• Journal of Welding and Joining
• /
• v.6 no.4
• /
• pp.16-26
• /
• 1988

The effect of carbon content on hot cracking of welded carbon steel was investigated Eight steel plates whose carbon content range from 0.02 to 0.23 percent were welded by autogeous gas tungsten are process. Constant strain was applied to the hot crack test specimen under the strain rate of 0.15 mm per second during welding. The hot cracking susceptibility ws high in the rnage of 0.02-0.05 and 0.12-0.23 percent carbon contents. The critical carbon content immune to hot cracking is in the range from 0.07 to 0.12 percent carbon. By electron probe microanalyser, amanganese segregation was not seen significantly in the whole carbon range. But segregation of silicon was higher in the region of low carbon contents. However, sulphur was segregated remarkably in the region betwen 0.18 and 0.23 percent carbon by peritectic reaction. Very smal lamount of dnedritic structure was observed in the region from 0.02 to 0.05 percent carbon by peritectic reaction. Very small amount of dendritic structure was observed in the region from 0.02 to 0.05 percent carbon but the predominant solidification structure was smooth by cellular growth. The higher the carbon content is, the more the columnar dendritic structure was observed.

• Structural Engineering and Mechanics
• /
• v.38 no.4
• /
• pp.443-457
• /
• 2011

The loss of strength in a structure as a result of cyclic loads over a period of life time is an important phenomenon for the life-cycle analysis. Service loads are accentuated at the areas of stress concentration, mainly at the connection of components. Structural components unavoidably are affected by defects such as surface scratches, surface roughness and weld defects of random sizes, which usually occur during the manufacturing and handling process. These defects are shown to have an important effect on the fatigue life of the structural components by promoting crack initiation sites. The value of equivalent initial flaw size (EIFS) is calculated by using the back extrapolation technique and the Paris law of fatigue crack growth from results of fatigue tests. We try to analyze the effect of EIFS distribution in a multiple site damage (MSD) specimen by using the extended finite element method (XFEM). For the analysis, fatigue tests were conducted on the centrally-cracked specimens and MSD specimens.

• Journal of Welding and Joining
• /
• v.19 no.6
• /
• pp.622-629
• /
• 2001

The aim of this experiment is to establish the method that obtains symmetrically two nuggets in microresistance series spot welding. The sheets of austenite stainless steel STS304 applied to various electronic parts were experimented by the inverter welding power source of polarity controllable type and by the twin head for left and right electrode force to be controlled separately. The experimental results were obtained as follows : 1) When series spot welding was carried out by DC 1 pulse as welding current with same electrode force at left and right, the asymmetry of nuggets was resulted from the larger nugget of the (-) pole because of the Peltier effect. The dynamic resistance of weld spot at left and right was appeared differently according to the growth of nuggets. 2) When AC 1 cycle by welding power source of polarity controllable type was applied, the nuggets were almost symmetrically formed. 3) In a twin head, if the electrode force of (-) pole was larger than that of (+) pole, the diameters of two nuggets became to same. It was confirmed that the dynamic resistance of (-) pole was decreased to the same level as it of (+) pole. 4) Although the forces of left and right electrode were same, and only DC 1 pulse was applied, symmetric nuggets were obtained if the conductivity of (+) pole was lower than it of (-) pole.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.19 no.3
• /
• pp.29-35
• /
• 2020

This paper studies the main parameters of tube-to-bar dissimilar material and shape friction welding for piping materials. The weldability of joint parts was investigated with respect to tensile tests, micro-Vickers hardness, the bond of area, and optical microstructure. The specimens are tested as-welded. Optimal welding conditions are n = 2000 rpm, HP = 50 MPa, UP = 100 MPa, HT = 5 sec, and UT = 10 sec when the metal loss (Mo) is 11 mm. Moreover, the same two materials for friction welding are strongly mixed with a well-combined structure of micro-particles without any molten material, particle growth, or defects. Therefore, the expected result of dissimilar material friction welding includes a reduction of cost and material in the welding process.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.61-61
• /
• 2009

This paper has been performed in order to figure out the reason of failure in T23 weldments used for boiler tube at 550 $^{\circ}C$. Defects such as cracks and cavities occurred in CGHAZ (coarse grain heat-affected-zone) and multi pass of weld metal, and these crack propagated along grain boundary. Microstructure evolution such as grain growth and carbide precipitation was investigated by optical microscope (OM), transmission electron microscope(TEM). Moreover, Auger electron spectroscope (AES) was employed in order to examine segregation along the grain boundaries. There is significant difference in grain size and precipitation distribution in the region where cracking took place. In addition, sulfur segregation was observed. Based on the results of this investigation, it has been possible to establish that this type of cracks were consistent with reheat cracking and creep damage. Selection of optimal filler metal, heat input, and PWHT temperature is required for prevention in order to avoid this type of cracking.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.21 no.6
• /
• pp.910-914
• /
• 2012

