Abstract
Recently, more researches have been actively performed for the assessment of material degradation and residual-life of elevated temperature plant components, as some of domestic fossil power plants become older than 30 years. In this paper, results of on_site residual life assessment are reported for main steam pipes of Youngwol power station #2 which have operated since 1965. For critical weld locations such as butt welds branch welds, Y_sections and a T-section, replication technique and hardness measurement technique were employed for life_assessment. When cracks were detected by conventional NDT tests, crack growth life was calculated using a computer code. On the other hand, for matrix of pipes, residual life was quantitatively estimated by an analytic method and material degradation was estimated qualitatively using diameter measurement data and grain-boundary etching method. Also, direction in further improvement of on-site life assessment techniques are proposed.
최근에 국내 화력발전설비도 사용 기간이 30년을 넘게 됨에 따라, 고온설비의 경년열화도 평가 및 수명예측 기술에 대한 연구가 활발해지고 있다. 본 논문에서는 l965년부터 사용되어 노 후된 영월화력발전소 2호기의 주증기 파이프를 대상으로 실시한 열화도 및 수명평가 결과를 보고하였다. 주증기관의 취약부인 맞대기 용접부, 지류 용접부, Y부 및 T부 등의 용접부에 대해 표면복제법, 경도측정법을 사용하여 수명평가를 실시하였으며, 비파괴 검사에 의해 균열이 탐지된 경우에는 수명평가 컴퓨터 코드를 사용하여 균열성장에 의한 잔여수명을 계산하였다. 또한 파이프 모재의 잔여 수명은 해석적 방법에 의해 정량적으로 잔여수명을 계산한 후, 외경 패출량 측정, 입계부식법 등에 의해 재질 열화도를 정성적으로 평가하였다. 본 논문에서 사용한 기법 이외의 방법을 사용하여 수명평가 정확도를 개선하는 방향에 대한 의견도 제시하였다.