• Transactions on Electrical and Electronic Materials
• /
• v.9 no.1
• /
• pp.1-5
• /
• 2008

ZnS is an attractive material for future optical and electrical devices since it has a direct and wide band gap to provide blue emission at room temperature. In this study, inductively coupled $BCl_3/Ar$ plasma was used to etch ZnS:Mn thin films. The maximum etch rate of 164.2 nm/min for ZnS:Mn was obtained at a $BCl_3(20)/Ar(80)$ gas mixing ratio, an rf power of 700 W, a dc bias voltage of -200V, a total gas flow of 20 sccm, and a chamber pressure of 1Pa. The etch behaviors of ZnS:Mn thin films under various plasma parameters showed that the ZnS:Mn were effectively removed by the chemically assisted physical etching mechanism. The surface reaction of the ZnS:Mn thin films was investigated by X-ray photoelectron spectroscopy. The XPS analysis revealed that Mn had detected on the surface ZnS:Mn etched in $BCl_3/Ar$ plasma.

• Electrical & Electronic Materials
• /
• v.10 no.10
• /
• pp.1005-1010
• /
• 1997

ZnS:Mn thin film was made by coevaporation with Electron Beam Evaparation(EBE) method. And structural and optical characteristics of ZnS:Mn thin films were investigated by substrate temperature annealing temperature and dopant Mn. When ZnS:Mn thin film was well deposited with cubic crystalline at substrate temperature of 30$0^{\circ}C$ its surface index was [111] and its lattice constant of a was 5.41$\AA$. Also When ZnA:Mn thin film was well made with hexagonal crystalline at substrate temperature of 30$0^{\circ}C$annealing temperature of 50$0^{\circ}C$and annealing time of 60min its miller indices were (0002) (1011), (1012) and (1120). And its lattice constant of a and c was 3.88$\AA$and 12.41$\AA$ respectively. Finally hexagonal ZnS:Mn thin film with dopant Mn of 0.5wt% had fundamental absorption wavelength of 342nm. And so its energy bandgap was about 3.62eV.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.30 no.1
• /
• pp.42-47
• /
• 2017

In this study, the physical and optical properties of $ZnS:Mn^{2+}$ Quantum Dot prepared by wet-process condition with Mn/Zn ratio was valuated. The powder characteristics and optical behavior were investigated through XRD, TEM and Photo spectrometer exicted by various UV light source. We found the main peak of ZnS (111) was shifted by 0.8 degree to low angle position with increasing stirring energy from 200 RPM to 600 RPM, which is thought to be the increase of lattice defects during wet process. The photo luminescence at 600 RPM shows also higher blue intensity which is well correlated with XRD results. With increasing Mn/Zn ratio, the PL intensity become higher and shifed by 8.5nm to right side, by the increment of substitutional $Mn^{2+}$ ions.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.05a
• /
• pp.102-105
• /
• 2004

With varying rapid thermal annealing (RTA) temperature, luminescent properties of ZnMgS:Mn thin film sputter-deposited with one target were measured. Although all samples have the same composition, $Zn_{1-x}Mg_xS:Mn$ (x=0.25) can emit luminescence between 580 and 614 nm, which is controlled by only RTA temperature. It is understood that the energy band gap shift of ZnMgS:Mn thin film phosphor occurs with varying RTA temperature.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.141-141
• /
• 2010

ZnS:Mn yellow phosphors doped with Cu for white light emitting diodes were synthesized by solid state reaction method. Photoluminescence excitation spectra originated from $Mn^{2+}$ were ranged from 450 nm to 500 nm. The yellow emission at around 580 nm was associated with $^4T_1{\rightarrow}^6A_1$ transition of $Mn^{2+}$ ions in ZnS:Mn,Cu phosphors. The highest photoluminescence intensity of the phosphors under 405 nm excitation was obtained at Cu concentration of 0.02 mol%.

