• 한국태양에너지학회 논문집
• /
• 제38권1호
• /
• pp.37-44
• /
• 2018

Solar panels are modules made up of many cells, like the N-type monosilicon, P-type monosilicon, P-type multisilicon, amorphous thin-film silicon, and CIGS solar cells. An efficient photovoltaic (PV) power is important to use to determine what kind of cell types are used because residential solar systems receive attention. In this study, we used 3-type solar panels - such as N-type monosilicon, P-type monosilicon, and CIGS solar cells - to investigate what kind of solar panel on a house or building performs the best. PV systems were composed of 3-type solar panels on the roof with each ~1.8 kW nominal power. N-type monosilicon solar panel resulted in the best power generation when monitored. Capacity Utilization Factor (CUF) and Performance Ratio (PR) of the N-type Si solar panel were 14.6% and 75% respectively. In comparison, N-type monosilicon and CIGS solar panels showed higher performance in power generation than P-type monosilicon solar power with increasing solar irradiance.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2016년도 제50회 동계 정기학술대회 초록집
• /
• pp.258-258
• /
• 2016

최근 디스플레이 산업의 발전에 따라 고성능 디스플레이가 요구되며, 디스플레이의 백플레인 (backplane) TFT (thin film transistor) 구동속도를 증가시키기 위한 연구가 활발히 진행되고 있다. 트랜지스터의 구동속도를 증가시키기 위해 높은 이동도는 중요한 요소 중 하나이다. 그러나, 기존 백플레인 TFT에 주로 사용된 amorphous silicon (a-Si)은 대면적화가 용이하며 가격이 저렴하지만, 이동도가 낮다는 (< $1cm2/V{\cdot}s$) 단점이 있다. 따라서 전기적 특성이 우수한 산화물 반도체가 기존의 a-Si의 대체 물질로써 각광받고 있다. 산화물 반도체는 비정질 상태임에도 불구하고 a-Si에 비해 이동도 (> $10cm2/V{\cdot}s$)가 높고, 가시광 영역에서 투명하며 저온에서 공정이 가능하다는 장점이 있다. 하지만, 차세대 디스플레이 백플레인에서는 더 높은 이동도 (> $30cm2/V{\cdot}s$)를 가지는 TFT가 요구된다. 따라서, 본 연구에서는 차세대 디스플레이에서 요구되는 높은 이동도를 갖는 TFT를 제작하기 위하여, amorphous In-Ga-Zn-O (a-IGZO) 채널하부에 화학적으로 안정하고 전도성이 뛰어난 SnO2 채널을 얇게 형성하여 TFT를 제작하였다. 표준 RCA 세정을 통하여 p-type Si 기판을 세정한 후, 열산화 공정을 거쳐서 두께 100 nm의 SiO2 게이트 절연막을 형성하였다. 본 연구에서 제안된 적층된 채널을 형성하기 위하여 5 nm 두계의 SnO2 층을 RF 스퍼터를 이용하여 증착하였으며, 순차적으로 a-IGZO 층을 65 nm의 두께로 증착하였다. 그 후, 소스/드레인 영역은 e-beam evaporator를 이용하여 Ti와 Al을 각각 5 nm와 120 nm의 두께로 증착하였다. 후속 열처리는 퍼니스로 N2 분위기에서 $600^{\circ}C$의 온도로 30 분 동안 실시하였다. 제작된 소자에 대하여 TFT의 전달 및 출력 특성을 비교한 결과, SnO2 층을 형성한 TFT에서 더 뛰어난 전달 및 출력 특성을 나타내었으며 이동도는 $8.7cm2/V{\cdot}s$에서 $70cm2/V{\cdot}s$로 크게 향상되는 것을 확인하였다. 결과적으로, 채널층 하부에 SnO2 층을 형성하는 방법은 추후 높은 이동도를 요구하는 디스플레이 백플레인 TFT 제작에 적용이 가능할 것으로 기대된다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 추계학술대회 논문집 Vol.21
• /
• pp.80-81
• /
• 2008

Schottky barrier thin film transistors (SB-TFT) on polycrystalline silicon(poly-Si) are fabricated by platinum silicided source/drain for p-type SB-TFT. High quality poly-Si film were obtained by crystallizing the amorphous Si film with excimer laser annealing (ELA) or solid phase crystallization (SPC) method. The fabricated poly-Si SB-TFTs showed low leakage current level and a large on/off current ratio larger than $10^5$. Significant improvement of electrical characteristics were obtained by the additional forming gas annealing in 2% $H_2/N_2$ ambient, which is attributed to the termination of dangling bond at the poly-Si grain boundaries as well as the reduction of interface trap states at gate oxide/poly-Si channel.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 하계학술대회 논문집
• /
• pp.456-456
• /
• 2009

