat-plates using effective beam concept are suggested. The results of this study are as follows. 1) The effective beam width model suggested in this study is very useful to model flat-Plate structures subjected to seismic loading for three dimensional analysis 2) The result of analysis for idealized flat-plate example using the effective beam widths considering the effect of the slab crack is shown upper value for displacements. Whereas the model considering effective beam width coefficients only is shown upper value for unbalanced moments

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.9 no.3
• /
• pp.101-110
• /
• 2005

In Seoul, structural deterioration is severe in the private masonry buildings which have been built since 1906s. But most of these structures remain without any repair works. As a result, the rate of deterioration is getting faster and these dangerous structures may cause hazardous circumstances to the adjacent structures and neighborhood. The purpose of this study is to investigate the actual conditions of wall cracks among the defect types which occur in private masonry buildings and to analyze the correlation between safety grades and wall cracks for offering the fundamental data. Using these date we can establish basic criteria for safety grades of structures and improve the quality of masonry buildings. The result of this study indicate that there are high correlations between safety grades and the width of crack but much less so with the length. Furthermore, with regard to crack patterns, vertical cracks much more negatively effected the safety grades.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.4
• /
• pp.1-12
• /
• 2017

This paper concerns the structural behavior of high-strength concrete beams with compressive strength of 80 MPa subjected to flexure. Main test variables were nominal yielding strength of longitudinal rebar including normal strength rebar(SD 400) and high strength rebar(SD 600), reinforcement ratio from 0.98 to 1.58% and beam section size with $200{\times}250$, $200{\times}300mm$. The nine beams were cast and tested under flexure. The study investigated ultimate flexural strength, load-deflection relationship, crack patterns, failure patterns and ductility of the test beams. Test results indicate that when rebar ratio increased flexural strength increased and ductility decreased. In addition, the number of cracks increased and the crack width decreased as the reinforcement ratio increased. The yield strength of rebar did not affect significantly load-crack width relationship. Nonlinear analysis of test beams was performed and then test results and analytical results of ultimate load were compared. Analytical results of high-strength concrete beams overall underestimated flexural strength of test beams.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.4
• /
• pp.404-412
• /
• 2020

Herein, the properties and self-healing performance of cement mortar incorporating calcium sulfoaluminate(CSA), crystalline admixture(CA), and magnesium oxide(MgO) were investigated. Mortar strength test and water permeability experiments were conducted to analyze self-healing performance of the mortar. Also, variation in crack width were measured via digital optical microscope observation. The hydration products formed in the crack via self-healing were analyzed using x-ray diffraction(XRD), thermogravimetry(TG), and digital optical microscope. The analysis revealed that compressive strength and tensile strength increased as CA substitutional ratio increased. However, in the case of MgO replacement, the compressive strength and tensile strength decreased as the CA substitution ratio increased. The products in the recovered cracks are found to be mostly Ca(OH)2, MgCO3, and CaCO3. CaCO3 was shown to be the main healing product and had a higher portion than Ca(OH)2 and MgCO3 in the recovery products. Moreover, the optimal mix derived via water permeability and crack width results was 8% CSA + 1% CA + 2.5% MgO.

• Tunnel and Underground Space
• /
• v.22 no.3
• /
• pp.205-213
• /
• 2012

In this study, scaled model tests were performed to investigate the stability of twin tunnels constructed in anisotropic rocks with $30^{\circ}$ inclined bedding planes under the condition of lateral pressure ratio, 2. Five types of test models which had respectively different pillar widths and shapes of tunnel sections were experimented, where both crack initiating pressures and deformation behaviors around tunnels were investigated. The models with shallower pillar width showed shear failure of pillar according to the existing bedding planes and they were cracked under lower pressure than the models with thicker pillar width. In order to find the effect of tunnel sectional shape on stability, the models with four centered arch section, circular section and semi-circular arch section were experimented. As results of the comparison of the crack initiating pressures and the deformation behaviors around tunnels, the semi-circular arched tunnel model was the most unstable whereas the circular tunnel model was the most stable among them. Furthermore, the results of FLAC analysis were qualitatively coincident with the experimental results.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.583-588
• /
• 2002

