• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.8
• /
• pp.658-662
• /
• 2001

This paper describes on the fabrication and characteristics of hot-film type micro-flowsensors integrated with Pt-RTD(resistance thermometer device) and micro-heater on the SOI(Si-on-insulator) membrane and trench structures, in which MGO thin-film was used as medium layer in order to improve adhesion of Pt thin-film to SiO$_2$ layer. Output voltages increased due to increase of heat-loss from sensor to external. The output voltage was 250 nV at N$_2$ flow rate of 2000 sccm/min, heating power of 0.3 W. The response time($\tau$:63%) was about 42 msec when input flow was step-input. The results indicated that micro-flowsensors with the SOI membrane and trench structures have properties of a high-resolution and ow consume power.

• Proceedings of the KIEE Conference
• /
• 2008.10a
• /
• pp.117-118
• /
• 2008

The $V_{1.85}W_{0.15}O_5$ thin films deposited on Pt/Ti/$SiO_2$/Si substrates by RF sputtering method exhibited fairly good TCR and dielectric properties. It was found that film crystallinity, dielectric properties, and TCR properties were strongly dependent upon the annealing temperature. The dielectric constants of the $V_{1.85}W_{0.15}O_5$ thin films annealed at $400^{\circ}C$ were 38.11, with a dielectric loss of 1%, respectively. Also, the TCR values of the $V_{1.85}W_{0.15}O_5$ thin films annealed at $400^{\circ}C$ were about -3.45%/K.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.703-706
• /
• 2002

Piezoelectric thin film such as ZnO and AlN can be applicable to FBAR (Film Bulk Acoustic Resonator) device of thin film type and FBAR can be applicable to MMIC. The characteristic of FBAR device is variable according to the deposition conditions of piezoelectric thin film when preparation of thin film by sputtering method. In this study, we prepared ZnO thin film for FBAR using Facing Targets Sputtering apparatus which can be deposited fine Quality thin film because temperature increase of substrate due to the bombardment of high-energy particles can be restrained. And crystalline and c-axis preferred orientation of ZnO thin film with deposition conditions was investigated by XRD.

• Journal of the Korean Magnetics Society
• /
• v.18 no.1
• /
• pp.32-35
• /
• 2008

Thermally stable diffusion barrier of tungsten carbon nitride(W-C-N) and of tungsten boron carbon nitride(W-B-C-N) thin films have studied to investigate the impurity behaviors of boron and nitrogen. In this paper we newly deposited tungsten boron carbon nitride(W-B-C-N) thin film for various $W_2B$ target power on silicon substrate. The impurities of the 100nm-thick W-C-N and W-B-C-N thin films provide stuffing effect for preventing the inter-diffusion between W-C-N or W-B-C-N thin films and silicon during the high temperature($700^{\circ}C{\sim}1000^{\circ}C$) annealing process.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.87-88
• /
• 2007

반도체 소자가 초고집적화 되어감에 따라 반도체 공정에서 선폭은 줄어들고 박막은 다층화 되어가고 있다. 이와 같은 제조 공정 하에서는 Si 기판과 금속 박막간의 확산이 커다란 문제로 부각되어 왔다. 특히 Cu는 높은 확산성에 의하여 Si 기판과 접합에서 많은 확산에 의한 문제가 발생하게 되며, 또한 선폭이 줄어듦에 따라 고열이 발생하여 실리콘으로 spiking이 발생하게 된다. 이러한 확산을 방지하기 위하여 이 논문에서는 Tungsten - Carbon - Nitrogen (W-C-N)에 Boron (B)을 첨가하였고, Boron 타겟 power을 조절하여 다양한 조성을 가지는 W-B-C-N 확산방지막을 제작하여 각 조성에 따른 증착률을 조서하였고 $1000^{\circ}C$까지 열처리하여 그 비저항을 측정하여 각 특성을 확인하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.566-569
• /
• 2001

