• Nuclear Engineering and Technology
• /
• v.49 no.7
• /
• pp.1463-1471
• /
• 2017

In order to monitor the pipe thinning caused by flow-accelerated corrosion (FAC) that occurs in coolant piping systems, a shear horizontal ultrasonic pitch-catch waveguide technique was developed for accurate pipe wall thickness monitoring. A clamping device for dry coupling contact between the end of the waveguide and pipe surface was designed and fabricated. A computer program for multi-channel on-line monitoring of the pipe thickness at high temperature was also developed. Both a four-channel buffer rod pulse-echo type and a shear horizontal ultrasonic waveguide type for high-temperature thickness monitoring system were successfully installed to the test section of the FAC proof test facility. The overall measurement error can be estimated as ${\pm}10{\mu}m$ during a cycle from room temperature to $200^{\circ}C$.

• Steel and Composite Structures
• /
• v.37 no.3
• /
• pp.353-369
• /
• 2020

Eight cold-formed thin-walled steel beams were performed to investigate the effect of corrosion damage on the flexural behavior of steel beams. The relationships between failure modes or load-displacement curves and corrosion degree of steel beams were investigated. A series of parametric analysis with more than forty finite element models were also performed with different corrosion degrees, types and locations. The results showed that the reduction of cross-section thickness as well as corrosion pits on the surface would lead to a decline in the stiffness and flexural capacity of steel beams, and gradually intensified with the corrosion degree. The yield load, ultimate load and critical buckling load of the corroded specimen IV-B46-4 decreased by 22.2%, 26% and 45%, respectively. The failure modes of steel beams changed from strength failure to stability failure or brittle fracture with the corrosion degree increasing. In addition, thickness damage and corrosion pits at different locations caused the degradation of flexural capacity, the worst of which was the thickness damage of compression zone. Finally, the method for calculating flexural capacity of corroded cold-formed thin-walled steel beams was also proposed based on experimental investigation and numerical analysis results.

• Journal of the Korean institute of surface engineering
• /
• v.51 no.6
• /
• pp.372-380
• /
• 2018

Anodization techniques are widely used in the area of surface treatment of aluminum alloys because of its simplicity, low-cost and good corrosion resistance. In this study, we investigated the relationship between the properties (porosity and thickness) of anodic aluminum oxide (AAO) and its corrosion behavior. Aluminum 5052 alloy was anodized in 0.3 M oxalic acid at $0^{\circ}C$. The anodizing of aluminum 5052 was performed at 20 V, 40 V and 60 V for various durations. The corrosion behavior was studied in 3.5 wt % NaCl using potentiodynamic polarization method. Results showed that the pore diameter and thickness increased as voltage and anodization time increased. The relatively thick oxide film revealed a lower corrosion current density and a higher corrosion potential value.

• Journal of Ocean Engineering and Technology
• /
• v.11 no.2
• /
• pp.28-38
• /
• 1997

The corrosion fatigue test was conducted in air to investigate the corrosion fatigue strength of SM 30 C steel by which was corroded in the under sea and surface in the conditions of 3.0% NaCl salt solution. The fatigue tests were carried out on a rotary bending testing machine of cantilever type. The corrosion effect of the sea surface conditionwas served more than that of the under sea condition which was due ti the periodic contact of air thus accelerate the corrosion. The difference of the fatgue strength between sea surface and under sea conditions decreased with increase of stree level and corroded period. Inthe case of the solid shaft and thickness 2mm of hollow shaft, the difference of corrosion fatigue strength decreased as stress level and corrosion periodic increasing. Onthe contrary in the case of thickness 1mm of hollow sgaft, the difference of it increased as stress level, corrosionn periooodic increasing and also the condition of corrosion chaanged. The main factors affecting the degradation of fatigue strength due to corrosion were the reduction of sectional area and the increase of surface roughness. The interference phenomenon increase with stress level got higher.

• Corrosion Science and Technology
• /
• v.21 no.4
• /
• pp.290-299
• /
• 2022

Anodizing is an electrochemical surface treatment method conferring corrosion resistance and durability by forming a thick anodization film on the metal surface. Aluminum has a long service life and high thermal conductivity and formability, as well as excellent corrosion resistance. Aluminum 3003 alloy has improved formability, strength, and corrosion resistance due to the addition of a small amount of manganese. However, corrosion occurs in seawater and environments polluted with corrosion-inducing substances, which reduce corrosion resistance. Therefore, it is necessary to artificially form a thick anodized film to improve corrosion resistance. In this study, the anodization treatment time was 4 minutes, and voltages of 10 V, 20 V, 30 V, 40 V, 50 V, 60 V, 70 V, 80 V, 90 V, and 100 V were applied. The thickness and pore size of the oxide film increased according to the applied voltage. A barrier film was formed under voltage conditions from 10 V to 50 V, and a porous film was formed under voltage conditions from 60 V to 100 V. After anodizing, coating was applied. Wettability and corrosion resistance were observed before and after coating according to the surface shape and thickness of the oxide film.

