• 한국결정성장학회지
• /
• 제8권4호
• /
• pp.573-580
• /
• 1998

MgO와 Al 분말을 자전고온연소합성법으로 $MgAl_2O_4$ 스피넬 상을 합성하였다. MgO 와 Al을 테르밋 반응으로 생성하였으며, 가열반응생성으로 $800^{\circ}C$ 예열온도에서 반응시켰다. DTA/TG, 합성생성물, 최고온도 공정조건에 대해 연구하였고, MgO와 Al은 MgO+2Al+ 3/$2O_3$ $\rightarrow$ $MgAl_2O_4$ 로 합성되었다. 미반응된 재료로부터 MgAl2O4 스피넬의 활성화 에너지는 -264.8kcal/mol의 발생열량과 5634K의 최고 반응온도로 계산되었다. 테르밋 반응후의 시험편의 체적느 6% 증가하였다.

• 한국세라믹학회지
• /
• 제29권9호
• /
• pp.719-728
• /
• 1992

ZrO2/Al2O3-Mullite composites were prepared by infiltration of the silica sol to the porous ZrO2/Al2O3 bodies. The porous ZrO2/Al2O3 bodies for infiltration were fabricated using ZrO2 (20wt%)/Al2O3 composite powders synthesized by the emulsion-hot kerosene drying method. The preparation of silica sols was conducted by the hydrolysis-peptization of an alcoholic TEOS solution. When ZrO2/Al2O3-Mullite and ZrO2/Al2O3 composites were sintered at 1$650^{\circ}C$ for 4 hrs, both of them showed an excellent sinterability. As the amount of mullite added in the composites increased, the ratio of the tetragonal phase of zirconia to the monoclinic phase at the room temperature became higher. It was known that values of the fracture toughness of the ZrO2/Al2O3-Mullite composites were about 5.48 MPa.m1/2 much larger than that of the ZrO2/Al2O3 system.

• 전기전자학회논문지
• /
• 제22권4호
• /
• pp.1230-1233
• /
• 2018

에어로졸 데포지션 (aerosol deposition)공정을 통해 $Al_2O_3$막을 4H-SiC 상에 50 nm 두께로 제조하였고, 후열처리 공정에 따른 전기적 특성을 분석하였다. 그 결과 $N_2$분위기 열처리 시 $Al_2O_3$와 SiC 계면의 고정전하량이 감소하였으나 산소공공 생성에 의한 누설전류의 증가를 확인하였다. 본 결과로부터 계면특성 향상과 누설전류의 감소를 위해서는 적절한 $N_2$와 $O_2$가스의 혼합이 중요함을 확인하였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 하계학술대회 논문집
• /
• pp.387-390
• /
• 2000

The $Al_2$O$_3$specimens were prepared by the conventional mixed oxide method with addition La$_2$O$_3$, Bi$_2$O$_3$. The specimens were sintered at 15$25^{\circ}C$, 5hr., in air. The structural properties of the specimens were investigated by XRD and SEM. The $Al_2$O$_3$ceramics with dopants had hexagonal structure and didn't show secondary phases. In the case of specimens with 0.25wt% La$_2$O$_3$and 0.25wt% Bi$_2$O$_3$bulk densities and lattice parameter of c/a were 3.818g/cm$^3$, 3.783g/cm$^3$and ca=2.725, c/a=2.723, respectively. The bulk densities of $Al_2$O$_3$ceramics were decreased with dopants.

• 한국결정성장학회지
• /
• 제7권2호
• /
• pp.259-270
• /
• 1997

$\alpha-Al_2O_3$와 비정질 $TiO_2$부터 $Al_2TiO_5$를 합성하기 위한 고체상태반응의 반응속도를 $1200~1300^{\circ}C$ 온도 범위에서 연구하였다. 반응속도는 $Al_2O_3$분말을 코팅한 50 mol%의. $TiO_2$와 일정한 온도에서 여러 시간동안 가열하여 생성된 혼합물에 의하여 결정되었다. MgO안의 반응물과 미반응물의 양은 X-선 회절분석에 의하여 결정되었다. $Al_2TiO_5$의 부피율과 peak intensity비의 자료로부터 $Al_2O_3$와 $TiO_2$의 pseudobrookite(Tialite)형태로의 반응은 $1280^{\circ}C$와 $1300^{\circ}C$ 사이에서 시작되었다. 고체상태반응 활성화 에너지는 Arrhenius식에 의하여 결정되었다. 활성화 에너지는 622.4 kJ/mol이다.

