• Transactions of the Korean Society of Mechanical Engineers
• /
• v.6 no.3
• /
• pp.232-238
• /
• 1982

The behavior of corner crack propagation by unidirectional plane bending fatigue was investigated in the butt welded joints of SS41 and SM50 steel plates including an edge through-thickness notch. The properties of fatigue crack propagation were inspected in the weld metal, heat-affected zone, and base metal of the welded joints. Main results obtained are as follows; (1) When a plate with an edge through-thickness notch is loaded by plane bending fatigue in indirection, the 2 variant corner cracks on the upper and lower edge of the plate are initiated and propagated respectively from the notch. (2) In case of a specimen containing a corner crack, it is more reasonable to estimate the crack propagation rate by area of fracture surface than by crack surface length. (3) The rate of fatigue crack propagation becomes faster in the following order; weld metal, heat-affected zone, and base metal. (4) The specimen including reinforcement shape is rapidly failed throughout bond due to effect of its shape when the repeated load exceeds a certain cycle.

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.67-71
• /
• 2003

A hot press method was used to create the optimal fabrication condition for a Shape Memory Alloy(SMA) composite. The bonding strength between the matrix and the reinforcement within the SMA composite by the hot press method was more increased by cold rolling. In this study, the objective was to develop an on-line monitoring system in order to prevent the crack initiation and propagation by shape memory effect in SMA composite. Shape memory effect was used to prevent the SMA composite from crack propagation. For this system an optimal AE parameter should be determined according to the degree of damage and crack initiation. When the SMA composite was heated by the plate heater attached at the composite, the propagating cracks could be controlled by the compressive force of SMA.

• Transactions of Materials Processing
• /
• v.18 no.5
• /
• pp.377-384
• /
• 2009

The shape of edge cracking in rolling process generally occurred "V" shape. This cracking is successively generated at width edge of strip. The edge cracking is developed to center of strip during rolling process. In the results, the strip is occurred fracture, and the productivity is gone down because of the extensive production time. Accordingly, we need to control crack propagation during rolling process. But, the control of cracking is very difficult in rolling process. Previously the studies of edge cracking were mainly performed on hot rolling process. In this paper, the shape of the edge cracking in rolling was estimated according to process conditions such as initial edge crack size, reduction ratio and tension using FE-simulation and the simplicity experiments on cold rolling process.

• Composites Research
• /
• v.17 no.4
• /
• pp.68-73
• /
• 2004

An analytical study was conducted to characterize the fatigue crack growth behavior of pre-cracked aluminum plates repaired with asymmetric bonded composite patch. For single-sided repairs, due to the asymmetry and the presence of out-of$.$plane bending, crack front shape would become skewed curvilinear started from a uniform through-crack profile, as observed from Previous studies. Therefore, for the accurate investigation of fatigue behavior, it is necessary to predict the actual crack front evolution and take it into consideration in the analysis. In this study, the fatigue analysis of single-sided repairs considering crack front shape development was conducted by implementing three-dimensional successive finite element method coupled with linear elastic fracture mechanics (LEFM) concept, which enables the growing crack front to be directly traced and modeled in a step by step way. Through conducting present analysis technique, crack path of the patched plate as well as the fatigue life was evaluated with sufficient accuracy. The analytical predictions of both the crack front shape evolution and the fatigue life were in good agreement with the experimental observations.

• Journal of Mechanical Science and Technology
• /
• v.17 no.3
• /
• pp.343-349
• /
• 2003

The fuselage-wing intersection suffers from the cyclic bending moment of variable amplitude. Therefore, the influence of cyclic bending moment on the delamination and the fatigue crack propagation behavior in AFRP/Al laminate of fuselage-wing was investigated in this study. The cyclic bending moment fatigue test in AFRP/Al laminate was performed with five levels of bending moment. The shape and size of the delamination Lone formed along the fatigue crack between aluminum sheet and aramid fiber-adhesive layer were measured by an ultrasonic C-scan. The relationships between da/dN and ΔK, between the cyclic bending moment and the delamination zone size, and between the fiber bridging behavior and the delamination zone were studied. As results, fiber failures were not observed in the delamination zone in this study, the fiber bridging modification factor increases and the fatigue crack growth rate decrease and the shape of delamination zone is semi-elliptic with the contour decreasing non-linearly toward the crack tip.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.22 no.3
• /
• pp.680-683
• /
• 1998

In case of the infinite body containing a rigid inclusion with line crack shape, stress intensity factor is determined and the relation between stress intensity factor and stress distribution near a crack tip is developed. Also, the relation between stress intensity factor and Kolosoff stress function is developed. Finally, these results are compared with those that the crack surface is under no traction.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.7 no.7
• /
• pp.214-220
• /
• 1999

In order to use effectively a machinery part with fillet, it is necessary to determine a proper fillet shape in design step, Study of such problem by fracture mechanical criterion is rare. So, this paper focuses on the design of fillet radius in fracture mechanical aspect. Finite element method was used to obtain crack tip stress intensity factor. Stress intensity factor was calculated by COD(crack opening displacement0method proposed by Ingraffea and Manu. The parameter used in this study are thickness ration, filet radium and crack length . If fillet radius increase , crack propagation may be accelerated. Critical crack length is inversely proportional to fillet radius.

• Journal of Ocean Engineering and Technology
• /
• v.5 no.1
• /
• pp.88-96
• /
• 1991

Fatigue life and retardtion behavior after through-thickness were examined experimentally by using a CT specimen and surface-cracked specimen. The material used was 3% Ni-Cr-Mo steel. The fatigue crack shape before through-thickness is almost semicircular, and the measured aspect ratio is larger than the value obtained by calculation using the K value proposed by Newman-Raju. It is found that the crack growth behavior on the back side after through-ghickness is unique and can be divided into three stages a, b and c. A retardation parameter has been used successfully to predict the growth of cracks in specimen, and in this time, retardation factor is 4.3. By using the crack propagation rule considering on retardation state and the K value proposed by the authors, the remarkable crack growth behavior and the change in crack shape can be evaluated quantitatively.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.7
• /
• pp.1217-1222
• /
• 2002

The dynamic photoelasticity with the aid of Cranz-Shardin type high speed camera system is utilized to record the dynamically propagating behavior of the interface crack. This paper investigates the effects of the hole (existed along the path of the crack propagation) shape on the dynamic interface crack propagation behavior by comparing the experimental isochromatic fringes to the theoretical stress fields.

• Proceedings of the KSME Conference
• /
• 2001.11a
• /
• pp.278-285
• /
• 2001

Aluminum/Aramid Fiber Reinforced Plastic(Al/AFRP) laminates are applied to the fuselage-wing intersection. The main objective of this study was to evaluate the delamination zone behavior of Al/AFRP with a saw-cut and circular hole using average stress criterion and the effect of notch geometry. Mechanical tests were carried out to determine the cyclic-bending moment and delamination zone observed ultrasonic C-scan pictures. In case of Al/AFRP containing saw-cut specimen, the shape and size of the delamination zone formed along the fatigue crack. However, in case of Al/AFRP containing circular hole specimen, the shape and size of delamination zone formed two types. first type, delamination zone formed along the fatigue crack. Second type, not observed fatigue crack. Therefore, delamination zone was formed dependently of the circular hole shape.