• Environmental Engineering Research
• /
• v.24 no.2
• /
• pp.246-253
• /
• 2019

This study was conducted to explore the optimum proportion of zeolite and zeolite-kaolin as additives to cement clinker and gypsum samples, while maintaining the strength properties of produced environmentally sustainable cements. According to the British standard method, zeolite was added to cement clinker in proportions of 5-12% and 10-12% by weight, respectively, in the preparation of samples of zeolite-containing cement and zeolite-kaolin-based cement. Kaolin was used as a second additive as 10-20% of the total weight. The compressive strength tests were performed on base cement samples according to a standard procedure given in ASTM C109 Compressive Strength of Hydraulic Cement. These values were compared with those of the reference sample and the Omani allowable limits. The results indicated that the best compressive strength values were obtained with 88% cement clinker, 5% gypsum, and 7% zeolite for the zeolite-containing cement. Quantities of 70% cement clinker, 5% gypsum, 10% zeolite, and 15% kaolin gave the best results for zeolite-kaolin-based cement, resulting in a substitution of than 25% cement clinker. The study concluded that the partial cement clinker replacement using zeolite/kaolin combination may have a great influence on the reduction of $CO_2$ emission and energy saving in cement manufacturing.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.04a
• /
• pp.355-360
• /
• 1999

Polymer cement is made by the modifying ordinary cement concrete with polymer additive. Until now polymer cement concrete is not used for the structural member, but it is growing to be considered as developing uses such as a waterproof of roof slab, the structural member for protecting corrosion, and a road pavement. The plymer cement concrete, being used for those uses, is superior to the cement concrete against the inorganic, organic acid, salt of acetic acid and organic solvents generally. In this paper, the polymer cement concrete was made by the ratio of 1:1 of sands and tailing in fine aggregate in order to solve the environmental pollution which causes the social problem by the tailing, It was measured for the compressive strength, flexural strength, and chemicals resistance was tested by dealing with 10% HCI, 20% NaOH and 10% NaCl aqueous solution.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.04a
• /
• pp.175-180
• /
• 1999

The heating system of korea apartment house is called Ondol. The surface finishing mortar of this floor system typically used the cement based mortar, where the surface finishing mortar easily appears the crack. To order to crack control, the cement that added expansive additive used to reducing dry-shrinkage. For the surface finishing mortar, the types of shrinkage is known as plastic shrinkage, dry-shrinkage and autogenous This experimental study is to investigate the difference on dry-shrinkage of the cement that added expansive additives and OPC. The test method is varied the ration of water/cement (W/C) and the ratio of sand/cement(S/C). For OPC, The increase of the ratio of S/C is reduced dry-shirnkage but for the cement that added expansive additives, the increase of the ratio of S/C is augmented dry-shrinkage For OPC, The increase of the ratio of W/C is augmented dry-shrinkage but for the cement that added expensive, the increased of the ratio of W/C is reduced dry-shrinkage.

• Journal of the Korean Ceramic Society
• /
• v.43 no.12 s.295
• /
• pp.846-851
• /
• 2006

This paper discuss the adsorption and fluidity properties of recycled cement powder with different hydration hysteresis and particle size. Reactivity of hydrated fine powder was negligible low. Therefore, the adsorption and fluidity properties with super-plasticizer for hydrated recycled cement powder was very important for using additive material. Adsorption amount of super-plasticizer was increased by the finer hydrated recycled cement powder addition. And the fluidity of hydrated recycled cement powder was very poor than un-hydrated cement powder. To Improve the fluidity of hydrated recycled cement powder, PC super-plasticizer is the more effective than NS super-plasticizer.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.04b
• /
• pp.687-692
• /
• 1998