• 한국표면공학회지
• /
• 제34권2호
• /
• pp.105-114
• /
• 2001

$Al_2$$O_3$ coatings were deposited on M2 high speed steels by the plasma enhanced chemical vapor deposition (PECVD) process, using a gas mixture of AlC1$_3$, $H_2$, $CO_2$ and Ar $Al_2$$O_3$ coatings had interference color and showed amorphous phase. $A1_2$X$A1_3$/($Ti_{0.5}$ /$Al_{0.5}$ )N double layer coatings were produced in the sequence of substrate $NH_3$ plasma pretreatment, ($Ti_{0.5}$$Al_{0.5}$)N depoition process, $Al_2$$O_3$ deposition process. $Al_2$ $O_3$/( $Ti_{0.5}$A $l_{0.5}$)N double layer coatings showed NaCl structure in ( $Ti_{0.5}$A $l_{0.5}$)N layer and amorphous phase in A1$_2$ $O_3$ layer. It was shown that $Al_2$ $O_3$ columns continuously grew onto ( $Ti_{0.5}$A $l_{0.5}$)N columns. ( $Ti_{0.5}$A $l_{0.5}$)N single coating and $Al_2$ $O_3$/( $Ti_{0.5}$A $l_{0.5}$)N double layer coating were oxidized at $700^{\circ}C$, 80$0^{\circ}C$, 90$0^{\circ}C$ for 1hr, 3hr in atmosphere. At 80$0^{\circ}C$, single layer coatings were oxidized, which were examined substrate oxide particle. But $Al_2$ $O_3$/ ( $Ti_{0.5}$A $l_{0.5}$)N double layer coatings maintained the asdeposited state. Therefore, $Al_2$ $O_3$/ ( $Ti_{0.5}$A $l_{0.5}$)N double layer coatings have moreexcellent oxidation resistance than ( $Ti_{0.5}$A $l_{0.5}$)N single layer coatings.X> 0.5/)N single layer coatings.s.

• 한국세라믹학회지
• /
• 제28권4호
• /
• pp.269-278
• /
• 1991

Fine AlN powder was synthesized by carbothermal reduction and nitridation of alumimun hydroxide prepared from Al-isopropoxide. AlN ceramics with Y2O3 and CaO were prepared by hot-pressing under the pressure of 30 MPa at 180$0^{\circ}C$ for 1 h in N2 atmosphere. Grain boundary behavior and purification mechanism of AlN lattice were examined by heat treatment of AlN ceramics at 185$0^{\circ}C$ for 1-6 h in N2 atmosphere. AlN ceramics without sintering additives showed poor sinterability. However, Y2O3-doped and CaO-doped AlN ceramics were fully densified nearly to theoretical density. As the heat treatment time increased, c-axis lattice parameter increased. This is attributed to the removal of Al2O3 in AlN lattice. This purification effect of AlN attice depended upon the quantity of secondary oxide phase in the inintial stage of heat treatment and the heat treatment time.

• 대한기계학회논문집
• /
• 제19권7호
• /
• pp.1619-1629
• /
• 1995

The Al/Al$_{2}$O$_{3}$ SiC and Al/Al$_{2}$O$_{3}$/C hybrid metal matrix composites (MMCs) were fabricated by squeeze infiltration method. Uniform distribution of reinforcements were found in the microstructure of metal matrix composites. Mechanical tests were carried out under various test conditions to clearly identify mechanical behavior of MMCs, and the wear mechanism of Al/Al$_{2}$O$_{3}$/(SiC or C) hybrid metal matrix composites were investigated. The tensile strength and hardness of hybrid composites was resulted in increasing compared with those of the unreinforced matrix alloy. Wear resistance was strongly dependent upon kinds of fiber, volume fraction and sliding speed. The wear resistance of metal matrix composites was remarkably improved by the addition of reinforcements. Especially, the wear resistance of the hybrid composites of carbon fibers was more effective than in the composites reinforced with alumina and SiC whiskers of reinforcements. This was due to the effect of carbon fiber on the solid lubrication. Wear mechanisms of hybrid composites were suggested from wear surface analyses. The major wear mechanism of hybrid composites was the abrasive wear at low to intermediate sliding speed, and the melting wear at intermediate to high sliding speed.

• 한국세라믹학회지
• /
• 제24권5호
• /
• pp.423-430
• /
• 1987

Characteristics of Al2O3-ZrO2 powders prepared by sol-gel process and their sintering behavior were investigated as a function of calcination temperature. The sol-gel processed powders were calcined at 800, 900, 1000, 1100, 1200$^{\circ}C$, and analyzed by X-ray diffraction technique. Pore size and distribution of green compact of the calcined powders were measured by mercury porosimeter. It is suggested that the optimal temperature of calcination for the sintering of Al2O3-ZrO2 powder prepared by sol-gel process is 1100$^{\circ}C$. In the Al2O3-17vol.% ZrO2 sintered specimen, which was sintered at 1600$^{\circ}C$ for 2hrs in air, 69vol.% tetragonal phse existed.

• Advances in materials Research
• /
• 제5권4호
• /
• pp.263-277
• /
• 2016

Mechanical properties of $Al/Al_2O_3$ and $Al/B_4C$ composites prepared through powder metallurgy are estimated up to 50% $Al_2O_3$ and 35% $B_4C$ weight fractions using micromechanics models and experiments. The experimental Young's modulus up to 0.40 weight fraction of ceramic is found to lie closely between Ravichandran's/Hashin-Shtrikman lower/upper bounds, and close to self consistent method/Miller and Lannutti method/modified rule of mixture/fuzzy logic method single value predictions. Measured Poisson's ratio lies between rule of mixture/Ravichandran lower and upper bound/modified Ravichandran upper bounds. Experimental Charpy energy lies between Hopkin-chamis method/equivalent charpy energy/Ravichandran lower limit up to 20%, and close to the reciprocal rule of mixture for higher $Al_2O_3$ content. Rockwell hardness (RB) and Micro-hardness of $Al/Al_2O_3$ are closer to modified rule of mixture predictions.