• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.1
• /
• pp.14-17
• /
• 2010

$ZnGa_2O_4$ powder were prepared by combustion method and $Mn^{2+}$ ions, a green luminescence activator, and $Cr^{3+}$ ions, a red luminescence activator were separately doped into $ZnGa_2O_4$. The characteristics of the synthesized nano powder were investigated by means of X-ray diffraction (XRD), Scanning Electron Microscope (SEM), and photoluminescence (PL). The various $ZnGa_2O_4$ peaks, with the (311) main peak, appeared at all sintering temperature XRD patterns. The PL specctrums of $ZnGa_2O_4$ powder showed main peak of 425 nm, and maximum intensity at the sintering temperature of $1200^{\circ}C$. SEM images shown that nano sized particles(about 200 nm) were of spherical shape. The characteristics of $ZnGa_2O_4$ containing 0.004 mol $Mn^{2+}$(505 nm, green) and $ZnGa_2O_4$ containg 0.002 mol $Cr^{3+}$ (696 nm, red) were shown to be the best.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.539-542
• /
• 2004

The $ZnGa_2O_4$ phosphor target is synthesized through solid-state reactions at the calcine temperature of $700^{\circ}C$ and sintering temperature of $1300^{\circ}C$ in order to deposit $ZnGa_2O_4$ phosphor thin film by rf magnetron sputtering system. The $ZnGa_2O_4$ phosphor thin film is deposited on Si(100) substrate and prepared $ZnGa_2O_4$ phosphor thin film is annealed by rapid thermal processor(RTP) at $700^{\circ}C$, 15sec. The x-ray diffraction patterns of $ZnGa_2O_4$ phosphor target and thin film show the position of (311) main peak. The cathodoluminescenre(CL) spectrums of $ZnGa_2O_4$ phosphor thin film show main peak of 420nm and maximum intensity at the substrate temperature of $500^{\circ}C$ and annealing temperature of $700^{\circ}C$ 15sec.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.8
• /
• pp.749-753
• /
• 2006

The $ZnGa_2O_4$ phosphor thick films were fabricated using a screen printing method on Si(100) substrates at various sintering temperatures. The XRD patterns show that the $ZnGa_2O_4$ thick films have a (311) main peak and a spinel structure with increasing sintering temperatures. The particle sizes of $ZnGa_2O_4$ phosphor were about 100 nm and the thickness of $ZnGa_2O_4$ thick film was $10{\mu}m$. The CL and PL properties of $ZnGa_2O_4$ showed main peak of 420nm and maximum intensity at the sintering temperature of $900^{\circ}C$. These results indicate that $ZnGa_2O_4$ phosphor thick films hold promise for displays such as plasma display panel and field emission display.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.2
• /
• pp.158-162
• /
• 2009

$Zn_2SiO_4$:Mn green phosphors doped with Ga for PDP were synthesized by solid state reaction method. Photoluminescence measurements showed a new emission peak at around 600 nm for $Zn_2SiO_4$:Mn phosphors doped with Ga. Also, the luminescent color with doping $Ga^{3+}$ in the $Zn_2SiO_4$:Mn phosphors changed to green from yellowish green. Consequently, the new peak and charge of the luminescent color in the $Zn_2SiO_4$:Mn, Ga phosphors were attributed to $^2E{\rightarrow}^6A_2$ transition of $Mn^{4+}$.

• Electrical & Electronic Materials
• /
• v.9 no.10
• /
• pp.1040-1046
• /
• 1996

Low voltage phosphor, ZnGa$_{2}$O$_{4}$:Mn, was synthesized and sintered at the high temperature in Ar or vacuum. By XRD analysis, it is confirmed that poly crystalline ZnGa$_{2}$O$_{4}$:Mn solid solution was formed. From EPMA analysis of the samples prepared in Ar and vacuum, the change of oxygen content was investigated and as a result, it was observed that the oxygen amounts were reduced in ZnGa$_{2}$O$_{4}$:Mn prepared in vacuum. It caused the deficiency in oxygen amounts in the phosphor and then consequently, it results in the formation of the energy level near 513 nm. It contributes to the improvement of the brightness of ZnGa$_{2}$O$_{4}$:Mn.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.26 no.3
• /
• pp.109-114
• /
• 2016

