• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2018년도 추계 학술논문 발표대회
• /
• pp.23-24
• /
• 2018

Reinforced concrete is a building material that is generally used in modern society. Also, reinforced concrete structures in high salinity environments have low durability due to corrosion of reinforcing bars due to infiltrated chlorine ions. Anion exchange resins have an ability to immobilize chlorine ions in the resin while releasing their anions. As a material, it has already been shown that it is possible to fix the chloride ion inside the cementitious material through the cement mortar experiment. The purpose of this study is to confirm the compressive strength of cement mortar using powdered anion exchange resin after powdering an anion exchange resin. In order to confirm the chloride ion fixation ability of the powder anion exchange resin, chlorine ion penetration resistance test was carried out.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2014년도 추계 학술논문 발표대회
• /
• pp.40-41
• /
• 2014

As a result of strength test on BFS concrete, those mixed with 30% and 50% of BFS8000, respectively, showed higher or equivalent strength compare to OPC. As a result of test of chloride penetration on BFS, diffusion coefficients of concrete mixed with 30% FA4000 and FA5000, respectively, showed to restrain average 6.5% of diffusion coefficient compared to OPC. And in case of BFS concrete, those mixed with BFS6000 and BFS8000, restrained diffusion of chloride ions 253% and 336%, respectively, compared to OPC. Therefore, Mixing 50% of BFS was most efficient in order to maximize restraint of chloride penetration according to metathesis of large amount. In this study, when mixing BFS to concrete for long-run durability and restraint against chloride penetration, for BFS, as fineness was higher and mixing it to concrete with less or equivalent 50% of replacement rate, there were results of higher strength compared to OPC and more efficient restraint of chloride ions.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2014년도 춘계 학술논문 발표대회
• /
• pp.108-109
• /
• 2014

The purpose of this study is to enhance durability of solidifying mat. solidifying mat excellent mechanical properties of geotextile. multi-layer coating system is applied to the mat and the chloride ions penetration resistance, chemical resistance, accelerated carbonation test were evaluated by testing the durability. Durability test results are as follows. chloride ions penetration resistance results are coated mat is approximately 70 % lower than plain. chemical resistance test results are coated mat no discoloration. accelerated carbonation test results are coated mat is approximately 90 % lower than the plain.

• Computers and Concrete
• /
• 제9권5호
• /
• pp.375-387
• /
• 2012

The objective of this investigation was to develop rules for automatic categorization of concrete quality using selected artificial intelligence methods based on machine learning. The range of tested materials included concrete containing a new waste material - solid residue from coal combustion in fluidized bed boilers (CFBC fly ash) used as additive. The rapid chloride permeability test - Nordtest Method BUILD 492 method was used for determining chloride ions penetration in concrete. Performed experimental tests on obtained chloride migration provided data for learning and testing of rules discovered by machine learning techniques. It has been found that machine learning is a tool which can be applied to determine concrete durability. The rules generated by computer programs AQ21 and WEKA using J48 algorithm provided means for adequate categorization of plain concrete and concrete modified with CFBC fly ash as materials of good and acceptable resistance to chloride penetration.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2016년도 추계 학술논문 발표대회
• /
• pp.148-149
• /
• 2016

In this paper, the increase in chloride resistance of footing concrete at coastal area was evaluated by replacement of Mineral Admixture. In KBC 2009, the footing concrete's minimum specific concrete strength at coastal area is determined to 35MPa. However, this is criteria only based on the strength aspect. Thus, it is not considered to increase the chloride resistance by replacement of Mineral Admixture. According to the test results of chloride ions penetration resistance, 35MPa class concrete with OPC 100% shown inaccessible state. Low-strength (24~30MPa class) concretes with Mineral Admixture, however, presented better performances. In addition, chloride diffusion coefficient tests showed identical appearance. Therefore, the current KBC's chloride resistance criteria based on only concrete strength has to review for the reason it can cause many problems (ex. cost increases by growing concrete strength and the environmental issues by a lot of cement use).

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2009년도 춘계 학술대회 제21권1호
• /
• pp.417-418
• /
• 2009

해안 및 매립지 구조물은 염화물의 침투로 인해 매입된 철근의 피막파괴로 철근부식이 일어나 콘크리트 구조체에 열화가 급속하게 진행되기 때문에 앞으로의 해안 구조물의 수밀성, 내염해성을 필요로 한다. 따라서 본 연구에서는 내염해성 개선에 효과적인 액상형태의 Si/Al 복합 무기염을 모르타르에 적용하여 시간경과(7, 14, 28, 56일)에 따른 내염해특성을 파악하고자 하였다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2003년도 학술.기술논문 발표회
• /
• pp.43-48
• /
• 2003

