• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.291-292
• /
• 2006

A steel/cemented carbide couple is selected to generate a tough/hard two layers material. Sintering temperature and composition are deduced from phase equilibria, and experimental studies are used to determine optimal conditions. Liquid migration from the hard layer to the tough one is observed. Microstructure evolution during sintering of the tough material (TEM, SEM, image analysis) evidences coupled mechanisms of pore reduction and WC dissolution. Liquid migration, as well as interface crack formation due to differential densification are limited by suitable temperature and time conditions.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2007년도 Techno-Fair 및 추계학술대회 논문집 전기물성,응용부문
• /
• pp.102-103
• /
• 2007

Recently, the dependence of the electric energy is increased in accordance with a growth of industry. Therefore, scientific investigation is needed for the security of electrical safety and the judgement of accident causes. Accordingly, this paper consist of the analysis for the carbonization patterns of phenolic resin and the mechanism. As the follows, spider-legs as a carbide are generated around the rods, when the electric current flows on the surface of phenolic resin. The IR absorption peak generated by the thermal effects is appeared at about $1720cm^{-1}$. As the case of Joule's heat, the crystal of a carbide is generated beca use of the rarefied oxygen. It's estimated that the formation of carbonization conductivity as the currents are easily flowed.

• 한국정밀공학회지
• /
• 제12권7호
• /
• pp.178-188
• /
• 1995

A study on the temperature distribution of tungsten carbide alloy steel(WC-Co) in surface grinding was conducted to improve the surface finish and to find optimum grinding conditions which would lead to efficient grinding operation by theoretical finite element method analysis and experimental test of workpiece under various conditions. Based on the comparixion of test results and FEM analysis data, it is concluded that the FEM computer simulation of heat transfer is useful in predicting the temperature distribution of test material that the increase of temperature is more infuleneced by the grinding depth than the grinding speed. And that the grinding energy flux of dey grinding is 4 to 6 time greater than wet grinding regardless of grinding speed and finally that the heat transfer does not take place in depth deeper than 3mm from the grinding surface.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2003년도 추계학술발표강연 및 논문개요집
• /
• pp.88-88
• /
• 2003

• 한국생산제조학회지
• /
• 제22권5호
• /
• pp.812-817
• /
• 2013

This study demonstrates the diffusion bonding process between a tungsten carbide shank (K30) and tungsten carbide (DX5) for micro WC-PCD tool fabrication. A type of nickel alloy was used as the filler met alto improve the bond ability between K30 and DX5. The bonding pressure, time, and surrounding conditions were kept constant. In particular, the normal pressure was controlled precisely under buckling analysis. Diffusion bonding was performed at various operation temperatures (1170-1770 K) by using a specially designed jig. The microstructure on the localized bonded surface was analyzed using scanning electron microscopy and optical microscopy. In the case of diffusion bonding of WCat 1370-1770K, the filler metal melted completely and diffused between the two base metals, and they were bonded more tightly on both sides than at temperatures below 1370 K. Our results demonstrated the importance of sensitive temperature dependence of diffusion bonding.

• Corrosion Science and Technology
• /
• 제5권4호
• /
• pp.123-128
• /
• 2006

It was analyzed the causes of boiler tube rupture due to a degradation and corrosion on the boiler tubes in fossil power plant. The experiments were carried out among samples taken from the operating facilities. The result were analyzed based on experimental results from mechanical strength, microstructure observation, and hardness measurement in order to determine the cause of local rupture on boiler tubes. In general, 2.25Cr-1Mo steel generates carbides, it is coarsened, its ductility and strength abruptly decreased as degradation is in progress, In order to confirm this phenomenon, we observed changes of the mount of Cr and Mo of carbide by carrying out EDX chemical composition analysis. The amount of Cr and Mo in the degraded material or service exposed material gradually increased the amount of Mo but initially they were almost maintained at the same amount. Furthermore, we observed that the carbide become coarsened both in the grain and at the grain boundary. Tensile test was carried out to measure a material hardness and to recognize a drop-off of hardness. Overall result for tensile strength and hardness turned out to be lower than new material and mechanical strength and hardness was degraded as the material degradation was in progress.