• Bulletin of the Korean Chemical Society
• /
• v.34 no.4
• /
• pp.1181-1187
• /
• 2013

Water-dispersible ZnS:Mn nanocrystals were synthesized by capping the surface of the nanocrystal with O-(2-Aminoethyl)polyethylene glycol (PEG-$NH_2$, Mw = 10,000 g/mol) and O-(2-Carboxyethyl)polyethylene glycol (PEG-COOH, Mw = 10,000 g/mol) molecules. The modified PEG capped ZnS:Mn nanocrystal powders were thoroughly characterized by XRD, HR-TEM, EDXS, ICP-AES and FT-IR spectroscopy. The optical properties were also measured by UV/Vis and photoluminescence (PL) spectroscopies. The PL spectra showed broad emission peaks at 600 nm with similar PL efficiencies of 7.68% (ZnS:Mn-PEG-NH2) and 9.18% (ZnS:Mn-PEG-COOH) respectively. The measured average particle sizes for the modified PEG capped ZnS:Mn nanocrystals by HR-TEM images were 5.6 nm (ZnS:Mn-PEG-NH2) and 6.4 nm (ZnS:Mn-PEG-COOH), which were also supported by Debye-Scherrer calculations. In addition, biological toxicity effects of the nanocrystals over the growth of wild type E. coli were investigated. They showed no biological toxicity to E. coli until very high concentration dosage of 1 mg/mL of the both nanocrystal samples.

• Bulletin of the Korean Chemical Society
• /
• v.33 no.2
• /
• pp.657-662
• /
• 2012

Mercaptoacetic acid (MAA) and mercaptopropionic acid (MPA) capped ZnS:Mn nanocrystals were synthesized and their physical characteristics were examined by XRD, HR-TEM, EDXS, and FT-IR spectroscopy. The optical properties of the MPA capped ZnS:Mn nanocrystals dispersed in aqueous solution were also measured by UV/Vis and solution photoluminescence (PL) spectra, which showed a broad emission peak around 598 nm (orange light emissions) with calculated relative PL efficiency of 5.2%. Comparative toxicity evaluation of the uncoordinated ligands, MAA and MPA, with the corresponding ZnS:Mn nanocrystals revealed that the original ligands significantly suppressed the growth of wild type E. coli whereas the ligandcapped nanocrystals did not show significant toxic effects. The reduced cytotoxicity of the conjugated ZnS:Mn nanocrystals was also observed in NIH/3T3 mouse embryonic fibroblasts. These results imply that potential toxicities of the capping ligands can be neutralized on ZnS:Mn surface.

• Proceedings of the Korean Society Of Semiconductor Equipment Technology
• /
• 2006.05a
• /
• pp.225-231
• /
• 2006

.고상반응법 (solid state reaction)합성된 ZnS:Mn,Cu,Cl 형광체는 약 $20^{\sim}25{\mu}m$ 의 구형이고, Cubic/hexagonal 구조를 보였다. Electroluminescent device(ELD)는 실크 스크린된 형광층(ZnS:Mn,Cu,Cl)/유전체층 ($BaTiO_3$)으로 구성되었으며, 각층은 $30^{\sim}50{\mu}m,\;50^{\sim}60{\mu}m$ 정도로 도포 하였다. 100 V-400 Hz 의 구동조건에서, ELD 의 백색 발광은 450 nm, 480 nm 픽에서 각각 $Cl_s{\to}Cu^{+}\;_{Zn},\;Cl_s{\to}Cu^{2+}\;_{Zn}$ 전이에 의해 중첩된 청색, 녹색 밴드의 발광과, 580 nm 픽에서 Mn 의 $^{4}T_1{\to}^{6}A_1$ 전이에 의한 황색 밴드의 발광으로 이루어진다. Cu 농도의 증가에 따라 450 nm 의 발광 밴드의 휘도는 감소하며 580 nm 의 발광 밴드의 휘도가 증가하였고 발광 휘도가 향상되었다. 즉, 색온도가 높은 cold white(10000 K)에서 색온도가 낮은 Warm white(3000 K) 로 변한다. 이것은 450 nm 의 발광 밴드가 580 nm 의 발광 밴드에 흡수되는 에너지 전이 (Energy transfer) 현상에 기인한다. ZnS:Mn,Cu,Cl 의 Mn 1.5 wt %, Cu 2.5 wt.% 에서 최적 발광 휘도를 보이며, 100 V-400 Hz 에서 약 $12cd/cm^2$이였다.

