• Journal of the Korea Institute of Building Construction
• /
• v.16 no.6
• /
• pp.595-601
• /
• 2016

The insulation performance of the insulation currently used in building structures is reflected only during design based on initial performance and the reduction in heat insulation performance due to the degradation of long-term durability is not reflected. This study reviewed the degradation of heat insulation performance due to the durability degradation of insulating materials through the accelerated durability test. The study findings showed that the foamed polystyrene insulation bead method did not show performance degradation due to aging in the standard environmental condition and laboratory accelerated test condition but the performance is degraded in the freeze-thaw test condition. On the other hand, in the case of the extrusion method, the degradation of the heat insulation performance was less in the freeze-thaw test condition, but the rapid performance degradation was caused by the release of the internal gas at the beginning of aging. In addition, the hard polyurethane foam insulation showed better initial insulation performance than other insulation materials, but the performance was found to be degraded somewhat under laboratory accelerated test conditions and freeze-thaw test conditions.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.41 no.5
• /
• pp.38-43
• /
• 2009

A conservation corrugated box for storing document archives was developed. The specifications of the double-walled E-flute corrugated conservation box were modified from those of the Library of Congress, USA. The Photographic activity test (PAT) of ISO 18916 was used to ensure protection of the archival contents from adverse effects of the container itself. Accelerated aging was conducted to evaluate the conservative properties of the box components. Atomic force microscopy was also used to evaluate changes in the cellulose surface due to accelerated aging.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2008.11a
• /
• pp.549-550
• /
• 2008

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.25 no.6
• /
• pp.103-110
• /
• 2021

Elastomeric bearings composed of flexible rubber materials and steel reinforcement plates are widely used for seismic retrofit of bridges due to their excellent vertical stiffness and flexible lateral stiffness. Especially, it has the advantages of simple construction and low cost. Chloroprene rubber, a type of rubber material, has greater resistance to aging than natural rubber, but its performance is also degraded due to various deterioration factors. Although these aging characteristics are not reflected in the seismic design standards and seismic performance evaluation guidelines, it is reasonable to reflect this when related studies are accumulated. For chloroprene rubber, accelerated heat aging test was performed with variables of heating temperatures and exposure time to analyze shear characteristics. As aging progresses the maximum shear stress and shear strain decrease. Also, the shear stiffness is greatly increased at the same shear strain.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.402-403
• /
• 2009

Accelerated aging tests were conducted under laboratory conditions on two generator stator bars. Electrical stress is applied in No. 1 model stator bar. Electrical and thermal stresses are applied in No. 2 model stator bar. As aging times increased from 0 to 11460h, dissipation factor($tan{\delta}$) test was performed on No. 1 and No.2 model stator bars. The ${\Delta}tan{\delta}$ of No. 1 and No. 2 stator bars increased with increased in aging time.

• Textile Coloration and Finishing
• /
• v.29 no.3
• /
• pp.155-161
• /
• 2017

In CPB(Cold-Pad-Batch) dyeing, the rubber of the padder roll is influenced by the heat, chemical and mechanical influences and thus aging of the padder roll rubber occurs. This study presents an accelerated thermal aging test of the CPB padder roll rubber with strong alkali conditions. Using Arrhenius formula of the various property values for the various aging temperatures($80^{\circ}C$, $90^{\circ}C$, $100^{\circ}C$) of the padder roll, the accelerated life predictions could be calculated. The threshold value of the property was set at different values. The hardness was set at the point where 5% degradation occurs based on the actual use conditions, and the tensile strength was set at the point where 50% degradation occurs based on the general life prediction standards. From the results of the different physical properties at differing temperatures, the Arrhenius plot could be obtained. Through the usage of the Arrhenius Equation, significant duration expectation could be predicted, and the chemical aging behavior of the CPB padder roll could be found at the arbitrary and actual temperatures.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.9
• /
• pp.783-789
• /
• 2003

The winding problems of traction motor are the major determinant of motor's life. The root cause of winding failure is gradual deterioration of the insulation due to thermal, electrical, mechanical and environmental stresses. The aging of the insulation reduces the electrical and mechanical strength of the insulation. At same point, a voltage surge or mechanical shock from a traction motor start will fracture or break down the insulation. To achieve the expected life usually requires extensive laboratory evaluation of the insulation systems and the use of accelerated aging tests. There are several nondestructive test available for checking, the condition of motor insulation, the probable extent of aging, and the rate of which aging is taking place. So the insulation characteristics of stator coil were each analyzed by measurement of dielectric loss(tan$\sigma$), capacitance and partial discharge. The method of diagnosis is able to analyze the insulation condition and evaluate the life of the traction motor.

• The Transactions of the Korean Institute of Power Electronics
• /
• v.27 no.3
• /
• pp.206-213
• /
• 2022

This paper presents setting up a laboratory-scale testbed to estimate the aging of power MOSFET devices and integrated power modules by measuring its on-state voltage and current. Based on the aging mechanisms of the component inside the power module (e.g., bond-wire, solder layer, and semiconductor chip), a system to measure the on-state resistance of device-under-test (DUT) is designed and experimented: a full-bridge circuit applies current stress to DUT, and a temperature chamber controls the ambient temperature of DUT during the aging test. The on-state resistance of SiC MOSFET measured by the proposed testbed was increased by 2.5%-3% after 44-hour of the aging test.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.38 no.3 s.116
• /
• pp.66-71
• /
• 2006

The objective of this study was to find in what color Hanji(Korean hand-made paper) is dyed when it is dyed with a pigment extracted from clove tree using different kinds of mordant, and how the paper is discolored and variety of strength under the condition of accelerated aging test. The results of this experiment are as follows. The Hanji dyed with aluminum acetate mordant was colored yellowish brown at pH 4.82, discoloration after aging was as much as a slight difference of color was recognized, and the decrease of strength after aging test was small. Thus, the method using aluminum acetate mordant was usable in coloring Hanji. The second most useful Hanji dyeing moth of was using distilled water and ferrous sulfate mordant, which dyed Hanji light brown at pH 6.03. However, when pigment was extracted using distilled water and copper sulfate mordant was used, discoloration was satisfactory but strength decreased too much and pale brown was obtained. Thus, this method was not usable.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.480-483
• /
• 2002

This paper through shift norm of insulator and research by accident prevention countermeasure special skill authoritativeness verification of insulator and Long Term aging factor for power transmission analysis and evaluate and prove quality of insulator wish to. Assessment technique by aging of own porcelain insulator observes ageing factor for reciprocity comparison through several examinations. Through cool and heat accelerated Aging test, can measure the leakage current change amount that ensue to each Cycle. Can confirm own blazing fire factor as distribution freshness that ensue in HRB Test's hardness value.