This paper investigate that the effect of the concrete containing mineral admixtures(pozzolanic materials such as fly-ash, ground granulated blast-furnace slag, silica fume and meta kaolin) on the resistance properties to chloride ion invasion. The purposed testing procedure was applied to the concrete added mineral admixtures for 3~4 replacement ratios under W/B ratios ranged from 0.40 to 0.55. For the electrical migration test, Tang and Nilsson's method was used to estimate the migration coefficient of chloride ion. As a results, the W/B ratios, kinds of admixture and replacement ratios, water curing periods had a great effect on the migration coefficient of chloride ion, and the optimal replacement ratios of admixture had a limitation for each admixtures. Also, the addition of mineral admixtures by mass(replacement of OPC) enhanced the resistance of the mixture to chloride penetration compared with the plain concrete. The amount of acid soluble chloride ions and water soluble chloride ions were varied with the kinds of mineral admixtures. The compressive strength was shown related to the migration coefficient of chloride ion, the compressive strength increased with the decreasing migration coefficient of chloride ion. Below the 50MPa, the variation of migration coefficient of concrete added mineral admixtures was bigger than plain concrete.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2003년도 학술.기술논문발표회
• /
• pp.43-48
• /
• 2003

This paper investigate that the effect of the concrete containing mineral admixtures(pozzaolanic materials such as fly-ash, ground granulated blast-furnace slag, silica fume and meta kaolin) on the resistance properties to chloride ion invasion. The purposed testing procedure was applied to the concrete added mineral admixtures for 3∼4 replacement ratios under W/B ratios ranged from 0.40 to 0.55. For the electrical migration test, Tang and Nilsson's method was used to estimate the migration coefficient of chloride ion. As a results, the W/B ratios, kinds of admixture and replacement ratios, water curing periods had a great effect on the migration coefficient of chloride ion, and the optimal replacement ratios of admixture had a limitation for each admixtures. Also, the addition of mineral admixtures by mass(replacement of OPC) enhanced the resistance of the mixture to chloride penetration compared with the plain concrete. The amount of acid soluble chloride ions and water soluble chloride ions were varied with the kinds of mineral admixtures. The compressive strength was shown related to the migration coefficient of chloride ion, the compressive strength increased with the decreasing migration coefficient of chloride ion. Below the 50MPa, the variation of migration coefficient of concrete added mineral admixtures was bigger than plain concrete.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2004년도 학술대회지
• /
• pp.71-76
• /
• 2004

This paper investigate that the effect of the concrete containing mineral admixtures(pozzolanic materials such as fly-ash, ground granulated blast-furnace slag, silica fume and meta kaolin) on the resistance properties to chloride ion invasion. The purposed testing procedure was applied to the concrete added mineral admixtures for $3\sim4$ replacement ratios under W/B ratios ranged from 0.40 to 0.55. Specimens were immersed in $3.6\%$ NaCl solution for 330 days, and penetration depth, water soluble chloride contents and acid soluble chloride contents were measured in 28, 91, 182 and 330 days. Then, diffusion coefficient were calculated using total chloride contents. As a results. the kinds of mineral admixture and replacement ratios had a great effect on the resistance property of the concrete to chloride ion invasion compared with the plain concrete. And the optimal replacement ratios of mineral admixture had a limitation for each admixtures. The amount of acid soluble chloride ions and water soluble chloride ions were varied with the kinds of mineral admixtures and the penetration depth from the concrete skin. Chloride diffusion coefficient of each concretes decreased with the time elapsed. and the diffusion coefficients of the concrete immersed salt water for 330 days had a establishment with the compressive strength measured before immersing.

• 한국구조물진단유지관리공학회 논문집
• /
• 제19권6호
• /
• pp.80-87
• /
• 2015

본 연구에서는 칼슘알루미네이트 시멘트(CAC) 모르타르의 수화생성물, 강도, 흡수율, 표면전기 저항성 및 염소이온 침투저항성을 실험적으로 고찰하였다. CAC 모르타르의 성능은 보통포틀랜드 시멘트(OPC) 모르타르의 성능과 상호 비교되었다. 실험 결과에 따르면, CAC 모르타르의 주요 수화생성물은 $C_2AH_8$ 및 $CAH_{10}$으로 조사되었으며, 압축 및 부착강도는 OPC 모르타르에 비하여 우수하게 나타났다. 뿐만 아니라, 표면전기 저항성 및 염소이온 침투저항성도 대체적으로 좋은 결과를 나타냄으로서, CAC의 우수한 성능도 확인하였다. 그러나, CAC 모르타르의 흡수율은 초기재령부터 OPC 모르타르에 비하여 다소 크게 나타남으로써, CAC 경화체의 표면흡수 성능을 개선하기 위한 연구가 더 필요할 것으로 판단된다. 반면, CAC 및 OPC 혼용배합 모르타르의 역학적 성능은 CAC 모르타르에 비하여 대체적으로 다소 떨어지는 것으로 조사됨으로써, CAC계 경화체 제조시 주의가 요구된다.