• Journal of the Korea Furniture Society
• /
• v.21 no.4
• /
• pp.284-292
• /
• 2010

This research was carried out to examine the properties of fancy cherry veneer overlaid on the PF resin bonded Meranti plywood floor, which 2.5% green tea leaf powder was applied in the UV varnishes and the adhesives for scavenging the volatile organic compounds. The results were as follows: 1. The various properties of the treated samples, such as density, moisture content, thickness swelling, bending strength(MOR), adhesion shear strength, surface abrasion, curling, cyclic delamination test with boiling water, boiling property, cold-resistance and heat resistance, acid resistance and alkali resistance, and anti-contamination property showed no significant difference between the properties of the control samples. 2.5% green tea leaf powder treated floor gave a little better results than the control for surface scratch test. 2. In case of QUV and weathering test, no difference between the treated sample and control was found. 3. The floor was discolored by adding 10% green tea leaf powder to UV coating, and the floor was also discolored to light green during by the soaking test. The color of floor was not changed up to 5% addition level.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.33 no.1
• /
• pp.149-159
• /
• 2009

The purposes of this study are to evaluate physical performance of metallic Jacquard fabrics, and to contribute to the research and development of the women's suit made of the metallic Jacquard fabrics. First, eight fabrics were woven with two kinds of warp yarns(nylon and rayon) and weft yarn blended with various contents(0, 7, 14, 21%) of metallic yarn. Second, the mechanical properties were measured by using the KES-FB system, and physical properties such as tensile strength, tearing strength, abrasion resistance, drape, pilling, snagging, degree of crease resistance, flexural stiffness, specular gloss, folding endurance and electrostatic propensity were measured. The results were as follows. As the metal fiber content increased, bending, shear, thickness and weight increased, which imply low recovery of wrinkles. It means that metallic Jacquard fabrics enable to use as a memory fabric. 7% metallic Jacquard fabric showed a low value at total hand value, but there was little change. As the metal fiber content increased, tensile strength, tearing strength, drape coefficient, specular gloss and flexural stiffness increased, however the degree of crease resistance, electrostatic propensity and folding endurance decreased. The metallic Jacquard fabrics were excellent in snagging, abrasion resistance and pilling.

• Textile Coloration and Finishing
• /
• v.29 no.3
• /
• pp.131-138
• /
• 2017

Most of high performance fabrics for the car racing protective clothing have been developed to have thermal resistance, flame retardant property, impact resistance and anti-frictional properties to protect the racer from the crucial accident. In this study, the meta-aramid fabric, which has inherent flame retardant, was coated with nanoparticles of SiC to enhance the impact resistance and anti-friction properties. Uniform coating of the nanoparticles onto the fabrics was obtained by using tape casting method. As the experimental parameters, size and content of the SiC nanoparticle were varied with the coating conditions of the fabric surface. The effects of the nanoparticle coating on the properties of meta-aramid fabric were examined with various instrumental analyses such as SEM, tensile strength and abrasion test.

• Advances in concrete construction
• /
• v.5 no.6
• /
• pp.575-586
• /
• 2017

The disposal of polythene waste and fly ash is causing serious threat to the environment. Aim of this study is to decrease environmental pollution by using polythene waste and fly ash in concrete. In this study, cement was partially replaced with 0%, 5%, 10%, 15% and 20% fly ash (by weight) and plastic waste was added in shredded form at 0.6% by weight of concrete. The specimens were prepared for the concrete mix of M25 grade and water to cementitious material ratio (w/c) was maintained as 0.45. Fresh concrete property like workability was examined during casting the specimens. Hardened properties were found out by carrying out the experimental work on cubes, cylinders and beams which were cast in laboratory and their behavior under test were observed at 7 & 28 days for compressive strength and at 28 days for density, flexural strength, dynamic modulus of elasticity, abrasion resistance, water permeability and impact resistance. Overall results of this study show that addition of 0.6% (by weight of the concrete) plastic waste with 10% (by weight of cement) replacement of cement by fly ash result an improvement in properties of the concrete than conventional mix.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.57 no.5
• /
• pp.19-27
• /
• 2015

The results of Saemangeum seadike field inspection and material testing of armor stones in order to analyze causes of abrasion according to material characteristics of seaside armor stones in Saemangeum seadike are in the following: 1. The armor stones in Saemangeum seadike have been constructed by using internal stones (mainly, sinsi stones) and external stones, which had less strength (77.3 %) and more abrasion rate (133.3 %) compared with sinsi stones. 2. The compressive strength and abrasion rate were compared between ordinary wave section and high wave section for the purpose of analyzing the influence of waves. In compressive strength, sinsi stones were 4.0 % stronger and external stones were 0.6 % stronger in ordinary wave section than those of high wave section in average. In the case of abrasion rate, sinsi stones were 3.0 % higher and external stones were 8.2 % higher in the high wave section than those in the ordinary section. 3. The result of comparing compressive strength according to a zone is that the compressive strength in the Intertidal area was less strong in most of the zones. 4. Considering that deviated stones are moving around over the surface of armor stones in situ, it is important to compare material characteristics. So the comparison test about this factor showed that deviated sinsi stones were stronger than armor stones in situ in terms of compressive strength and resistance to abrasion. Based on these results, abraded armor stones may have resulted from their durability. Therefore it is assumed that armor stones are likely to be abraded when deviated stones which are more durable are moving around over armor stones which are less durable.