The purpose of the study is to evaluate fracture toughness on the Laser and the electron beam welded joints of high tensile steels (HT500, HT550, HT650) by using 3-point bend CTOD and Charpy impact test. WM (weld metal) CTOD tests have been carried out using two kinds of CTOD specimen, the Laser beam welding (108mm length, and 24mm width, and 12mm thickness) and the electron beam welding (l71mm length, and 38mm width, and 19mm thickness). WM Charpy impact specimen is a standard V-notch type, and the temperature of the experiment is changed from -45 to 20 degree of centigrade. FE-analysis is also performed in order to investigate the effect of stress-strain fields on fracture characteristics. Results of the standard V-notch Charpy test are influenced by strength mis-match effect and the absorbed energy vE depends on crack path, and The transition temperature of Laser beam welded joints is more higher than that of electron beam welded joints. Results of the 3-point bend test give low critical CTOD and the crack path is in the weld metal of al specimens. These results indicate fracture toughness characteristics of the welded joints and transition temperature of HT500 are similar both a Laser beam welded joint and an electron beam welded joint. But the fracture toughness and the transition temperature of the electron beam welded joints of HT550 and HT650 are higher than those o the Laser beam welded joints.

• Steel and Composite Structures
• /
• v.49 no.4
• /
• pp.381-392
• /
• 2023

This study experimentally investigates the flexural behavior of steel-UHPC composite slabs composed of an innovative negative Poisson's ratio (NPR) steel plate and Ultra High Performance Concrete (UHPC) slab connected via demountable high-strength bolt shear connectors. Eight demountable composite slab specimens were fabricated and tested under traditional four-point bending method. The effects of loading histories (positive and negative bending moment), types of steel plate (NPR steel plate and Q355 steel plate) and spacings of high-strength bolts (150 mm, 200 mm and 250 mm) on the flexural behavior of demountable composite slab, including failure mode, load-deflection curve, interface relative slip, crack width and sectional strain distribution, were evaluated. The results revealed that under positive bending moment, the failure mode of composite slabs employing NPR steel plate was distinct from that with Q355 steel plate, which exhibited that part of high-strength bolts was cut off, part of pre-embedded padded extension nuts was pulled out, and UHPC collapsed due to instantaneous instability and etc. Besides, under the same spacing of high-strength bolts, NPR steel plate availably delayed and restrained the relative slip between steel plate and UHPC plate, thus significantly enhanced the cooperative deformation capacity, flexural stiffness and load capacity for composite slabs further. While under negative bending moment, NPR steel plate effectively improved the flexural capacity and deformation characteristics of composite slabs, but it has no obvious effect on the initial flexural stiffness of composite slabs. Meanwhile, the excellent crack-width control ability for UHPC endowed composite members with better durability. Furthermore, according to the sectional strain distribution analysis, due to the negative Poisson's ratio effect and high yield strength of NPR steel plate, the tensile strain between NPR steel plate and UHPC layer held strain compatibility during the whole loading process, and the magnitude of upward movement for sectional plastic neutral axis could be ignored with the increase of positive bending moment.

• Journal of Korean Society of Steel Construction
• /
• v.10 no.3 s.36
• /
• pp.355-367
• /
• 1998

To evaluate the mechanical behavior and the compressive stress distribution in high tension bolted joints according to the size of bolt hole, the experimental and analytical studies are performed with enlarging bolt hole size. In experimental study, the static test is performed to measure the slip coefficient, and the fatigue test is also performed to evaluate the fatigue strength and failure pattern of fatigue crack. In analytical study, the compressive stress distribution is investigated by using the finite element analysis. From the result of experimental study, the slip coefficient and fatigue strength of the high tension bolted joints with oversize hole are not much different but somewhat it has decreased. These are because the size of bolt hole is larger than the holes of nominal size, therefore the width of clamping force is decreased and the compressive stress distribution area is smaller, this is certificated in the finite element analysis. In addition, the origin of fatigue crack in the oversize holes is closer to the hole than in the holes of nominal size, consequently it is investigated that the origin of fatigue crack is intimately associated with the compressive stress distribution which is formulated by the clamping force in both base metal and splice plate.