• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.12a
• /
• pp.107-108
• /
• 2006

High $J_c$ $YBa_2Cu_3O_x$, superconducting films were fabricated by MOD method using fluorine-free dichloroacetic acid(DCA) as chelating solvent for preparing precursor solution. DCA-MOD precursor solution was coated on a single crystal (001) $LaAlO_3$(LAO) substrate by a dip coating method with a speed of 25 mm/min. Coated films were calcined at lower temperature up to $500^{\circ}C$ and Conversion heat treatment was performed at various temperatures of $780{\sim}810^{\circ}C$. SEM observations showed that films have very dense microstructures for the films prepared at the temperature higher than $800^{\circ}C$ regardless of diluting solvent; methanol or 2-methoxyethanol. A High critical current density ($J_c$) of 1.28 $MA/cm^2$ (@77 K and self-field) was obtained for the YBCO film prepared using 2-methoxyethanol as a solvent.

• Progress in Superconductivity
• /
• v.5 no.1
• /
• pp.75-79
• /
• 2003

YBCO films were deposited with various thicknesses from 100nm to 1.6$\mu\textrm{m}$ on single crystal $SrTiO_3$ substrates by pulsed laser deposition (PLD). The effects of different deposition conditions, especially different deposition rates by means of changing the pulsed laser frequency up to 200Hz, on the J$_{c}$ value were studied. For YBCO film with the thickness of 200nm, the $J_{c}$ value of $2.1MA/\textrm{cm}^2$ has been achieved under the high deposition rate of 3.2nm/s (190nm/min). The $J_{c}$ can be maintained greater than $1M/\textrm{cm}^2$ with the thickness less than 1$\mu\textrm{m}$. The X-ray analysis was used to examine the texture, crystallization and surface quality. The SEM was employed to analyze the surface of YBCO, and it was shown the surface of YBCO film became rougher with increasing the thickness. There were many large singular outgrowths and networks of outgrowths on the surface of YBCO films which lowered the density of thick YBCO film. The outgrowth network was probably the a-axis YBCO corresponding to XRD $\theta$-2$\theta$scan and $\chi$-scan which were used to characterize a-axis orientation of YBCO film. The reason for J$_{c}$ declining with increasing the thickness was studied and discussed.sed.

• 한국초전도학회:학술대회논문집
• /
• v.9
• /
• pp.392-396
• /
• 1999

Superconducting YBa$_2Cu_3O_{7-{\delta}}$(YBCO) thin films were grown on Hastelloy(Ni-Cr-Mo alloys) with CeO$_2$ buffer layer in-situ by pulsed laser deposition in a multi-target processing chamber. To apply superconducting property on power transmission line, we have deposited YBCO thin film on flexible metallic substrate. However, it is difficult to grow the YBCO films on flexible metallic substrates due to both interdiffusion problem between metallic substrate and superconducting overlayers and non-crystallization of YBCO on amorphous substrate. It is necessary to use a buffer layer to overcome the difficulties. We have chosen CeO$_2$ as a buffer layer which has cubic structure of 5.41 ${\AA}$ lattice parameter and only 0.2% of lattice mismatch with 3.82 ${\AA}$ of a-axis lattice parameter of YBCO on [110] direction of CeO$_2$ In order to enhance the crystallization of YBCO films on metallic substrates, we deposited CeO$_2$ buffer layers with varying temperature and 02 pressure. By XRD, it is observed that dominated film orientation is strongly depending on the deposition temperature of CeO$_2$ layer. The dominated orientation of CeO$_2$ buffer layer is changed from (200) to(111) by increasing the deposition temperature and this transition affects the crystallization of YBCO superconducting film on CeO$_2$ buffered Hastelloy.