• Textile Coloration and Finishing
• /
• v.1 no.1
• /
• pp.35-46
• /
• 1989

Experiments described in which cotton fabrics at different stages of chemical processing were abraded to different extents on a Stoll Abrasion Tester with three different abradants, namely, a worsted fabric, flax fabric and silicon carbide paper. The four different plain-weave cotton fabrics selected were 1) desized, 2) scoured and bleached, 3) mercerized, 4) resin-treated. The surface abrasive damages of treated fabrics were observed by SAM, and load-elongation percent retentions of abraded samples were measured by Instrong Tester. The result were as follows: 1. The maximum percent retention of load-elongation with three different abradants was exhibited by the scoured and bleached fabrics and the minimum by the resin finished fabric. 2. The electron micrographs of four different cotton fabrics abraded by flax, worsted fabric abradants for 900 rubs showed a large number of criss-crossing stray fibers in fabric structure. It may be the molecular adhesion for frictional resistance to be explained. 3. The electron micrographs of four different cotton fabrics abraded by silicone carbide abradants showed the form of busing or mashing fibers in fabric structure. The above might be on the basis of the ploughing theory.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1998.04a
• /
• pp.271-276
• /
• 1998

To apply the wear resistant steel plate for heavy duty vehicle, the wear characterisms of various kinds of commercial steel plates were invesigated by dry sand/rubber wheel tester which was tested under scratch abrasion mode. The wear tested pnaterials were boron steels which were manufactured by thereto machanical control process (TMCP) in order to achieve higher hardness. As the result of the test, wear resistance of steel plate increases with the hardness and carbon content. The wear loss of wear resistance steel plate (Hv440) is a half times than tinat of SWS490A (Hv160) steel plate in dry sand-rubber wheel test and the result in field test is similar to this dry sand/rubber wheel test result. Therefore, dry sand/rubber wheel tester can be used to predict the scratch abrasion life of the parts for heavy duty vehicle.

• Journal of the Korea Furniture Society
• /
• v.26 no.4
• /
• pp.392-397
• /
• 2015

This study was carried out to analyze the effects on mechanical properties of deteriorated wood member by outdoor condition. The surface color, mechanical properties and structural stability of traditional wooden structures, exposed in water and UV, could be changeable. For the purpose, accelerated weathering test based on outdoor condition was carried out. The weathering time levels were composed 0, 500, 1000, 1,500 and 2,000 hours and mechanical properties were evaluated on each specimen according to weathering time level. Bending properties were decreased on weathering but recovered after 1,000 hours. Fatigue and impact strength were decreased to 1,000 hours and did not changed since then. Abrasion resistance was minimized in 1,000 hours. This results could be utilized for effectively stability management of traditional wooden structures and members.

• Journal of the Korean Applied Science and Technology
• /
• v.37 no.5
• /
• pp.1248-1256
• /
• 2020

In this study, the polyurethane resin was synthesized by applying PTMG and DMBA of different composition ratios for the synthesis of water-dispersible polyurethane used in wound coating resin. The varying properties of the synthesized water-dispersible polyurethane were measured through tensile strength, elongation, and abrasion resistance analysis. As for the tensile strength measurement result according to the PTMG content, the sample with the highest reaction molar ratio was measured as 1.08 kgf/mm2 and the elongation was measured as 520%. As for the tensile strength result according to the DMBA content, the sample with the highest reaction molar ratio was measured as 0.51 kgf/mm2, and the elongation was measured as 435%. The degree of surface destruction by the abrasion resistance measurement was visually confirmed through SEM.

• Textile Coloration and Finishing
• /
• v.22 no.1
• /
• pp.61-70
• /
• 2010

This effects of drawing conditions on the physical properties of the drawn worsted yarns were investigated. The drawn worsted yarns were made on the yarn drawing system with various drawing conditions such as concentration of reducing agent, draw ratio, setting time of drawn yarn and concentration of oxidizing agent. The dry and wet shrinkage, irregularity(CV%), thin and thick part, hairiness and abrasion resistance of these various specimens were measured and discussed in terms of various drawing conditions.