In constructing all kinds of equipment and steel structures, discontinuous areas such as weld defects formed in a welded structure tend to generate cracks that will result in damage. In this study, ATOS high-strength steel welding becomes important in butt welding where the tensile strength of the steel is over 80kg/$mm^2$. Structural discontinuities such as joints are more susceptible cracks in part due to their repeated loading and fatigue crack growth. The quality of parts produced depend or the shielded amounts of steel and on the skill of the welders in making strong welds. It is true that there are many factors that can be used to generate a lot of research in this area. However geometry and load conditions due to the combined effects with many issues could be solved through this study. Butt welding material at a plate thickness of 12t in ATOS 80 high-strength steel with a 4 pass, 20l/min, 24V/200A welder is good at making specimens with the quality shown in radiographic testing.

• Journal of Welding and Joining
• /
• v.32 no.2
• /
• pp.14-17
• /
• 2014

Ferritic stainless steels are widely used in the construction industry and in exhaust manifolds due to their low cost and relatively superior stress corrosion cracking resistance and pitting corrosion resistance compared to austenite stainless steels. Ferritic stainless steels are currently welded by various welding process including gas tungsten arc welding (GTAW), electron resistance welding (ERW) and laser beam welding. However, when these stainless steels are welded by fusion welding, some problems occur in the fusion zone (FZ) and heat affected zone (HAZ). First, the ductility of the weld is reduced due to the grain growth in the FZ and HAZ. Second, as its HAZ is frequently sensitized during welding, corrosion resistance deteriorates in this region due to the Cr depletion zone. To prevent these problems, it is recommended that ferritic stainless steels be welded with a low heat input. In this study, recent researches in the view of friction stir welded ferritic stainless steels are briefly reviewed.

• Transactions of Materials Processing
• /
• v.13 no.6 s.70
• /
• pp.484-489
• /
• 2004

This paper employed a systematic analysis using a 2-D hybrid special finite element containing an edge crack in order to describe the fracture behavior of spot-welds in automotive structures. The 2-D hybrid special finite element is derived form a mixed formulation with a complex potential function with the description of the singularity of a stress field. The hybrid special finite element containing an edge crack can give a better description of its singularity with only one hybrid element surrounding one crack. The advantage of this special element is that it can greatly simplify the numerical modeling of the spot welds. Some numerical examples demonstrate the validity and versatility of the present analysis method. The lap-shear, lap-tension and angle-clip specimens are analyzed and some useful fracture parameters such as the stress intensity factor and the initial direction of crack growth are obtained simultaneously.

• Journal of Welding and Joining
• /
• v.13 no.2
• /
• pp.12-24
• /
• 1995

Recently, more researches have been actively performed for the assessment of material degradation and residual-life of elevated temperature plant components, as some of domestic fossil power plants become older than 30 years. In this paper, results of on_site residual life assessment are reported for main steam pipes of Youngwol power station #2 which have operated since 1965. For critical weld locations such as butt welds branch welds, Y_sections and a T-section, replication technique and hardness measurement technique were employed for life_assessment. When cracks were detected by conventional NDT tests, crack growth life was calculated using a computer code. On the other hand, for matrix of pipes, residual life was quantitatively estimated by an analytic method and material degradation was estimated qualitatively using diameter measurement data and grain-boundary etching method. Also, direction in further improvement of on-site life assessment techniques are proposed.

• Journal of Korean Society of Steel Construction
• /
• v.11 no.4 s.41
• /
• pp.339-350
• /
• 1999

In this study, blowholes, a kind of solid defects, were intentionally introduced in transverse butt-welded joints which are widely used for the connection of main members in steel structures to evaluate the fatigue characteristics of these joints with blowholes according to the difference of the size and shape of blowholes, and a series of tests were performed. Static test results proved that the static strength of these joints with blowholes was not affected by their size and shape. From the fatigue test results on these joints with blowholes, the size and shape of blowholes inside the weld metals were strongly affected in fatigue strength, and we suggested the relationship between fatigue strength and their size and shape quantitatively. Also, Using the relationship of fatigue crack growth rate and stress intensity factor range, the fatigue life of transverse butt-welded joints with blowholes can be estimated properly.