• 한국초전도학회:학술대회논문집
• /
• v.10
• /
• pp.66-69
• /
• 2000

We have observed the morphology of YBCO thin films grown on the SrTiO$_3$(100) substrates by the Pulsed Laser Deposition method. AFM and SEM images show that the YBCO grains grow spirally from their own seeds whereas outgrowths are considered to remain unchained as the film thickness increases. The images of various stages of film growth suggest that the outgrowths of 1000${\sim}$2000 ${AA}$ size are mainly formed at the very early stage of film growth. The results of XRD measurement clearly show that even a film of about 10 ${AA}$ thickness already forms orthorhombic YBCO structure although common superconducting resistivity behavior is known to be observed for the films with thickness above 100 ${AA}$.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2003.05a
• /
• pp.359-362
• /
• 2003

Electrophoretic deposition (EPD) of alcohol YBCO suspensions on the Ag wire electrode is studied. Poly(ethylene glycol) was coordinated to a structure formed by the EPD process with YBCO particles. The suspension is characterized in terms of zeta potential and conductivity. The d.c electric fields of 200-300 V/cm are applied for 1-10 min. The optimal condition for the EPD allows modifying the properties and microstructure of the deposited films. Superconducting coatings with nanometer-sized pores and a preferred orientation along the c-axis were prepared from the result with chemically modified precursor solution. In contrast, YBCO coatings of submicrometer-sized pores and randomly orientated grains were prepared from the solution without PEG.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.617-619
• /
• 2001

The effect of the superconducting film thickness on the substrate temperature has been investigated. Superconducting YBCO thin films have been grown on MgO substrates by pulsed laser deposition. The dependence of the orientation of YBCO film on thickness has been investigated by X-ray diffraction technique. X-ray diffraction indicated that the film orientation was changed by increasing the film thickness and by changing the substrate temperature.

• 한국초전도학회:학술대회논문집
• /
• v.9
• /
• pp.138-141
• /
• 1999

For the enhancement of communication system performance, high quality filters are required. Conventional metal filters made of copper can be substituted by high quality high temperature superconductivity(HIS) flms for better performance. In order to reduce the size of the filter for the integration of device in the limited area, we have fabricated hairpin type filters using pulsed laser deposition(PLD) technique. The superconducting YBCO thin films have been grown on MgO substrates by PLD with Nd:YAC laser. The YBCO films were patterned by conventional wet-etching process. We have compared YBCO filters and copper filters which were made with the same spec. Simulated and measured frequency responses reveal that HIS YBCO hairpin type bandpass filters show better performance than copper filters.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.288-291
• /
• 2001

It is very important to select suspension solution for forming electrophoretic deposited YBCO thick mm, because it is heavily affected to its superconducting properties. In this paper, high-temperature superconductor films of $YBa_{2}Cu_{3}O_{7-x}$ were fabricated by electrophoretic deposition (EPD) from alcohol-based suspension such as iso-propanol, iso-butanol, and their mixture. For the formation of YBCO dense and adherent coating on a silver wire by EPD, 1 % PEG(1000) 2 ml, as a additive for making their surface crack-free, was used for electrophoresis. As a results, the cracks were considerably decreased and the superconducting critical current density $(J_e)$ without/with PEG was $1200A/cm^2$ and $2020A/cm^2$, which films deposited in mix iso-propanol and iso-butanol suspension.

• Progress in Superconductivity
• /
• v.9 no.2
• /
• pp.188-192
• /
• 2008

We investigated the size effect on quench development in $Au/YBa_2Cu_3O_7$ (YBCO) thin film meander lines on sapphire substrates. The meander lines were fabricated by patterning YBCO films coated with gold layers. The lines were subjected to simulated AC fault current, and immersed in liquid nitrogen during the experiment. After the initial rapid rise, the resistance increased moderately and then slowly. In 4 inch-diameter meander lines, the period during which the resistance increased moderately was considerably longer than in 2 inch-diameter line. Moderate increase of resistance was originated from quench propagation. The film temperature was about 180 K at the point when the propagation was completed. The rate of resistance increase after the quench completion was not affected by the film size.

• Journal of information and communication convergence engineering
• /
• v.1 no.1
• /
• pp.27-30
• /
• 2003

Electrophoretic deposition (EPD) of alcohol YBCO suspensions on the Ag wire electrode is studied. Poly(ethylene glycol) was coordinated to a structure formed by the EPD process with YBCO particles. The suspension is characterized in terms of zeta potential and conductivity. The d.c electric fields of 200-300 V/cm are applied for 1-10 min. The optimal condition for the EPD allows modifying the properties and microstructure of the deposited films. Superconducting coatings with nanometer-sized pores and a preferred orientation along the c-axis were prepared from the result with chemically modified precursor solution. In contrast, YBCO coatings of submicrometer-sized pores and randomly orientated grains were prepared from the solution without PEG.