• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.394-397
• /
• 2001

In this paper, in-situ deposited $Ru/RuO_2$ bottom electrodes have been investigated as new bottom electrodes for PZT thin film capacitor application. As a comparison, structural and electrical properties of PZT thin films on Pt/Ti and $RuO_2$ bottom electrodes are also investigated. The use of $Ru/RuO_2$ hybrid electrodes showed better electrical properties in compression with $RuO_2$ bottom electrode. With increasing Ru electrode thickness, the PZT thin films showed preferred orientation along the (110) direction and and leakage current of PZT thin films were improved. The PZT thin films on Ru (100nm)/$RuO_2$ electrodes exhibited excellent ferroelectric properties such as remant polarization and coercive field of $7.2C/cm^2$ and 46.35 kV/cm, respectively.

• Proceedings of the KIEE Conference
• /
• 1999.11d
• /
• pp.848-850
• /
• 1999

In this study, PZT etching was performed using planar inductively coupled Ar(20)/$Cl_2/BCl_3$ plasma, The etch rate of PZT film was 2450 $\AA/min$ at Ar(20)/$BCl_3$(80) gas mixing ratio and substrate temperature of $80^{\circ}C$. X-ray photoelectron spectroscopy (XPS) analysis for film composition was utilized. The chemical bond of PbO is broken by ion bombardment, and the peak of metal Pb in a Pb 4f peak begins to appear upon etching, decreasing Pb content faster than Zr and Ti. As increase content of additive $BCl_3$, the relative content of oxygen decreases rapidly. We thought that abundant Band BCl radicals made volatile oxy-compound such as $B_{x}O_{y}$ and/or $BClO_x$ bond. To understand etching mechanism, Langmuir probe and optical emission spectroscopy (OES) analysis were utilized for plasma diagnostic.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2006.05a
• /
• pp.125-126
• /
• 2006

The characteristics of the tool system give many effects into the costs and qualities for the finished components. Therefore, a tool life is one of the important issues on cold forging industry. However, since variables related with tool life are many complicated, the studies for solution should be investigated by the systematic research approach. In this study, heat-treatment of tool material is investigated to improve the tool life. Deep cryogenic treatment of tool steel is very efficient to improve the wear resistance due to the fine carbide. And, it is investigated that the shape and dimension of tool give effect into both tool life and quality of forged product.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2002.10a
• /
• pp.172-175
• /
• 2002

High speed machining is one of the most effective technologies to improve productivity. It can give great advantage for manufacture of die and Moulds. However, when machining of micro groove in high speed machining a severely thermal damage was generated on workpiece and cutting tool. Generally, the cutting fluid is used to improve penetration. lubrication. and cooling effect. In order to rise the performance of lubrication. it contains extreme pressure agents (Cl, S, P). But the environment of work room go bad by those additive. Therefore, the compressed chilly air with oil mist system was developed to replace the conventional cutting fluid system. This paper carried out the tests to evaluate the machinability by the cutting environment in high speed micro groove machining of NAK80 (HrC40). Compressed chilly air with oil mist was ejected on the contact area between cutting edge and workpiece. The effect of this developed compressed chilly air with oil mist system was evaluated in terms of tool life. The results showed that the tool lift of carbide tool coated TiAlN with compressed chilly air mist cooling was much longer than that of the dry and flood coolant when cutting the material.

• The Bulletin of The Korean Astronomical Society
• /
• v.41 no.1
• /
• pp.77.2-77.2
• /
• 2016

We present preliminary results of the analysis of chemical abundances for seven hypervelocity star (HVS) candidates. These objects are G and K dwarfs in the Galactic disk selected from the Sloan Extension for Galactic Understanding and Exploration. Unlike other HVSs discovered thus far, their stellar orbits and kinematics suggest that they do not originate in the Galactic center or in an accretion event. These factors imply yet-unknown mechanisms that give rise to these kinematically-extreme disk stars. In order to study in detail their progenitors and possible formation mechanisms, we obtained spectra of these stars at a resolving power of R~6000, with the Dual Imaging Spectrograph at the Apache Point Observatory. We derive the abundances of chemical elements, C, Mg, Ca, Ti, Cr, Fe, and Ba from the observed spectra, using MOOG. We compare them with the ones of typical Galactic disk stars and discuss discrepancies between them to search for clues to their origin.