• Journal of The Korean Society of Grassland and Forage Science
• /
• v.24 no.3
• /
• pp.193-200
• /
• 2004

This pot experiment was conducted to investigate the effects of systematic variation application of Fe, Mn, Cu, and Zn on forage performance of orchardgrass and white clover. The treatments of systematic variation were 0/100, 25/75, 50/50, 75/25, and $100/0\%$ in the Fe/Cu(trial-1), Mn/Zn(trial-2), and Fe+Cu/Mn+Zn(trial-3), respectively. The treatments of Fe/Mn/Cu/Zn(trial-4) were composed of $70\%$ in main element and $10\%$ in other 3 elements, respectively. 1. By the systematic variations of Fe, Mn, Cu, and Zn, the yields were more significantly influenced in white clover than in orchardgrass. In addition, the yields of white clover were closely correlated to the trends of root/nodule growth and flowering. In the Fe/Cu trial, the relatively high yields were obtained at the $100/0\%$ in orchardgrass and at the $75/25\%$ in white clover. The yields of white clover were more negatively influenced by the 100/0(Cu control) than by the 0/100(Fe control). The yields of orchardgrass, however, tended to be opposite to the above trends. 2. In the Mn/Zn trial, both forages showed generally high yields at the high ratios of Mn/Zn. Compared with orchardgrass, the yields of white clover were greatly decreased by the Mn-deficiency(low ratio of Mn/Zn). The effects of Zn on forage yields, however, were not recognized. 3. In the Fe+Cu/Mn+Zn trial, the yields of orchardgrass tended to be slightly different among the treatments. The yields of white clover, however, were relatively' high at the 75/25, and showed a severe decrease at the 100/0 in the 2nd half cuts. In the Fe/Mn/Cu/Zn trial, the yields of white clover tended to be relatively high at the Cu and Zn treatments. It was likely to be caused by the balanced Fe/Mn ratio.

• Journal of the Korean Ceramic Society
• /
• v.55 no.1
• /
• pp.55-60
• /
• 2018

In this study, quantum dots composed of $Mn^{2+}$ doped ZnS core and ZnS shell were synthesized using MPA precursor at room temperature. The ZnS: Mn/ZnS quantum dots were prepared by varying the content of MPA in the synthesis of ZnS shells. XRD, Photo-Luminescence (PL), XPS and TEM were used to characterize the properties of the ZnS: Mn/ZnS quantum dots. As a result of PL measurement using UV excitation light at 365 nm, the PL intensity was found to greatly increase when MPA was added at 15 ml, compared to the case with no MPA; the PL peaks shifted from 603 nm to 598 nm. A UV sensor was fabricated by using a sputtering process to form a Pt pattern and placing a QD on the Pt pattern. To verify the characteristics of the sensor, we measured the electrical properties via irradiation with UV, Red, Green, and Blue light. As a result, there were no reactions for the R, G, and B light, but an energy of 3.39 eV was produced with UV light irradiation. For the sensor using ZnS: Mn/ZnS quantum dots, the maximum current (A) value decreased from $4.00{\times}10^{-11}$ A to $2.62{\times}10^{-12}$ A with increasing of the MPA content. As the MPA content increases, the PL intensity improves but the electrical current value dropped because of the electron confinement effect of the core-shell.