Monodispersed $ZnGa_2O_4$ microspheres were synthesized by a facile two-step process consisting of a solvothermal method and calcination process. The prepared monodispersed $ZnGa_2O_4$ microspheres were aggregated into 3D microstructures by self-assembly with a large number of small $ZnGa_2O_4$ particles generated in nucleation. This nucleation and self-assembly making hierarchical microstructures were depended on the concentration of PEG (polyethylene glycol) due to CAC (critical aggregation concentration) theory. And also we controlled the amount of zinc acetate to make pure $ZnGa_2O_4$ phase. Additionally, to fix the optimized calcination condition, sample was characterized by TG-DTA to prove the thermal property in the calcination process and by FT-IR to identify the changes of functional group bonding between each element of the $ZnGa_2O_4$ precursor and oxide calcined at $900^{\circ}C$ for 1 h.

• Transactions on Electrical and Electronic Materials
• /
• v.12 no.1
• /
• pp.11-15
• /
• 2011

In this study, $ZnGa_2O_4$ phosphors in its application to field emission displays and electroluminescence were synthesized through the precipitation method and $Mn^{2+}$ ions. A green luminescence activator, $Cr^{3+}$ ions, and a red luminescence activator were separately doped into $ZnGa_2O_4$, which was then screen printed to an indium tin oxide substrate. The thick films of the $ZnGa_2O_4$ were deposited with the various thicknesses using nano-sized powder. The best luminescence characteristics were shown at a thickness of 60 ${\mu}m$. Additionally, green-emission $ZnGa_2O_4:Mn^{2+}$ and red-emission $ZnGa_2O_4:Cr^{3+}$ phosphor thick films, which have superior characteristics, were manufactured through the screen-printing method. These results indicate that $ZnGa_2O_4$ phosphors prepared through the precipitation method have wide application as phosphor of the full color emission.

• Journal of the Korean Vacuum Society
• /
• v.15 no.5
• /
• pp.541-546
• /
• 2006

In this study we have investigated cathodoluminescence (CL) and structural properties of thin film $ZnGa_2O_4:Mn$ oxide phosphor by using field emission scanning electron microscopy (FESEM), atomic force microscopy (AFM), photoluminescence (PL), and cathodoluminescence. PL emission peaked at 506 nm was observed from the $ZnGa_2O_4:Mn$ phosphor target and it was attributed to the $^4T_1-^6A_1$ transition in $Mn^{2+}$ ion. The color coordinates of the emission were x = 0.09 and y = 0.67. The $ZnGa_2O_4:Mn$ films showed the excitation spectrum peaked at 294 nm by $Mn^{2+}$ ion absorption. It was found that the higher intensity of CL emission at 505 nm appears to result from the denser and closely-packed structure in $ZnGa_2O_4:Mn$ phosphor films deposited at lower pressures. The CL intensity did not show any systematic dependence on film surface roughness.

• Journal of the Korean Ceramic Society
• /
• v.38 no.2
• /
• pp.112-116
• /
• 2001

고상반응법에 의한 제조한 ZnGa$_2$O$_4$형광체에 Li 및 Tm 원소를 도핑함에 따른 발광특성을 조사하였다. 254nm 여기 하에서, 환원 처리된 ZnGa$_2$O$_4$형광체는 245nm에서 흡수피크와 380nm에서 발광피크를 나타내며, 이는 스피넬 구조에서 Ga$^{3+}$ 이온의 $^4$T$_2$$\longrightarrow$$^4$A$_2$천이에 기인한다. ZnGa$_2$O$_4$형광체에 있어서 Li 및 Tm을 도핑했을 경우가 도핑하지 않은 시료에 비해 발광강도 및 색순도가 개선되었으며, Li 및 Tm을 각각 0.1 mol, 0.01 mol 첨가했을 때 가장 우수한 발광강도 및 색순도 특성을 보였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.301-302
• /
• 2005

The $ZnGa_2O_4$:Cr phosphor was synthesized through solid-state reactions at the various molar ratio of Cr from 0.002 % to 0.01 %. The XRD patterns show that the Cr-doped $ZnGa_2O_4$ has a (311) main peak and a spinel phase. Also the emission wavelength shills from 510 to 705 nm in comparison with $ZnGa_2O_4$:Mn when Cr is doped in $ZnGa_2O_4$. These results indicate that $ZnGa_2O_4$ phosphors hold promise for potential applications in field-emission display devices with high brightness operating in full color regions.