• 비파괴검사학회지
• /
• 제37권2호
• /
• pp.75-83
• /
• 2017

In this paper, we investigate the capacity of the lock-in infrared thermography technique for the evaluation of non-uniform top layers of a silicon carbide coating with a nickel based superalloy sample. The method utilized a multilayer heat transfer model to analyze the surface temperature response. The modelling of the sample was done in ANSYS. The sample consists of three layers, namely, the metal substrate, bond coat and top coat. A sinusoidal heating at different excitation frequencies was imposed upon the top layer of the sample according to the experimental procedures. The thermal response of the excited surface was recorded, and the phase angle image was computed by Fourier transform using the image processing software, MATLAB and Thermofit Pro. The correlation between the coating thickness and phase angle was established for each excitation frequency. The most appropriate excitation frequency was found to be 0.05 Hz. The method demonstrated potential in the evaluation of coating thickness and it was successfully applied to measure the non-uniform top layers ranging from 0.05 mm to 1 mm with an accuracy of 0.000002 mm to 0.045 mm.

• 비파괴검사학회지
• /
• 제30권5호
• /
• pp.489-496
• /
• 2010

발전 및 화학플랜트의 많은 고온 설비는 장시간 운전으로 인해 재질열화 현상이 필연적으로 발생된다. 이러한 고온설비의 건전성 확보와 신뢰성 있는 수명평가를 위해서는 비파괴평가기법인 표면복제시험을 통한 미세조직분석 평가법이 현재까지 유용한 것으로 인식되어왔다. 이러한 표변복제기법은 기존의 평가법과 함께 탄화물평가를 통한 재질열화도 평가 등 새로운 정량적 접근법이 필요하며 다양하게 시도되고 있다. 본 논문에서는 표면복제기법과 관련한 기술개발 현황과 현장 적용사례들을 소개하고, 합리적인 평가결과 여부에 대해 기술하였으며, 현장설비에 대해 표면복제시험 후 미세조직을 분석한 결과 탄화물 평가방법이 정량적으로 유용함을 입증하였다.

• 한국세라믹학회지
• /
• 제48권5호
• /
• pp.454-457
• /
• 2011

We report the preparation of nanocrystalline cobalt ferrite, $CoFe_2O_4$, particles using recycled $Co_3O_4$ and their surface coating with silica using micro emulsion method. Firstly, the $Co_3O_4$ powders were separated from waste cemented carbide with acid-base chemical treatment. The cobalt ferrite nanoparticles with the size 10 nm are prepared by thermal decomposition method using recycled $Co_3O_4$. $SiO_2$ was coated onto the $CoFe_2O_4$ particles by the micro-emulsion method. The $SiO_2$-coated $CoFe_2O_4$ particles were studied their physical properties and characterized by X-ray diffraction (XRD), high resolution-transmission electron microscopy (TEM) analysis and CIE Lab value.

• 한국산업융합학회 논문집
• /
• 제24권5호
• /
• pp.517-523
• /
• 2021

In this study, in the selection of materials for the elements of a small plant, those with high resistance to corrosion are selected and the material properties of coatings for corrosion prevention are evaluated. In addition, corrosion characteristics and material analysis were performed on the welded part, and the hardness characteristics of the welded part, heat-affected part, and the base metal were evaluated. In the case of the post-weld-heat-treated(PWHT) specimen, the corrosion resistance of STS 316 was lower than that of the specimen without the PWHT due to the formation of intergranular carbide. As a result of evaluating the distribution of the hardness of the weld before and after the PWHT, the hardness of the specimen after the PWHT increased by about 20 Hv. As a result of the corrosion test on the welded specimen, the weight loss tended to increase as the time increased. In the case of the PWHT specimen, the corrosion resistance tended to be significantly lower than that of the specimen without PWHT due to the formation of intergranular carbide.