Boron doping on an n-type Si wafer is requisite process for IBC (Interdigitated Back Contact) solar cells. Fiber laser annealing is one of boron doping methods. For the boron doping, uniformly coated or deposited film is highly required. Plasma enhanced chemical vapor deposition (PECVD) method provides a uniform dopant film or layer which can facilitate doping. Because amorphous silicon layer absorption range for the wavelength of fiber laser does not match well for the direct annealing. In this study, to enhance thermal affection on the existing p-a-Si:H layer, a ${\mu}c$-Si:H intrinsic layer was deposited on the p-a-Si:H layer additionally by PECVD. To improve heat transfer rate to the amorphous silicon layer, and as heating both sides and protecting boron eliminating from the amorphous silicon layer. For p-a-Si:H layer with the ratio of $SiH_4$ : $B_2H_6$ : $H_2$ = 30 : 30 : 120, at $200^{\circ}C$, 50 W, 0.2 Torr for 30 minutes, and for ${\mu}c$-Si:H intrinsic layer, $SiH_4$ : $H_2$ = 10 : 300, at $200^{\circ}C$, 30 W, 0.5 Torr for 60 minutes, 2 cm $\times$ 2 cm size wafers were used. In consequence of comparing the results of lifetime measurement and sheet resistance relation, the laser condition set of 20 ~ 27 % of power, 150 ~ 160 kHz, 20 ~ 50 mm/s of marking speed, and $10\;{\sim}\;50 {\mu}m$ spacing with continuous wave mode of scanner lens showed the correlation between lifetime and sheet resistance as $100\;{\Omega}/sq$ and $11.8\;{\mu}s$ vs. $17\;{\Omega}/sq$ and $8.2\;{\mu}s$. Comparing to the singly deposited p-a-Si:H layer case, the additional ${\mu}c$-Si:H layer for doping resulted in no trade-offs, but showed slight improvement of both lifetime and sheet resistance, however sheet resistance might be confined by the additional intrinsic layer. This might come from the ineffective crystallization of amorphous silicon layer. For the additional layer case, lifetime and sheet resistance were measured as $84.8\;{\Omega}/sq$ and $11.09\;{\mu}s$ vs. $79.8\;{\Omega}/sq$ and $11.93\;{\mu}s$. The co-existence of $n^+$layeronthesamesurfaceandeliminating the laser damage should be taken into account for an IBC solar cell structure. Heavily doped uniform boron layer by fiber laser brings not only basic and essential conditions for the beginning step of IBC solar cell fabrication processes, but also the controllable doping concentration and depth that can be established according to the deposition conditions of layers.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2009년도 춘계학술대회 논문집
• /
• pp.80-82
• /
• 2009

The dependence of the efficiency characteristics of hydrogenated amorphous silicon single junction solar cells on the various intrinsic layer thickness has been investigate in the glass/$SnO_2$:F/p,i,n a-Si:H/Al type of amorphous silicon solar cells by cluster PECVD system. The open circuit voltage, short circuit current, fill factor and conversion efficiency have been measured under AM 1.5 condition. The result of the cell performance was improved about 8.2% due to an increase in the short circuit current.

• 대한전자공학회논문지
• /
• 제26권6호
• /
• pp.48-56
• /
• 1989

밀착형 1차원 영상감지소자로서 팩시밀리에 사용될 광도전막을 사일랜듸 글로방전 분해법으로 제작하였다. 우선 rf전력, 사일랜유량, 분위기 가스압, $H_2/SiH_4$비 및 기판온도의 증착조건에 따른 단층광전도막의 전기적 및 광학적특성을 조사하였다. 이 단층구조 영상감지막은 광전감도 0.85와 100lux 조도하에서 $I_{ph}/I_d=100$을 나타내었다. 그러나 이러한 단층박막은 양 전극으로 부터의 캐리어주입으로 인해 큰 암전류도 0.2nA 이하를 나타내었다. 또한 다층막은 단층막에 비해 단파장 가시광영역이 보상되어 팩시밀리용 1차원 영상감지소자에 사용될 만한 결과를 나타내었다.