• Proceedings of the KIEE Conference
• /
• 1998.07g
• /
• pp.2501-2503
• /
• 1998

In this paper, the silicon-nitride membrane structure for IR sensor was fabricated through the etching and the direct bonding. The PTO layer as a IR detection layer was deposited on the membrane and its characteristics were measured. The attack of PTO layer during the etching of silicon wafer as well as the thermal isolation of the IR detection layer can be solved through the method of bonding/etching of silicon wafer. Because the PTO layer of c-axial orientation raised thermal polarization without polling, the more integration capability can be achieved. The surface roughness of the membrane was measured by AFM, the micro voids and the non-contacted area were inspected by IR detector, and the bonding interface was observed by SEM. The polarization characteristics and the dielectric characteristics of the PTO layer were measured, too.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.25-26
• /
• 2008

Electrical properties of Pt/Ti/Au/Pt contacts to n-GaAs were characterized as the V/III ratio of GaAs grown by metalorganic chemical vapor deposition were 25, 50, and 100, respectively. The samples have been annealed during 30sec at 350 and $450^{\circ}C$ in rapid thermal annealing, and those specific contact resistance investigated by using transmission line method. According to experimental results, the specific contact resistance between p-metal and GaAs was decreased as the V/III ratio was lower. These results indicate that Si doping concentration of GaAs increased as the vacancy of V-series of GaAs was high.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.329-332
• /
• 1999

In this paper, BST((Bao.&o,dTi0:3) thin films were deposited by the rf magnetron sputtering method on Pt/$SiO_2$/Si substrate. Pt, $RuO_2$, Ag, Cu films for the formation of top electrode were deposited on BST thm films. And then Top Electrodes/BST/Pt capacitors were annealed with rapid thermal annealing(RTA) at various temperature. We have investigated effect of post-annealing on the electrical properties such as dielectric constant and leakage current of the capacitors. It was found that electrical properties of the capacitors were greatly depended on the annealing temperatures as well as the materials of top electrodes. In BST thin films with Pt top electrode was annealed at $700^{\circ}C$. the dielectric constant was measured to the value of 346 at l[kHzl and the leakage current was obtained to the value of $8.76\times10^8$[A/$\textrm{cm}^2$] at the forward bias of 2[V].

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.3
• /
• pp.207-213
• /
• 2003

The Sr$\_$0.7/Bi$\_$2.6/Ta$_2$O$\_$9/(SBT) thin films are deposited on Pt-coated electrode(Pt/TiO$_2$/SiO$_2$/Si) using RF magnetron sputtering method. The structural and electrical properties of SBT capacitors were influenced with annealing atmosphere. In the XRD pattern, the SBT thin films in all annealed atmosphere had (105) orientation. In the SEM images, Bi-layered perovskite phase was crystallized in all annealing atmosphere and grain largely grew in oxygen annealing atmosphere. The maximum remnant polarization and the coercive electric field in oxygen annealing atmosphere are 12.40[${\mu}$C/cm$^2$] and 30[kV/cm] respectively. The dielectric constant and leakage current density of capacitors annealed oxygen atmosphere are 340 and 2.13${\times}$10$\^$-9/ [A/cm$^2$] respectively. The fatigue characteristics of SBT capacitors did not change up to 10$\^$10/ switching cycles.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.920-923
• /
• 2000

All solid-state thin film supercapacitor(TFSC) based on $RuO_2$ electrode was fabricated. Ruthenium oxide$(RuO_2)$ thin film was deposited on Pt/Ti/Si subsrate by d.c. magnetron sputtering. LiPON(lithium phosphorus oxynitride) thin film were deposited by r.f. reactive sputtering. X-ray diffraction patterns of $RuO_2$ and LiPON films revealed that crystal structures of both films were amorphous. To decrease resistivity of $RuO_2$ thin film, $RuO_2$ thin film was deposited with $H_2O$ vapor. In order to decide the maximum ionic conductivity, the LiPON films were prepared by various sputtering condition. The maximum ionic conductivity was $9.5\times{10}^7S/cm$. A charge-discharge measurements showed the capacity of $3\times{10-2}\;F/cm^2-\mu{m}$ for the as-fabricated TFSC. The discharging efficiency was decreased after 500 cycles by 40 %.