• Journal of Korean Society of Steel Construction
• /
• v.21 no.3
• /
• pp.301-310
• /
• 2009

Steel has been widely used as a material in temporary structures. Corrosion attack often reduces the long-term durability of temporary steel members that are not protected from corrosion. In designing temporary steel structures, it is difficult to evaluate their long-term durability, since the thickness loss of steel members is not clear. In this study, laboratory and field exposure corrosion tests were performed on structural steel plate specimens, and the loss of thickness of specimens that were exposed to a subway construction site for 11 months and of specimens that were exposed to environments with controlled humidity and calcium chloride for six months were measured. Finally, a thickness loss equation was formulated based on the environmental conditions and the testing periods.

• Nuclear Engineering and Technology
• /
• v.54 no.1
• /
• pp.186-192
• /
• 2022

Flow accelerated corrosion (FAC) is a type of pipe corrosion in which the pipe thickness decreases depending on the fluid flow conditions. In nuclear power plants, FAC mainly occurs in the carbon steel pipes of a secondary system. However, because the temperature of a secondary system pipe is over 150 ℃, in situ monitoring using a conventional ultrasonic non-destructive testing method is difficult. In our previous study, we developed a waveguide ultrasonic thickness measurement system. In this study, we applied a waveguide ultrasonic thickness measurement system to monitor the thinning of the pipe according to the change in pH. The Korea Atomic Energy Research Institute installed FAC-proof facilities, enabling the monitoring of internal fluid flow conditions, which were fixed for ~1000 h to analyze the effect of the pH. The measurement system operated without failure for ~3000 h and the pipe thickness was found to be reduced by ~10% at pH 9 compared to that at pH 7. The thickness of the pipe was measured using a microscope after the experiment, and the reliability of the system was confirmed with less than 1% error. This technology is expected to also be applicable to the thickness-reduction monitoring of other high-temperature materials.

• Journal of Mechanical Science and Technology
• /
• v.16 no.7
• /
• pp.889-895
• /
• 2002

This paper presents the effect of external corrosion, material properties, operation condition and design thickness in pipeline on failure prediction using a failure probability model. The predicted failure assessment for the simulated corrosion defects discovered in corroded pipeline is compared with that determined by ANSI/ASME B31G code and a modified B31G method. The effects of environmental, operational, and random design variables such as defect depth, pipe diameter, defect length, fluid pressure, corrosion rate, material yield stress and pipe thickness on the failure probability are systematically studied using a failure probability model for the corrosion pipeline.

• Corrosion Science and Technology
• /
• v.15 no.2
• /
• pp.78-83
• /
• 2016

The e-coating to inhibit induced corrosion can deposit a coating not only on the exterior surface but also on the inside of whole metallic components of body-in-white (BIW). But it is difficult to deposit paint films on the inside area because metallic components are multi layered. It may cause shortness of e-coating thickness. The only way to properly verify e-coating thickness is by performing the use of tear-down prototypes. When paint films' thickness is inadequate, a structural modification on each metallic component is needed. Verification of the thickness improvement for a structural modification requires much manual effort and leads to increasing development time. Recently, the simulation technology has been developed to predict the e-coating thickness in e-coating field. By applying the simulation to BIW, improvement in paint thickness quality and shortening of development period are expected. The paper explains a validated solution that allows simulating the effect of design changes to the e-coating thickness and current density, thereby delivering results within a time frame of a few days.

• Corrosion Science and Technology
• /
• v.21 no.2
• /
• pp.121-129
• /
• 2022

A study on water-based epoxy coated on mild steel using the electroplating method was conducted to optimize the process parameters for dry film thickness to achieve superior paint quality at optimal cost in an automotive plant. The regression model was used to adjust various parameters such as electrode voltage, bath temperature, processing time, non-volatile matter, and surface area to optimize the dry film thickness. The average dry film thickness computed using the model was in the range of 15 - 35 ㎛. The error in the computed dry film thickness with reference to the experimentally measured dry film thickness value was - 0.5809%, which was well within the acceptable limits of all paint shop standards. Our study showed that the dry film thickness on mild steel was more sensitive to electrode voltage and bath temperature than processing time. Further, the presence of non-volatile matter was found to have the maximum impact on dry film thickness.