In this paper, we investigated the electrical characteristics through DC power at manufacturing the MIS capacitor insulator AIN thin film based on reactive sputtering method. In case of deposition temperature 250$^{\circ}C$, pressure 5mTorr, total flow rate 8sccm(Ar:4sccm N2:4sccm), AIN thin film was deposited with changing DC power. As DC power increses, resistivity is observed a little increase. When AIN thin film is deposited at 100W, the result shows leakage current 10$\^$-8/A/$\textrm{cm}^2$ at 0.1MV/cm. Otherwise, In case of depositing at 150W and 200W, the result shows that the characteristic of leakage current is under 10$\^$-9//$\textrm{cm}^2$ at 0.1MV/cm. In C-V characteristic with DC power, deep depletion phenomenon is observed at inversion region in 100W and 150W. In 200W, that phenomenon, however, was showed to decrease. It shows that the hysterisis increases with being increasing DC power.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.7
• /
• pp.612-616
• /
• 2000

This paper describes on the fabrication and characteristics of hot-film type micro-flowsensors integrated with Pt-RTD(resistance thermometer device) and micro-heater on the Si membrane in which MgO thin-film was used as medium layer in order to improve adhesion of Pt thin-film to SiO$_2$layer. The MgO layer improved adhesion of Pt thin-film to SiO$_2$layer without any chemical reactions to Pt thin-film under high annealing temperatures. Output voltages increased due to increase of heat-loss from sensor to external. The output voltage was 82 mV at $N_2$flow rate of 2000 sccm/min heating power of 1.2 W. The response time($\tau$:63%) was about 50 msec when input flow was stepinput

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.12S
• /
• pp.1175-1180
• /
• 2003

Transformer Coupled Plasma Chemical Vapor Deposited (TCP-CVD) silicon nitride (SiNx) is widely used as a gate dielectric material for thin film transistors (TFT). This paper reports the SiNx films, grown by TCP-CVD at the low temperature (30$0^{\circ}C$). Experimental investigations were carried out for the optimization o(SiNx film as a function of $N_2$/SiH$_4$ flow ratio varying ,3 to 50 keeping rf power of 200 W, This paper presents the dielectric studies of SiNx gate in terms of deposition rate, hydrogen content, etch rate and leakage current density characteristics lot the thin film transistor applications. And also, this work investigated means to decrease the leakage current of SiNx film by employing $N_2$ plasma treatment. The insulator layers were prepared by two step process; the $N_2$ plasma treatment and then PECVD SiNx deposition with SiH$_4$, $N_2$gases.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.50-50
• /
• 2011

The aluminum nitride films were prepared by RF magnetron sputtering using an AlN ceramic target. The crystallinity, grain size, Al-N bonding and thermal conductivity were investigated in dependence on the plasma power densities (4.93, 7.40, 9.87 W/$cm^2$) during sputtering. High thermal conductivity is important properties of A1N passivation layer for functioning properly in thermal inkjet printhead. The crytallinity, grain size, Al-N bonding formation and chemical composition were observed using X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), fourier transform infrared (FTIR) and X-ray photoelectron spectroscopy (XPS), respectively. The AlN thin film was changed from amorphous to crystalline as the power density was increased, and the largest grain size appeared at medium power density. The near stoichiometry Al-N bonding ratio was acquired at medium power density. So, we know that the AlN thin film had better thermal conductivity with crystalline phase and near stoichometry Al-N bonding ratio at 7.40 W/$cm^2$ power density.

• Korean Journal of Materials Research
• /
• v.14 no.6
• /
• pp.402-406
• /
• 2004

$WSi_2$, $TiSi_2$, $CoSi_2$, and $TaSi_2$ are general silicides used today in semiconductor devices. $WSi_2$ thin films have been proposed, studied and used recently in CMOS technology extensively to reduce sheet resistance of polysilicon and $n^{+}$ region. However, there are several serious problems encountered because $WSi_2$ is oxidized and forms a native oxide layer at the interface between $WSi_2$ and $Si_3$$N_4$. In this study, we have introduced 20 $slm-N_2$ gas from top to bottom of the furnace in order to control native oxide films between $WSi_2$ and $Si_3$$N_4$ film. In resulting SEM photographs, we have observed that the native oxide films at the surface of $WSi_2$ film are removed using the long injector system.