This paper covers concrete durability made with portland cement type I and V, and granulated blast furnace slag blended cements 40 and 60%. Typical properties of cements and compressive strength development, drying shrinkage, carbonation, freezing and thawing properties of concretes were investigated. In addition, effects of CI penetration on various concretes with/without a freezing and thawing treatment were also studied. Portland cement type I and V were superior to the blended cement in the properties of compressive strength development, drying shrinkage, carbonation and freezing and thawing durability. In the respect of resistant of CI Blended cement showed better than the portland cement due to high permeability. But the blended cement with a freezing and thawing treatment presented a much decreased resistance of CI penetration.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2014.05a
• /
• pp.252-253
• /
• 2014

This study is to XRD and image analysis of low carbon type recycled cement from waste concrete powder and cement raw materials. Waste concrete powder possible to low carbon type recycled cement in small part of additive materials. Also, low carbon type recycled cement using waste concrete powder is suitable for ordinary portland cement.

• Korean Journal of Materials Research
• /
• v.25 no.11
• /
• pp.590-597
• /
• 2015

In this article, poly methyl triethoxy silane was compounded with an inorganic waterproof admixture at a certain ratio to improve the performance of gypsum products; a new type of high-efficiency compound water-proofing additive was also investigated. Furthermore, the waterproof mechanism and the various properties on the hardened gypsum plaster were investigated in detail by XRD and SEM. The results show that the intenerate coefficient of gypsum plaster increased to more than 0.9; the water absorbing rate decreased to less than 10 %. Both the bending strength and the compressive strength of gypsum plaster increased by various degrees. The intenerate coefficient reached a maximum value of 0.73 and the strength of the samples showed almost no change when 5% cement alone was added. In this new type of the high-efficiency compound with waterproof additive, the optimal technological parameters for formulas were obtained to be: 5% cement, 18 % mineral powder, and 0.8% poly methyl triethoxy silane, to compound gypsum plaster. Meanwhile, the production of high performance gypsum as a building material has become possible.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2003.05a
• /
• pp.81-87
• /
• 2003

The purpose of this study is the development of a recycling process to recover the hydrated ability of cement hydrate which accounts for a large proportion of cementitious powder by concrete waste in order to recycle cementitious powder by concrete waste as recycle cement. Therefore, after having theoretical consideration based on the properties of high-heated concrete, we consider the properties of hydration of cementitious powder in hardened mortar under various temperature conditions. As a result of experiment, it is revealed that an effective development of recycling cement is possible since the cementitious powder by concrete waste recovers a hydraulic property during burning at $600^{\circ}C$ or $700^{\circ}C$. And it is shown that the fluidity of mortar decreases rapidly as the burning temperature of recycle cement increases. however, the improved effect of fluidity is predominant if adding the additive such as fly-ash or blast furnace slag.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2022.04a
• /
• pp.188-189
• /
• 2022

With the development of nano-reinforcement technology, TiO₂ nanomaterials have received widespread attention as one of the additives without pozzolanic reaction, which can be used to improve the mechanical properties of cement-based materials. Meanwhile, with the development of additive manufacturing technology or known as 3D printing technology, its application in the construction field has also got noticed. Therefore, in this work, the effect of three sizes of TiO₂ on the compressive strength of hardened cement-based materials fabricated by binder jetting 3d printing was evaluated. According to the results, the TiO₂ particles with larger sizes can provide better reinforcement to the hardened cement due to its more significant filling effect.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2022.04a
• /
• pp.255-256
• /
• 2022

We synthesized catechol-conjugated chitosan (CCC) to study its usefulness as a construction material additive in cement mortar. The degree of catechol conju-gation (DOC_cat) of the synthesized CCC was determined to be approximately14% by UV-vis and ¹H NMR spectroscopy. Furthermore, the hydroxyl and amine groups in CCC could play a crucial role in hydrogen bonding, metal coordination, and cross-linking processes via interaction with adducts from cement mortar. In this study, we observedanimprovement in the compressive strength and absorption rate, suggesting that CCC is a promising candidateforhigh-performance cement mortar.