• 한국결정성장학회지
• /
• 제24권3호
• /
• pp.106-110
• /
• 2014

Atomic layer deposition(ALD)을 이용하여 $Al_2O_3$ 박막을 형성하고 이에 대한 패시베이션 특성에 대한 연구를 수행하였다. ALD로 증착된 $Al_2O_3$ 박막은 $400^{\circ}C$ 5분간 후속 열처리 공정 후에도 $Al_2O_3$ - 실리콘 계면 반응 없이 비정질 상태를 유지할 만큼 구조적으로 안정한 특성을 나타내었다. 후속 열처리 후 $Al_2O_3$ 박막의 패시베이션 특성이 향상되었으며, 이는 field effective 패시베이션과 화학적 패시베이션 효과가 동시에 상승에 기인하는 것으로 판단된다. $Al_2O_3$ 박막의 음고정 전하를 정량적으로 평가하기 위해서 후속 열처리 공정을 거친 $Al_2O_3$ 박막을 이용하여 metal-oxide-semiconductor(MOS) 소자를 제작하고 capacitance-voltage(C-V) 분석을 수행하였다. C-V 결과로부터 추출된 flatband voltage($V_{FB}$)와 equivalent oxide thickness(EOT)의 관계식을 통하여 $Al_2O_3$ 박막의 고정음전하는 $2.5{\times}10^{12}cm^{-2}$로 계산되었으며, 이는 본 연구에서 제시된 $Al_2O_3$ 박막 공정이 N-type 실리콘 태양전지의 패시베이션 공정에 응용 가능하다는 것을 의미한다.

• 대한전자공학회논문지SD
• /
• 제40권7호
• /
• pp.481-485
• /
• 2003

25㎛ 두께의 폴리이미드 박핀 기판을 glass 기판에 부착하여 최대 온도 150℃에서 비정질 실리콘 TFT를 제작하였다. 본 논문은 plastic 기판 위에 TFT가 제작되는 공정 절차를 요약하고 glass 위에 제작된 TFT와 ON/OFF 전달특성과 전계효과 이동도를 서로 비교해 보았다. a-SiN:H 코팅층은 plastic 기판의 표면 거칠기를 감소시키는 중요한 역할을 하여 TFT의 누설전류를 감소시키고 전계효과 이동도를 증가시켰다. 따라서 a-SiN:H 코팅층을 이용하여 plastic 기판에 양철의 TFT를 제작하였다.

• 반도체디스플레이기술학회지
• /
• 제16권4호
• /
• pp.75-78
• /
• 2017

The $CO_2$ gas responsibility of $SnO_2$ thin films was researched with various annealing temperatures. $SnO_2$ was prepared on n-type Si substrate by RF magnetron sputtering system and annealed in a vacuum condition. The bonding structure of $SnO_2$ was changed from amorphous to crystal structure with increasing the annealing temperature, and the content of oxygen vacancy was researched the highest of the annealed at $60^{\circ}C$. The $SnO_2$ annealed at $60^{\circ}C$ had the characteristics of the highest capacitance. The special properties of $CO_2$ gas responsibility was found at the $SnO_2$ thin film annealed at $60^{\circ}C$ with amorphous structure because of the combination with the oxygen vacancies and $CO_2$ gases changed the resistivity. The amorphous structure enhanced the responsibility at the $SnO_2$ surface and the conductivity of $SnO_2$ thin film.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 하계학술대회 논문집
• /
• pp.134-134
• /
• 2009

In this work, we report that crystallization speed as well as the electrical and optical properties about the N-doped $Ge_2Sb_2Te_5$ thin films. The 200-nm-thick N-doped $Ge_2Sb_2Te_5$ thin film was deposited on p-type (100) Si and glass substrate by RF reactive sputtering at room temperature. The amorphous-to-crystalline phase transformation of N-doped $Ge_2Sb_2Te_5$ thin films investigated by X-ray diffraction (XRD). Changes in the optical transmittance of as-deposited and annealed films were measured using a UV-VIS-IR spectrophotometer and four-point probe was used to measure the sheet resistance of N-doped $Ge_2Sb_2Te_5$ thin films annealed at different temperature. In addition, the surface morphology and roughness of the films were observed by Atomic Force Microscope (AFM). The crystalline speed of amorphous N-doped $Ge_2Sb_2Te_5$ films were measured by using nano-pulse scanner with 658 nm laser diode (power : 1~17 mW, pulse duration: 10~460 ns). It was found that the crystalline speed of thin films are decreased by adding N and the crystalline temperature is higher. This means that N-dopant in $Ge_2Sb_2Te_5$ thin film plays a role to suppress amorphous-to-crystalline phase transformation.